CN104277529A - 一种防污闪涂料 - Google Patents
一种防污闪涂料 Download PDFInfo
- Publication number
- CN104277529A CN104277529A CN201410555304.4A CN201410555304A CN104277529A CN 104277529 A CN104277529 A CN 104277529A CN 201410555304 A CN201410555304 A CN 201410555304A CN 104277529 A CN104277529 A CN 104277529A
- Authority
- CN
- China
- Prior art keywords
- parts
- mica powder
- pollution
- aluminium hydroxide
- catalyzer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防污闪涂料,由以下重量份数的成分组成:纯二氧化钛溶胶100-120份、双氧水10-20份、云母粉14-18份、有机锡25-45份、氢氧化铝20-40份、十溴联苯醚6-12份、三氯乙烯22-34份、有机硅憎水剂15-25份、改性有机硅树脂15-25份、纳米白炭黑1-12份、云母粉5-10份、氢氧化铝5-10份、纳米聚四氟乙烯微粉15-20份、钛白粉1-2份、催化剂0.1-1份、溶剂20-30份。本发明采用聚合物互穿网络结构形成,利用氟化物材料优异的抗静电吸附性和憎水性,以及有机硅材料优良的憎水性使涂层表面明显减少对水珠、尘埃及带电微粒的吸附效应,且有良好的自洁性和耐气候性,有效地达到电力***长期防污闪、防覆冰的目的,能提高瓷绝缘子的污闪电压,有利于提高输电线路运行的可靠性和延长正常的运行周期。
Description
技术领域
本发明属于化工涂料技术领域,具体涉及一种应用于高压输变电设备绝缘层表面的防污闪涂料及其制备方法。
背景技术
随着我国对电力需求的急剧增加,对交直流高压输变电设备的污秽外绝缘水平提出了更高要求。防污闪涂料在高压输变电设备上获得广泛的应用,并起到积极的防污闪效果。防污闪涂料配方的不同,其防粘性,憎水性,绝缘性和阻燃性的差异很大,其抵御不同污染源的侵蚀能力及防污闪的耐久效果也差别很大。
当前的防污闪涂料存在涂层使用寿命短、附着力差等问题,涂料综合性能不能满足超高压电力工程的进一步发展的需要。
发明内容
本发明要解决的技术问题是g服现有的缺陷,提供一种具有良好的自洁性和耐气候性防污闪涂料。为了解决上述技术问题,本发明提供了如下的技术方案:本发明提供了一种防污闪涂料,由以下成分组成:
纯二氧化钛溶胶100-120份、双氧水10-20份、云母粉14-18份、有机锡25-45份、氢氧化铝20-40份、十溴联苯醚6-12份、三氯乙烯22-34份、有机硅憎水剂15-25份、改性有机硅树脂15-25份、纳米白炭黑1-12份、云母粉5-10份、氢氧化铝5-10份、纳米聚四氟乙烯微粉15-20份、钛白粉1-2份、催化剂0.1-1份、溶剂20-30份;
其中所述的改性有机硅树脂的制备步骤如下:
一、硅醇的制备
向四口烧瓶中加入甲基三氯硅烷15~25g,苯基三氯硅烷25~35g,二苯基二氯硅烷20~30g,二甲苯90~105g,搅拌均匀后升温至60~80保持恒温,用滴液漏斗均匀滴加25~40g的去离子水,滴加时注意搅拌均匀,滴加完毕后保温4个小时,然后水洗得到透明的硅醇溶液;
二、有机硅化合物的合成
将步骤一中获得的硅醇溶液用减压蒸馏装置减压蒸馏至固含量为45~55%,加入500CST硅油20g~25g,在150℃下恒温缩合3~5小时,制得粘度为20~100帕·秒的淡黄色或棕色液体;粘度的测定方法为4杯法。
三、树脂成品配制
向步骤二中获得的有机硅化合物液体中加入占其质量分数为4~6%的助剂和质量分数为4~6%的催化剂,搅拌均匀后,喷涂在玻璃上,通过20-50分钟表干,48-72小时实干,即获得所述改性有机硅树脂,其中所述助剂和催化剂没有特殊要求,采用本领域的常规选择即可。
本发明的防污闪涂料与现有技术相比具有以下优点:
本发明采用聚合物互穿网络结构形成,它利用氟化物材料优异的抗静电吸附性和憎水性,以及有机硅材料优良的憎水性使涂层表面明显减少对水珠、尘埃及带电微粒的吸附效应,且有良好的自洁性和耐气候性,有效地达到电力***长期防污闪、防覆冰的目的,能提高瓷绝缘子的污闪电压,有利于提高输电线路运行的可靠性和延长正常的运行周期。
具体实施方式
以下结合实施例,更具体地说明本发明的内容。应当理解,此处所描述的实施例仅用于说明和解释本发明,并不用于限定本发明。
实施例1
本实施例的防污闪涂料包括以下组分
纯二氧化钛溶胶100份、双氧水10份、云母粉14份、有机锡25份、氢氧化铝20份、十溴联苯醚6份、三氯乙烯22份、有机硅憎水剂15份、改性有机硅树脂15份、纳米白炭黑1份、云母粉5份、氢氧化铝5份、纳米聚四氟乙烯微粉15份、钛白粉1份、催化剂0.1份、溶剂20份。
其中所述的改性有机硅树脂的制备步骤如下:
一、硅醇的制备
向四口烧瓶中加入甲基三氯硅烷15g,苯基三氯硅烷25g,二苯基二氯硅烷20g,二甲苯90g,搅拌均匀后升温至60保持恒温,用滴液漏斗均匀滴加25g的去离子水,滴加时注意搅拌均匀,滴加完毕后保温4个小时,然后水洗得到透明的硅醇溶液;
二、有机硅化合物的合成
将步骤一中获得的硅醇溶液用减压蒸馏装置减压蒸馏至固含量为45%,加入500CST硅油20gg,在150℃下恒温缩合3小时,制得粘度为26帕·秒的淡黄色或棕色液体;
三、树脂成品配制
向步骤二中获得的有机硅化合物液体中加入占其质量分数为4%的助剂和质量分数为4%的催化剂,搅拌均匀后,喷涂在玻璃上,通过20分钟表干,48小时实干获得。
实施例2
本实施例的防污闪涂料包括以下组分
纯二氧化钛溶胶120份、双氧水20份、云母粉18份、有机锡45份、氢氧化铝40份、十溴联苯醚12份、三氯乙烯34份、有机硅憎水剂25份、改性有机硅树脂25份、纳米白炭黑12份、云母粉10份、氢氧化铝10份、纳米聚四氟乙烯微粉20份、钛白粉2份、催化剂1份、溶剂30份。
其中所述的改性有机硅树脂的制备步骤如下:
一、硅醇的制备
向四口烧瓶中加入甲基三氯硅烷25g,苯基三氯硅烷30g,二苯基二氯硅烷30g,二甲苯100g,搅拌均匀后升温至70℃时保持恒温,用滴液漏斗均匀滴加30g的去离子水,滴加时注意搅拌均匀,滴加完毕后保温4个小时,然后水洗得到透明的硅醇溶液;
二、有机硅化合物的合成
将步骤一中获得的硅醇溶液用减压蒸馏装置减压蒸馏至固含量为50%,加入500CST硅油24.5g,在150℃下恒温缩合3~5小时,制得粘度为20~100帕·秒的淡黄色或棕色液体;
三、树脂成品配制
向步骤二中获得的有机硅化合物液体中加入占其质量分数为4%的助剂和质量分数为5%的催化剂,搅拌均匀后,喷涂在玻璃上,通过30分钟表干,50小时实干,即可。
实施例3
本实施例的防污闪涂料包括以下组分
纯二氧化钛溶胶110份、双氧水15份、云母粉16份、有机锡35份、氢氧化铝30份、十溴联苯醚9份、三氯乙烯28份、有机硅憎水剂20份、改性有机硅树脂20份、纳米白炭黑6份、云母粉8份、氢氧化8份、纳米聚四氟乙烯微粉18份、钛白粉1.5份、催化剂0.5份、溶剂25份。
其中所述的改性有机硅树脂的制备步骤如下:
一、硅醇的制备
向四口烧瓶中加入甲基三氯硅烷20g,苯基三氯硅烷35g,二苯基二氯硅烷25g,二甲苯105g,搅拌均匀后升温至80保持恒温,用滴液漏斗均匀滴加40g的去离子水,滴加时注意搅拌均匀,滴加完毕后保温4个小时,然后水洗得到透明的硅醇溶液;
二、有机硅化合物的合成
将步骤一中获得的硅醇溶液用减压蒸馏装置减压蒸馏至固含量为55%,加入500CST硅油25g,在150℃下恒温缩合5小时,制得粘度为90帕·秒的淡黄色或棕色液体;
三、树脂成品配制
向步骤二中获得的有机硅化合物液体中加入占其质量分数为6%的助剂和质量分数为6%的催化剂,搅拌均匀后,喷涂在玻璃上,通过30分钟表干,72小时实干,即获得所述改性有机硅树脂,其中所述助剂和催化剂没有特殊要求,采用本领域的常规选择即可。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (2)
1.一种防污闪涂料,其特征是由以下重量份数的成分组成:
纯二氧化钛溶胶100-120份、双氧水10-20份、云母粉14-18份、有机锡25-45份、氢氧化铝20-40份、十溴联苯醚6-12份、三氯乙烯22-34份、有机硅憎水剂15-25份、改性有机硅树脂15-25份、纳米白炭黑1-12份、云母粉5-10份、氢氧化铝5-10份、纳米聚四氟乙烯微粉15-20份、钛白粉1-2份、催化剂0.1-1份、溶剂20-30份;
其中所述的改性有机硅树脂的制备步骤如下:
一、硅醇的制备
向四口烧瓶中加入甲基三氯硅烷15~25g,苯基三氯硅烷25~35g,二苯基二氯硅烷20~30g,二甲苯90~105g,搅拌均匀后升温至60~80保持恒温,用滴液漏斗均匀滴加25~40g的去离子水,滴加完毕后保温4个小时,然后水洗得到透明的硅醇溶液;
二、有机硅化合物的合成
将步骤一中获得的硅醇溶液用减压蒸馏装置减压蒸馏至固含量为45~55%,加入500CST硅油20g~25g,在150℃下恒温缩合3~5小时,制得粘度为20~100帕·秒的淡黄色或棕色液体;
三、树脂成品配制
向步骤二中获得的有机硅化合物液体中加入占其质量分数为4~6%的助剂和4~6%的催化剂,搅拌均匀后,喷涂在玻璃上。
2.如权利要求1所述的防污闪涂料,其特征是由以下重量份数的成分组成:
纯二氧化钛溶胶100份、双氧水10份、云母粉14份、有机锡25份、氢氧化铝20份、十溴联苯醚6份、三氯乙烯22份、有机硅憎水剂15份、改性有机硅树脂15份、纳米白炭黑1份、云母粉5份、氢氧化铝5份、纳米聚四氟乙烯微粉15份、钛白粉1份、催化剂0.1份、溶剂20份。