CN104277531A - Anticorrosion latex paint - Google Patents

Anticorrosion latex paint Download PDF

Info

Publication number
CN104277531A
CN104277531A CN201310273453.7A CN201310273453A CN104277531A CN 104277531 A CN104277531 A CN 104277531A CN 201310273453 A CN201310273453 A CN 201310273453A CN 104277531 A CN104277531 A CN 104277531A
Authority
CN
China
Prior art keywords
parts
latex paint
sanitas
emulsion paint
anticorrosion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310273453.7A
Other languages
Chinese (zh)
Inventor
胡浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HAIAN ZHONGLI CHEMICAL INDUSTRY Co Ltd
Original Assignee
HAIAN ZHONGLI CHEMICAL INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HAIAN ZHONGLI CHEMICAL INDUSTRY Co Ltd filed Critical HAIAN ZHONGLI CHEMICAL INDUSTRY Co Ltd
Priority to CN201310273453.7A priority Critical patent/CN104277531A/en
Publication of CN104277531A publication Critical patent/CN104277531A/en
Pending legal-status Critical Current

Abstract

Disclosed anticorrosion latex paint comprises the following raw materials in parts by mass: 100-150 parts of magnesium powder, 3-5 parts of methyl trioctyl ammonium chloride, 8-10 parts of ethanol, 30-40 parts of n-butanol, 1-2 parts of an antiseptic, 80-90 parts of barium sulfate, 2-4 parts of aluminium stearate, 50-80 parts of an antiseptic, 2-3 parts of calcium fluoride, and 300-320 parts of deionized water. The latex paint is small in toxicity, not inflammable, safe in usage, easily available in raw materials, low in cost and strong in covering power, and is applicable to coating of indoor wall surfaces.

Description

A kind of anticorrosive emulsion paint
Technical field
The present invention relates to a kind of emulsion paint, be specifically related to that a kind of cost is low, the anticorrosive emulsion paint of strong covering power.
Background technology
Emulsion paint is also called synthetic resin emulsion coating, is by the one of machine coating, is be that base-material adds the formulated class water-borne coatings of pigment, filler and various auxiliary agent with synthetic resin emulsion.
In prior art, emulsion paint adopts multiple formulations to eliminate harmful organic substance mostly, and ubiquity raw material is complicated and cost is higher, and some environment friendly emulsion paint, while raising environmental-protecting performance, reduces the wear resisting property of emulsion paint, safety performance etc. accordingly.
Summary of the invention
Goal of the invention: the present invention, in order to solve deficiency of the prior art, provides that a kind of cost is low, the anticorrosive emulsion paint of strong covering power.
Technical scheme: a kind of anticorrosive emulsion paint of the present invention, comprise the raw material of following mass fraction: magnesium powder 100-150 part, methyl tricapryl ammonium chloride 3-5 part, ethanol 8-10 part, propyl carbinol 30-40 part, sanitas 1-2 part, barium sulfate 80-90 part, aluminum stearate 2-4 part, sanitas 50-80 part, Calcium Fluoride (Fluorspan) 2-3 part, deionized water 300-320 part.
Beneficial effect: emulsion paint of the present invention has that toxicity is little, nonflammable, use safety and raw material is easy to get, cost is low, strong covering power, is applicable to the application of indoor wall.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1
A kind of anticorrosive emulsion paint, comprises the raw material of following mass fraction: 100 parts, magnesium powder, methyl tricapryl ammonium chloride 3 parts, ethanol 8 parts, propyl carbinol 30 parts, sanitas 1 part, 80 parts, barium sulfate, aluminum stearate 2 parts, sanitas 50 parts, 2 parts, Calcium Fluoride (Fluorspan), deionized water 300 parts.
Embodiment 2
A kind of anticorrosive emulsion paint, comprises the raw material of following mass fraction: 150 parts, magnesium powder, methyl tricapryl ammonium chloride 5 parts, ethanol 10 parts, propyl carbinol 40 parts, sanitas 2 parts, 90 parts, barium sulfate, aluminum stearate 4 parts, sanitas 80 parts, 3 parts, Calcium Fluoride (Fluorspan), deionized water 320 parts.
Embodiment 3
A kind of anticorrosive emulsion paint, comprises the raw material of following mass fraction: 120 parts, magnesium powder, methyl tricapryl ammonium chloride 4 parts, ethanol 9 parts, propyl carbinol 35 parts, sanitas 1.5 parts, 85 parts, barium sulfate, aluminum stearate 3 parts, sanitas 65 parts, 2.5 parts, Calcium Fluoride (Fluorspan), deionized water 310 parts.

Claims (1)

1. an anticorrosive emulsion paint, it is characterized in that: the raw material comprising following mass fraction: magnesium powder 100-150 part, methyl tricapryl ammonium chloride 3-5 part, ethanol 8-10 part, propyl carbinol 30-40 part, sanitas 1-2 part, barium sulfate 80-90 part, aluminum stearate 2-4 part, sanitas 50-80 part, Calcium Fluoride (Fluorspan) 2-3 part, deionized water 300-320 part.
CN201310273453.7A 2013-07-02 2013-07-02 Anticorrosion latex paint Pending CN104277531A (en)