CN104384887A - 一种提高铰刀使用寿命的铰刀制造方法 - Google Patents
一种提高铰刀使用寿命的铰刀制造方法 Download PDFInfo
- Publication number
- CN104384887A CN104384887A CN201410480856.3A CN201410480856A CN104384887A CN 104384887 A CN104384887 A CN 104384887A CN 201410480856 A CN201410480856 A CN 201410480856A CN 104384887 A CN104384887 A CN 104384887A
- Authority
- CN
- China
- Prior art keywords
- reamer
- blank
- rough forging
- temperature
- service life
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种提高铰刀使用寿命的铰刀制造方法，属于刀具加工技术领域。其加工步骤为：（1）铰刀材料的准备；（2）毛坯的锻造；（3）锻造毛坯的退火；（4）锻造毛坯的渗碳；（5）锻造毛坯渗碳后的热处理；（6）锻造毛坯的高温正火；（7）锻造毛坯的初加工；（8）热处理；（9）铰刀的深加工。本发明解决了现有铰刀制造用毛坯因盐浴中不纯物质含量过高、脱氧不良、捞渣不彻底导致毛坯淬火脱碳，使得所制得的铰刀使用寿命大大降低的问题，具有方法简单，成本低，加工容易的优点。
Description
技术领域
本发明属于刀具加工技术领域，更具体地说，涉及一种提高铰刀使用寿命的铰刀制造方法。
背景技术
铰孔是孔的精加工方法之一，在生产中应用广泛。而作为铰孔用的铰刀，由于其加工余量小，齿数多，加工精度和表面质量都较高，常用于中小孔的半精加工和精加工。但常常在其制造用毛坯的制造过程中，因盐浴中不纯物质含量过高、脱氧不良、捞渣不彻底导致毛坯淬火脱碳，使得所制得的铰刀使用寿命大大降低。
发明内容
针对现有铰刀制造用毛坯因盐浴中不纯物质含量过高、脱氧不良、捞渣不彻底导致毛坯淬火脱碳，使得所制得的铰刀使用寿命大大降低的问题，本发明提供一种提高铰刀使用寿命的铰刀制造方法，其通过改变铰刀的毛坯组分，并通过退火和渗碳的办法来消除淬火脱碳的问题，使得毛坯得到改善，所制得的铰刀使用寿命得到提高。
为解决上述问题，本发明采用如下的技术方案。
一种提高铰刀使用寿命的铰刀制造方法，包括以下步骤：
（1）铰刀材料的准备：
铰刀毛坯组分的质量百分比为：C：0.65-0.84%、Mn：≦0.60%、Si：≦0.45%、S：≦0.15%、P：≦0.045%，余量为Fe；
（2）毛坯的锻造：
将坯料放在中频感应加热炉中加热到始锻温度，再将加热的坯料放入轧机中利用轧制模具轧成铰刀毛坯；
（3）锻造毛坯的退火：
对经步骤（2）得到的锻造毛坯进行退火，其退火温度为500-530℃，退火时间为7-8小时，在退火后进行炉冷，冷却至220-250℃后进行空冷；
（4）锻造毛坯的渗碳：
将经步骤（3）得到的锻造毛坯放入渗碳介质中，加热到900-940℃，保温8-10小时；
（5）锻造毛坯渗碳后的热处理：
将经步骤（4）得到的锻造毛坯出炉后空冷至800-840℃，进行淬火，淬火温度为950-970℃，然后在200-220℃温度下进行低温回火；
（6）锻造毛坯的高温正火：
对经步骤（5）得到的锻造毛坯进行高温正火，其正火温度为840-860℃，正火时间为3-4小时，在正火后进行炉冷，冷却至350-370℃后进行风冷；
（7）锻造毛坯的初加工：
在车床上进行铰刀的初加工；
（8）热处理：
将经步骤（7）初加工的铰刀，在25分钟内加热到790-810℃，保温35分钟后淬火，油淬，然后在160-190℃温度下进行低温回火；
（9）铰刀的深加工：
先去除表层氧化层，并在磨床上进行精加工。
优选的，所述的步骤（1）中，铰刀毛坯组分的质量百分比为：C：0.75%、Mn：≦0.60%、Si：≦0.45%、S：≦0.15%、P：≦0.045%，余量为Fe。
优选的，所述的步骤（5）中，锻造毛坯出炉后空冷至820℃，进行淬火，淬火温度为960℃，然后在210℃温度下进行低温回火。
相比于现有技术，本发明的有益效果为：
（1）本发明通过改变铰刀的毛坯组分，并通过退火和渗碳的办法来消除淬火脱碳的问题，使得毛坯得到改善，所制得的铰刀使用寿命得到提高，进而节约了成本，提高了生产效率。
（2）本发明方法简单，成本低，加工容易。
具体实施方式
下面结合实施例对本发明进行详细描述。
实施例1
一种提高铰刀使用寿命的铰刀制造方法，包括以下步骤：
（1）铰刀材料的准备：
铰刀毛坯组分的质量百分比为：C：0.75%、Mn：≦0.60%、Si：≦0.45%、S：≦0.15%、P：≦0.045%，余量为Fe。
（2）毛坯的锻造：
将坯料放在中频感应加热炉中加热到始锻温度，再将加热的坯料放入轧机中利用轧制模具轧成铰刀毛坯；
（3）锻造毛坯的退火：
对经步骤（2）得到的锻造毛坯进行退火，其退火温度为520℃，退火时间为7小时，在退火后进行炉冷，冷却至230℃后进行空冷；
（4）锻造毛坯的渗碳：
将经步骤（3）得到的锻造毛坯放入渗碳介质中，加热到930℃，保温9小时；
（5）锻造毛坯渗碳后的热处理：
将经步骤（4）得到的锻造毛坯出炉后空冷至820℃，进行淬火，淬火温度为960℃，然后在210℃温度下进行低温回火；
（6）锻造毛坯的高温正火：
对经步骤（5）得到的锻造毛坯进行高温正火，其正火温度为850℃，正火时间为3小时，在正火后进行炉冷，冷却至360℃后进行风冷；
（7）锻造毛坯的初加工：
在车床上进行铰刀的初加工；
（8）热处理：
将经步骤（7）初加工的铰刀，在25分钟内加热到800℃，保温35分钟后淬火，油淬，然后在180℃温度下进行低温回火；
（9）铰刀的深加工：
先去除表层氧化层，并在磨床上进行精加工。
Claims (3)
1.一种提高铰刀使用寿命的铰刀制造方法，其特征在于以下步骤：
（1）铰刀材料的准备：
铰刀毛坯组分的质量百分比为：C：0.65-0.84%、Mn：≦0.60%、Si：≦0.45%、S：≦0.15%、P：≦0.045%，余量为Fe；
（2）毛坯的锻造：
将坯料放在中频感应加热炉中加热到始锻温度，再将加热的坯料放入轧机中利用轧制模具轧成铰刀毛坯；
（3）锻造毛坯的退火：
对经步骤（2）得到的锻造毛坯进行退火，其退火温度为500-530℃，退火时间为7-8小时，在退火后进行炉冷，冷却至220-250℃后进行空冷；
（4）锻造毛坯的渗碳：
将经步骤（3）得到的锻造毛坯放入渗碳介质中，加热到900-940℃，保温8-10小时；
（5）锻造毛坯渗碳后的热处理：
将经步骤（4）得到的锻造毛坯出炉后空冷至800-840℃，进行淬火，淬火温度为950-970℃，然后在200-220℃温度下进行低温回火；
（6）锻造毛坯的高温正火：
对经步骤（5）得到的锻造毛坯进行高温正火，其正火温度为840-860℃，正火时间为3-4小时，在正火后进行炉冷，冷却至350-370℃后进行风冷；
（7）锻造毛坯的初加工：
在车床上进行铰刀的初加工；
（8）热处理：
将经步骤（7）初加工的铰刀，在25分钟内加热到790-810℃，保温35分钟后淬火，油淬，然后在160-190℃温度下进行低温回火；
（9）铰刀的深加工：
先去除表层氧化层，并在磨床上进行精加工。
2.根据权利要求1所述的一种提高铰刀使用寿命的铰刀制造方法，其特征在于，所述的步骤（1）中，铰刀毛坯组分的质量百分比为：C：0.75%、Mn：≦0.60%、Si：≦0.45%、S：≦0.15%、P：≦0.045%，余量为Fe。
3.根据权利要求1所述的一种提高铰刀使用寿命的铰刀制造方法，其特征在于，所述的步骤（5）中，锻造毛坯出炉后空冷至820℃，进行淬火，淬火温度为960℃，然后在210℃温度下进行低温回火。