CN104327573A - Anticorrosive switch cabinet - Google Patents
Anticorrosive switch cabinet Download PDFInfo
- Publication number
- CN104327573A CN104327573A CN201410552611.7A CN201410552611A CN104327573A CN 104327573 A CN104327573 A CN 104327573A CN 201410552611 A CN201410552611 A CN 201410552611A CN 104327573 A CN104327573 A CN 104327573A
- Authority
- CN
- China
- Prior art keywords
- parts
- protective layer
- mineral oil
- distilled water
- anticorrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anticorrosive switch cabinet, comprising a box body, wherein the outer surface of the box body is coated with a protective layer, and the protective layer consists of the following components in parts by weight: 2-3 parts of hydrogenated mineral oil, 1-2 parts of alkylolamide polyoxyethane ether, 3-4 parts of hexyldecanol, 4-5 parts of film forming agent, 4-5 parts of distilled water, 3-4 parts of red iron oxide, 3-4 parts of aluminum triphosphate, 2-3 parts of dodecanedioic acid, 6-7 parts of talc powder and 1-2 parts of gamma-(methacryloxy) propyl trimethoxy silane. The outer surface of the box body is coated with the protective layer, so that the anticorrosive switch cabinet has good rust, corrosion and water resistance.
Description
Technical field
The present invention relates to anticorrosion switching cabinet.
Background technology
The environment for use of switching cabinet is relatively more severe, needs to carry out antirust, anticorrosion, WATER REPELLENT to it.
Summary of the invention
The object of the present invention is to provide a kind of anticorrosion switching cabinet, its box outer surface is coated with protective layer, antirust, anti-corrosive good water-proof effect.
For achieving the above object, technical scheme of the present invention is a kind of anticorrosion switching cabinet of design, and comprise casing, described box outer surface is coated with protective layer, and described protective layer is grouped into by the one-tenth of following weight part:
2 ~ 3 parts of hydrogenated mineral oil,
1 ~ 2 part of alkylol amide polyethylene oxide ether,
3 ~ 4 parts of hexyl decyl alcohol,
4 ~ 5 parts of membrane-forming agents,
4 ~ 5 parts of distilled water,
3 ~ 4 parts of red iron of oxidation,
3 ~ 4 parts of aluminium triphosphates,
2 ~ 3 parts of bay diacid,
6 ~ 7 parts of talcum powder,
1 ~ 2 part of γ-(methacryloxypropyl) propyl trimethoxy silicane.
Preferably, described protective layer is grouped into by the one-tenth of following weight part:
3 parts of hydrogenated mineral oil,
2 parts of alkylol amide polyethylene oxide ethers,
4 parts of hexyl decyl alcohol,
5 parts of membrane-forming agents,
5 parts of distilled water,
4 parts of red iron of oxidation,
4 parts of aluminium triphosphates,
3 parts of bay diacid,
7 parts of talcum powder,
2 parts of γ-(methacryloxypropyl) propyl trimethoxy silicanes.
Preferably, described protective layer is grouped into by the one-tenth of following weight part:
2 parts of hydrogenated mineral oil,
1 part of alkylol amide polyethylene oxide ether,
3 parts of hexyl decyl alcohol,
4 parts of membrane-forming agents,
4 parts of distilled water,
3 parts of red iron of oxidation,
3 parts of aluminium triphosphates,
2 parts of bay diacid,
6 parts of talcum powder,
1 part of γ-(methacryloxypropyl) propyl trimethoxy silicane.
Preferably, described protective layer is grouped into by the one-tenth of following weight part:
2.3 parts of hydrogenated mineral oil,
1.2 parts of alkylol amide polyethylene oxide ethers,
3.4 parts of hexyl decyl alcohol,
4.5 parts of membrane-forming agents,
4.5 parts of distilled water,
3.4 parts of red iron of oxidation,
3.4 parts of aluminium triphosphates,
2.3 parts of bay diacid,
6.7 parts of talcum powder,
1.2 parts of γ-(methacryloxypropyl) propyl trimethoxy silicanes.
Advantage of the present invention and beneficial effect are: provide a kind of anticorrosion switching cabinet, its box outer surface is coated with protective layer, antirust, anti-corrosive good water-proof effect.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
Anticorrosion switching cabinet, comprises casing, and described box outer surface is coated with protective layer, and described protective layer is grouped into by the one-tenth of following weight part:
3 parts of hydrogenated mineral oil,
2 parts of alkylol amide polyethylene oxide ethers,
4 parts of hexyl decyl alcohol,
5 parts of membrane-forming agents,
5 parts of distilled water,
4 parts of red iron of oxidation,
4 parts of aluminium triphosphates,
3 parts of bay diacid,
7 parts of talcum powder,
2 parts of γ-(methacryloxypropyl) propyl trimethoxy silicanes.
Embodiment 2
Anticorrosion switching cabinet, comprises casing, and described box outer surface is coated with protective layer, and described protective layer is grouped into by the one-tenth of following weight part:
2 parts of hydrogenated mineral oil,
1 part of alkylol amide polyethylene oxide ether,
3 parts of hexyl decyl alcohol,
4 parts of membrane-forming agents,
4 parts of distilled water,
3 parts of red iron of oxidation,
3 parts of aluminium triphosphates,
2 parts of bay diacid,
6 parts of talcum powder,
1 part of γ-(methacryloxypropyl) propyl trimethoxy silicane.
Embodiment 3
Anticorrosion switching cabinet, comprises casing, and described box outer surface is coated with protective layer, and described protective layer is grouped into by the one-tenth of following weight part:
2.3 parts of hydrogenated mineral oil,
1.2 parts of alkylol amide polyethylene oxide ethers,
3.4 parts of hexyl decyl alcohol,
4.5 parts of membrane-forming agents,
4.5 parts of distilled water,
3.4 parts of red iron of oxidation,
3.4 parts of aluminium triphosphates,
2.3 parts of bay diacid,
6.7 parts of talcum powder,
1.2 parts of γ-(methacryloxypropyl) propyl trimethoxy silicanes.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. anticorrosion switching cabinet, is characterized in that, comprises casing, and described box outer surface is coated with protective layer, and described protective layer is grouped into by the one-tenth of following weight part:
2 ~ 3 parts of hydrogenated mineral oil,
1 ~ 2 part of alkylol amide polyethylene oxide ether,
3 ~ 4 parts of hexyl decyl alcohol,
4 ~ 5 parts of membrane-forming agents,
4 ~ 5 parts of distilled water,
3 ~ 4 parts of red iron of oxidation,
3 ~ 4 parts of aluminium triphosphates,
2 ~ 3 parts of bay diacid,
6 ~ 7 parts of talcum powder,
1 ~ 2 part of γ-(methacryloxypropyl) propyl trimethoxy silicane.
2. anticorrosion switching cabinet according to claim 1, is characterized in that, described protective layer is grouped into by the one-tenth of following weight part:
3 parts of hydrogenated mineral oil,
2 parts of alkylol amide polyethylene oxide ethers,
4 parts of hexyl decyl alcohol,
5 parts of membrane-forming agents,
5 parts of distilled water,
4 parts of red iron of oxidation,
4 parts of aluminium triphosphates,
3 parts of bay diacid,
7 parts of talcum powder,
2 parts of γ-(methacryloxypropyl) propyl trimethoxy silicanes.
3. anticorrosion switching cabinet according to claim 1, is characterized in that, described protective layer is grouped into by the one-tenth of following weight part:
2 parts of hydrogenated mineral oil,
1 part of alkylol amide polyethylene oxide ether,
3 parts of hexyl decyl alcohol,
4 parts of membrane-forming agents,
4 parts of distilled water,
3 parts of red iron of oxidation,
3 parts of aluminium triphosphates,
2 parts of bay diacid,
6 parts of talcum powder,
1 part of γ-(methacryloxypropyl) propyl trimethoxy silicane.
4. anticorrosion switching cabinet according to claim 1, is characterized in that, described protective layer is grouped into by the one-tenth of following weight part:
2.3 parts of hydrogenated mineral oil,
1.2 parts of alkylol amide polyethylene oxide ethers,
3.4 parts of hexyl decyl alcohol,
4.5 parts of membrane-forming agents,
4.5 parts of distilled water,
3.4 parts of red iron of oxidation,
3.4 parts of aluminium triphosphates,
2.3 parts of bay diacid,
6.7 parts of talcum powder,
1.2 parts of γ-(methacryloxypropyl) propyl trimethoxy silicanes.