CN104313882A - Cotton fabric crease-resisting finishing agent - Google Patents
Cotton fabric crease-resisting finishing agent Download PDFInfo
- Publication number
- CN104313882A CN104313882A CN201410554279.8A CN201410554279A CN104313882A CN 104313882 A CN104313882 A CN 104313882A CN 201410554279 A CN201410554279 A CN 201410554279A CN 104313882 A CN104313882 A CN 104313882A
- Authority
- CN
- China
- Prior art keywords
- parts
- finishing agent
- cotton fabric
- crease
- urea
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cotton fabric crease-resisting finishing agent. The cotton fabric crease-resisting finishing agent contains the following ingredients in parts by weight: 2 to 3 parts of alkylolamides polyoxy ethanol ether, 1 to 2 parts of methylbenzene, 90 parts of urea-formaldehyde resin, 1 to 2 parts of polyvinylpyrrolidone, 2 to 3 parts of triethanolamine, 8 to 9 parts of potassium nitrate, 2 to 3 parts of N-phenyl-2-naphthylamine and 1 to 2 parts of iso-tridecanol polyoxyethylene ether. After being processed by the cotton fabric crease-resisting finishing agent, the fabric is smooth and not creased; meanwhile, the original color can be maintained, and the color fading can be avoided.
Description
Technical field
The present invention relates to crease-resistant cotton fabric finishing agent.
Background technology
Textile finishing is on fabric, apply a kind of finishing agent, and it can change the surface property of fabric, thus gives fabric special function.
Summary of the invention
The object of the present invention is to provide a kind of crease-resistant cotton fabric finishing agent, after it can make process, fabric is smoothly comfortable, wrinkle resistant, can keep original color and luster simultaneously, can not fade.
For achieving the above object, technical scheme of the present invention is a kind of crease-resistant cotton fabric finishing agent of design, consists of the following composition by weight:
2 ~ 3 parts of alkylolamides polyethylene oxide ethers,
1 ~ 2 part of toluene,
90 parts of urea-formaldehyde resins,
1 ~ 2 part of polyvinylpyrrolidone,
2 ~ 3 parts of triethanolamines,
8 ~ 9 parts of potassium nitrate,
2 ~ 3 parts of N-phenyl-2-naphthylamines,
1 ~ 2 part of isomerous tridecanol polyoxyethylene ether.
Preferably, described crease-resistant cotton fabric finishing agent, consists of the following composition by weight:
2.3 parts of alkylolamides polyethylene oxide ethers,
1.2 parts of toluene,
90 parts of urea-formaldehyde resins,
1.2 parts of polyvinylpyrrolidones,
2.3 parts of triethanolamines,
8.9 parts of potassium nitrate,
2.3 parts of N-phenyl-2-naphthylamines,
1.2 parts of isomerous tridecanol polyoxyethylene ethers.
Preferably, described crease-resistant cotton fabric finishing agent, consists of the following composition by weight:
2 parts of alkylolamides polyethylene oxide ethers,
1 part of toluene,
90 parts of urea-formaldehyde resins,
1 part of polyvinylpyrrolidone,
2 parts of triethanolamines,
8 parts of potassium nitrate,
2 parts of N-phenyl-2-naphthylamines,
1 part of isomerous tridecanol polyoxyethylene ether.
Preferably, described crease-resistant cotton fabric finishing agent, consists of the following composition by weight:
3 parts of alkylolamides polyethylene oxide ethers,
2 parts of toluene,
90 parts of urea-formaldehyde resins,
2 parts of polyvinylpyrrolidones,
3 parts of triethanolamines,
9 parts of potassium nitrate,
3 parts of N-phenyl-2-naphthylamines,
2 parts of isomerous tridecanol polyoxyethylene ethers.
Advantage of the present invention and beneficial effect are: provide a kind of crease-resistant cotton fabric finishing agent, and after it can make process, fabric is smoothly comfortable, wrinkle resistant, can keep original color and luster simultaneously, can not fade.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of crease-resistant cotton fabric finishing agent, consists of the following composition by weight:
2.3 parts of alkylolamides polyethylene oxide ethers,
1.2 parts of toluene,
90 parts of urea-formaldehyde resins,
1.2 parts of polyvinylpyrrolidones,
2.3 parts of triethanolamines,
8.9 parts of potassium nitrate,
2.3 parts of N-phenyl-2-naphthylamines,
1.2 parts of isomerous tridecanol polyoxyethylene ethers.
Embodiment 2
A kind of crease-resistant cotton fabric finishing agent, consists of the following composition by weight:
2 parts of alkylolamides polyethylene oxide ethers,
1 part of toluene,
90 parts of urea-formaldehyde resins,
1 part of polyvinylpyrrolidone,
2 parts of triethanolamines,
8 parts of potassium nitrate,
2 parts of N-phenyl-2-naphthylamines,
1 part of isomerous tridecanol polyoxyethylene ether.
Embodiment 3
A kind of crease-resistant cotton fabric finishing agent, consists of the following composition by weight:
3 parts of alkylolamides polyethylene oxide ethers,
2 parts of toluene,
90 parts of urea-formaldehyde resins,
2 parts of polyvinylpyrrolidones,
3 parts of triethanolamines,
9 parts of potassium nitrate,
3 parts of N-phenyl-2-naphthylamines,
2 parts of isomerous tridecanol polyoxyethylene ethers.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. crease-resistant cotton fabric finishing agent, is characterized in that, consists of the following composition by weight:
2 ~ 3 parts of alkylolamides polyethylene oxide ethers,
1 ~ 2 part of toluene,
90 parts of urea-formaldehyde resins,
1 ~ 2 part of polyvinylpyrrolidone,
2 ~ 3 parts of triethanolamines,
8 ~ 9 parts of potassium nitrate,
2 ~ 3 parts of N-phenyl-2-naphthylamines,
1 ~ 2 part of isomerous tridecanol polyoxyethylene ether.
2. crease-resistant cotton fabric finishing agent according to claim 1, is characterized in that, consist of the following composition by weight:
2.3 parts of alkylolamides polyethylene oxide ethers,
1.2 parts of toluene,
90 parts of urea-formaldehyde resins,
1.2 parts of polyvinylpyrrolidones,
2.3 parts of triethanolamines,
8.9 parts of potassium nitrate,
2.3 parts of N-phenyl-2-naphthylamines,
1.2 parts of isomerous tridecanol polyoxyethylene ethers.
3. crease-resistant cotton fabric finishing agent according to claim 1, is characterized in that, consist of the following composition by weight:
2 parts of alkylolamides polyethylene oxide ethers,
1 part of toluene,
90 parts of urea-formaldehyde resins,
1 part of polyvinylpyrrolidone,
2 parts of triethanolamines,
8 parts of potassium nitrate,
2 parts of N-phenyl-2-naphthylamines,
1 part of isomerous tridecanol polyoxyethylene ether.
4. crease-resistant cotton fabric finishing agent according to claim 1, is characterized in that, consist of the following composition by weight:
3 parts of alkylolamides polyethylene oxide ethers,
2 parts of toluene,
90 parts of urea-formaldehyde resins,
2 parts of polyvinylpyrrolidones,
3 parts of triethanolamines,
9 parts of potassium nitrate,
3 parts of N-phenyl-2-naphthylamines,
2 parts of isomerous tridecanol polyoxyethylene ethers.