CN104277382A - Antifouling heat preservation door and window plastic steel profile and preparation method thereof - Google Patents
Antifouling heat preservation door and window plastic steel profile and preparation method thereof Download PDFInfo
- Publication number
- CN104277382A CN104277382A CN201410623624.9A CN201410623624A CN104277382A CN 104277382 A CN104277382 A CN 104277382A CN 201410623624 A CN201410623624 A CN 201410623624A CN 104277382 A CN104277382 A CN 104277382A
- Authority
- CN
- China
- Prior art keywords
- parts
- section bar
- antifouling
- water
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an antifouling heat preservation door and window plastic steel profile. The antifouling heat preservation door and window plastic steel is prepared from the following raw materials in parts by weight: 0.4-0.6 part of polystyrene microsphere, 0.5-1 part of calcium stearate, 0.2-0.6 part of stearic acid, 0.2-0.5 part of barium stearate, 0.4-0.6 part of magnesium nitrate, 2-3 parts of fluoric (meth)acrylate, 3-4 parts of talcum powder, 3-4 parts of siloxane-containing (meth)acrylate monomer, 13-18 parts of nanosilicon dioxide, 0.4-0.6 part of ammonium persulphate, 90-100 parts of SG-5PVC, 10-14 parts of enhancing auxiliary and 20-30 parts of water. The antifouling heat preservation door and window plastic steel profile has the advantages that fluoric (meth)acrylate, siloxane-containing (meth)acrylate monomer and nanosilicon dioxide are added, so that the profile has good antifouling property, good toughness and high strength; polystyrene microsphere is added, so that heat preservation property of the profile is enhanced; by adopting the enhancing auxiliary, strength, toughness and ageing-resistant performance of the plastic steel profile can be enhanced.
Description
Technical field
The invention belongs to plastic-steel section bar field, particularly relate to a kind of antifouling & insulation plastic-steel door window section bar and preparation method thereof.
Background technology
Plastic-steel section bar is called for short plastic-steel, and main chemical compositions is PVC, is therefore also PVC profile.Be a kind of novel material of construction be widely used, because its physicals is as rigidity, elasticity, corrosion-resistant, ageing resistance is excellent, and being typically used as is the good surrogate of the non-ferrous metals such as copper, zinc, aluminium.
In building construction, be mainly used in push-and-pull, the application of horizontally-opening windows and doors, guardrail, tubing and ceiling material, be also widely used in motor car engine protecting sheet aspect by new technical process process; not only lightweight; and good toughness, there is firm advantageous property, be sometimes also referred to as alloy plastic-steel.
Although plastic-steel material widespread use, along with the progress of society, its performance be improved constantly, the performances such as such as intensity, toughness, thermotolerance, heat retaining property, sound-proofing, static resistance, ultra-violet resistance.
And China's plastic-steel section bar overwhelming majority section bar inferior uses lead salt stabilizer, finished product lead tolerance is between 0.6%-1.2%.Lead is a kind of harmful material, when section bar inferior is aging, can separate out leaded dust, lead content in blood can be made to exceed standard, even lead poisoning after Long Term Contact.Therefore need the security improving plastic-steel section bar, do not raise the cost simultaneously.
Summary of the invention
The object of the present invention is to provide a kind of antifouling & insulation plastic-steel door window section bar and preparation method thereof, this plastic-steel section bar has good antifouling property, and good toughness, intensity are high, good heat insulating.
Technical scheme of the present invention is as follows:
A kind of antifouling & insulation plastic-steel door window section bar, is characterized in that being made up of the raw material of following weight part: polystyrene microsphere 0.4-0.6, calcium stearate 0.5-1, stearic acid 0.2-0.6, barium stearate 0.2-0.5, magnesium nitrate 0.4-0.6, fluorine-containing (methyl) acrylate 2-3, talcum powder 3-4, (methyl) acrylate monomer 3-4 of silicone-containing, nano silicon 13-18, ammonium persulphate 0.4-0.6, SG-5PVC90-100, reinforcing aids 10-14, water 20-30;
Described reinforcing aids is made up of the raw material of following weight part: polynite 6-8, silane coupling agent kh-550 0.3-0.4, four acicular type zinc oxide crystal whisker 5-6, SG-5PVC powder 3-4, nano titanium oxide 2-3, carbon nanotube 0.4-0.6, nanometer boron fibre 0.3-0.5, tetraethoxy 2-3, ethanol 20-25, water 10-13; Preparation method is: be added to the water by silane coupling agent kh-550, add polynite after stirring, and adds nano titanium oxide, carbon nanotube while stirring, magnetic agitation 1-2 hour, dries, pulverizes, cross 100 mesh sieves, obtain powder; Added in ethanol by tetraethoxy and dissolve, then add described powder and other remaining components, magnetic agitation 30-40 minute, is heated to 80-90 DEG C, does not stop to be stirred to ethanol and evaporates completely, pulverizes, to obtain final product.
The preparation method of described antifouling & insulation plastic-steel door window section bar, is characterized in that comprising the following steps:
(1) (methyl) acrylate monomer of fluorine-containing (methyl) acrylate, silicone-containing is added to the water, talcum powder is added again after stirring, warming while stirring is to 75-85 DEG C, add ammonium persulphate again, stirring reaction 2-3 hour, spraying dry, obtains particle;
(2) particle that (1) step obtains is mixed with other remaining components, with high-speed mixer mixing 5-7 minute at 110-120 DEG C, be cooled to room temperature, discharging, obtain Preblend;
(3) twin screw extruder is sent in the Preblend (2) step obtained, and extruder screw speed adjustment is 10-15 rev/min, and barrel and head temperature are 160-180 DEG C, extrusioning shaping, and water-cooled process, obtains section bar;
(4) section bar (3) step obtained sends into-15 to-30 DEG C, cools 15-20 second under vacuum environment, then through traction, shaping, to obtain final product.
Beneficial effect of the present invention
Plastic-steel section bar of the present invention, by adding fluorine-containing (methyl) acrylate, (methyl) acrylate monomer of silicone-containing, nano silicon, makes section bar have good antifouling property, and good toughness, intensity are high; By adding polystyrene microsphere, add the heat-insulating property of section bar; The application of the invention reinforcing aids, the intensity of plastic-steel section bar, toughness and ageing-resistant performance can be increased.
Embodiment
A kind of antifouling & insulation plastic-steel door window section bar, is made up of the raw material of following weight part (kilogram): polystyrene microsphere 0.5, calcium stearate 0.8, stearic acid 0.4, barium stearate 0.4, magnesium nitrate 0.5, fluorine-containing (methyl) acrylate 2.5, talcum powder 3.5, (methyl) acrylate monomer 3.5 of silicone-containing, nano silicon 15, ammonium persulphate 0.5, SG-5PVC95, reinforcing aids 12, water 25;
Described reinforcing aids is made up of the raw material of following weight part (kilogram): polynite 7, silane coupling agent kh-550 0.3, four acicular type zinc oxide crystal whisker 5.5, SG-5PVC powder 3.5, nano titanium oxide 2.5, carbon nanotube 0.5, nanometer boron fibre 0.4, tetraethoxy 2.5, ethanol 23, water 12; Preparation method is: be added to the water by silane coupling agent kh-550, add polynite after stirring, and adds nano titanium oxide, carbon nanotube while stirring, magnetic agitation 1.5 hours, dries, and pulverizes, and crosses 100 mesh sieves, obtains powder; Added in ethanol by tetraethoxy and dissolve, then add described powder and other remaining components, magnetic agitation 35 minutes, is heated to 85 DEG C, does not stop to be stirred to ethanol and evaporates completely, pulverizes, to obtain final product.
The preparation method of described antifouling & insulation plastic-steel door window section bar, comprises the following steps:
(1) (methyl) acrylate monomer of fluorine-containing (methyl) acrylate, silicone-containing is added to the water, adds talcum powder again after stirring, warming while stirring to 80 DEG C, add ammonium persulphate again, stirring reaction 2.5 hours, spraying dry, obtains particle;
(2) particle that (1) step obtains is mixed with other remaining components, at 115 DEG C, mix 6 minutes with high-speed mixer, be cooled to room temperature, discharging, obtain Preblend;
(3) twin screw extruder is sent in the Preblend (2) step obtained, and extruder screw speed adjustment is 13 revs/min, and barrel and head temperature are 170 DEG C, extrusioning shaping, and water-cooled process, obtains section bar;
(4) section bar (3) step obtained sends into-20 DEG C, cools 18 seconds under vacuum environment, then through traction, shaping, to obtain final product.
Experimental data:
After tested, the bending elastic modulus of this plastic-steel section bar is 2870MPa, and simple beam impact strength is 23J/ ㎡, and Dimensional shrinkage under heat is 1.1%, bubble-free, pit, slight crack in 150 DEG C of heating temperatures tests.
Claims (2)
1. an antifouling & insulation plastic-steel door window section bar, is characterized in that being made up of the raw material of following weight part: polystyrene microsphere 0.4-0.6, calcium stearate 0.5-1, stearic acid 0.2-0.6, barium stearate 0.2-0.5, magnesium nitrate 0.4-0.6, fluorine-containing (methyl) acrylate 2-3, talcum powder 3-4, (methyl) acrylate monomer 3-4 of silicone-containing, nano silicon 13-18, ammonium persulphate 0.4-0.6, SG-5PVC90-100, reinforcing aids 10-14, water 20-30;
Described reinforcing aids is made up of the raw material of following weight part: polynite 6-8, silane coupling agent kh-550 0.3-0.4, four acicular type zinc oxide crystal whisker 5-6, SG-5PVC powder 3-4, nano titanium oxide 2-3, carbon nanotube 0.4-0.6, nanometer boron fibre 0.3-0.5, tetraethoxy 2-3, ethanol 20-25, water 10-13; Preparation method is: be added to the water by silane coupling agent kh-550, add polynite after stirring, and adds nano titanium oxide, carbon nanotube while stirring, magnetic agitation 1-2 hour, dries, pulverizes, cross 100 mesh sieves, obtain powder; Added in ethanol by tetraethoxy and dissolve, then add described powder and other remaining components, magnetic agitation 30-40 minute, is heated to 80-90 DEG C, does not stop to be stirred to ethanol and evaporates completely, pulverizes, to obtain final product.
2. the preparation method of antifouling & insulation plastic-steel door window section bar according to claim 1, is characterized in that comprising the following steps:
(1) (methyl) acrylate monomer of fluorine-containing (methyl) acrylate, silicone-containing is added to the water, talcum powder is added again after stirring, warming while stirring is to 75-85 DEG C, add ammonium persulphate again, stirring reaction 2-3 hour, spraying dry, obtains particle;
(2) particle that (1) step obtains is mixed with other remaining components, with high-speed mixer mixing 5-7 minute at 110-120 DEG C, be cooled to room temperature, discharging, obtain Preblend;
(3) twin screw extruder is sent in the Preblend (2) step obtained, and extruder screw speed adjustment is 10-15 rev/min, and barrel and head temperature are 160-180 DEG C, extrusioning shaping, and water-cooled process, obtains section bar;
(4) section bar (3) step obtained sends into-15 to-30 DEG C, cools 15-20 second under vacuum environment, then through traction, shaping, to obtain final product.