CN104356816B - A kind of anticorrosive paint - Google Patents
A kind of anticorrosive paint Download PDFInfo
- Publication number
- CN104356816B CN104356816B CN201410751549.4A CN201410751549A CN104356816B CN 104356816 B CN104356816 B CN 104356816B CN 201410751549 A CN201410751549 A CN 201410751549A CN 104356816 B CN104356816 B CN 104356816B
- Authority
- CN
- China
- Prior art keywords
- parts
- anticorrosive paint
- agent
- coalescents
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of anticorrosive paint, count by weight, be made up of 50 60 parts of zinc acrylate resin, 10 15 parts of coalescents, 10 20 parts of magnesium oxide, 12 22 parts of silicon oxides, 12 parts of ferrum oxides, 58 parts of toluenesulfonic acids, 58 parts of calcium carbonate, 23 parts of suspending agents, 35 parts of alcohols solvents, 12 parts of bonding agents, 46 parts of phenolic aldehyde amine, 12 parts of nitrile rubbers, 0.7 1.2 parts of thickening agents, 0.5 1 parts of defoamer, 0.4 0.8 parts of levelling agents and 20 30 parts of deionized waters.The sulfur resistance of the coating of the present invention is good, antiseptic property is good.
Description
Technical field
The present invention relates to a kind of anticorrosive paint.
Background technology
For some base material, when its exposed outside time, because being corroded by the material in air, base material is easy to cure, thus affects the mechanics of base material, heat-resisting, weather-proof, wear-resisting and decay resistance etc..For this technical problem, how to reduce the sulfuration to base material now with a lot of people in research.One way in which is sprayed coating on base material, and as disclosed a kind of sulfuration resistant coating in the patent documentation of Application No. 200610078245.1, although studying the coating of this aspect now with a lot of people, but the sulfuration resistant of coating could be improved at present.For coating, if antiseptic property is poor, then the effect duration of coating is difficult to ensure that.
Summary of the invention
In order to improve sulfuration resistant performance, improve antiseptic property, the invention provides a kind of anticorrosive paint.
For reaching above-mentioned purpose, a kind of anticorrosive paint, count by weight, be made up of 50-60 part zinc acrylate resin, 10-15 part coalescents, 10-20 part magnesium oxide, 12-22 part silicon oxide, 1-2 part ferrum oxide, 5-8 part toluenesulfonic acid, 5-8 part calcium carbonate, 2-3 part suspending agent, 3-5 part alcohols solvent, 1-2 part bonding agent, 4-6 part phenolic aldehyde amine, 1-2 part nitrile rubber, 0.7-1.2 part thickening agent, 0.5-1 part defoamer, 0.4-0.8 part levelling agent and 20-30 part deionized water.
Further, described coalescents is butyl glycol ether.
Further, described suspending agent is lithium bentonite.
Further, described bonding agent be ratio of weight and number be phenolic resin and the Colophonium of 3:1.
Further, described thickening agent is polyvinyl butyral.
Further, described defoamer is broken bubble polysiloxane solution.
Further, described levelling agent is terminal groups modification organosilicon.
The invention has the beneficial effects as follows: after coating is sprayed onto on base material, when the sulfur in air touches paint film, under the effect of toluenesulfonic acid, the product that zinc acrylate resin, magnesium oxide generate after reacting with sulfurous gas remains in coating, prevents sulfurous gas directly to contact with substrate interface.It is suspending agent with lithium bentonite, this bentonite is with natural calcium base bentonite as raw material, through a kind of mineral material that artificial lithiumation modification is prepared, it can form colloidal material with alcohols solvent under the initiation of deionized water, the expansion thickening ability obtained, phenolic resin and Colophonium is selected to make binding agent, phenolic resin room temperature cohesive force is strong, coating can be made to obtain high normal temperature surface intensity, but gas forming amount is bigger, addition big coating when lighting easy to crack and easily cause base material produce gas hole defect, Colophonium is the most easy to crack after coating is lighted.Therefore, use phenolic resin and a small amount of Colophonium with the use of, be possible not only to reduce the addition of binding agent, improve the adhesion strength of coating, and carrier viscosity can be improved so that it is sulfur resistance is more preferable.Phenolic aldehyde amine as firming agent, can fast setting at low ambient temperatures, and there is good antiseptic property.The membership that adds of a small amount of nitrile rubber improves antiseptic property further, improves impact resistance.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention is further elaborated.
Anticorrosive paint, count by weight, be made up of 50-60 part zinc acrylate resin, 10-15 part coalescents, 10-20 part magnesium oxide, 12-22 part silicon oxide, 1-2 part ferrum oxide, 5-8 part toluenesulfonic acid, 5-8 part calcium carbonate, 2-3 part suspending agent, 3-5 part alcohols solvent, 1-2 part bonding agent, 4-6 part phenolic aldehyde amine, 1-2 part nitrile rubber, 0.7-1.2 part thickening agent, 0.5-1 part defoamer, 0.4-0.8 part levelling agent and 20-30 part deionization.Described coalescents is butyl glycol ether.Described suspending agent is lithium bentonite.Described bonding agent be ratio of weight and number be phenolic resin and the Colophonium of 3:1.Described thickening agent is polyvinyl butyral.Described defoamer is broken bubble polysiloxane solution.Described levelling agent is terminal groups modification organosilicon.
Embodiment 1.
(1) weigh 10 parts of coalescents, 10 parts of magnesium oxide, 12 parts of silicon oxides, 1 part of ferrum oxide, 5 parts of toluenesulfonic acids, 5 parts of calcium carbonate, 2 parts of suspending agents, 3 parts of alcohols solvents, 1 part of bonding agent and 20 parts of deionized waters to stir under the rotating speed of the temperature 400 ~ 800r/min of 60-70 DEG C.
(2) weigh 50 parts of zinc acrylate resin, 4 parts of phenolic aldehyde amine, 1 part of nitrile rubber, joined in step (1), and in the water-bath of 90-110 DEG C, react 25-35min while stirring.
(3) weigh 0.7 part of thickening agent, 0.5 part of defoamer, 0.4 part of levelling agent join in step (2), under 200 ~ 400r/min speed conditions, stir 10 ~ 13 minutes;Through being filtrated to get coating.
Embodiment 2.
(1) weigh 15 parts of coalescents, 20 parts of magnesium oxide, 22 parts of silicon oxides, 2 parts of ferrum oxides, 8 parts of toluenesulfonic acids, 8 parts of calcium carbonate, 3 parts of suspending agents, 5 parts of alcohols solvents, 2 parts of bonding agents and 30 parts of deionized waters to stir under the rotating speed of the temperature 400 ~ 800r/min of 60-70 DEG C.
(2) weigh 60 parts of zinc acrylate resin, 6 parts of phenolic aldehyde amine, 2 parts of nitrile rubbers, joined in step (1), and in the water-bath of 90-110 DEG C, react 25-35min while stirring.
(3) weigh 1.2 parts of thickening agents, 1 part of defoamer, 0.8 part of levelling agent join in step (2), under 200 ~ 400r/min speed conditions, stir 10 ~ 13 minutes;Through being filtrated to get coating.
Embodiment 3.
(1) weigh 12 parts of coalescents, 15 parts of magnesium oxide, 17 parts of silicon oxides, 1.5 parts of ferrum oxides, 6.5 parts of toluenesulfonic acids, 7 parts of calcium carbonate, 4 parts of alcohols solvents of 2.5 parts of suspending agents, 1.5 parts of bonding agents and 25 parts of deionized waters to stir under the rotating speed of the temperature 400 ~ 800r/min of 60-70 DEG C.
(2) weigh 55 parts of zinc acrylate resin, 5 parts of phenolic aldehyde amine, 1.5 parts of nitrile rubbers, joined in step (1), and in the water-bath of 90-110 DEG C, react 25-35min while stirring.
(3) weigh 0.9 part of thickening agent, 0.8 part of defoamer, 0.6 part of levelling agent join in step (2), under 200 ~ 400r/min speed conditions, stir 10 ~ 13 minutes;Through being filtrated to get coating.
In the present invention, after coating is sprayed onto on base material, when the sulfur in air touches paint film, under the effect of toluenesulfonic acid, the product that zinc acrylate resin, magnesium oxide generate after reacting with sulfurous gas remains in coating, prevents sulfurous gas directly to contact with substrate interface.It is suspending agent with lithium bentonite, this bentonite is with natural calcium base bentonite as raw material, through a kind of mineral material that artificial lithiumation modification is prepared, it can form colloidal material with alcohols solvent under the initiation of deionized water, the expansion thickening ability obtained, phenolic resin and Colophonium is selected to make binding agent, phenolic resin room temperature cohesive force is strong, coating can be made to obtain high normal temperature surface intensity, but gas forming amount is bigger, addition big coating when lighting easy to crack and easily cause base material produce gas hole defect, Colophonium is the most easy to crack after coating is lighted.Therefore, use phenolic resin and a small amount of Colophonium with the use of, be possible not only to reduce the addition of binding agent, improve the adhesion strength of coating, and carrier viscosity can be improved so that it is sulfur resistance is more preferable.Phenolic aldehyde amine as firming agent, can fast setting at low ambient temperatures, and there is good antiseptic property.The membership that adds of a small amount of nitrile rubber improves antiseptic property further, improves impact resistance.
Claims (6)
1. an anticorrosive paint, it is characterized in that: count by weight, be made up of 50-60 part zinc acrylate resin, 10-15 part coalescents, 10-20 part magnesium oxide, 12-22 part silicon oxide, 1-2 part ferrum oxide, 5-8 part toluenesulfonic acid, 5-8 part calcium carbonate, 2-3 part suspending agent, 3-5 part alcohols solvent, 1-2 part bonding agent, 4-6 part phenolic aldehyde amine, 1-2 part nitrile rubber, 0.7-1.2 part thickening agent, 0.5-1 part defoamer, 0.4-0.8 part levelling agent and 20-30 part deionized water;Described bonding agent be ratio of weight and number be phenolic resin and the Colophonium of 3:1.
Anticorrosive paint the most according to claim 1, it is characterised in that: described coalescents is butyl glycol ether.
Anticorrosive paint the most according to claim 1, it is characterised in that: described suspending agent is lithium bentonite.
Anticorrosive paint the most according to claim 1, it is characterised in that: described thickening agent is polyvinyl butyral.
Anticorrosive paint the most according to claim 1, it is characterised in that: described defoamer is broken bubble polysiloxane solution.
Anticorrosive paint the most according to claim 1, it is characterised in that: described levelling agent is terminal groups modification organosilicon.