CN104275032A - Tough active carbon filtration material applied to air conditioner and preparation method of tough active carbon filtration material - Google Patents
Tough active carbon filtration material applied to air conditioner and preparation method of tough active carbon filtration material Download PDFInfo
- Publication number
- CN104275032A CN104275032A CN201410467983.XA CN201410467983A CN104275032A CN 104275032 A CN104275032 A CN 104275032A CN 201410467983 A CN201410467983 A CN 201410467983A CN 104275032 A CN104275032 A CN 104275032A
- Authority
- CN
- China
- Prior art keywords
- tough
- parts
- active carbon
- filtration material
- carbon filtration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a tough active carbon filtration material applied to an air conditioner. The tough active carbon filtration material applied to the air conditioner is characterized by being prepared from the following raw materials in parts by weight: 135-145 parts of wooden activated carbon, 1-1.5 parts of fatty alcohol-polyoxyethylene ether, 1-2 parts of sodium pyrophosphate, 2-3 parts of cerium oxide, 6-8 parts of wheat meal, 1.5-3 parts of sodium alginate, 2-3 parts of puffed corn starch, 1-2 parts of sodium tripolyphosphate, 2.5-3.5 parts of polyethylene glycol, 12-14 parts of zircon power, 4-6 parts of an adsorption additive and a proper amount of water. According to the tough active carbon filtration material applied to the air conditioner, sticky materials such as sodium alginate and puffed corn starch are added into the tough active carbon filtration material, so that the toughness of the active carbon is improved; the tough active carbon filtration material is solid and durable; in addition, fatty alcohol-polyoxyethylene ether and the like are added into the tough active carbon filtration material; due to the adoption of the characteristic of forming pores in the high-temperature process and the cooperation of the adsorption additive, the adsorption efficiency is improved; poisonous and harmful gases such as powerful formaldehyde and benzene can be effectively removed; the purpose of purifying and freshening air is achieved; according to the tough active carbon filtration material, the process is simple and raw materials are easily available; the prepared tough active carbon filtration material is tough in texture, solid and durable.
Description
Technical field
The present invention relates to a kind of filtering material and preparation method thereof, particularly a kind of strong but pliable in texture carbon leaching material for air-conditioning and preparation method thereof.
Background technology
Pollutant in current air is the gas, vehicle exhaust, the toxic and harmful that produces in production that produce of industrial fuel burning mainly.Also have in people's life and many times need to remove toxin, such as air conditioning filter has a lot of bacterium, toxin on the net, and newly-decorated has the harmful substances such as formaldehyde, all needs to remove toxin.All removing toxin often uses adsorbent at present, mainly contains silica gel, activated alumina, active carbon, molecular sieve etc., also has in addition for the absorption of certain compositional selecting and the sorbing material of development.But the most limited sorption capacity of these adsorbents, needs to study different adsorbents for different requirements, plays best effect.Meanwhile, find new raw material, to strengthen adsorption effect, cost-saving.People are for urgently craving for healthy air, and the market of air purifier is unprecedentedly wide, and the air purifier on market normally filters deficiency or poor effect, and the good cost of effect is high especially again.
Active carbon with high specific surface area has loose structure, various organic matter and inorganic matter can be adsorbed, have the advantages that adsorption capacity is large, adsorption rate is fast, it is a kind of high-efficiency adsorbent of high-quality, the present invention adds many kinds of substance and carries out modification to active carbon, obtains the strong but pliable in texture carbon leaching material of fine and closely woven porous.
Summary of the invention
The object of this invention is to provide a kind of strong but pliable in texture carbon leaching material for air-conditioning and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
The strong but pliable in texture carbon leaching material for air-conditioning, is made up of the raw material of following weight portion: wood activated charcoal 135-145, AEO 1-1.5, sodium pyrophosphate 1-2, cerium oxide 2-3, wheat flour 6-8, sodium alginate 1.5-3, expanded corn starch 2-3, sodium phosphate trimer 1-2, polyethylene glycol 2.5-3.5, zirconium English powder 12-14, adsorption aid 4-6, water are appropriate;
Described adsorption aid is made up of the raw material of following weight portion: pinecone 12-14, walnut shell 9-11, attapulgite 12-14, molybdenum carbide 2-4, bamboo fibre 2-3, river shell powder 3-5, manganese dioxide 2-3, lemon 0.5-0.8, malic acid 0.8-1; Preparation method is by the pinecone, walnut shell dry 1-1.5 hour under 100 DEG C of-120 DEG C of conditions, be ground into 40-60 order powder, then add suitable quantity of water to stir with all the other residual components except bamboo fibre, lemon, form purees, then the retort putting into 400 DEG C-500 DEG C carbonizes 2-3 hour, is ground into 80-100 order powder after taking out cooling, adds bamboo fibre and pure water grinding 1-2 hour, spraying dry, is finally sprayed at powder surface by lemon.
A kind of strong but pliable in texture carbon leaching material for air-conditioning of the present invention, be made up of following concrete steps:
(1) appropriate water is added by wheat flour, sodium alginate, expanded corn starch, polyethylene glycol, zirconium English powder, slurry is made in continuous stirring, then AEO, sodium pyrophosphate, cerium oxide is added, be heated to 45 DEG C-60 DEG C, insulation also constantly stirs 1.5-2.5 hour, obtains mixed slurry stand-by;
(2) wood activated charcoal pulverizing is mixed with mixed slurry, be placed in Muffle furnace at 400 DEG C ~ 500 DEG C, activate 70 ~ 90 minutes, after cooling, be ground into 100-120 order powder;
(3) will add all the other residual components in powder, namely mixing and stirring obtains filtering material.
The invention has the beneficial effects as follows: the present invention adds the toughness of the tool such as sodium alginate, expanded corn starch sticking material enhanced activity charcoal, durable, add AEO etc., in the process through high temperature, form the characteristic of porous, coordinate adsorption aid again, improve adsorption efficiency, can effectively remove the toxic and harmfuls such as strong formaldehyde, benzene, reach the object of purification fresh air, present invention process is simple, raw material is easy to get, strong but pliable in texture, durable.
Specific embodiments
Below by instantiation, the present invention is described in detail.
The strong but pliable in texture carbon leaching material for air-conditioning, is made up of the raw material of following weight portion (kilogram): wood activated charcoal 135, AEO 1, sodium pyrophosphate 1, cerium oxide 2, wheat flour 6, sodium alginate 1.5, expanded corn starch 2, sodium phosphate trimer 1, polyethylene glycol 2.5, zirconium English powder 12, adsorption aid 4, water are appropriate;
Described adsorption aid is made up of the raw material of following weight portion (kilogram): the pinecone 12, walnut shell 9, attapulgite 12, molybdenum carbide 2, bamboo fibre 2, river shell powder 3, manganese dioxide 2, lemon 0.5, malic acid 0.8; Preparation method is by the pinecone, walnut shell dry 1-1.5 hour under 100 DEG C of-120 DEG C of conditions, be ground into 40-60 order powder, then add suitable quantity of water to stir with all the other residual components except bamboo fibre, lemon, form purees, then the retort putting into 400 DEG C-500 DEG C carbonizes 2-3 hour, is ground into 80-100 order powder after taking out cooling, adds bamboo fibre and pure water grinding 1-2 hour, spraying dry, is finally sprayed at powder surface by lemon.
A kind of strong but pliable in texture carbon leaching material for air-conditioning of the present invention, be made up of following concrete steps:
(1) appropriate water is added by wheat flour, sodium alginate, expanded corn starch, polyethylene glycol, zirconium English powder, slurry is made in continuous stirring, then AEO, sodium pyrophosphate, cerium oxide is added, be heated to 45 DEG C-60 DEG C, insulation also constantly stirs 1.5-2.5 hour, obtains mixed slurry stand-by;
(2) wood activated charcoal pulverizing is mixed with mixed slurry, be placed in Muffle furnace at 400 DEG C ~ 500 DEG C, activate 70 ~ 90 minutes, after cooling, be ground into 100-120 order powder;
(3) will add all the other residual components in powder, namely mixing and stirring obtains filtering material.
Utilize the obtained filter screen of filtering material of the present invention to carry out performance test, important technological parameters is: the technical indicator of air purification processing equipment is: the dust granules minimum grain size scope 0.5-10 μm caught; Trapping micronic dust efficiency >=99%; Through the effect of 4 hours, concentration of formaldehyde declined 90.1%.
Claims (2)
1. the strong but pliable in texture carbon leaching material for air-conditioning, it is characterized in that, be made up of the raw material of following weight portion: wood activated charcoal 135-145, AEO 1-1.5, sodium pyrophosphate 1-2, cerium oxide 2-3, wheat flour 6-8, sodium alginate 1.5-3, expanded corn starch 2-3, sodium phosphate trimer 1-2, polyethylene glycol 2.5-3.5, zirconium English powder 12-14, adsorption aid 4-6, water are appropriate;
Described adsorption aid is made up of the raw material of following weight portion: pinecone 12-14, walnut shell 9-11, attapulgite 12-14, molybdenum carbide 2-4, bamboo fibre 2-3, river shell powder 3-5, manganese dioxide 2-3, lemon 0.5-0.8, malic acid 0.8-1; Preparation method is by the pinecone, walnut shell dry 1-1.5 hour under 100 DEG C of-120 DEG C of conditions, be ground into 40-60 order powder, then add suitable quantity of water to stir with all the other residual components except bamboo fibre, lemon, form purees, then the retort putting into 400 DEG C-500 DEG C carbonizes 2-3 hour, is ground into 80-100 order powder after taking out cooling, adds bamboo fibre and pure water grinding 1-2 hour, spraying dry, is finally sprayed at powder surface by lemon.
2. a kind of strong but pliable in texture carbon leaching material for air-conditioning according to claim 1, is characterized in that, be made up of following concrete steps:
(1) appropriate water is added by wheat flour, sodium alginate, expanded corn starch, polyethylene glycol, zirconium English powder, slurry is made in continuous stirring, then AEO, sodium pyrophosphate, cerium oxide is added, be heated to 45 DEG C-60 DEG C, insulation also constantly stirs 1.5-2.5 hour, obtains mixed slurry stand-by;
(2) wood activated charcoal pulverizing is mixed with mixed slurry, be placed in Muffle furnace at 400 DEG C ~ 500 DEG C, activate 70 ~ 90 minutes, after cooling, be ground into 100-120 order powder;
(3) will add all the other residual components in powder, namely mixing and stirring obtains filtering material.