CN104290158A - Wax cooking process for dehydrating rosewood boards - Google Patents
Wax cooking process for dehydrating rosewood boards Download PDFInfo
- Publication number
- CN104290158A CN104290158A CN201410525520.4A CN201410525520A CN104290158A CN 104290158 A CN104290158 A CN 104290158A CN 201410525520 A CN201410525520 A CN 201410525520A CN 104290158 A CN104290158 A CN 104290158A
- Authority
- CN
- China
- Prior art keywords
- wax
- sheet material
- boards
- thickness
- different
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wax cooking process for dehydrating rosewood boards. The wax cooking process comprises the following steps: (1) classifying boards, namely putting the cut boards which are random in length and width and the same in thickness together, and placing the boards different in thickness in different piles; (2) preparing a wax solution, namely purchasing waxy products which can be used for wax cooking and blending the waxy products and then putting the mixture in a large cooker; (3) wax cooking, namely completely immersing the differently cut boards of the same thickness and the boards different in thickness in the cooker separately, and adjusting the wax cooking temperature and the wax cooking time so that the moisture of the boards is completely displaced with the wax; (4) taking out the finished products, wherein the boards different in thickness are taken out at different movements, the thinner boards can be taken out earlier, and subsequent finish machining can be performed directly on the taken-out boards. The wax cooking process for dehydrating the rosewood boards is simple, good in dehydration effect, and short in time taken, and the products are good in weather fastness, good in quality and stable in properties without cracking or deformation.
Description
Technical field
The present invention relates to blackwood products, be specifically related to a kind of redwood sheet material and anhydrate with boiling ceroplastic.
Background technology
Mahogany furniture refers to the furniture made with classic redwood such as sour branch, rosewoods, be bright clear since general designation to rare hardwood high-quality furniture.In existing life, mahogany furniture is all widely loved by the people as a kind of luxury goods.In the production process of mahogany furniture, for removing the moisture in sheet material, normally put sheet material into baking room or natural air drying, but this can not stop the deformation of furniture completely, because common oven dry or air-dry only to reduce the water content of wood, but can not completely wood be shaped.And wood has wood, may there is deformation in it in larger warm and humid change.And this type of oven drying method generally needs the time of about 18 days, consuming time longer.
Summary of the invention
The object of the present invention is to provide a kind of technique simple, anhydrate effective, consuming time short, product good weatherability, not craze and transfiguration, quality redwood sheet material that is good, stable performance are anhydrated with boiling ceroplastic.
Technical scheme of the present invention is, a kind of redwood sheet material anhydrates with boiling ceroplastic, comprises following processing step:
(1) sheet material classification: sheet material identical for length and width thickness any after sawing sheet is put together, the different sheet material of thickness divides heap placement;
(2) wax liquid configuration: purchase can be used as the waxy product boiling wax, and be placed in large-scale saucepan by allotment;
(3) wax is boiled: distinguished by sheet material different from thickness for sheet material identical for different sawing sheet thickness and be placed on to immersing completely in saucepan, and wax temperature is boiled in adjustment, boils the wax time, the moisture of sheet material is cemented out by wax completely;
(4) finished product is taken out: different according to the thickness of sheet material, the time of taking out sheet material is also different, and sheet material is thinner, and take-off time more early, directly can carry out follow-up fine finishining process to sheet material after taking-up.
In a preferred embodiment of the present invention, described waxy product comprises animal wax and the paraffin such as the vegetable wax such as rice bran wax, palm wax, beeswax, lanocerin.
In a preferred embodiment of the present invention, described in boil wax temperature control at 130-170 DEG C.
In a preferred embodiment of the present invention, it is described that to boil the wax time not identical according to the sheet material different time used yet, it is 24 hours that sheet material below 5mm thickness boils the wax time usually, and it is that to boil the wax time be more than 72 hours for the sheet material of 36-72 hour, more than 15mm that the sheet material of 5mm-15mm boils the wax time usually.
Of the present inventionly anhydrate with boiling ceroplastic for a kind of redwood sheet material, present invention process is simple, anhydrate effective, consuming time short, product good weatherability, not craze and transfiguration, quality are good, stable performance.
Detailed description of the invention
Below preferred embodiment of the present invention is described in detail, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
Of the present inventionly anhydrating with boiling ceroplastic for a kind of redwood sheet material, comprising following processing step:
(1) sheet material classification: sheet material identical for length and width thickness any after sawing sheet is put together, the different sheet material of thickness divides heap placement;
(2) wax liquid configuration: purchase can be used as the waxy product boiling wax, and be placed in large-scale saucepan by allotment;
(3) wax is boiled: distinguished by sheet material different from thickness for sheet material identical for different sawing sheet thickness and be placed on to immersing completely in saucepan, and wax temperature is boiled in adjustment, boils the wax time, the moisture of sheet material is cemented out by wax completely;
(4) finished product is taken out: different according to the thickness of sheet material, the time of taking out sheet material is also different, and sheet material is thinner, and take-off time more early, directly can carry out follow-up fine finishining process to sheet material after taking-up.
Further, described waxy product comprises animal wax and the paraffin such as the vegetable wax such as rice bran wax, palm wax, beeswax, lanocerin.
Further, the temperature of boiling wax described in controls at 130-170 DEG C.
Further, it is described that to boil the wax time not identical according to the sheet material different time used yet, it is 24 hours that sheet material below 5mm thickness boils the wax time usually, and it is that to boil the wax time be more than 72 hours for the sheet material of 36-72 hour, more than 15mm that the sheet material of 5mm-15mm boils the wax time usually.
The thickness of usual sheet material all shorter boils in the wax time, no longer than 5 days at one.
Of the present inventionly anhydrate with boiling ceroplastic for a kind of redwood sheet material, present invention process is simple, anhydrate effective, consuming time short, product good weatherability, not craze and transfiguration, quality are good, stable performance.
The foregoing is only the specific embodiment of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the technical scope disclosed by the present invention; the change can expected without creative work or replacement, all should be encompassed within protection scope of the present invention.Therefore, the protection domain that protection scope of the present invention should limit with claims is as the criterion.
Claims (4)
1. redwood sheet material anhydrates with boiling a ceroplastic, it is characterized in that: comprise following processing step:
(1) sheet material classification: sheet material identical for length and width thickness any after sawing sheet is put together, the different sheet material of thickness divides heap placement;
(2) wax liquid configuration: purchase can be used as the waxy product boiling wax, and be placed in large-scale saucepan by allotment;
(3) wax is boiled: distinguished by sheet material different from thickness for sheet material identical for different sawing sheet thickness and be placed on to immersing completely in saucepan, and wax temperature is boiled in adjustment, boils the wax time, the moisture of sheet material is cemented out by wax completely;
(4) finished product is taken out: different according to the thickness of sheet material, the time of taking out sheet material is also different, and sheet material is thinner, and take-off time more early, directly can carry out follow-up fine finishining process to sheet material after taking-up.
2. redwood sheet material according to claim 1 anhydrates with boiling ceroplastic, it is characterized in that: described waxy product comprises animal wax and the paraffin such as the vegetable wax such as rice bran wax, palm wax, beeswax, lanocerin.
3. redwood sheet material according to claim 1 anhydrates with boiling ceroplastic, it is characterized in that: described in boil wax temperature control at 130-170 DEG C.
4. redwood sheet material according to claim 1 anhydrates with boiling ceroplastic, it is characterized in that: described in boil the wax time not identical according to the sheet material different time used yet, it is 24 hours that sheet material below 5mm thickness boils the wax time usually, it is that to boil the wax time be more than 72 hours for the sheet material of 36-72 hour, more than 15mm that the sheet material of 5mm-15mm boils the wax time usually.