CN104277454A - Preparation method of high-impact weather-resistant flame-retardant reinforced nylon 6 for high glow-wire - Google Patents

Preparation method of high-impact weather-resistant flame-retardant reinforced nylon 6 for high glow-wire Download PDF

Info

Publication number
CN104277454A
CN104277454A CN201410532881.1A CN201410532881A CN104277454A CN 104277454 A CN104277454 A CN 104277454A CN 201410532881 A CN201410532881 A CN 201410532881A CN 104277454 A CN104277454 A CN 104277454A
Authority
CN
China
Prior art keywords
content
retardant
flame
reinforced nylon
weather
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410532881.1A
Other languages
Chinese (zh)
Inventor
刘淳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHUZHOU HUASHENG NEW MATERIAL TECHNOLOGY Co Ltd
Original Assignee
CHUZHOU HUASHENG NEW MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHUZHOU HUASHENG NEW MATERIAL TECHNOLOGY Co Ltd filed Critical CHUZHOU HUASHENG NEW MATERIAL TECHNOLOGY Co Ltd
Priority to CN201410532881.1A priority Critical patent/CN104277454A/en
Publication of CN104277454A publication Critical patent/CN104277454A/en
Pending legal-status Critical Current

Abstract

The invention discloses a preparation method of high-impact weather-resistant flame-retardant reinforced nylon 6 for a high glow-wire. The high-impact weather-resistant flame-retardant reinforced nylon 6 is prepared from the following raw materials: PA6 resin, a coupling agent KH550, a flexibilizer, a flame retardant, UV, a lubricant, a release agent, an antioxidant and glass fiber. A preparation method of the high-impact weather-resistant flame-retardant reinforced nylon 6 comprises the following steps: S1, mixing PA6 resin, the flexibilizer and the coupling agent for one minute in a mixing machine; S2, adding the flame retardant, the antioxidant, the release agent, UV and the lubricant and mixing for 0.5 minute; S3, discharging; and S4, processing in a twin-screw extruder so as to finally obtain weather-resistant flame-retardant reinforced nylon 6. The high-impact weather-resistant flame-retardant reinforced nylon 6 for the high-glow wire can be used as a material for electrical part products such as terminal blocks, switches and coil frameworks, especially for high-impact weather-resistant flame-retardant electrical accessories of the high glow-wire, has excellent product performance, has the high-rigidity characteristic and is capable of meeting the needs of the materials of the electronic electrical parts.

Description

A kind of preparation method of high glow-wire HI high impact weather-resistance flame-retardant reinforced nylon 6
Invention field
The present invention relates to a kind of preparation method of high glow-wire HI high impact weather-resistance flame-retardant reinforced nylon 6, belong to industrial injection moulding and manufacture field.
Background technology
Polymeric amide-6, namely nylon 6, is PA6 again, have excellent mechanical strength, wear resistance, erosion resistance etc., but its notched Izod impact strength deficiency, weathering resistance, dimensional stability, glowing filament performance has much room for improvement; Electronic apparatus accessory is mainly used in, as terminal board, switch, coil rack etc. as a kind of injectable plastic material; Require that high rigidity, high notched Izod impact strength, high glowing filament ignition temperature GWIT, flame retardant properties are good, weathering resistance performance is good and need good processing characteristics, but directly adopting resins for universal use material or conventional flame retardant modification to be difficult to meet product requirement.
Summary of the invention
The present invention is the problem solving current nylon flame-proof weather-resisting performance deficiency, and then a kind of preparation method of high glow-wire HI high impact weather-resistance flame-retardant reinforced nylon 6 is proposed, be equipped with raw material and comprise: PA6 resin, coupling agent KH550, toughner, fire retardant, UV, lubricant, releasing agent, oxidation inhibitor and glass fibre; Described PA6 resin formulations content is 45-48%; Described coupling agent KH550 content is 0.2-0.5%; Described toughner content is 3-5%; Described flame retardant agent content is 22-28%; Described UV content is 0.5-0.8%; Described lubricant content is 0.2-0.5%; Described releasing agent content is 0.1-0.3%; Described antioxidant content is 0.3-0.5%; Described content of glass fiber is 23-27%.
As preferably, described Nylon 6 viscosity is 2.45; Described toughner is maleic anhydride grafted ethene octene copolymer; Described fire retardant is compound flame redundant; Described glass fibre is alkali free glass fibre; Described oxidation inhibitor is 1010 and 168 in the mixture of 2: 1 ratios; Described lubricant is N, N '-ethylene bis stearamide; Described releasing agent is high-molecular polythene sodium; To be that UV234 and UV622 is composite form described UV.
Making of the present invention has been come by following steps:
S1: first PA6 resin, toughner, coupling agent are put into blender mixed 1 minute;
S2: add fire retardant, oxidation inhibitor, releasing agent, mixed 0.5 minute of lubricant;
S3: discharging;
S4: put into twin-screw extrusion machining, finally obtains weather-resistance flame-retardant reinforced nylon 6.
Invention effect: high glow-wire HI high impact weather-resistance flame-retardant Reinforced Nylon can be used as the material of the electric component products such as terminal board, switch, coil rack, especially the material of the electric fittings that high glow-wire HI high impact weather-resistance flame-retardant requires is applicable to, whole excellent product performance, there is the features such as high rigidity, high impact property, high glow-wire performance, high durable performance, high flame resistance, high-dimensional stability, processibility, the requirement of electric component product material can be met.
The performance index of high glow-wire HI high impact weather-resistance flame-retardant Reinforced Nylon of the present invention: glowing filament flammability index GWFI 960 DEG C of GB/T 5169.12-2006), glowing filament ignition temperature GWIT 900 DEG C of GB/T5169.13-2006). tensile strength 120MPa, flexural strength 220MPa, modulus in flexure 7500Mpa, 13KJ/M during Izod notched impact strength 23 DEG C 2, flame retardant properties 1.6mm, UL94V0, weather resistance (500h), color grade 3-4 level.
Embodiment
A preparation method for high glow-wire HI high impact weather-resistance flame-retardant reinforced nylon 6, is equipped with raw material and comprises: PA6 resin, coupling agent KH550, toughner, fire retardant, UV, lubricant, releasing agent, oxidation inhibitor and glass fibre; Described PA6 resin formulations content is 45-48%; Described coupling agent KH550 content is 0.2-0.5%; Described toughner content is 3-5%; Described flame retardant agent content is 22-28%; Described UV content is 0.5-0.8%; Described lubricant content is 0.2-0.5%; Described releasing agent content is 0.1-0.3%; Described antioxidant content is 0.3-0.5%; Described content of glass fiber is 23-27%.
As preferably, described Nylon 6 viscosity is 2.45; Described toughner is maleic anhydride grafted ethene octene copolymer; Described fire retardant is compound flame redundant; Described glass fibre is alkali free glass fibre; Described oxidation inhibitor is 1010 and 168 in the mixture of 2: 1 ratios; Described lubricant is N, N '-ethylene bis stearamide; Described releasing agent is high-molecular polythene sodium; To be that UV234 and UV622 is composite form described UV.
Making of the present invention has been come by following steps:
S1: first PA6 resin, toughner, coupling agent are put into blender mixed 1 minute;
S2: add fire retardant, oxidation inhibitor, releasing agent, mixed 0.5 minute of lubricant;
S3: discharging;
S4: put into twin-screw extrusion machining, finally obtains weather-resistance flame-retardant reinforced nylon 6.
Heat-processed is that S4 and raw material are put into and extruded the heating of mach whole process, and specific process is as follows: engine speed 400 revs/min, main frame feeding 250 revs/min, additional glass 6, and temperature is set to 180-230 DEG C:
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and when not deviating from spirit of the present invention or essential characteristic, the present invention can be realized in other specific forms.Therefore, no matter from which point, all should example be regarded as exemplary, and be nonrestrictive, scope of the present invention is limited by claims instead of above-mentioned explanation, and all changes be therefore intended in the implication of the equivalency by dropping on claim and scope are included in the present invention.Any Reference numeral in claim should be considered as the claim involved by limiting.

Claims (2)

1. a preparation method for high glow-wire HI high impact weather-resistance flame-retardant reinforced nylon 6, is equipped with raw material and comprises: PA6 resin, coupling agent KH550, toughner, fire retardant, UV, lubricant, releasing agent, oxidation inhibitor and glass fibre; It is characterized in that: described PA6 resin formulations content is 45-48%; Described coupling agent KH550 content is 0.2-0.5%; Described toughner content is 3-5%; Described flame retardant agent content is 22-28%; Described UV content is 0.5-0.8%; Described lubricant content is 0.2-0.5%; Described releasing agent content is 0.1-0.3%; Described antioxidant content is 0.3-0.5%; Described content of glass fiber is 23-27%;
Preparation process:
S1): first PA6 resin, toughner, coupling agent are put into blender mixed 1 minute;
S2): add fire retardant, oxidation inhibitor, releasing agent, UV, mixed 0.5 minute of lubricant;
S3): discharging;
S4): put into twin-screw extrusion machining, weather-resistance flame-retardant reinforced nylon 6 is finally obtained.
2. the preparation method of a kind of high glow-wire HI high impact weather-resistance flame-retardant reinforced nylon 6 according to claim 1, is characterized in that: described Nylon 6 viscosity is 2.45; Described toughner is maleic anhydride grafted ethene octene copolymer; Described fire retardant is compound flame redundant; Described glass fibre is alkali free glass fibre; Described oxidation inhibitor is 1010 and 168 in the mixture of 2: 1 ratios; Described lubricant is N, N '-ethylene bis stearamide; Described releasing agent is high-molecular polythene sodium; To be that UV234 and UV622 is composite form described UV; Heat-processed is that S4 and raw material are put into and extruded the heating of mach whole process, and specific process is as follows: engine speed 400 revs/min, main frame feeding 250 revs/min, additional glass 6, and temperature is set to 180-230 DEG C:
CN201410532881.1A 2014-09-28 2014-09-28 Preparation method of high-impact weather-resistant flame-retardant reinforced nylon 6 for high glow-wire Pending CN104277454A (en)