CN104264462A - Oiling agent for polyester fiber spinning - Google Patents
Oiling agent for polyester fiber spinning Download PDFInfo
- Publication number
- CN104264462A CN104264462A CN201410476475.8A CN201410476475A CN104264462A CN 104264462 A CN104264462 A CN 104264462A CN 201410476475 A CN201410476475 A CN 201410476475A CN 104264462 A CN104264462 A CN 104264462A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyoxyethylene
- fatty acid
- polyster fibre
- castor oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an oiling agent for polyester fiber spinning. The oiling agent is prepared from the following component in parts by weight: 1-2 parts of hydroxy propyl methylcellulose, 7-8 parts of polyoxyethylene castor oil ester, 5-6 parts of deionized water, 6-7 parts of coconut oil fatty acid diethanolamide, 8-9 parts of trimethylolpropane trioctoate, 3-4 parts of triethanolamine, 2-3 parts of polyoxyethylene sorbitan fatty acid ester, 2-3 parts of polyoxyethylene lauryl phosphate potassium salt, 4-5 pars of polyoxyethylene fatty acid and 4-5 parts of iso-tridecanol polyoxyethylene ether. The oiling agent is suitable for polyester fibers and can smoothen and soften the polyester fibers and improve the antistatic property of the polyester fibers.
Description
Technical field
The present invention relates to polyster fibre spinning finish.
Background technology
Finish is a kind of requisite auxiliary agent in procedure of fibre production and processing, and especially polyster fibre spinning finish is polyster fibre important textile auxiliary of requisite one in spinning process.
Summary of the invention
The object of the present invention is to provide a kind of polyster fibre spinning finish, be applicable to polyster fibre, make polyster fibre smooth, soft, and improve the antistatic behaviour of polyster fibre.
For achieving the above object, technical scheme of the present invention is a kind of polyster fibre spinning finish of design, consists of the following composition by weight percentage:
1 ~ 2 part of HYDROXY PROPYL METHYLCELLULOSE,
7 ~ 8 parts of castor oil polyoxyethylene fat,
5 ~ 6 parts of ionized waters,
6 ~ 7 parts of cocoanut fatty acid diethanolamides,
8 ~ 9 parts of trimethylolpropane tris caprylates,
3 ~ 4 parts of triethanolamines,
2 ~ 3 parts of polyoxyethylene sorbitan fatty acid esters,
2 ~ 3 portions of polyoxyethylene laural base phosphoric acid ester first salt,
4 ~ 5 parts of polyoxyethylene carboxylates,
4 ~ 5 parts of isomerous tridecanol polyoxyethylene ethers.
Preferably, polyster fibre spinning finish, consists of the following composition by weight percentage:
1 part of HYDROXY PROPYL METHYLCELLULOSE,
7 parts of castor oil polyoxyethylene fat,
5 parts of ionized waters,
6 parts of cocoanut fatty acid diethanolamides,
8 parts of trimethylolpropane tris caprylates,
3 parts of triethanolamines,
2 parts of polyoxyethylene sorbitan fatty acid esters,
2 portions of polyoxyethylene laural base phosphoric acid ester first salt,
4 parts of polyoxyethylene carboxylates,
4 parts of isomerous tridecanol polyoxyethylene ethers.
Preferably, polyster fibre spinning finish, consists of the following composition by weight percentage:
2 parts of HYDROXY PROPYL METHYLCELLULOSE,
8 parts of castor oil polyoxyethylene fat,
6 parts of ionized waters,
7 parts of cocoanut fatty acid diethanolamides,
9 parts of trimethylolpropane tris caprylates,
4 parts of triethanolamines,
3 parts of polyoxyethylene sorbitan fatty acid esters,
3 portions of polyoxyethylene laural base phosphoric acid ester first salt,
5 parts of polyoxyethylene carboxylates,
5 parts of isomerous tridecanol polyoxyethylene ethers.
Preferably, polyster fibre spinning finish, consists of the following composition by weight percentage:
1.2 parts of HYDROXY PROPYL METHYLCELLULOSE,
7.8 parts of castor oil polyoxyethylene fat,
5.6 parts of ionized waters,
6.7 parts of cocoanut fatty acid diethanolamides,
8.9 parts of trimethylolpropane tris caprylates,
3.4 parts of triethanolamines,
2.3 parts of polyoxyethylene sorbitan fatty acid esters,
2.3 portions of polyoxyethylene laural base phosphoric acid ester first salt,
4.5 parts of polyoxyethylene carboxylates,
4.5 parts of isomerous tridecanol polyoxyethylene ethers.
Advantage of the present invention and beneficial effect are: provide a kind of polyster fibre spinning finish, be applicable to polyster fibre, make polyster fibre smooth, soft, and improve the antistatic behaviour of polyster fibre.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
Polyster fibre spinning finish, consists of the following composition by weight percentage:
1 part of HYDROXY PROPYL METHYLCELLULOSE,
7 parts of castor oil polyoxyethylene fat,
5 parts of ionized waters,
6 parts of cocoanut fatty acid diethanolamides,
8 parts of trimethylolpropane tris caprylates,
3 parts of triethanolamines,
2 parts of polyoxyethylene sorbitan fatty acid esters,
2 portions of polyoxyethylene laural base phosphoric acid ester first salt,
4 parts of polyoxyethylene carboxylates,
4 parts of isomerous tridecanol polyoxyethylene ethers.
Embodiment 2
Polyster fibre spinning finish, consists of the following composition by weight percentage:
2 parts of HYDROXY PROPYL METHYLCELLULOSE,
8 parts of castor oil polyoxyethylene fat,
6 parts of ionized waters,
7 parts of cocoanut fatty acid diethanolamides,
9 parts of trimethylolpropane tris caprylates,
4 parts of triethanolamines,
3 parts of polyoxyethylene sorbitan fatty acid esters,
3 portions of polyoxyethylene laural base phosphoric acid ester first salt,
5 parts of polyoxyethylene carboxylates,
5 parts of isomerous tridecanol polyoxyethylene ethers.
Embodiment 3
Polyster fibre spinning finish, consists of the following composition by weight percentage:
1.2 parts of HYDROXY PROPYL METHYLCELLULOSE,
7.8 parts of castor oil polyoxyethylene fat,
5.6 parts of ionized waters,
6.7 parts of cocoanut fatty acid diethanolamides,
8.9 parts of trimethylolpropane tris caprylates,
3.4 parts of triethanolamines,
2.3 parts of polyoxyethylene sorbitan fatty acid esters,
2.3 portions of polyoxyethylene laural base phosphoric acid ester first salt,
4.5 parts of polyoxyethylene carboxylates,
4.5 parts of isomerous tridecanol polyoxyethylene ethers.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. polyster fibre spinning finish, is characterized in that, consists of the following composition by weight percentage:
1 ~ 2 part of HYDROXY PROPYL METHYLCELLULOSE,
7 ~ 8 parts of castor oil polyoxyethylene fat,
5 ~ 6 parts of ionized waters,
6 ~ 7 parts of cocoanut fatty acid diethanolamides,
8 ~ 9 parts of trimethylolpropane tris caprylates,
3 ~ 4 parts of triethanolamines,
2 ~ 3 parts of polyoxyethylene sorbitan fatty acid esters,
2 ~ 3 portions of polyoxyethylene laural base phosphoric acid ester first salt,
4 ~ 5 parts of polyoxyethylene carboxylates,
4 ~ 5 parts of isomerous tridecanol polyoxyethylene ethers.
2. polyster fibre spinning finish according to claim 1, is characterized in that, consist of the following composition by weight percentage:
1 part of HYDROXY PROPYL METHYLCELLULOSE,
7 parts of castor oil polyoxyethylene fat,
5 parts of ionized waters,
6 parts of cocoanut fatty acid diethanolamides,
8 parts of trimethylolpropane tris caprylates,
3 parts of triethanolamines,
2 parts of polyoxyethylene sorbitan fatty acid esters,
2 portions of polyoxyethylene laural base phosphoric acid ester first salt,
4 parts of polyoxyethylene carboxylates,
4 parts of isomerous tridecanol polyoxyethylene ethers.
3. polyster fibre spinning finish according to claim 1, is characterized in that, consist of the following composition by weight percentage:
2 parts of HYDROXY PROPYL METHYLCELLULOSE,
8 parts of castor oil polyoxyethylene fat,
6 parts of ionized waters,
7 parts of cocoanut fatty acid diethanolamides,
9 parts of trimethylolpropane tris caprylates,
4 parts of triethanolamines,
3 parts of polyoxyethylene sorbitan fatty acid esters,
3 portions of polyoxyethylene laural base phosphoric acid ester first salt,
5 parts of polyoxyethylene carboxylates,
5 parts of isomerous tridecanol polyoxyethylene ethers.
4. polyster fibre spinning finish according to claim 1, is characterized in that, consist of the following composition by weight percentage:
1.2 parts of HYDROXY PROPYL METHYLCELLULOSE,
7.8 parts of castor oil polyoxyethylene fat,
5.6 parts of ionized waters,
6.7 parts of cocoanut fatty acid diethanolamides,
8.9 parts of trimethylolpropane tris caprylates,
3.4 parts of triethanolamines,
2.3 parts of polyoxyethylene sorbitan fatty acid esters,
2.3 portions of polyoxyethylene laural base phosphoric acid ester first salt,
4.5 parts of polyoxyethylene carboxylates,
4.5 parts of isomerous tridecanol polyoxyethylene ethers.