CN104292690B - A kind of impact resistance plastic inspection well - Google Patents
A kind of impact resistance plastic inspection well Download PDFInfo
- Publication number
- CN104292690B CN104292690B CN201410468548.9A CN201410468548A CN104292690B CN 104292690 B CN104292690 B CN 104292690B CN 201410468548 A CN201410468548 A CN 201410468548A CN 104292690 B CN104292690 B CN 104292690B
- Authority
- CN
- China
- Prior art keywords
- parts
- inspection well
- plastic inspection
- impact resistance
- stabilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of impact resistance plastic inspection well, the parts by weight of described plastic inspection well constitutive material are: Corvic 30 35 parts, polrvinyl chloride reclaimed materials 25 40 parts, reactive polyamide resin 9 11 parts, acrylic ester impact-resisting modifier ACR2 3 parts, Tissuemat E 26 parts, politef 26 parts, complex stabilizer 28 parts, filler 35 parts, metallic fiber 68 parts, modified polycarbonate 2 parts.Instant invention overcomes the deficiencies in the prior art, by reasonable disposition tubing material composition so that it is case hardness and tensile strength have and improves more by force, can the most adaptively descend adverse circumstances.
Description
Technical field
The present invention relates to plastic inspection well field of material technology, particularly belong to a kind of impact resistance plastic inspection well.
Background technology
According to plastic inspection well standard, material prescription comprises: polyvinyl chloride resin, impact modifying agent, stabilizer, modifier, filler, colorant and external lubricant etc..The main component of plastic inspection well is polrvinyl chloride or polypropylene, it is possible to additionally incorporate other composition to strengthen its thermostability, toughness, ductility etc..Plastic inspection well is mainly used in plumbing, drainage project.Its case hardness of existing plastic inspection well and tensile strength are poor, and service life is short, are not suitable with adverse circumstances and use.
Summary of the invention
For the problems referred to above, it is an object of the invention to provide a kind of impact resistance plastic inspection well, overcome the deficiencies in the prior art, by reasonable disposition tubing material composition, make its case hardness and tensile strength have to improve more by force, can the most adaptively descend adverse circumstances.
The technical solution used in the present invention is as follows:
A kind of impact resistance plastic inspection well, the parts by weight of described plastic pipe constitutive material are: Corvic 30-35 part, polrvinyl chloride reclaimed materials 25-40 part, reactive polyamide resin 9-11 part, acrylic ester impact-resisting modifier ACR2-3 part, Tissuemat E 2-6 part, politef 2-6 part, complex stabilizer 2-8 part, filler 3-5 part, metallic fiber 6-8 part, modified polycarbonate 2 parts.
Described complex stabilizer is stabilizer, plasticizer, fire retardant, foaming agent, processing modified agent composition.
Described stabilizer is Powdery calcium-zinc complex heat stabilizer.
Described plasticizer is dioctyl adipate.
Described packing agent is wood powder, potter's clay, calcium carbonate or white carbon black.
Compared with the prior art, beneficial effects of the present invention is as follows:
The present invention passes through reasonable disposition tubing material composition, adds rational metallic fiber component raw material in composition of raw materials.Make its case hardness and tensile strength have to improve more by force, can the most adaptively descend adverse circumstances.
Detailed description of the invention
Embodiment 1, a kind of impact resistance plastic inspection well, the parts by weight of described plastic inspection well constitutive material are: Corvic 30 parts, polrvinyl chloride reclaimed materials 25 parts, reactive polyamide resin 9 parts, acrylic ester impact-resisting modifier ACR2 part, Tissuemat E 2 parts, politef 2 parts, complex stabilizer 2 parts, filler 3 parts, metallic fiber 6 parts, modified polycarbonate 2 parts；Described complex stabilizer is Powdery calcium-zinc complex heat stabilizer, dioctyl adipate, fire retardant, foaming agent, processing modified agent composition；Described packing agent is wood powder, potter's clay, calcium carbonate or white carbon black.
Embodiment 2, a kind of impact resistance plastic inspection well, the parts by weight of described plastic inspection well constitutive material are: Corvic 35 parts, polrvinyl chloride reclaimed materials 40 parts, reactive polyamide resin 11 parts, acrylic ester impact-resisting modifier ACR3 part, Tissuemat E 6 parts, politef 6 parts, complex stabilizer 8 parts, filler 5 parts, metallic fiber 8 parts, modified polycarbonate 2 parts；Described complex stabilizer is Powdery calcium-zinc complex heat stabilizer, dioctyl adipate, fire retardant, foaming agent, processing modified agent composition；Described packing agent is wood powder, potter's clay, calcium carbonate or white carbon black.
Embodiment 3, a kind of impact resistance plastic inspection well, the parts by weight of described plastic inspection well constitutive material are: Corvic 35 parts, polrvinyl chloride reclaimed materials 30 parts, reactive polyamide resin 10 parts, acrylic ester impact-resisting modifier ACR3 part, Tissuemat E 4 parts, politef 4 parts, complex stabilizer 5 parts, filler 3 parts, metallic fiber 7 parts, modified polycarbonate 2 parts；Described complex stabilizer is Powdery calcium-zinc complex heat stabilizer, dioctyl adipate, fire retardant, foaming agent, processing modified agent composition；Described packing agent is wood powder, potter's clay, calcium carbonate or white carbon black.
Embodiment 4, a kind of impact resistance plastic inspection well, the parts by weight of described plastic inspection well constitutive material are: Corvic 35 parts, polrvinyl chloride reclaimed materials 30 parts, reactive polyamide resin 9 parts, acrylic ester impact-resisting modifier ACR3 part, Tissuemat E 2 parts, politef 4 parts, complex stabilizer 6 parts, filler 4 parts, metallic fiber 4 parts, modified polycarbonate 2 parts；Described complex stabilizer is Powdery calcium-zinc complex heat stabilizer, dioctyl adipate, fire retardant, foaming agent, processing modified agent composition；Described packing agent is wood powder, potter's clay, calcium carbonate or white carbon black.
Preparation method comprises the following steps:
(1) each raw material is weighed by the weight portion of constitutive material in embodiment；
(2) add in extruder after part material stir 8 minutes at 185 DEG C, add remaining raw material, heat 20 minutes at 180 DEG C, then after being added in 170 DEG C and stirring 16 minutes, after blowing is cooled to 40 DEG C, gained material, through moulding process, obtains product.
The performance data of the plastic inspection well of the present embodiment is as follows:
Claims (4)
1. an impact resistance plastic inspection well, it is characterised in that described plastic inspection well
The parts by weight of constitutive material are: Corvic 30-35 part, polrvinyl chloride reclaim
Material 25-40 part, reactive polyamide resin 9-11 part, acrylic ester impact-resisting modifier
ACR 2-3 part, Tissuemat E 2-6 part, politef 2-6 part, complex stabilizer 2-8
Part, filler 3-5 part, metallic fiber 6-8 part, modified polycarbonate 2 parts.
A kind of impact resistance plastic inspection well the most according to claim 1, its feature
Be: described complex stabilizer be stabilizer, plasticizer, fire retardant, foaming agent,
Processing modified agent composition.
A kind of impact resistance plastic inspection well the most according to claim 2, its feature
It is: described stabilizer is Powdery calcium-zinc complex heat stabilizer.
A kind of impact resistance plastic inspection well the most according to claim 2, its feature
It is: described plasticizer is dioctyl adipate.