CN104263971B - The system of APT is prepared by tungsten mineral material no pollution - Google Patents

The system of APT is prepared by tungsten mineral material no pollution Download PDF

Info

Publication number
CN104263971B
CN104263971B CN201410527541.XA CN201410527541A CN104263971B CN 104263971 B CN104263971 B CN 104263971B CN 201410527541 A CN201410527541 A CN 201410527541A CN 104263971 B CN104263971 B CN 104263971B
Authority
CN
China
Prior art keywords
leaching
grog
raw material
tungsten
ammonium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410527541.XA
Other languages
Chinese (zh)
Other versions
CN104263971A (en
Inventor
李小斌
崔源发
周秋生
李建圃
齐天贵
徐双
刘桂华
林国荣
彭志宏
李继红
徐向明
王霖
王一霖
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangxi Rare Earth and Rare Metals Tungsten Group Holding Co Ltd
Central South University
Original Assignee
Jiangxi Rare Earth and Rare Metals Tungsten Group Holding Co Ltd
Central South University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangxi Rare Earth and Rare Metals Tungsten Group Holding Co Ltd, Central South University filed Critical Jiangxi Rare Earth and Rare Metals Tungsten Group Holding Co Ltd
Priority to CN201410527541.XA priority Critical patent/CN104263971B/en
Publication of CN104263971A publication Critical patent/CN104263971A/en
Application granted granted Critical
Publication of CN104263971B publication Critical patent/CN104263971B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The metallurgical system of a kind of tungsten mineral material, during raw material preparation, the addition of calcareous material at least generates Ca by the tungsten made in tungsten mineral material3WO6And/or Ca2FeWO6And/or Ca2MnWO61.0 times of theoretical amount, the mineralizer allocated into is fluoride, it is therefore preferable to calcium fluoride, and the addition of calcium fluoride is 0.5 7 mass % of dry tungsten mineral material amount；The raw material sintering temperature of calcining kiln is not less than 500 DEG C；Roasting time is 0.5 8.0h；Leaching device has leaching agent entrance, leaching slurry outlet, feedback gas recovery port, slurry separating, washing liquid recovery port, slag phase cleaning mixture recovery port, crystal seed entrance；The equipment for separating liquid from solid of leaching slurry, it has leached mud feedback port, washing liquid feedback outlet, the receiving port of evaporative crystallization condensed water, crystal seed feedback port；Crystallization apparatus has the gas feedback mouth feeding back to leaching device；The liquid-solid separation device of slurry has crystalline mother solution and is back to the outlet of leaching device.Present invention achieves wastewater zero discharge, reach the technical merit of green metallurgical.

Description

The system of APT is prepared by tungsten mineral material no pollution
Technical field
The present invention relates to a kind of system being prepared APT by tungsten mineral material, belong to Tungsten smelting technical field.
Term " raw material " refers to tungsten mineral material, dispensing, after proportioning, and is milled to the mixed material of certain fineness.
Term " grog " refer to tungsten mineral material, dispensing through levigate, be mixed into raw material, then the material of gained after high-temperature roasting.
Term " mineralizer " refers to the reaction that can accelerate between tungsten mineral material and dispensing in raw material roasting process or reduces roasting The material of temperature.
Background technology
In prior art, the commercial run preparing APT mainly comprises the steps: by caustic soda or soda leaching tungsten mineral Raw material, it is thus achieved that coarse sodium tungstate；Exchanged by solution purification-ion or solvent extraction is made the transition and (or exchanged by ion or molten Agent abstraction impurity removal also makes the transition), it is thus achieved that pure tungsten acid ammonium solution；Pass through evaporative crystallization again, it is thus achieved that APT product.
All there is following essence defect in prior art: all uses and do not circulate or half cycle process system, be not carried out whole circulation industrial Skill.At least there is techniques below problem in prior art: must arrange waste water discharge opening, and waste water pollution problem cannot thoroughly be eradicated； Supplies are mostly expendable consumed product, and the leaching agent of leaching process is excessively used, and these supplies walk in corresponding technique Rapid outer row otherwise need to use in corresponding acid or alkali and after outer row again, supplies consume many, Production cost is high；Inevitably taking part wolfram element in waste water out of, the wolfram element response rate is low；Equipment investment is big, technique stream Journey is long, and productivity ratio is relatively low, it is more difficult to realize producing continuously.
In such APT preparation process, auxiliary material consumes relatively big, and produces a large amount of waste water；Sodium tungstate solution made the transition Producing substantial amounts of high bisulfate waste liquor in journey, evaporative crystallization mother solution produces ammonia nitrogen waste water.
If the open circuit flow process having discharge of wastewater being become and there is no the closed circuit flow process of discharge of wastewater, it is not without technical possibility Property, but input is possibly even more than profit, to this end, enterprise has to select discharge, result causes serious environment Pollute.
Summary of the invention
It is an object of the invention to provide a kind of system preparing APT from tungsten mineral material, its flow process is short, solution reusable edible, Environmental pollution is almost uprooted, low cost, be prone to industrialization.
To this end, according to an aspect of the invention, it is provided a kind of method preparing APT from tungsten mineral material, the method bag Include following steps:
1) by tungsten mineral material, after dispensing is levigate, mix homogeneously prepares raw material；
2) raw material are carried out roasting, it is thus achieved that grog, and grog is crushed, levigate；
3) with ammonium carbonate, ammonium carbonate-ammonium hydrogen carbonate, ammonium carbonate-ammonium tungstate, ammonium carbonate-CO2, ammonium carbonate-ammonia-CO2, carbon Acid ammonium-ammonia, ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate, ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate-CO2, ammonium carbonate-ammonia-ammonium tungstate, Ammonium carbonate-ammonium tungstate-CO2, ammonium carbonate-ammonia-ammonium tungstate-CO2System leaches grog；
4) leaching slurry washs mutually through solid-liquid separation and slag, obtains thick ammonium tungstate solution and leached mud, and part leached mud is as joining Material returns step 1) carry out raw material configuration, remainder is stored up；
5) thick ammonium tungstate solution purification and impurity removal；
6) after purifying, solution uses evaporative crystallization to separate out APT, obtains ammonia and carbon dioxide simultaneously；
7) serosity after crystallization being carried out solid-liquor separation, obtain crystalline mother solution and solid phase, solid phase is washed through water and/or ammonium salt solution, APT product, crystalline mother solution and step 6 is i.e. obtained after washing after drying) return to step together with the ammonia that obtains and carbon dioxide , and (can be by ammonium hydrogen carbonate or ammonia and CO at the ammonium carbonate of supplementary loss 3)2Part substitutes) Posterior circle leaching grog.
Preferably, described tungsten mineral material includes, scheelite, wolframite, Scheelite-Wolframite Mixed Mine and/or tungsten slurry；
Preferably, during raw material preparation, the addition of leached mud at least generates Ca by the tungsten made in tungsten mineral material3WO6With/ Or Ca2FeWO6And/or Ca2MnWO61.0 times of theoretical amount, preferably 1.1-1.5 times, more preferably 1.1-1.2 times； Raw material granularity is not particularly limited, preferably not greater than 200 μm, more preferably not more than 100 μm, more preferably not more than 40μm；During raw material roasting, temperature for being not less than 500 DEG C, preferably 800-1050 DEG C, more preferably 850-950 DEG C；
Preferably, the time of raw material roasting is 0.5-8.0h, preferably 1.0-3.0h, more preferably 2.0h；Tungsten mineral material is During scheelite, calcination atmosphere is not particularly limited, and is preferably neutral or oxidizing atmosphere；
Preferably, when tungsten mineral material is wolframite, Scheelite-Wolframite Mixed Mine and/or tungsten slurry, calcination atmosphere is neutral or goes back Originality atmosphere, preferably neutral atmosphere；The granularity of grog is not particularly limited, preferably not greater than 200 μm, is further preferably It is not more than 74 μm, is further preferably no more than 45 μm；
Preferably, the CO in Leaching Systems2A part is from stove (kiln) gas or commodity produced by raw material roasting process CO2, another part is from CO produced by ammonium tungstate solution evaporation and crystal process2；
Preferably, CO2Can be passed through in leaching process, it is also possible to be passed through before leaching.
Preferably, leach ammonium carbonate concentration in initial system and be more than 20g-(NH4)2CO3/100g-H2O, is preferably under this system The concentration of its saturated solution, ammonium hydrogen carbonate then adds with the form of solution or solid, and the addition of ammonium hydrogen carbonate is limited the most especially System, preferably not less than makes the calcium in grog be converted into CaCO31.0 times of aequum (theoretical amount), more preferably theoretical amount 1.1-1.4 times, ammonium tungstate concentration is not particularly limited, if the ammonium tungstate that can ensure that after tungsten fully leaches in grog in gained solution Concentration is less than the equilibrium concentration under this system, and the addition of ammonia is also not particularly limited, and preferably leaches initial system Middle NH3Weight/mass percentage composition be 0%～28%, more preferably 5%～20%, more preferably 5%～10%；The leaching of grog Process is carried out in enclosed system, with Ammonium Carbonate system, ammonium carbonate-ammonium hydrogen carbonate system, ammonium carbonate-ammonia-water systems, ammonium carbonate When-ammonium hydrogen carbonate-ammonium tungstate system, ammonium carbonate-ammonia-ammonium tungstate system and ammonium carbonate-ammonium tungstate system leach grog, reactant The absolute pressure of system is not particularly limited, with ammonium carbonate-CO2System, ammonium carbonate-ammonium hydrogen carbonate-CO2System, ammonium carbonate-ammonia Water-CO2System, ammonium carbonate-ammonium tungstate-CO2System, ammonium carbonate-ammonia-ammonium tungstate-CO2System and ammonium carbonate-ammonium hydrogen carbonate- Ammonium tungstate-CO2When system leaches grog, the absolute pressure of reaction system need to be controlled not less than 1atm, preferably 2atm；
Preferably, extraction temperature is not less than 5 DEG C, preferably 10-80 DEG C, more preferably 20-70 DEG C, more preferably 30-50 DEG C；
Preferably, extraction time is not particularly limited, as long as can ensure that in grog, tungsten can fully leach, when preferably leaching Between be 0.5-8.0h, more preferably extraction time be 2-5h；Purification and impurity removal process include except molybdenum, phosphorus, stannum, arsenic, silicon, ferrum, Sodium, potassium, bismuth, antimony, calcium, magnesium process at least one；
According to another aspect of the present invention, it is provided that a kind of method used described in claim 1 prepares the system of APT, Including:
1) grinding attachment A, tungsten mineral material, dispensing after batching metering, use grinding attachment A by levigate for various raw materials, Mixing, preparation has the raw material of certain fineness and the uniformity；
2) raw material of preparation are added roasting in calcining kiln (stove), obtain grog after cooling by calcining kiln (stove)；
3) grinding attachment B, the grog burnt till uses grinding attachment B levigate；
4) leaching equipment, grog leaches in leaching equipment；
5) filter plant, leaching slurry uses filter plant to carry out filtration washing；
6) impurity removing equipment, thick ammonium tungstate solution purification and impurity removal in impurity removing equipment；And
7) crystallizer, ammonium tungstate refined liquid evaporative crystallization in crystallizer.
Preferably, described grinding attachment A is selected from: vibrating mill, ball mill, rod mill, autogenous tumbling mill, agitator mill, outstanding Roller pulverizer, tower mill, colloidal mill, centrifugal mill, high pressure disc mill, Raymond mill, jet mill.
Preferably, described calcining kiln (stove) including: static calcining kiln (stove) and dynamic roasting kiln (stove),.
Preferably, described grinding attachment B is selected from: vibrating mill, twin rollers, ball mill, rod mill, autogenous tumbling mill, stirring Grinding machine, overhang roll pulverizer, tower mill, colloidal mill, centrifugal mill, high pressure disc mill, Raymond mill, jet mill.
Preferably, described leaching equipment can be an independent leaching equipment, it is also possible to 2-4 leaching equipment is used in series.
Preferably, described leaching equipment can be leaching equipment, it is also possible to be ball milling leaching equipment.
Preferably, described leaching equipment can seal, and can bear 3atm pressure.
Preferably, described filter plant is pumping and filtering device, filtering equipment and/or natural filtration groove.
Preferably, described impurity removing equipment is decleaning tank, filter plant and/or subsider.
Preferably, it is provided with agitating device, attemperator in described decleaning tank.
The present invention industrial process relative to existing APT, has an advantage in that:
1) achieve and prepared the closed cycle of solution during APT by tungsten mineral material, thus it is raw to eradicate APT in theory The problem of environmental pollution caused due to a large amount of discharge of wastewater during product；
2) by tungsten mineral material roasting is made the transition, make wolfram element change and be contained in the material easily leached by ammonium carbonate salt solution, Achieving the low-temp extraction of tungsten, reduce the energy expenditure in leaching process and cost, meanwhile, leached mud again can be as tungsten mineral Dispensing in raw material transformation process and recycle；
3) use low cost, the ammonium carbonate salts system of easily circulation leaches tungsten mineral grog, directly obtains ammonium tungstate solution, cancels Step transition from sodium tungstate solution to ammonium tungstate solution, flow process is simple；
4) recycling due to multiple supplies, supplies consumption is greatly reduced, and processing charges is greatly lowered；
5) simple to operate, it is simple to control, it is easy to commercial Application.
According to the present invention, with " ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate " or " ammonium carbonate-ammonium tungstate-CO2" or " ammonium carbonate-ammonia Water-ammonium tungstate " or " ammonium carbonate-ammonia " or " ammonium carbonate " or " ammonium carbonate-ammonium hydrogen carbonate " or " ammonium carbonate-ammonia-CO2” Or " ammonium carbonate-ammonia-ammonium tungstate-CO2" or " ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate-CO2" or " ammonium carbonate-CO2" or " carbon Acid ammonium-ammonium tungstate " or " ammonium carbonate-ammonium hydrogen carbonate-CO2" system is non-obvious as leachate, this is because: alkalescence System do not process the relatively low raw material of the chemical reactivities such as scheelite, wolframite, Scheelite-Wolframite Mixed Mine and tungsten slurry (or process Extremely inefficient).Tungsten smelting industry typically use at present strong acid (example hydrochloric acid) or highly basic (such as sodium hydroxide) gonosome system and high temperature, Leaching tungsten mineral material under environment under high pressure, and " ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate ", " ammonium carbonate-ammonium tungstate-CO2", " carbon Acid ammonium-ammonia-ammonium tungstate ", " ammonium carbonate-ammonia ", " ammonium carbonate ", " ammonium carbonate-ammonium hydrogen carbonate ", " ammonium carbonate-ammonia-CO2”、 " ammonium carbonate-ammonia-ammonium tungstate-CO2", " ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate-CO2", " ammonium carbonate-CO2", " ammonium carbonate -ammonium tungstate " and " ammonium carbonate-ammonium hydrogen carbonate-CO2" system belongs to alkalescence system, it is necessary to make the transition step ability through raw material Realize leaching.
According to the present invention, select " ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate " or " ammonium carbonate-ammonium tungstate-CO2" or " ammonium carbonate- Ammonia-ammonium tungstate " or " ammonium carbonate-ammonia " or " ammonium carbonate " or " ammonium carbonate-ammonium hydrogen carbonate " or " ammonium carbonate-ammonia-CO2” Or " ammonium carbonate-ammonia-ammonium tungstate-CO2" or " ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate-CO2" or " ammonium carbonate-CO2" or " carbon Acid ammonium-ammonium tungstate " or " ammonium carbonate-ammonium hydrogen carbonate-CO2" system leaches, Leaching Systems material converts after crystallisation step Become ammonia and carbon dioxide, just can replenish Leaching Systems, it is achieved thereby that the whole of supplies recycle, thoroughly get rid of Abandon traditional open circuit not circulating system or open circuit half cycle system, eradicated disposal of pollutants, be truly realized green metallurgical.
According to the present invention, the tungsten leaching effect that not only can obtain when leaching liquid-solid comparison and being high, leaching liquid-solid ratio less than 10 Time, in grog, the leaching rate of tungsten does not declines, WO in gained leachate3Concentration still enough industrialized production.
According to the present invention, use " ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate " or " ammonium carbonate-ammonium tungstate-CO2" or " ammonium carbonate- Ammonia-ammonium tungstate " or " ammonium carbonate-ammonia " or " ammonium carbonate " or " ammonium carbonate-ammonium hydrogen carbonate " or " ammonium carbonate-ammonia-CO2” Or " ammonium carbonate-ammonia-ammonium tungstate-CO2" or " ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate-CO2" or " ammonium carbonate-CO2" or " carbon Acid ammonium-ammonium tungstate " or " ammonium carbonate-ammonium hydrogen carbonate-CO2" system leaching grog, when leaching liquid-solid ratio and being 4, remain to obtain Preferably tungsten leaching effect, WO in gained leachate3Concentration is higher, is adapted to very much industrialized production.
According to the present invention, using close circulation technology, only arrange waste residue outlet, no longer need to arrange waste water discharge opening, waste water is arranged The pollution problem put has obtained thorough elimination.
According to the present invention, supplies are no longer expendable consumed products, and the leaching agent of leaching process recycles, though adminicle Material is excessively used, corresponding processing step outer row, it is no longer necessary to use in corresponding acid or alkali With, therefore, supplies consumption is greatly decreased, and production cost is greatly reduced.
According to the present invention, it is achieved that circulation metallurgical technology, it is clean that " waste water " of conventional process systems is blotted squeezing, thoroughly avoids portion Dividing wolfram element to be emitted in vain, therefore, the wolfram element response rate also improves.
According to the present invention, can realize integrated production, the working environment in workshop can greatly improve, and equipment investment return rate substantially carries Height, technological process shortens, and productivity ratio is largely increased, it is possible to achieve continuous print automated production.
According to the present invention, add the pretreatment process of tungsten mineral material, use " ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate " or " ammonium carbonate-ammonium tungstate-CO2" or " ammonium carbonate-ammonia-ammonium tungstate " or " ammonium carbonate-ammonia " or " ammonium carbonate " or " carbon Acid ammonium-ammonium hydrogen carbonate " or " ammonium carbonate-ammonia-CO2" or " ammonium carbonate-ammonia-ammonium tungstate-CO2" or " ammonium carbonate-bicarbonate Ammonium-ammonium tungstate-CO2" or " ammonium carbonate-CO2" or " ammonium carbonate-ammonium tungstate " or " ammonium carbonate-ammonium hydrogen carbonate-CO2" system Leaching tungsten mineral grog, leaching condition is gentle, and leaching agent is cheap, be easy to get, and supplies reusable edible can disappear in theory Except the discharge of wastewater in production process.
According to the present invention, completely disengage from prior art, it is proposed that a kind of brand-new theory preparing APT and technique, saved Sodium tungstate solution step transition of a large amount of waste water can be produced, directly obtain ammonium tungstate solution, be inherently eliminated APT production During the discharge of waste water, and achieve recycling of supplies and solution.
According to the present invention, technological process is simple, and easy to operate, production cost is low, non-wastewater discharge, and environmental pollution is reduced to Low degree.
Accompanying drawing explanation
Fig. 1 is a kind of process chart being prepared APT by tungsten mineral material according to the present invention.
Fig. 2 is the structural principle schematic diagram of a kind of system being prepared APT by tungsten mineral material according to the present invention.
Detailed description of the invention
Embodiments of the invention are described further by 1-2 below in conjunction with the accompanying drawings.
As it is shown in figure 1, the metallurgical technology containing tungsten mineral material of the present invention comprises the following steps:
Make to become raw material 101 containing W raw mineral materials 100 and dispensing MN (M represents that cation, N represent anion) proportioning；
Roasting raw material 200, promote it and chemical reaction occur, to be transformed into containing M and the grog containing W ion, so that grog obtains Obtain high chemical reactivity；
Weak base AN (A is cation) solution is used to leach (the excessive highly basic of thorough abandoning tradition leaches prejudice) grog, so that grog Leach 300, and in circular response, reclaim the solution that each link feeds back, and supplement loss according to being actually needed Weak base AN；
Leaching slurry is carried out solid-liquid separation 400, obtains the thick solution containing A and containing W ion and the leached mud containing M, to slag Washing mutually, cleaning mixture feeds back to grog and leaches link (I closed loop), according to actual needs, takes at least part of leached mud and feeds back to Raw material configuration link (ii closed loop), as dispensing, if leached mud has remainder, are then stored up；
At least first class purification remove impurity 500 is carried out to containing A and the thick solution containing W ion；
It is evaporated crystallizing 600 to the solution after purifying, to separate out the intermediate products containing W element；Meanwhile, will discharge with Gas and the gas relevant to N element that element A is relevant are back to leach the step (ii I closed loop) of grog 300, and evaporate The water gone out feeds back to the solid-liquid separation link (iv closed loop) of leaching slurry 300；
Serosity after crystallization is carried out solid-liquor separation 700, and to obtain crystalline mother solution and solid phase, solid phase i.e. obtains after water washs and contains The final products (preferably solid phase dissolved again and crystallize, to obtain the final products of higher purity) of W element；And tie Brilliant mother solution also returns to the step (V closed loop) leaching grog,
To this end, this technique comprises multiple closed cycle, omnidistance non-wastewater discharge.
As in figure 2 it is shown, the metallurgical system of the tungsten mineral material of the present invention includes successively:
Raw material preparation facilities 10, it has raw mineral materials metering (dosage) entrance 11 and batching metering (dosage) entrance 12 (is preferably gone back Be provided with mineralizer metering (dosage) entrance 13), raw material fine mill (containing vortex mixer) 14, raw material outlet 15 and leached mud receive Mouth 16；
Calcining kiln (stove) 20, it connects with raw material outlet 15 with raw material silo through feeding measurement device, has heater, insulation dress Put (the most also including chiller 21) and thick grog outlet 22；
Grog fine mill 30, it connects with thick grog outlet 22 through grog storehouse, has ore grinding device and thin grog outlet 31；
Leaching device 40, itself and thin grog outlet 31, there is leaching agent entrance 41, leaching slurry outlet 42, feedback gas Body recovery port 43, slurry separating, washing liquid recovery port 44, slag phase cleaning mixture recovery port 45, crystal seed entrance 46 are (preferably, Also include that carbon dioxide is passed through mouth 47)；
The equipment for separating liquid from solid (preferably defecator) of leaching slurry, it connects with leaching slurry outlet 42, has containing dispensing unit The filtration washing device 50 of the leached mud of element, thick taphole 51 containing wolfram element, leached mud feedback port 52, to remaining leached mud The outlet 53 of heap warehousing, washing liquid feedback outlet 54, the receiving port 55 of evaporative crystallization condensed water, this equipment for separating liquid from solid is in feedback Connect with the crystal seed entrance 46 of leaching device 40 to the way of the leached mud receiving port 16 of raw material preparation facilities 10；
At least first class purification knot screen 60, the entrance 61 of the first order connects with the thick taphole 51 containing wolfram element, at different levels Having purification and impurity removal agent entrance and impurity collector, afterbody has smart taphole containing wolfram element 62 (preferably, Rear stage adds extractor fan)；
Crystallization apparatus 70, its entrance 71 connects with the smart taphole 62 containing wolfram element, has slurry outlet 72, anti- It is fed to gas feedback mouth 73 and the condensation-water drain 74 (preferably there is smart solution evaporation cerium sulphate crystal device) of leaching device；
The liquid-solid separation device 80 of slurry, it connects with slurry outlet 72, has crystalline mother solution and is back to leach dress The outlet 83 of outlet 81, solid phase wash water entrance 82 and the tungsten product of putting 40 (preferably, is dissolved with next stage, crystallize, is carried Pure subsystem connects).
According to the present invention, by tungsten mineral material and a certain amount of calcareous material and mineralizer after levigate, mix homogeneously obtains raw material； During raw material preparation, the addition of calcareous material at least generates Ca by the tungsten made in tungsten mineral material3WO6And/or Ca2FeWO6 And/or Ca2MnWO61.0 times of theoretical amount, preferably 1.1-1.5 times, more preferably 1.1-1.2 times.
During raw material preparation, the mineralizer allocated into is fluoride, it is therefore preferable to calcium fluoride, and the addition of calcium fluoride is that dry tungsten mineral is former The 0.5-7% (mass percent) of doses, preferably 1-3% (mass percent)；Raw material granularity is not particularly limited, and is preferably not More than 200 μm, more preferably not more than 100 μm, more preferably not more than 40 μm；Raw material sintering temperature is not less than 500 DEG C, Preferably raw material sintering temperature is 800～1050 DEG C, more preferably 850～950 DEG C；Roasting time is not particularly limited, and temperature is low Then need to extend roasting time, for making the tungsten in raw material be fully converted into Ca3WO6And/or Ca2FeWO6And/or Ca2MnWO6, preferably roasting time is 0.5-8.0h, more preferably 1.0～3.0h, more preferably roasts at 850～950 DEG C Burn 2.0h.
For scheelite raw material, calcination atmosphere is not particularly limited, and is preferably neutral or oxidizing atmosphere；For wolframite, black White tungsten composite ore, tungsten slurry raw material, calcination atmosphere is neutral or reducing atmosphere, preferably neutral atmosphere.The present invention will contain Ca3WO6And/or Ca2FeWO6And/or Ca2MnWO6Mixed material join in ammonium salt solution system, at airtight bar Leach under part, after having leached, the separated washing of leaching slurry, obtain ammonium tungstate solution.
Preferably, described Ca3WO6And/or Ca2FeWO6And/or Ca2MnWO6Can be the pure compound of synthetic, Can also be tungsten mineral material obtain after treatment containing Ca3WO6And/or Ca2FeWO6And/or Ca2MnWO6Mixing Thing (grog)；Ca3WO6And/or Ca2FeWO6And/or Ca2MnWO6The granularity of mixed material be not more than 200 μm, It is preferably less than 45 μm；Described ammonium salt solution system, can be ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate system, ammonium carbonate-tungsten Acid ammonium-CO2System, ammonium carbonate-ammonia-ammonium tungstate system, ammonium carbonate-ammonia-water systems, Ammonium Carbonate system, ammonium carbonate-bicarbonate Ammonium system, ammonium carbonate-ammonia-CO2System, ammonium carbonate-ammonia-ammonium tungstate-CO2System, ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate -CO2System, ammonium carbonate-CO2System, ammonium carbonate-ammonium tungstate system, can also be ammonium carbonate-ammonium hydrogen carbonate-CO2System.
Preferably, with Ammonium Carbonate system, ammonium carbonate-ammonium hydrogen carbonate system, ammonium carbonate-ammonia-water systems, ammonium carbonate-ammonium hydrogen carbonate- Ammonium tungstate system, ammonium carbonate-ammonia-ammonium tungstate system and ammonium carbonate-ammonium tungstate system leach Ca3WO6And/or Ca2FeWO6 And/or Ca2MnWO6Time, the absolute pressure of Leaching Systems is not particularly limited；With ammonium carbonate-CO2System, ammonium carbonate-carbon Acid hydrogen ammonium-CO2System, ammonium carbonate-ammonia-CO2System, ammonium carbonate-ammonium tungstate-CO2System, ammonium carbonate-ammonia-ammonium tungstate -CO2System and ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate-CO2System leaches Ca3WO6And/or Ca2FeWO6And/or Ca2MnWO6Time, leaching process is passed through CO2, the absolute pressure controlling Leaching Systems is not less than 1atm, is preferably 1.5-2.5atm, more preferably 2atm.
Preferably, Leaching Systems ammonium carbonate concentration is more than 20g-(NH4)2CO3/100g-H2O, the most saturated ammonium carbonate is molten Liquid.
Preferably, described ammonium carbonate-ammonium tungstate-ammonium hydrogen carbonate, ammonium carbonate-ammonium tungstate-CO2, ammonium carbonate-ammonia-ammonium tungstate, carbon Acid ammonium-ammonium tungstate, ammonium carbonate-ammonia-ammonium tungstate-CO2With ammonium carbonate-ammonium hydrogen carbonate-ammonium tungstate-CO2In solution system, wolframic acid Ammonium concentration is also not particularly limited, as long as meeting Ca3WO6And/or Ca2FeWO6And/or Ca2MnWO6In tungsten abundant After leaching, in gained solution, ammonium tungstate concentration is less than its dissolubility in this system.
Preferably, described ammonium carbonate-ammonium hydrogen carbonate, ammonium carbonate-ammonium tungstate-ammonium hydrogen carbonate, ammonium carbonate-ammonium hydrogen carbonate-CO2And carbon Acid ammonium-ammonium hydrogen carbonate-ammonium tungstate-CO2Solution system, ammonium hydrogen carbonate addition is not particularly limited, preferably not less than theoretical amount 1.0 times, more preferably 1.1～1.4 times of theoretical amount.
Preferably, described ammonium carbonate-ammonia-ammonium tungstate, ammonium carbonate-ammonia-ammonium tungstate-CO2, ammonium carbonate-ammonia and ammonium carbonate- Ammonia-CO2In solution system, the addition of ammonia is also not particularly limited, and preferably leaches NH in initial system3Quality Percentage composition is 0%～28%, more preferably 5%～20%, more preferably 5%～10%.
Preferably, Leaching Systems pH is controlled not less than 8.0.Extraction temperature is not less than 5 DEG C, preferably 10-80 DEG C, more preferably For 20-70 DEG C, more preferably 30-50 DEG C；Extraction time is not particularly limited, as long as Ca can be made3WO6And/or Ca2FeWO6 And/or Ca2MnWO6In tungsten fully leach, preferably 0.5-8.0h, more preferably extraction time are 2.0-5.0h.
Preferably, the initial liquid-solid ratio of Leaching Systems is not less than 1:1mL/g, preferably 10:1-4:1mL/g.
Preferably, the final liquid-solid ratio of Leaching Systems by the way of multistage feeds, can be reduced, preferably by two sections of chargings, The liquid-solid ratio controlling final Leaching Systems is 3:1～4:1mL/g.
Preferably, described sal volatile also can be by ammonium bicarbonate soln and ammonia or ammonia and CO2Part substitutes.
As (the NH in solution4)2WO4When concentration is higher, especially there is a large amount of NH4In the presence of OH, (NH4)2WO4 The high activity CaCO that can generate with leaching process3There is secondary response, generate and to be difficult to be leached by ammonium carbonate salt solution CaWO4, cause tungsten loss.Dominant response is probably:
Ca(OH)2+(NH4)2WO4=CaWO4+2NH4OH (2)
Reaction (2) is easier to carry out, and generally reacts (1) and be difficult to, but at Ca3WO6Leaching process in newborn CaCO3Activity is high, and reaction (1) is the most likely carried out, and carries out NH along with leaching process4OH and (NH4)2WO4Dense Degree is continuously increased, and reaction (1) and reaction (2) are strengthened, and ultimately result in (NH4)2WO4When concentration is higher, the loss of tungsten increases. Therefore, in airtight Leaching Systems, it is passed through CO2, neutralize rapidly the NH in solution4OH, makes reaction (1) be suppressed；With Time by add CaCO3Crystal seed, makes newborn CaCO3Growing up rapidly at seed surface, reduce its activity, suppression is anti-further Answer the carrying out of (1).Thus it is expected to obtain (the NH of high concentration simultaneously4)2WO4Solution and high tungsten leaching rate.
Additionally, be passed through CO in enclosed system2, it is also possible to improve CO2Utilization rate.
According to embodiments of the invention, by thick ammonium tungstate solution purification and impurity removal, the method for purification and impurity removal is not particularly limited, as long as After purification in solution the content of the impurity such as P, As, Si, Mo, S, Sn, Sb, K, Na, Ca, Mg meet prepare qualified APT product quality requires.According to one embodiment of present invention, the sedimentation method can be used to remove in ammonium tungstate solution Impurity, thus prepares ammonium tungstate refined liquid.
According to embodiments of the invention, ammonium tungstate refined liquid employing evaporative crystallization legal system can be taken APT, the bar of evaporative crystallization Part is not particularly limited.According to one embodiment of present invention, at 95 DEG C, it is 6.5 that ammonium tungstate solution is evaporated to pH, After solid-liquid separation and product wash, it is thus achieved that APT product purity meet 0 grade of product standard in GB/T 10116-2007.
Embodiment 1: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.1 times of theoretical amount, allocate grog leached mud into and (are mainly composed of CaCO3) and mineralizer calcium fluoride carry out Levigate, mixing after obtain raw material, the addition of calcium fluoride is 5.2% (mass percent) of dry tungsten mineral material amount, nodules Degree≤40 μm, then, in roaster, under air atmosphere, 800 DEG C of roasting 2.0h, obtain grog.Clinker cooling is to room temperature After, levigate with vibrating mill, grog granularity≤45 μm.Weigh 5.0g levigate after grog join band ventilation and machinery stir Mix in the reactor of device, be simultaneously introduced 50g-(NH4)2CO3/100g-H2The sal volatile 50mL of O is the most airtight, then It is passed through CO2Gas, the absolute pressure controlling reaction system is 2atm, reacts 5h at 80 DEG C.After reaction terminates, leach Ore pulp uses vacuum filtration, with pure water filter cake three times.In grog, the leaching rate of tungsten is 97.15%.
Embodiment 2: by certain Scheelite-Wolframite Mixed Mine (WO3Weight/mass percentage composition is 63.75%, and Fe weight/mass percentage composition is 5.90%) By generating Ca3WO6And Ca2FeWO61.5 times of theoretical amount, allocate into grog leached mud carry out levigate, mixing after obtain raw material, Raw material granularity≤45 μm, then, in shaft furnace, under weak reducing atmosphere, 950 DEG C of roasting 3.0h, obtain grog.Grog is cold But to after room temperature, levigate with ball mill, grog granularity≤45 μm.Weigh 20.0g grog and join band ventilation and mechanical agitation dress In the reactor put, it is simultaneously introduced 35g-(NH4)2CO3/100g-H2The sal volatile 100mL of O is the most airtight, then leads to Enter CO2Gas, the absolute pressure controlling reaction system is 2atm, reacts 4h at 70 DEG C.After reaction terminates, leach ore deposit Slurry uses vacuum filtration, with pure water filter cake three times.In grog, the leaching rate of tungsten is 87.17%.
Embodiment 3: by certain wolframite (WO3Weight/mass percentage composition is 62.40%, and Fe weight/mass percentage composition is 14.08%, Mn Weight/mass percentage composition is 2.25%) by generating Ca3WO6And Ca2FeWO6And Ca2MnO61.13 times of theoretical amount, allocate into Grog leached mud and calcium fluoride carry out levigate, mixing after obtain raw material, the addition of calcium fluoride is the 7% of dry tungsten mineral material amount (mass percent), raw material granularity≤40 μm, then, in pipe type calciner, under neutral atmosphere, roasting 6.0h at 800 DEG C, Obtain grog, after clinker cooling to room temperature, levigate with rod mill, grog granularity≤45 μm；Leaching equipment selects ball milling infuser, Built-in ammonium carbonate saturated solution, and according to 1.0 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, at 80 DEG C Lower reaction 4h.After reaction terminates, leach ore pulp and use vacuum filtration, with pure water filter cake three times.The leaching rate of tungsten is 97.13%.Then, by thick ammonium tungstate solution purification and impurity removal, after purification, solution uses evaporative crystallization to separate out APT, obtains simultaneously Ammonia and carbon dioxide, carry out solid-liquor separation to the serosity after crystallization, obtain crystalline mother solution and solid phase, and solid phase is washed through water After i.e. obtain APT product, APT product reach country 0 grade of product standard-required；The ammonia obtained returns together with carbon dioxide To leaching equipment, and in supplementary lossAmmonium carbonatePosterior circle leaches grog.
Embodiment 4: by certain wolframite (WO3Weight/mass percentage composition is 42.17%, and Fe weight/mass percentage composition is 11.34%) by raw Become Ca3WO6And Ca2FeWO61.0 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after given birth to Material, the addition of calcium fluoride is 1.5% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45 μm, then, In roaster, under week reduction atmosphere, 850 DEG C of roasting 5.0h, obtain grog, after clinker cooling to room temperature, use Ball-stirring mill Levigate, grog granularity≤45 μm；Leaching equipment selection ball milling digester, built-in ammonium carbonate saturated solution, and according to theoretical amount 1.1 times add ammonium hydrogen carbonate；Grog is put into leaching equipment, at 40 DEG C, reacts 4h.After reaction terminates, leach ore pulp and adopt With vacuum filtration, with pure water filter cake three times.The leaching rate of tungsten is 97.78%.Then, similar embodiment 3 but supplementCarbon Acid hydrogen ammonium and ammonia。
Embodiment 5: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO62.0 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride Addition is 3% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45 μm, then, at roaster neutrality gas Roasting 4h at 870 DEG C of atmosphere, obtains grog, after clinker cooling to room temperature, levigate with twin rollers, grog granularity≤45 μm；Leach The leaching tanks of equipment choice band stirring, built-in ammonium carbonate saturated solution, and according to 1.3 times of addition ammonium hydrogen carbonate of theoretical amount；Will Leaching equipment put into by grog, is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 5%) and airtight, so After be passed through carbon dioxide, the absolute pressure controlling Leaching Systems is 2atm, reacts 5h at 30 DEG C.After reaction terminates, Leach ore pulp pure water filter cake three times.The leaching rate of tungsten is 98.51%.Then, similar embodiment 3 but supplementAmmonia and CO 2。
Embodiment 6: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO62.33 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw Material granularity≤45 μm, then, roasting 7h at roaster neutral atmosphere 1000 DEG C, obtain grog, after clinker cooling to room temperature, Levigate with centrifugal mill, grog granularity≤45 μm；Leaching equipment selects ball milling infuser, and built-in sal volatile, ammonium carbonate is dense Degree is 35g-(NH4)2CO3/100g-H2O, and according to 1.3 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching set Standby, at 40 DEG C, react 9h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 98.99%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 7: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO62.33 times of theoretical amount, allocate into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤40 μm, Then, roasting 5h at roaster neutral atmosphere 950 DEG C, obtain grog, after clinker cooling to room temperature, grind with planet mill Carefully, grog granularity≤45 μm；Leaching equipment selects the leaching tanks of band stirring, built-in unsaturated carbonate ammonium and containing 20g/LWO3Tungsten Acid ammonium mixed solution, and according to 1.4 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, is simultaneously introduced ammonia (make NH in infusion solution3Weight/mass percentage composition is 9.5%) and airtight, then, it is passed through carbon dioxide, controls to leach The absolute pressure of system is 3atm, reacts 6h at 20 DEG C.After reaction terminates, leach ore pulp sucking filtration, use pure water filter cake Three times.The leaching rate of tungsten is 99.01%.Then, similar embodiment 3 but supplement ammonia and CO2。
Embodiment 8: by certain tungsten slurry (WO3Weight/mass percentage composition is 16.22%) by generating Ca3WO62.67 times of theoretical amount, Allocating into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤40 μm, then, roaster reducing atmosphere 940 DEG C Lower roasting 3h, obtains grog, after clinker cooling to room temperature；Leaching equipment selects the leaching tanks of band stirring, built-in unsaturated carbonate Ammonium and the WO Han 120g/L3Ammonium tungstate mixed solution, and according to 1.4 times of theoretical amount addition ammonium hydrogen carbonate；Grog is put into Leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 10%) and airtight, at 30 DEG C Reaction 4h.After reaction terminates, leach ore pulp, with pure water filter cake three times.The leaching rate of tungsten is 97.51%.Then, class Like embodiment 3 but supplement ammonia and CO2。
Embodiment 9: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO60.5 times of theoretical amount, allocates into after grog leached mud carries out levigate mixing and obtains raw material, raw material Granularity≤45 μm, then, roasting 1.5h at roaster neutral atmosphere 965 DEG C, obtain grog, after clinker cooling to room temperature, Levigate with twin rollers, grog granularity≤45 μm；Leaching equipment selects ball milling infuser, built-in sal volatile, ammonium carbonate concentration For 67g-(NH4)2CO3/100g-H2O, and according to 1.4 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, 6.5h is reacted at 18 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 29.30%.
Embodiment 10: by certain Scheelite-Wolframite Mixed Mine (WO3Weight/mass percentage composition is 43.20%, and Fe weight/mass percentage composition is 7.18%) By generating Ca3WO6And Ca2FeWO60.4 times of theoretical amount, allocates into after grog leached mud carries out levigate mixing and obtains raw material, Raw material granularity≤45 μm, then roasting 3h at roaster neutral atmosphere 500 DEG C, obtains grog, after clinker cooling to room temperature, Levigate with vibrating mill, grog granularity≤45 μm；Leaching equipment selects ball milling infuser, and built-in sal volatile, ammonium carbonate is dense Degree is 50g-(NH4)2CO3/100g-H2O, and according to 1.25 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching set Standby, at 28 DEG C, react 3.5h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten It is 9.76%.
Embodiment 11: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO63.0 times of theoretical amount, allocate into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤200 μm, Then, roasting 4h at roaster neutral atmosphere 950 DEG C, obtain grog, after clinker cooling to room temperature, grind with vibrating mill Carefully, grog granularity≤40 μm；The leaching tanks of leaching equipment selection band stirring, built-in ammonium carbonate saturated solution, and according to theoretical amount 1.1 times addition ammonium hydrogen carbonate；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Quality hundred Dividing content is 10%) and airtight, at 27 DEG C, react 4.5h.After reaction terminates, leach ore pulp filter pressing, filter with pure water Cake three times.The leaching rate of tungsten is 89.05%.Then, similar embodiment 3 but supplement ammonia and CO2。
Embodiment 12: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO60.77 times of theoretical amount, allocates into after grog leached mud carries out levigate mixing and obtains raw material, the addition of calcium fluoride For 1% (mass percent) of dry tungsten mineral material amount, raw material granularity≤100 μm, then, roaster neutral atmosphere 845 DEG C Lower roasting 2.5h, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤45 μm；Leaching equipment selects Select the leaching tanks of band stirring, built-in ammonium carbonate saturated solution, and add ammonium hydrogen carbonate according to 1.2 times of theoretical amount；Grog is put Enter leaching equipment, be simultaneously introduced ammonia and (make NH in infusion solution3Weight/mass percentage composition be 5.9%) and airtight, then, Being passed through carbon dioxide, the absolute pressure controlling Leaching Systems is 2.5atm, reacts 4.5h at 27 DEG C.After reaction terminates, Leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 73.65%.Then, similar embodiment 3 but supplement Ammonia and ammonium hydrogen carbonate.
Embodiment 13: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.2 times of theoretical amount, allocate into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤45 μm, Then, roasting 1h at roaster neutral atmosphere 870 DEG C, obtain grog, after clinker cooling to room temperature, use jet mill Levigate, grog granularity≤74 μm；The leaching tanks of leaching equipment selection band stirring, built-in ammonium carbonate saturated solution, and according to theory 1.4 times of addition ammonium hydrogen carbonate of amount；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Quality Percentage composition is 20%) and airtight, at 32 DEG C, react 3.8h.After reaction terminates, leach ore pulp sucking filtration, use pure water Filter cake three times.The leaching rate of tungsten is 96.15%.Then, similar embodiment 3 but supplement ammonium hydrogen carbonate.
Embodiment 14: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.5 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, fluorination The addition of calcium is 0.5% (mass percent) of dry tungsten mineral material amount, and raw material granularity≤50 μm, then, in roaster Roasting 2h at property atmosphere 920 DEG C, obtains grog, after clinker cooling to room temperature, levigate with agitator mill, grog granularity≤45 μm； Leaching equipment selects leaching device, built-in ammonium carbonate saturated solution, and adds ammonium hydrogen carbonate according to 1.2 times of theoretical amount；Will Leaching equipment put into by grog, reacts 2h at 38 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake 2 times. The leaching rate of tungsten is 98.22%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 15: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.13 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw Material granularity≤45 μm, then, roasting 2h at roaster neutral atmosphere 960 DEG C, obtain grog, after clinker cooling to room temperature, Levigate with rod mill, grog granularity≤200 μm；Leaching equipment selects ball milling infuser, built-in ammonium carbonate saturated solution, and presses According to reason 1.2 times of addition ammonium hydrogen carbonate of stoichiometric；Grog is put into leaching equipment, at 38 DEG C, reacts 5h.After reaction terminates, Leach ore pulp sucking filtration, with pure water filter cake 2 times.The leaching rate of tungsten is 98.35%.Then, similar embodiment 3, APT Product reaches 0 grade of product standard-required of country.
Embodiment 16: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.37 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw Material granularity≤61 μm, then, roasting 2h at roaster oxidizing atmosphere 970 DEG C, obtain grog, after clinker cooling to room temperature, Levigate with ball mill, grog granularity≤74 μm；Leaching equipment selection ball milling infuser, built-in ammonium carbonate saturated solution, and according to 1.4 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, at 55 DEG C, reacts 4h.After reaction terminates, leaching Go out ore pulp sucking filtration, with pure water filter cake 2 times.The leaching rate of tungsten is 97.31%.Then, similar embodiment 3, APT produces Product reach 0 grade of product standard-required of country.
Embodiment 17: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO62.17 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw Material granularity≤53 μm, then, roasting 0.5h at roaster neutral atmosphere 990 DEG C, obtain grog, after clinker cooling to room temperature, Levigate with planet mill, grog granularity≤45 μm；Leaching equipment selects leaching device, built-in ammonium carbonate saturated solution, and presses According to reason 1.5 times of addition ammonium hydrogen carbonate of stoichiometric；Grog is put into leaching equipment, at 62 DEG C, reacts 2h.After reaction terminates, Leach ore pulp sucking filtration, with pure water filter cake 5 times.The leaching rate of tungsten is 96.78%.Then, similar embodiment 3 but supplement Ammonium carbonate and ammonia, APT product reaches 0 grade of product standard-required of country.
Embodiment 18: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.57 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw Material granularity≤74 μm, then, roasting 2h at roaster neutral atmosphere 980 DEG C, obtain grog, after clinker cooling to room temperature, Levigate with high pressure disc mill, grog granularity≤45 μm；Leaching equipment selection leaching device, built-in ammonium carbonate saturated solution, and 1.6 times of addition ammonium hydrogen carbonate according to theoretical amount；Grog is put into leaching equipment, at 75 DEG C, reacts 3.5h.Reaction terminates After, leach ore pulp sucking filtration, with pure water filter cake 2 times.The leaching rate of tungsten is 97.01%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 19: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.27 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, the addition of calcium fluoride For 0.5% (mass percent) of dry tungsten mineral material amount, raw material granularity≤40 μm, then, roaster neutral atmosphere 880 DEG C Lower roasting 1h, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤45 μm；Leaching equipment selects Select the leaching tanks of band stirring, built-in ammonium carbonate saturated solution, and add ammonium hydrogen carbonate according to 1.4 times of theoretical amount；Grog is put Enter leaching equipment, be simultaneously introduced ammonia and (make NH in infusion solution3Weight/mass percentage composition be 8.2%) and airtight, then lead to Entering carbon dioxide, the absolute pressure controlling Leaching Systems is 3atm, reacts 3.8h at 32 DEG C.After reaction terminates, leaching Go out ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 98.15%.Then, similar embodiment 3 but supplement ammonia Water and CO2。
Embodiment 20: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.27 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, the addition of calcium fluoride For 5% (mass percent) of dry tungsten mineral material amount, raw material granularity≤30 μm, then, roaster neutral atmosphere 860 DEG C Lower roasting 1h, obtains grog, after clinker cooling to room temperature, levigate with tower mill, grog granularity≤45 μm；Leaching equipment Select the leaching tanks of band stirring, built-in unsaturated carbonate ammonium and the WO Han 60g/L3Ammonium tungstate mixed solution；Grog is put into leaching Go out equipment, be simultaneously introduced ammonia and (make NH in infusion solution3Weight/mass percentage composition be 15%) and airtight, then pass to two Carbon oxide gas, the absolute pressure controlling Leaching Systems is 1.2atm, reacts 6h at 35 DEG C.After reaction terminates, leach ore deposit Slurry filter pressing, with pure water filter cake three times.The leaching rate of tungsten is 98.03%.Then, similar embodiment 3 but supplement ammonia, CO2And ammonium carbonate.
Embodiment 21: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO60.67 times of theoretical amount, allocates into and obtains raw material after grog leached mud carries out levigate mixing, raw material granularity≤36 μm, Then, roasting 1h at roaster reducing atmosphere 880 DEG C, obtain grog, after clinker cooling to room temperature, use vibrating mill Levigate, grog granularity≤45 μm；The leaching tanks of leaching equipment selection band stirring, built-in ammonium carbonate saturated solution, and according to theory 1.4 times of addition ammonium hydrogen carbonate of amount；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Quality Percentage composition is 10.0%) and airtight, then passing to carbon dioxide, the absolute pressure controlling Leaching Systems is 1.5atm, 3.8h is reacted at 32 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 42.75%.Then, similar embodiment 3 but supplement ammonium hydrogen carbonate, ammonia and CO2。
Embodiment 22: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO60.6 times of theoretical amount, allocates into and obtains raw material after grog leached mud carries out levigate mixing, raw material granularity≤45 μm, Then, roasting 1h at roaster neutral atmosphere 880 DEG C, obtain grog, after clinker cooling to room temperature, levigate with ball mill, Grog granularity≤45 μm；The leaching tanks of leaching equipment selection band stirring, built-in ammonium carbonate saturated solution, and according to theoretical amount 1.4 times add ammonium hydrogen carbonate；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes the percent mass of NH3 in infusion solution Content is 7.4%) and airtight, then, it being passed through carbon dioxide, the absolute pressure controlling Leaching Systems is 1.9atm, 3.8h is reacted at 32 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 38.35%. Then, similar embodiment 3 but supplement ammonia and CO2。
Embodiment 23: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO60.5 times of theoretical amount, allocates into after grog leached mud carries out levigate mixing and obtains raw material, raw material Granularity≤33 μm, then, roasting 5h at roaster neutral atmosphere 965 DEG C, obtain grog, after clinker cooling to room temperature, use Vibrating mill is levigate, grog granularity≤74 μm；Leaching equipment selects ball milling infuser, built-in sal volatile, ammonium carbonate concentration For 80g-(NH4)2CO3/100g-H2O, and according to 1.4 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, 6.5h is reacted at 20 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 22.96%.Then, similar embodiment 3.
Embodiment 24: by certain Scheelite-Wolframite Mixed Mine (WO3Weight/mass percentage composition is 43.20%, and Fe weight/mass percentage composition is 7.18%) By generating Ca3WO6And Ca2FeWO60.97 times of theoretical amount, allocates into after grog leached mud carries out levigate mixing and obtains raw material, The addition of calcium fluoride is 2% (mass percent) of dry tungsten mineral material amount, and raw material granularity≤30 μm, then, in roasting Roasting 3h at stove neutral atmosphere 850 DEG C, obtains grog, after clinker cooling to room temperature, levigate with twin rollers, grog granularity≤74 μm； Leaching equipment selects ball milling infuser, and built-in sal volatile, ammonium carbonate concentration is 80g-(NH4)2CO3/100g-H2O, and 1.25 times of addition ammonium hydrogen carbonate according to theoretical amount；Grog is put into leaching equipment, at 28 DEG C, reacts 4h.After reaction terminates, Leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 95.71%.Then, similar embodiment 3 but supplement Ammonium carbonate, ammonium hydrogen carbonate and ammonia.
Embodiment 25: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.33 times of theoretical amount, allocate into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤28 μm, Then, roasting 4h at roaster oxidizing atmosphere 950 DEG C, obtain grog, after clinker cooling to room temperature, use grinding of ball grinder Carefully, grog granularity≤45 μm；Leaching equipment selects the leaching tanks of band stirring, built-in ammonium carbonate saturated solution；Grog is put into leaching Go out equipment, be simultaneously introduced ammonia and (make NH in infusion solution3Weight/mass percentage composition be 20%) and airtight, anti-at 27 DEG C Answer 4.5h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 98.35%.Then, Similar embodiment 3 but supplement ammonia.
Embodiment 26: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO60.77 times of theoretical amount, allocates into after grog leached mud carries out levigate mixing and obtains raw material, the addition of calcium fluoride For 4.5% (mass percent) of dry tungsten mineral material amount, raw material granularity≤41 μm, then, roaster neutral atmosphere 845 DEG C Lower roasting 2.5h, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤83 μm；Leaching equipment selects Select ball milling infuser, built-in ammonium carbonate saturated solution, and add ammonium hydrogen carbonate according to 1.2 times of theoretical amount；Grog is put into leaching Go out equipment, be simultaneously introduced ammonia (making the weight/mass percentage composition of NH3 in infusion solution is 9.8%) airtight, at 37 DEG C Reaction 4.5h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 68.65%.So After, similar embodiment 3 but supplement ammonium carbonate, ammonia and CO2。
Embodiment 27: by certain scheelite (WO3Weight/mass percentage composition is 52.27%, and Fe weight/mass percentage composition is 5.86%) by raw Become Ca3WO6And Ca2FeWO61.6 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, fluorination The addition of calcium is 2.5% (mass percent) of dry tungsten mineral material amount, and raw material granularity≤61 μm, then, in roaster Roasting 1h at property atmosphere 870 DEG C, obtains grog, after clinker cooling to room temperature, levigate with rod mill, grog granularity≤45 μm； Leaching equipment selects the leaching tanks of band stirring, built-in ammonium carbonate saturated solution, and adds ammonium hydrogen carbonate according to 1.4 times of theoretical amount； Grog is put into leaching equipment, at 32 DEG C, reacts 8.0h.After reaction terminates, leach ore pulp sucking filtration, use pure water filter cake Three times.The leaching rate of tungsten is 97.10%.Then, similar embodiment 3 but supplement ammonia and CO2。
Embodiment 28: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO6And Ca2MnO61.5 times of theoretical amount, allocate manganese spar into and limestone carries out levigate mixing After obtain raw material, raw material granularity≤14 μm, then, roasting 2h at roaster neutral atmosphere 920 DEG C, obtain grog, grog After being cooled to room temperature, levigate with vibromill, grog granularity≤45 μm；Leaching equipment selects ball milling infuser, and built-in ammonium carbonate is satisfied With solution, and according to 1.2 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, at 43 DEG C, reacts 5h. After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake 2 times.The leaching rate of tungsten is 98.42%.Then, similar real Executing example 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 29: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.63 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw Material granularity≤42 μm, then, roasting 2h at roaster neutral atmosphere 960 DEG C, obtain grog, after clinker cooling to room temperature, Levigate by planetary mills, grog granularity≤45 μm；Leaching equipment selection leaching device, built-in ammonium carbonate saturated solution, and according to 1.2 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, at 38 DEG C, reacts 5h.After reaction terminates, leaching Go out ore pulp sucking filtration, with pure water filter cake 2 times.The leaching rate of tungsten is 97.35%.Then, similar embodiment 3, APT produces Product reach 0 grade of product standard-required of country.
Embodiment 30: by certain scheelite (WO3Weight/mass percentage composition is 60.94%) by generating Ca3WO6And Ca2MnWO6 1.53 times of theoretical amount, allocate manganese spar into and grog leached mud carry out levigate mixing after obtain raw material, raw material granularity≤44 μm, Then, roasting 1.5h at roaster neutral atmosphere 980 DEG C, obtain grog, after clinker cooling to room temperature, levigate with Ball-stirring mill, Grog granularity≤45 μm；Leaching equipment selection leaching device, built-in ammonium carbonate saturated solution, and according to 1.5 times of theoretical amount Add ammonium hydrogen carbonate；Grog is put into leaching equipment, at 50 DEG C, reacts 4h.After reaction terminates, leach ore pulp sucking filtration, use Pure water filter cake 4 times.The leaching rate of tungsten is 97.99%.Then, similar embodiment 3, APT product reaches 0 grade of country Product standard-required.
Embodiment 31: by certain scheelite (WO3Weight/mass percentage composition is 60.94%) by generating Ca3WO61.43 times of theoretical amount, Allocating into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤48 μm, then, roaster neutral atmosphere 970 DEG C Lower roasting 2h, obtains grog, after clinker cooling to room temperature, levigate with rod mill, grog granularity≤45 μm；Leaching equipment selects Select leaching device, built-in ammonium carbonate saturated solution, and add ammonium hydrogen carbonate according to 1.2 times of theoretical amount；Grog is put into leaching Go out equipment, at 55 DEG C, react 4h.After reaction terminates, leach ore pulp sucking filtration, use pure water filter cake.The leaching rate of tungsten is 97.74%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 32: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.63 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw Material granularity≤38 μm, then, roasting 1h at roaster oxidizing atmosphere 990 DEG C, obtain grog, after clinker cooling to room temperature, Levigate with ball mill, grog granularity≤45 μm；Leaching equipment selection leaching device, built-in ammonium carbonate saturated solution, and according to 1.5 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, at 62 DEG C, reacts 4h.After reaction terminates, leaching Go out ore pulp sucking filtration, with pure water filter cake 5 times.The leaching rate of tungsten is 97.78%.Then, similar embodiment 3, APT produces Product reach 0 grade of product standard-required of country.
Embodiment 33: by certain scheelite (WO3Weight/mass percentage composition is 60.94%) by generating Ca3WO61.7 times of theoretical amount, Allocating into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤63 μm, then, roaster neutral atmosphere 980 DEG C Lower roasting 2h, obtains grog, after clinker cooling to room temperature, levigate with Ball-stirring mill, grog granularity≤45 μm；Leaching equipment selects Select leaching device, built-in ammonium carbonate saturated solution, and add ammonium hydrogen carbonate according to 1.3 times of theoretical amount；Grog is put into leaching Go out equipment, at 75 DEG C, react 0.5h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake 2 times.The leaching of tungsten Going out rate is 97.51%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 34: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO6And Ca2MnWO61.7 times of theoretical amount, allocate manganese spar into and grog leached mud carry out levigate mixing after obtain Raw material, the addition of calcium fluoride is 6.0% (mass percent) of dry tungsten mineral material amount, raw material granularity≤36 μm, then, Roasting 1h at roaster neutral atmosphere 880 DEG C, obtains grog, after clinker cooling to room temperature, levigate with Ball-stirring mill, grog Granularity≤45 μm；The leaching tanks of leaching equipment selection band stirring, built-in ammonium carbonate saturated solution, and according to 1.5 times of theoretical amount Add ammonium hydrogen carbonate；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition It is 5.0%) and airtight, at 32 DEG C, react 3.8h.After reaction terminates, leach ore pulp filter pressing, with pure water filter cake three times. The leaching rate of tungsten is 98.15%.Then, similar embodiment 3 but supplement ammonium carbonate, ammonium hydrogen carbonate, ammonia and CO2。
Embodiment 35: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO6And Ca2MnWO61.7 times of theoretical amount, allocate manganese spar into and grog leached mud carry out levigate mixing after obtain Raw material, raw material granularity≤36 μm, then, and roasting 1h at roaster neutral atmosphere 880 DEG C, obtain grog, clinker cooling is extremely After room temperature, levigate with Ball-stirring mill, grog granularity≤45 μm；Leaching equipment selects the leaching tanks of band stirring, and built-in ammonium carbonate is saturated Solution, and according to 1.5 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes leaching NH in solution3Weight/mass percentage composition be 5.0%) and airtight, at 32 DEG C, react 3.8h.After reaction terminates, leach ore deposit Slurry filter pressing, with pure water filter cake three times.The leaching rate of tungsten is 86.23%.Then, similar embodiment 3 but supplement ammonium carbonate, Ammonium hydrogen carbonate, ammonia and CO2。
Embodiment 36: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO60.83 times of theoretical amount, allocates into after grog leached mud carries out levigate mixing and obtains raw material, the addition of calcium fluoride For 4.5% (mass percent) of dry tungsten mineral material amount, raw material granularity≤37 μm, then, in roaster reducing atmosphere Roasting 1h at 880 DEG C, obtains grog, after clinker cooling to room temperature, levigate with vibromill, grog granularity≤53 μm；Leaching sets The leaching tanks of alternative band stirring, built-in ammonium carbonate saturated solution, and according to 1.15 times of addition ammonium hydrogen carbonate of theoretical amount；Will Leaching equipment put into by grog, is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 4.1%) and airtight, Then, being passed through carbon dioxide, the absolute pressure controlling Leaching Systems is 1.3atm, reacts 9h at 32 DEG C.Reaction knot Shu Hou, leaches ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 74.75%.Then, similar embodiment 3 But supplement ammonium hydrogen carbonate, ammonia and CO2。
Embodiment 37: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO60.73 times of theoretical amount, allocates into after limestone carries out levigate mixing and obtains raw material, and the addition of calcium fluoride is dry 1.5% (mass percent) of tungsten mineral material amount, raw material granularity≤24 μm, then, roaster reducing atmosphere 880 DEG C Lower roasting 3h, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤74 μm；Leaching equipment selects Select ball milling infuser, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, at 32 DEG C, reacts 8.0h.Reaction knot Shu Hou, leaches ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 55.45%.Then, similar embodiment 3 But supplement ammonia and CO2。
Embodiment 38: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO63.33 times of theoretical amount, allocate siderite into and grog leached mud carry out levigate mixing after obtain Raw material, raw material granularity≤38 μm, then, and roasting 1h at roaster neutral atmosphere 950 DEG C, obtain grog, clinker cooling is extremely After room temperature, levigate with vibromill, grog granularity≤45 μm；Leaching equipment selects ball milling infuser, built-in sal volatile, carbon Acid ammonium concentration is 58g-(NH4)2CO3/100g-H2O, and according to 1.3 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into Leaching equipment, reacts 9h at 40 DEG C.After reaction terminates, leach ore pulp filter pressing, with pure water filter cake three times.The leaching of tungsten Going out rate is 96.93%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 39: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.7 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, and the addition of calcium fluoride is 1.0% (mass percent) of dry tungsten mineral material amount, raw material granularity≤33 μm, then, roaster neutral atmosphere 895 DEG C Lower roasting 8h, obtains grog, after clinker cooling to room temperature, levigate with vibromill, grog granularity≤45 μm；Leaching equipment selects Select the leaching tanks of band stirring, built-in ammonium carbonate saturated solution, and add ammonium hydrogen carbonate according to 1.9 times of theoretical amount；Grog is put Enter leaching equipment, at 20 DEG C, react 6h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.Tungsten Leaching rate is 95.01%.Then, similar embodiment 3 but supplement ammonia and CO2。
Embodiment 40: by certain tungsten slurry (WO3Weight/mass percentage composition is 16.22%) by generating Ca3WO61.3 times of theoretical amount, Allocating into and obtain raw material after limestone carries out levigate mixing, raw material granularity≤40 μm, then, roaster reducing atmosphere 940 DEG C Lower roasting 3h, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤45 μm；Leaching equipment selects Select the leaching tanks of band stirring, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes leaching molten NH in liquid3Weight/mass percentage composition be 12%) and airtight, at 50 DEG C, react 4h.After reaction terminates, leach ore pulp and take out Filter, with pure water filter cake three times.The leaching rate of tungsten is 92.31%.Then, similar embodiment 3 but supplement ammonia and CO2。
Embodiment 41: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO62.17 times of theoretical amount, allocate into after limestone carries out levigate mixing and obtain raw material, calcium fluoride 0.7% (mass percent) that addition is dry tungsten mineral material amount, raw material granularity≤30 μm, then, neutral at roaster Roasting 1.5h at atmosphere 965 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤74 μm； Leaching equipment selects ball milling infuser, and built-in sal volatile, ammonium carbonate concentration is 67g-(NH4)2CO3/100g-H2O, and 1.4 times of addition ammonium hydrogen carbonate according to theoretical amount；Grog is put into leaching equipment, at 10 DEG C, reacts 20.0h.Reaction terminates After, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 91.96%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 42: by certain Scheelite-Wolframite Mixed Mine (WO3Weight/mass percentage composition is 43.20%, and Fe weight/mass percentage composition is 7.18%) By generating Ca3WO6And Ca2FeWO61.2 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, The addition of calcium fluoride is 2.6% (mass percent) of dry tungsten mineral material amount, and raw material granularity≤25 μm, then, in roasting Roasting 3h at stove neutral atmosphere 850 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤74 μm； Leaching equipment selects ball milling infuser, and built-in sal volatile, ammonium carbonate concentration is 70g-(NH4)2CO3/100g-H2O, and 1.2 times of addition ammonium hydrogen carbonate according to theoretical amount；Grog is put into leaching equipment, at 40 DEG C, reacts 3.5h.Reaction terminates After, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 98.76%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 43: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO63.33 times of theoretical amount, allocate into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤28 μm, Then, roasting 4h at roaster neutral atmosphere 845 DEG C, obtain grog, after clinker cooling to room temperature, levigate with vibromill, Grog granularity≤74 μm；Leaching equipment selects the leaching tanks of band stirring, built-in ammonium carbonate saturated solution；Grog is put into leaching set Standby, it is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 28%) and airtight, at 27 DEG C, react 4.5h. After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 96.01%.Then, similar real Execute example 3 but supplement ammonium carbonate, ammonia and CO2。
Embodiment 44: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.17 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, the addition of calcium fluoride For 5.5% (mass percent) of dry tungsten mineral material amount, raw material granularity≤40 μm, then, roaster neutral atmosphere 845 DEG C Lower roasting 10h, obtains grog, after clinker cooling to room temperature, levigate with twin rollers, grog granularity≤150 μm；Leaching equipment Select ball milling infuser, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes infusion solution Middle NH3Weight/mass percentage composition be 7.5%) and airtight, at 27 DEG C, react 4.5h.After reaction terminates, leach ore pulp and take out Filter, with pure water filter cake three times.The leaching rate of tungsten is 98.49%.Then, similar embodiment 3 but supplement ammonia and CO2。
Embodiment 45: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.5 times of theoretical amount, allocate into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤45 μm, Then, roasting 6h at roaster neutral atmosphere 1050 DEG C, obtain grog, after clinker cooling to room temperature, levigate with rod mill, Grog granularity≤45 μm；Leaching equipment selects the leaching tanks of band stirring, built-in ammonium carbonate saturated solution；Grog is put into leaching set Standby, it is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 9.1%) and airtight, react at 32 DEG C 3.8h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 97.15%.Then, Similar embodiment 3 but supplement ammonium hydrogen carbonate, ammonia and CO2。
Embodiment 46: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.5 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, fluorination The addition of calcium is 6% (mass percent) of dry tungsten mineral material amount, and raw material granularity≤45 μm, then, in roaster Roasting 0.5h at property atmosphere 995 DEG C, obtains grog, after clinker cooling to room temperature, levigate with Raymond mill, grog granularity≤8 μm； Leaching equipment selects leaching device, built-in ammonium carbonate saturated solution, and adds ammonium hydrogen carbonate according to 1.2 times of theoretical amount；Will Leaching equipment put into by grog, reacts 5h at 38 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake 2 times. The leaching rate of tungsten is 97.22%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 47: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.83 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, fluorine Changing 2% (mass percent) that addition is dry tungsten mineral material amount of calcium, raw material granularity≤45 μm, then, at roaster Roasting 2h at reducing atmosphere 960 DEG C, obtains grog, after clinker cooling to room temperature, levigate with jet mill, grog grain Degree≤20 μm；Leaching equipment selects leaching device, built-in ammonium carbonate saturated solution, and adds carbon according to 1.2 times of theoretical amount Acid hydrogen ammonium；Grog is put into leaching equipment, at 38 DEG C, reacts 5h.After reaction terminates, leach ore pulp sucking filtration, wash with pure water Wash filter cake 2 times.The leaching rate of tungsten is 98.16%.Then, similar embodiment 3, APT product reaches 0 grade of product standard of country Requirement.
Embodiment 48: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.4 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, fluorination The addition of calcium is 3.5% (mass percent) of dry tungsten mineral material amount, and raw material granularity≤45 μm, then, in roaster Roasting 0.5h at property atmosphere 850 DEG C, obtains grog, after clinker cooling to room temperature, levigate with Raymond mill, grog granularity≤8 μm； Leaching equipment selects leaching device, built-in ammonium carbonate saturated solution, and adds ammonium hydrogen carbonate according to 1.5 times of theoretical amount；Will Leaching equipment put into by grog, reacts 4h at 50 DEG C.After reaction terminates, leach ore pulp filter pressing, with pure water filter cake 4 times. The leaching rate of tungsten is 98.33%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 49: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.37 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw Material granularity≤53 μm, then, roasting 8h at roaster neutral atmosphere 930 DEG C, obtain grog, after clinker cooling to room temperature, Levigate with overhang roll pulverizer, grog granularity≤45 μm；Leaching equipment selection leaching device, built-in ammonium carbonate saturated solution, and 1.1 times of addition ammonium hydrogen carbonate according to theoretical amount；Grog is put into leaching equipment, at 25 DEG C, reacts 4h.After reaction terminates, Leach ore pulp sucking filtration, with pure water filter cake 2 times.The leaching rate of tungsten is 94.22%.Then, similar embodiment 3, APT Product reaches 0 grade of product standard-required of country.
Embodiment 50: by certain scheelite (WO3Weight/mass percentage composition is 60.94%) by generating Ca3WO61.87 times of theoretical amount, Allocating into after grog leached mud carries out levigate mixing and obtain raw material, the addition of calcium fluoride is 2.5% (matter of dry tungsten mineral material amount Amount percent), raw material granularity≤53 μm, then, and roasting 1h at roaster neutral atmosphere 910 DEG C, obtain grog, grog After being cooled to room temperature, levigate with ball mill, grog granularity≤45 μm；Leaching equipment selects leaching device, and built-in ammonium carbonate is satisfied With solution, and according to 1.5 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, at 62 DEG C, reacts 4h. After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake 5 times.The leaching rate of tungsten is 98.78%.Then, similar real Executing example 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 51: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.57 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, fluorine Changing 2.8% (mass percent) that addition is dry tungsten mineral material amount of calcium, raw material granularity≤74 μm, then, at roaster Roasting 2h at neutral atmosphere 900 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤45 μm； Leaching equipment selects leaching device, built-in ammonium carbonate saturated solution, and adds ammonium hydrogen carbonate according to 1.6 times of theoretical amount；Will Leaching equipment put into by grog, reacts 1.5h at 75 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake 2 Secondary.The leaching rate of tungsten is 95.01%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 52: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.27 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, the addition of calcium fluoride For 3.3% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45 μm, then, roaster neutral atmosphere 880 DEG C Lower roasting 1h, obtains grog, after clinker cooling to room temperature, levigate with vibromill, grog granularity≤45 μm；Leaching equipment selects Select the leaching tanks of band stirring, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes leaching molten NH in liquid3Weight/mass percentage composition be 8.0%) and airtight, at 50 DEG C, react 3.8h.After reaction terminates, leach ore pulp Sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 96.15%.Then, similar embodiment 3 but supplement ammonia and CO2。
Embodiment 53: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.6 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, and the addition of calcium fluoride is 7% (mass percent) of dry tungsten mineral material amount, raw material granularity≤40 μm, then, at roaster neutral atmosphere 810 DEG C Roasting 1h, obtains grog, after clinker cooling to room temperature, levigate by planetary mills, grog granularity≤45 μm；Leaching equipment selects The leaching tanks of band stirring, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes infusion solution Middle NH3Weight/mass percentage composition be 5.5%) and airtight, at 45 DEG C, react 6h.After reaction terminates, leach ore pulp sucking filtration, With pure water filter cake three times.The leaching rate of tungsten is 98.63%.Then, similar embodiment 3 but supplement ammonia and CO2。
Embodiment 54: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.0 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, and the addition of calcium fluoride is 5% (mass percent) of dry tungsten mineral material amount, raw material granularity≤96 μm, then, roaster reducing atmosphere 880 DEG C Lower roasting 1h, obtains grog, after clinker cooling to room temperature, levigate with Ball-stirring mill, grog granularity≤45 μm；Leaching equipment selects Select the leaching tanks of band stirring, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes leaching molten In liquid, the weight/mass percentage composition of NH3 is 3.5%) and airtight, at 32 DEG C, react 3.8h.After reaction terminates, leach ore pulp Sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 96.75%.Then, similar embodiment 3 but supplement ammonia and CO2。
Embodiment 55: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO64.0 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, and the addition of calcium fluoride is 1.5% (mass percent) of dry tungsten mineral material amount, raw material granularity≤36 μm, then, roaster neutral atmosphere 750 DEG C Lower roasting 5h, obtains grog, after clinker cooling to room temperature, levigate with twin rollers, grog granularity≤100 μm；Leaching equipment selects Select ball milling infuser, built-in ammonium carbonate saturated solution, and add ammonium hydrogen carbonate according to 1.4 times of theoretical amount；Grog is put into leaching Go out equipment, at 32 DEG C, react 3.8h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching of tungsten Going out rate is 86.35%.
Embodiment 56: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO62.33 times of theoretical amount, allocate into after limestone carries out levigate mixing and obtain raw material, nodules Degree≤106 μm, then, roasting 7h at roaster neutral atmosphere 1000 DEG C, obtain grog, after clinker cooling to room temperature, use Vibromill is levigate, grog granularity≤45 μm；Leaching equipment selects ball milling infuser, and built-in sal volatile, ammonium carbonate concentration is 35g-(NH4)2CO3/100g-H2O, and according to 1.3 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, 9h is reacted at 40 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 95.99%. Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 57: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO62.33 times of theoretical amount, allocate into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤45 μm, Then, roasting 5h at roaster neutral atmosphere 1200 DEG C, obtain grog, after clinker cooling to room temperature, levigate with vibromill, Grog granularity≤74 μm；Leaching equipment selection ball milling infuser, built-in ammonium carbonate saturated solution, and according to 1.4 times of theoretical amount Add ammonium hydrogen carbonate；Grog is put into leaching equipment, at 20 DEG C, reacts 6h.After reaction terminates, leach ore pulp sucking filtration, use Pure water filter cake three times.The leaching rate of tungsten is 78.01%.
Embodiment 58: by certain tungsten slurry (WO3Weight/mass percentage composition is 16.22%) by generating Ca3WO62.67 times of theoretical amount, Allocating into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤96 μm, then, at roaster reducing atmosphere Roasting 3h at 1400 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤45 μm；Leach The leaching tanks of equipment choice band stirring, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 6%) and airtight, at 30 DEG C, react 4h.After reaction terminates, leach ore deposit Slurry sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 81.51%.Then, similar embodiment 3 but supplement ammonium carbonate, Ammonium hydrogen carbonate, ammonia and CO2。
Embodiment 59: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.17 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw Material granularity≤45 μm, then, roasting 8h at roaster neutral atmosphere 965 DEG C, obtain grog, after clinker cooling to room temperature, Levigate with centrifugal mill, grog granularity≤45 μm；Leaching equipment selects ball milling infuser, and built-in sal volatile, ammonium carbonate is dense Degree is 20g-(NH4)2CO3/100g-H2O, and according to 1.4 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching set Standby, at 18 DEG C, react 6.5h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten It is 92.96%.Then, similar embodiment 3.
Embodiment 60: by certain Scheelite-Wolframite Mixed Mine (WO3Weight/mass percentage composition is 43.20%, and Fe weight/mass percentage composition is 7.18%) By generating Ca3WO6And Ca2FeWO61.07 times of theoretical amount, allocate grog leached mud into and after calcium fluoride carries out levigate mixing Obtaining raw material, the addition of calcium fluoride is 1.5% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45μM, so After, roasting 3h at roaster neutral atmosphere 850 DEG C, obtain grog, after clinker cooling to room temperature, levigate with vibromill, Grog granularity≤45 μm；Leaching equipment selection ball milling infuser, built-in ammonium carbonate saturated solution, and according to the 1.25 of theoretical amount Add ammonium hydrogen carbonate again；Grog is put into leaching equipment, at 28 DEG C, reacts 3.5h.After reaction terminates, leach ore pulp sucking filtration, With pure water filter cake three times.The leaching rate of tungsten is 96.76%.Then, similar embodiment 3, APT product reaches country 0 Level product standard-required.
Embodiment 61: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO63.0 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride Addition is 1% (mass percent) of dry tungsten mineral material amount, and raw material granularity≤45 μm, then, in roaster neutral atmosphere Roasting 4h at 950 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤96 μm；Leaching sets Alternative ball milling infuser, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes leaching molten NH in liquid3Weight/mass percentage composition be 5.9%) and airtight, at 47 DEG C, react 4.5h.After reaction terminates, leach ore pulp Sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 98.15%.Then, similar embodiment 3 but supplement ammonia and CO2。
Embodiment 62: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.07 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride 2.8% (mass percent) that addition is dry tungsten mineral material amount, raw material granularity≤45 μm, then, neutral at roaster Roasting 5h at atmosphere 845 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤45 μm；Leaching Going out the leaching tanks of equipment choice band stirring, built-in sal volatile, ammonium carbonate concentration is 40g-(NH4)2CO3/100g-H2O； Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 4%) and airtight, 4.5h is reacted at 45 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 97.65%.Then, similar embodiment 3 but supplement ammonia and CO2。
Embodiment 63: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.27 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride 1.2% (mass percent) that addition is dry tungsten mineral material amount, raw material granularity≤120 μm, then, in roaster Roasting 3h at property atmosphere 870 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤45 μm； The leaching tanks of leaching equipment selection band stirring, built-in sal volatile, ammonium carbonate concentration is 45g-(NH4)2CO3/100g-H2O； Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 7.9%) and airtight, 15h is reacted at 5 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 93.15%. Then similar embodiment 3 but supplement ammonium carbonate, ammonia and CO2。
Embodiment 64: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.5 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after given birth to Material, the addition of calcium fluoride is 5.4% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45 μm, then, Roasting 4h at roaster neutral atmosphere 750 DEG C, obtains grog, after clinker cooling to room temperature, levigate with vibromill, grog grain Degree≤45 μm；Leaching equipment selects ball milling infuser, built-in ammonium carbonate saturated solution, and adds carbon according to 1.2 times of theoretical amount Acid hydrogen ammonium；Grog is put into leaching equipment, at 38 DEG C, reacts 5h.After reaction terminates, leach ore pulp sucking filtration, wash with pure water Wash filter cake 2 times.The leaching rate of tungsten is 97.22%.Then, similar embodiment 3, APT product reaches 0 grade of product standard of country Requirement.
Embodiment 65: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.13 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain Raw material, the addition of calcium fluoride is 3% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45 μm, then, Roasting 15h at roaster neutral atmosphere 760 DEG C, obtains grog, after clinker cooling to room temperature, levigate with rod mill, grog grain Degree≤45 μm；Leaching equipment selects leaching device, built-in ammonium carbonate saturated solution, and adds carbon according to 1.2 times of theoretical amount Acid hydrogen ammonium；Grog is put into leaching equipment, at 38 DEG C, reacts 5h.After reaction terminates, leach ore pulp sucking filtration, wash with pure water Wash filter cake 2 times.The leaching rate of tungsten is 97.35%.Then, similar embodiment 3, APT product reaches 0 grade of product standard of country Requirement.
Embodiment 66: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.4 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw material Granularity≤45 μm, then, roasting 8h at roaster neutral atmosphere 980 DEG C, obtain grog, after clinker cooling to room temperature, use Ball mill is levigate, grog granularity≤45 μm；Leaching equipment selection leaching device, built-in ammonium carbonate saturated solution, and according to reason 4 times of addition ammonium hydrogen carbonate of stoichiometric；Grog is put into leaching equipment, at 50 DEG C, reacts 4h.After reaction terminates, leach ore deposit Slurry sucking filtration, with pure water filter cake 4 times.The leaching rate of tungsten is 96.33%.Then, similar embodiment 3, APT product reaches To 0 grade of product standard-required of country.
Embodiment 67: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.37 times of theoretical amount, allocate limestone into and fluorite carry out levigate mixing after obtain raw material, The addition of fluorite is 6% (mass percent) of dry tungsten mineral material amount, and raw material granularity≤48 μm, then, in roaster Roasting 2h at property atmosphere 970 DEG C, obtains grog, after clinker cooling to room temperature, levigate with agitator mill, grog granularity≤40 μm； Leaching equipment selects leaching device, and built-in sal volatile, ammonium carbonate concentration is 25g-(NH4)2CO3/100g-H2O, and 1.4 times of addition ammonium hydrogen carbonate according to theoretical amount；Grog is put into leaching equipment, at 80 DEG C, reacts 0.5h.Reaction terminates After, leach ore pulp sucking filtration, with pure water filter cake 2 times.The leaching rate of tungsten is 96.36%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 68: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO62.17 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw Material granularity≤53 μm, then, roasting 8h at roaster neutral atmosphere 990 DEG C, obtain grog, after clinker cooling to room temperature, Levigate with rod mill, grog granularity≤74 μm；Leaching equipment selection ball milling infuser, built-in ammonium carbonate saturated solution, and according to 3 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, at 62 DEG C, reacts 4h.After reaction terminates, leach Ore pulp sucking filtration, with pure water filter cake 5 times.The leaching rate of tungsten is 97.70%.Then, similar embodiment 3, APT product Reach 0 grade of product standard-required of country.
Embodiment 69: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.57 times of theoretical amount, allocate grog leached mud into and fluorite carry out levigate mixing after given birth to Material, the addition of fluorite is 4% (mass percent) of dry tungsten mineral material amount, and raw material granularity≤45 μm, then, in roasting Roasting 2h at stove neutral atmosphere 980 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤40 μm； Leaching equipment selects leaching device, built-in ammonium carbonate saturated solution, and adds ammonium hydrogen carbonate according to 1.6 times of theoretical amount；Will Leaching equipment put into by grog, reacts 3.5h at 75 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake 2 Secondary.The leaching rate of tungsten is 97.01%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 70: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.07 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride 2.5% (mass percent) that addition is dry tungsten mineral material amount, raw material granularity≤36 μm, then, neutral at roaster Roasting 1h at atmosphere 880 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤45 μm；Leaching Go out the leaching tanks of equipment choice band stirring, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 6.7%) and airtight, at 90 DEG C, react 0.5h.After reaction terminates, leaching Go out ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 93.15%.Then similar embodiment 3 but supplement ammonia And CO2。
Embodiment 71: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.27 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride 3.6% (mass percent) that addition is dry tungsten mineral material amount, raw material granularity≤90 μm, then, neutral at roaster Roasting 1h at atmosphere 860 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤45 μm；Leaching Go out the leaching tanks of equipment choice band stirring, built-in ammonium carbonate saturated solution, and add ammonium hydrogen carbonate according to 1.1 times of theoretical amount； Grog is put into leaching equipment, at 45 DEG C, reacts 6h.After reaction terminates, leach ore pulp filter pressing, with pure water filter cake three Secondary.The leaching rate of tungsten is 97.09%.Then, similar embodiment 3 but supplement ammonium carbonate, ammonium hydrogen carbonate, ammonia and CO2。
Embodiment 72: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.03 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride 4.8% (mass percent) that addition is dry tungsten mineral material amount, raw material granularity≤45 μm, then, roaster reduce Roasting 1h at property atmosphere 880 DEG C, obtains grog, after clinker cooling to room temperature, levigate with vibromill, grog granularity≤74 μm； Leaching equipment selection ball milling infuser, built-in ammonium carbonate saturated solution,；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 7.5%) and airtight, at 32 DEG C, react 3.8h.After reaction terminates, leaching Go out ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 97.75%.Then, similar embodiment 3 but supplement ammonia Water and CO2。
Embodiment 73: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.27 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride 0.7% (mass percent) that addition is dry tungsten mineral material amount, raw material granularity≤45 μm, then, neutral at roaster Roasting 9h at atmosphere 880 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤74 μm；Leaching Go out equipment choice ball milling infuser, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes leaching Go out NH in solution3Weight/mass percentage composition be 8.6%) and airtight, at 32 DEG C, react 3.8h.After reaction terminates, leach Ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 98.65%.Then similar embodiment 3 but supplement ammonium carbonate, Ammonia and CO2。
Embodiment 74: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.23 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride 4.5% (mass percent) that addition is dry tungsten mineral material amount, raw material granularity≤45 μm, then, in roaster, Under air atmosphere, 800 DEG C of roasting 2.0h, obtain grog.Clinker cooling is to after room temperature, levigate with vibrating mill, grog grain Degree≤45 μm.Weigh 25.0g levigate after grog join band ventilation and mechanical stirring device reactor in, be simultaneously introduced 60g-(NH4)2CO3/100g-H2The sal volatile 100mL of O is the most airtight, then, is passed through CO2Gas, controls reaction The absolute pressure of system is 2atm, reacts 4h at 80 DEG C.After reaction terminates, leach ore pulp and use vacuum filtration, use pure water Washing filter cake three times.In grog, the leaching rate of tungsten is 97.25%.
Embodiment 75: by certain Scheelite-Wolframite Mixed Mine (WO3Weight/mass percentage composition is 63.75%, and Fe weight/mass percentage composition is 5.90%) By generating Ca3WO6And Ca2FeWO61.5 times of theoretical amount, allocate grog leached mud into and calcium fluoride is carried out after levigate mixing To raw material, the addition of calcium fluoride is 0.5% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45 μm, then, In shaft furnace, under weak reducing atmosphere, 1000 DEG C of roasting 3.0h, obtain grog.Clinker cooling, to after room temperature, uses ball mill Levigate, grog granularity≤45 μm.Weigh 30.0g levigate after grog join band ventilation and mechanical stirring device reactor in, It is simultaneously introduced 45g-(NH4)2CO3/100g-H2The sal volatile 100mL of O is the most airtight, then passes to CO2Gas, control The absolute pressure of reaction system processed is 2atm, reacts 4h at 70 DEG C.After reaction terminates, leach ore pulp and use vacuum filtration, With pure water filter cake three times.In grog, the leaching rate of tungsten is 95.17%.
Embodiment 76: by certain wolframite (WO3Weight/mass percentage composition is 60.40%, and Fe weight/mass percentage composition is 15.08%) press Generate Ca3WO6And Ca2FeWO61.27 times of theoretical amount, allocate grog leached mud into and after calcium fluoride carries out levigate, mixing Obtaining raw material, the addition of calcium fluoride is 3% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45 μm, then, In pipe type calciner, under neutral atmosphere, roasting 6.0h at 800 DEG C, obtain grog, after clinker cooling to room temperature, use rod milling Machine is levigate, grog granularity≤45 μm；The leaching tanks of leaching equipment selection band stirring, built-in ammonium carbonate saturated solution, and according to reason 1.2 times of addition ammonium hydrogen carbonate of stoichiometric；Grog is put into leaching equipment, at 80 DEG C, reacts 4h.After reaction terminates, leach Ore pulp uses vacuum filtration, with pure water filter cake three times.The leaching rate of tungsten is 97.13%.Then, similar embodiment 3 is mended Fill the ammonium carbonate of loss.
Embodiment 77: by certain wolframite (WO3Weight/mass percentage composition is 42.17%, and Fe weight/mass percentage composition is 11.34%) press Generate Ca3WO6And Ca2FeWO61.17 times of theoretical amount, allocate grog leached mud into and calcium fluoride is carried out after levigate mixing To raw material, the addition of calcium fluoride is 0.9% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45 μm.Then, In roaster, under week reduction atmosphere, 950 DEG C of roasting 5.0h, obtain grog, after clinker cooling to room temperature, with stirring Grind levigate, grog granularity≤40 μm；Leaching equipment selection ball milling digester, built-in ammonium carbonate saturated solution, and according to theoretical amount 1.1 times addition ammonium hydrogen carbonate；Grog is put into leaching equipment, at 75 DEG C, reacts 4h.After reaction terminates, leach ore pulp Use vacuum filtration, with pure water filter cake three times.The leaching rate of tungsten is 96.78%.Then, similar embodiment 3 but supplement Ammonium hydrogen carbonate.
Embodiment 78: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO62.0 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride Addition is 2.4% (mass percent) of dry tungsten mineral material amount, and raw material granularity≤30 μm, then in roaster neutral atmosphere Roasting 4h at 870 DEG C, obtains grog, after clinker cooling to room temperature, levigate by planetary mills, grog granularity≤74 μm；Leaching sets Alternative ball milling infuser, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes leaching molten NH in liquid3Weight/mass percentage composition be 6.5%) and airtight, at 30 DEG C, react 4h.After reaction terminates, leach ore pulp and take out Filter, with pure water filter cake three times.The leaching rate of tungsten is 98.09%.Then similar embodiment 3 but supplement ammonia and CO2。
Embodiment 79: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO62.33 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw Material granularity≤25 μm, then, roasting 7h at roaster neutral atmosphere 1000 DEG C, obtain grog, after clinker cooling to room temperature, Levigate with vibrating mill, grog granularity≤45 μm；Leaching equipment selects ball milling infuser, and built-in sal volatile, ammonium carbonate is dense Degree is 60g-(NH4)2CO3/100g-H2O, and according to 1.3 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching set Standby, at 40 DEG C, react 9h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 98.03%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 80: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.0 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride Addition is 3.2% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45 μm, then, at roaster neutrality gas Roasting 5h at 950 DEG C of atmosphere, obtains grog, after clinker cooling to room temperature, levigate with Raymond mill, grog granularity≤8 μm；Leaching Go out the leaching tanks of equipment choice band stirring, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 10.0%) and airtight, the absolute pressure controlling Leaching Systems is 1.0atm, 12h is reacted at 20 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 96.20%.Then, similar embodiment 3 but supplement ammonium hydrogen carbonate, ammonia and CO2。
Embodiment 81: by certain tungsten slurry (WO3Weight/mass percentage composition is 16.22%) by generating Ca3WO62.67 times of theoretical amount, Allocating into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤45 μm, then, roaster reducing atmosphere 950 DEG C Lower roasting 3h, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤45 μm；Leaching equipment selects Select the leaching tanks of band stirring, built-in ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes leaching molten NH in liquid3Weight/mass percentage composition be 6.3%) and airtight, at 35 DEG C, react 15h.After reaction terminates, leach ore pulp and take out Filter, with pure water filter cake three times.The leaching rate of tungsten is 91.51%.Then, ammonia and CO are supplemented2。
Embodiment 82: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.2 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after given birth to Material, the addition of calcium fluoride is 4.1% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45 μm, then, Roasting 1.5h at roaster neutral atmosphere 965 DEG C, obtains grog, after clinker cooling to room temperature, levigate with vibromill, grog grain Degree≤60 μm；Leaching equipment selects ball milling infuser, and built-in ammonium carbonate-ammonium tungstate mixed solution, ammonium carbonate concentration is 45g-(NH4)2CO3/100g-H2O, WO in solution3Concentration is 40g/L, and according to 2 times of addition ammonium hydrogen carbonate of theoretical amount； Grog is put into leaching equipment, at 18 DEG C, reacts 6.5h.After reaction terminates, leach ore pulp sucking filtration, use pure water filter cake Three times.The leaching rate of tungsten is 97.96%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 83: by certain Scheelite-Wolframite Mixed Mine (WO3Weight/mass percentage composition is 43.20%, and Fe weight/mass percentage composition is 7.18%) By generating Ca3WO6And Ca2FeWO61.1 times of theoretical amount, allocate grog leached mud into and calcium fluoride is carried out after levigate mixing To raw material, the addition of calcium fluoride is 2.2% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45 μm, then Roasting 3h at roaster neutral atmosphere 850 DEG C, obtains grog, after clinker cooling to room temperature, levigate with rod mill, grog Granularity≤45 μm；Leaching equipment selects ball milling infuser, and built-in sal volatile, ammonium carbonate concentration is 40g-(NH4)2CO3 /100g-H2O, and according to 1.25 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, reacts at 42 DEG C 20h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 98.76%.Then, Similar embodiment 3 but supplement ammonium carbonate and ammonium hydrogen carbonate, APT product reaches 0 grade of product standard-required of country.
Embodiment 84: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO63.0 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride Addition is 0.55% (mass percent) of dry tungsten mineral material amount, raw material granularity≤30 μm, then, neutral at roaster Roasting 4h at atmosphere 950 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤45 μm；Leaching Go out the leaching tanks of equipment choice band stirring, built-in unsaturated carbonate ammonium and the WO Han 60g/L3Ammonium tungstate mixed solution；By grog Put into leaching equipment, be simultaneously introduced ammonia and (make NH in infusion solution3Weight/mass percentage composition be 9.1%) and airtight, at 37 DEG C Lower reaction 4.5h.After reaction terminates, leach ore pulp filter pressing, with pure water filter cake three times.The leaching rate of tungsten is 98.72%. Then similar embodiment 3 but supplement ammonia and CO2。
Embodiment 85: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO60.9 times of theoretical amount, allocates into and obtains raw material after grog leached mud carries out levigate mixing, raw material granularity≤45 μm, Then, roasting 2.5h at roaster neutral atmosphere 845 DEG C, obtain grog, after clinker cooling to room temperature, use overhang roll pulverizer Levigate, grog granularity≤74 μm；The leaching tanks of leaching equipment selection band stirring, built-in ammonium carbonate saturated solution, and according to theory 1.2 times of addition ammonium hydrogen carbonate of amount；Grog is put into leaching equipment, at 45 DEG C, reacts 4.5h.After reaction terminates, leach Ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 81.65%.Then similar embodiment 3 but supplement ammonia and CO2。
Embodiment 86: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.27 times of theoretical amount, allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, calcium fluoride 1.5% (mass percent) that addition is dry tungsten mineral material amount, raw material granularity≤45 μm, then, neutral at roaster Roasting 1h at atmosphere 870 DEG C, obtains grog, after clinker cooling to room temperature, levigate with ball mill, grog granularity≤45 μm；Leaching Going out the leaching tanks of equipment choice band ball milling, built-in supersaturation ammonium carbonate serosity, ammonium carbonate concentration is 100g (NH4)2CO3/100g H2O；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 6.5%) And airtight, at 52 DEG C, react 3.8h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching of tungsten Going out rate is 98.25%.Then similar embodiment 3 but supplement ammonium carbonate, ammonium hydrogen carbonate, ammonia and CO2。
Embodiment 87: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.5 times of theoretical amount, allocate limestone into and fluorite carry out levigate mixing after obtain raw material, firefly The addition of stone is 2.6% (mass percent) of dry tungsten mineral material amount, raw material granularity≤45 μm, then, at roaster also Roasting 2h at originality atmosphere 920 DEG C, obtains grog, after clinker cooling to room temperature, levigate with Raymond mill, grog granularity≤8 μm； Leaching equipment selects leaching device, built-in ammonium carbonate saturated solution, and adds ammonium hydrogen carbonate according to 1.2 times of theoretical amount；Will Leaching equipment put into by grog, reacts 5h at 38 DEG C.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake 2 times. The leaching rate of tungsten is 98.12%.Then, similar embodiment 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 88: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.13 times of theoretical amount, allocate the slag after grog leaches in embodiment 86 into and (are mainly composed of CaCO3) and calcium fluoride carry out levigate mixing after obtain raw material, the addition of calcium fluoride is 4.1% (matter of dry tungsten mineral material amount Amount percent), raw material granularity≤100 μm, then, and roasting 2h at roaster neutral atmosphere 960 DEG C, obtain grog, grog After being cooled to room temperature, levigate with vibromill, grog granularity≤45 μm；Leaching equipment selects leaching device, and built-in ammonium carbonate is satisfied With solution, and according to 1.2 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, at 50 DEG C, reacts 3h. After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake 5 times.The leaching rate of tungsten is 98.39%.Then, similar real Executing example 3, APT product reaches 0 grade of product standard-required of country.
Embodiment 89: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO61.4 times of theoretical amount, allocate the slag after grog leaches in embodiment 88 into and calcium fluoride is carried out Obtaining raw material after levigate mixing, the addition of calcium fluoride is 0.2% (mass percent) of dry tungsten mineral material amount, raw material granularity ≤ 74 μm, then, roasting 1.5h at roaster neutral atmosphere 980 DEG C, obtain grog, after clinker cooling to room temperature, with shaking Dynamic mill is levigate, grog granularity≤85 μm；Leaching equipment selects ball milling infuser, and built-in supersaturation ammonium carbonate serosity, ammonium carbonate is dense Degree is 120g (NH4)2CO3/100g H2O, and according to 1.5 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching set Standby, at 70 DEG C, react 6h.After reaction terminates, leach ore pulp filter pressing, with pure water filter cake 4 times.The leaching rate of tungsten is 97.23%.Then, similar embodiment 3 but supplement ammonium carbonate and ammonium hydrogen carbonate, APT product reaches 0 grade of product standard of country to be wanted Ask.
Embodiment 90: by certain scheelite (WO3Weight/mass percentage composition is 52.33%, and Fe weight/mass percentage composition is 2.04%) by raw Become Ca3WO6And Ca2FeWO62.33 times of theoretical amount, allocate into after grog leached mud carries out levigate mixing and obtain raw material, raw Material granularity≤80 μm, then, roasting 7h at roaster neutral atmosphere 1000 DEG C, obtain grog, after clinker cooling to room temperature, Levigate with vibromill, grog granularity≤45 μm；Leaching equipment selection ball milling infuser, built-in ammonium carbonate saturated solution, and according to 1.3 times of addition ammonium hydrogen carbonate of theoretical amount；Grog is put into leaching equipment, at 40 DEG C, reacts 24h.After reaction terminates, leaching Go out ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 98.66%.Then, similar embodiment 3, APT produces Product reach 0 grade of product standard-required of country.
Embodiment 91: by certain scheelite (WO3Weight/mass percentage composition is 49.53%, and Fe weight/mass percentage composition is 0.43%) by raw Become Ca3WO61.33 times of theoretical amount, allocate into and obtain raw material after grog leached mud carries out levigate mixing, raw material granularity≤53 μm, Then, roasting 10h at roaster neutral atmosphere 950 DEG C, obtain grog, after clinker cooling to room temperature, levigate with ball mill, Grog granularity≤45 μm；Leaching equipment selects the leaching tanks of band stirring, built-in ammonium carbonate saturated solution；Grog is put into leaching set Standby, it is simultaneously introduced ammonia and (makes NH in infusion solution3Weight/mass percentage composition be 13.0%) and airtight, react at 40 DEG C 20h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times.The leaching rate of tungsten is 99.01%.Then, Similar embodiment 3 but supplement ammonia and CO2。
Embodiment 92: by certain tungsten slurry (WO3Weight/mass percentage composition is 16.22%) by generating Ca3WO62.67 times of theoretical amount, Allocate grog leached mud into and calcium fluoride carry out levigate mixing after obtain raw material, the addition of calcium fluoride is dry tungsten mineral material amount 6.5% (mass percent), raw material granularity≤45 μm, then, and roasting 0.5h at roaster reducing atmosphere 750 DEG C, obtain ripe Material, after clinker cooling to room temperature, levigate with centrifugal mill, grog granularity≤45 μm；Leaching equipment selects ball milling infuser, interior Put ammonium carbonate saturated solution；Grog is put into leaching equipment, is simultaneously introduced ammonia and (makes NH in infusion solution3Percent mass contain Amount is 8.5%) and airtight, at 45 DEG C, react 4h.After reaction terminates, leach ore pulp sucking filtration, with pure water filter cake three times. The leaching rate of tungsten is 94.51%.Then, similar embodiment 3 but supplement ammonium carbonate, ammonium hydrogen carbonate, ammonia and CO2。
The present inventor's exploration and practice repeatedly for many years shows, those skilled in the art does not has motivation to go to consider the technology of the present invention , there is not employing " common knowledge " or the problem of " customary means " in design.Even so, even with design, relate to Multiple factors are the most all mutually restrictions, interactional, are not separate, even if using the modern times such as orthogonal design Change scientific method, still have infinite may combining, and enough excellent the technical scheme, " reality of limited number of time can not be doped Test " the suitable value of each factor can not be obtained, enough excellent technical scheme is less " obviously ".
Above numerous embodiments of the present invention are not limitation of the invention.It will be understood to those skilled in the art that the most inclined On the premise of the spirit and design of the present invention, amendment that any details to technical solution of the present invention and form are carried out, supplement, Improve and replace, all in the protection domain of appended claims.

Claims (15)

1. a metallurgical system for tungsten mineral material, including: raw material preparation facilities, tungsten mineral material is contained by it with a certain amount of Calcium substance and mineralizer are after levigate, and mix homogeneously obtains raw material, and during raw material preparation, the addition of calcareous material is at least by making Tungsten in tungsten mineral material generates Ca3WO6And/or Ca2FeWO6And/or Ca2MnWO61.0 times of theoretical amount, raw material During preparation, the mineralizer allocated into is fluoride, and raw material granularity is not particularly limited；Calcining kiln/roaster, its raw material roasting temperature Degree is not less than 500 DEG C；Roasting time is not particularly limited；Grog fine mill, it has the outlet of thin grog；Leaching device, It has leaching agent entrance, leaching slurry outlet, feedback gas recovery port, slurry separating, washing liquid recovery port, slag are washed mutually Wash liquid recovery port, crystal seed entrance；The equipment for separating liquid from solid of leaching slurry, it has leached mud feedback port, washing liquid feedback exports, The receiving port of evaporative crystallization condensed water, this equipment for separating liquid from solid in feeding back to the way of leached mud receiving port of raw material preparation facilities with The crystal seed entrance connection of leaching device；At least first class purification knot screen；Crystallization apparatus, it has the gas feeding back to leaching device Body feedback port；The liquid-solid separation device of slurry, it has crystalline mother solution and is back to the outlet of leaching device and going out of tungsten product Mouthful.
Metallurgical system the most according to claim 1, it is characterised in that the addition of calcareous material is at least by making tungsten ore Tungsten in raw material generates Ca3WO6And/or Ca2FeWO6And/or Ca2MnWO61.1-1.5 times of theoretical amount；Allocate into Mineralizer is calcium fluoride, and the addition of calcium fluoride is 0.5-7 mass % of dry tungsten mineral material amount；Raw material granularity is for being not more than 200μm；Raw material sintering temperature is 800～1050 DEG C；And/or, temperature is low, needs to extend roasting time, for making the tungsten in raw material It is fully converted into Ca3WO6And/or Ca2FeWO6And/or Ca2MnWO6, roasting time is 0.5-8.0h.
Metallurgical system the most according to claim 2, it is characterised in that the addition of calcareous material is at least by making tungsten ore Tungsten in raw material generates Ca3WO6And/or Ca2FeWO6And/or Ca2MnWO61.1-1.2 times of theoretical amount；Allocate into Mineralizer is calcium fluoride, and the addition of calcium fluoride is 1-3 mass % of dry tungsten mineral material amount；Raw material granularity is for being not more than 100μm；Raw material sintering temperature is 850～950 DEG C；And/or, roasting time is 1.0～3.0h.
Metallurgical system the most according to claim 3, it is characterised in that raw material granularity is no more than 40 μm；And/or At 850～950 DEG C, roasting roasting time is 2.0h.
5. the metallurgical system of a tungsten mineral material, it is characterised in that this metallurgical system includes successively:
Raw material preparation facilities, its have raw mineral materials metering/dosage entrance and batching metering/dosage entrance, raw material fine mill, Raw material outlet and leached mud receiving port；
Calcining kiln/stove, it is through feeding measurement device and raw material silo and raw material outlet, have heater, attemperator and Thick grog outlet；
Grog fine mill, it is through grog storehouse and thick grog outlet, has ore grinding device and the outlet of thin grog；
Leaching device, it is with thin grog outlet, have leaching agent entrance, leaching slurry outlet, feedback gas recovery port, Slurry separating, washing liquid recovery port, slag phase cleaning mixture recovery port, crystal seed entrance；
The equipment for separating liquid from solid of leaching slurry, itself and leaching slurry outlet, have the leached mud containing dispensing element crosses diafiltration Wash device, thick taphole containing wolfram element, leached mud feedback port, to the residue outlet of leached mud heap warehousing, washing liquid feedback outlet, The receiving port of evaporative crystallization condensed water, this equipment for separating liquid from solid in feeding back to the way of leached mud receiving port of raw material preparation facilities with The crystal seed entrance connection of leaching device；
At least first class purification knot screen, the entrance of the first order connects with the thick taphole containing wolfram element, and at different levels have purification and remove Miscellaneous dose of entrance and impurity collector, afterbody has the smart taphole containing wolfram element；
Crystallization apparatus, its entrance connects with the smart taphole containing wolfram element, has slurry outlet, feeds back to leaching device Gas feedback mouth and condensation-water drain；
The liquid-solid separation device of slurry, itself and slurry outlet, there is crystalline mother solution and be back to going out of leaching device Mouth, solid phase wash water entrance and the outlet of tungsten product.
System the most according to claim 1 or 5, it is characterised in that: described raw material preparation facilities and/or the levigate dress of grog Put and be selected from: vibrating mill, twin rollers, ball mill, rod mill, autogenous tumbling mill, agitator mill, overhang roll pulverizer, tower mill, Colloidal mill, centrifugal mill, high pressure disc mill, Raymond mill, jet mill；And/or, described calcining kiln/stove is static Calcining kiln/stove or dynamic roasting kiln/stove.
System the most according to claim 1 or 5, it is characterised in that: described leaching device is an independent leaching equipment, Or 2-4 leaching equipment is used in series.
System the most according to claim 1 or 5, it is characterised in that: include following additional technical feature at least one:
Described leaching device is leaching equipment, or ball milling leaching equipment；
Described leaching device seals, and bears the pressure of 3atm；
Filter plant is pumping and filtering device, filtering equipment and/or natural filtration groove；
Described impurity removing equipment is decleaning tank, filter plant and/or subsider；And
Agitating device, attemperator it is provided with in described decleaning tank.
Metallurgical system the most according to claim 5, it is characterised in that be additionally provided with mineralizer metering/dosage entrance；Raw material Fine mill contains vortex mixer；Attemperator also includes chiller；Crystal seed entrance also includes that carbon dioxide is passed through mouth；Leaching slurry Equipment for separating liquid from solid be defecator；Afterbody adds extractor fan；Condensation-water drain has smart solution evaporation cerium sulphate crystal Device；And/or, the outlet of tungsten product dissolves with next stage, crystallize, purify subsystem connects.
10. the metallurgical technology of a tungsten mineral material, it is characterised in that
Replace leaching agent in prior art and use highly basic or strong acid, use the weak base leaching agent contributing to forming local process circulation, Its leachate produces two or more gas in evaporation and crystal process, and each gas participates in synthesizing this leaching agent again, Separating, washing liquid after crystallization recycles as leaching agent equally；Slurry through solid-liquor separation and washing after, crystalline mother solution and The leaching device of grog is fed back to after the ammonia of washing liquid and collection and carbon dioxide mix, or crystalline mother solution and washing liquid and collection Ammonia and carbon dioxide feed back to the leaching device of grog respectively, and solid then or prepares product A PT after scrubbed drying, or enters Enter next stage to dissolve, crystallize, purify subsystem；And
Use one transition dispensing, its by with tungsten mineral material generation chemical reaction, can make wolfram element change be contained in the most described In the intermediate material that leaching agent dissolves, and leached mud also contains dispensing element, in order at least partly leached mud follows as dispensing Ring uses, and described tungsten mineral material includes scheelite, wolframite, Scheelite-Wolframite Mixed Mine and/or tungsten slurry；
To this end, this technique comprises multiple closed cycle, omnidistance non-wastewater discharge.
11. metallurgical technologies as claimed in claim 10, it is characterised in that this system includes:
In tungsten mineral material, add dispensing transition, grind, mix homogeneously, be configured to roasting after raw material so that wolfram element changes and contains In the intermediate material easily dissolved by described leaching agent；The means reclaiming at least part of leached mud are set in dispensing link；
Use selected leaching agent that intermediate material is leached, the hands reclaiming leaching agent reacting gas is set in this leaching link Section, the means of slurry separating, washing liquid, reclaim slag phase cleaning mixture means and according to being actually needed supplementary leaching agent Means；
Leaching slurry is carried out solid-liquid separation, to obtain the thick solution containing wolfram element and the leached mud containing dispensing element, slag is washed mutually Washing, cleaning mixture feeds back to grog and leaches link, according to actual needs, takes at least part of leached mud and feeds back as dispensing, to repeat Use dispensing, if leached mud has remainder, then store up；
Thick solution containing wolfram element is carried out at least first class purification remove impurity；
Solution after purifying is evaporated crystallization, to separate out the intermediate products containing wolfram element；Meanwhile, the gas discharged is returned It is back to leach link, and the water evaporated feeds back to the solid-liquid separation link of leaching slurry；
Serosity after crystallization is carried out solid-liquor separation, and to obtain crystalline mother solution and solid phase, solid phase is washed through water and/or ammonium salt solution, The final products containing wolfram element are i.e. obtained after drying；And crystalline mother solution also returns to leaching link.
12. metallurgical technologies according to claim 11, it is characterised in that be also added with in tungsten mineral material catalyst or Mineralizer；And/or, in final products, solid phase is dissolved again and crystallizes, to obtain the final products of higher purity.
13. metallurgical technologies according to claim 11, it is characterised in that include tungsten mineral material described transition, join Expect levigate, mix homogeneously, to prepare raw material；Raw material are carried out roasting, to obtain grog.
14. metallurgical technologies according to claim 11, it is characterised in that described weak base be ammonium carbonate, ammonium hydrogen carbonate, Ammonia+CO2Gas, their any mixture and/or their any mixture with ammonium tungstate.
15. metallurgical technologies according to claim 13, it is characterised in that carry out grog crushing, levigate.
CN201410527541.XA 2014-10-09 2014-10-09 The system of APT is prepared by tungsten mineral material no pollution Active CN104263971B (en)