CN104262886A - 一种trb高物性复合型注塑橡胶材料 - Google Patents
一种trb高物性复合型注塑橡胶材料 Download PDFInfo
- Publication number
- CN104262886A CN104262886A CN201410434434.2A CN201410434434A CN104262886A CN 104262886 A CN104262886 A CN 104262886A CN 201410434434 A CN201410434434 A CN 201410434434A CN 104262886 A CN104262886 A CN 104262886A
- Authority
- CN
- China
- Prior art keywords
- parts
- trb
- rubber
- styrene
- injection molded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种TRB高物性复合型注塑橡胶材料,所述材料是由以下重量份比的原料加工而成:SBS50-60份;SEBS10-20份;丁腈橡胶20-30份;聚苯乙烯15-20份;软化油15-20份;白炭黑4-8份;纳米碳酸钙5-7份;低温发泡剂4-5份;高分子耐磨油1.5-2份;接枝物质5-10份。
Description
技术领域
本发明涉及复合材料技术领域,尤其涉及一种TRB高物性复合型注塑橡胶材料。
背景技术
TPR是热塑性橡胶(Thermoplastic Rubber)的缩写,广泛应用于鞋材领域中,具有易塑形和价格低等优点,缺点是材质重、不耐磨,柔软度较差,弯曲性差、吸震能力差。
中国专利2014.05.14公开的公开号为CN 103788440 A的发明专利公开了一种TPR的改良配方,其特征在于该TPR材料由热塑性橡胶,甲苯二异氰酸酯和异戊橡胶混合制成,该TPR材料具有弹性、耐寒性(玻化温度 -68℃)及很高的拉伸强度,然而该种材料仍然没能有效解决TPR材质重和不耐磨等问题。
目前,仍然没有一种TPR改性材料可以同时具备可塑性、高弹性、耐应力开裂性、耐磨性和低密度等性质。
发明内容
本发明的目的在于提供一种具有可塑性、高弹性、耐应力开裂性、耐磨性和低密度等性质的一种TRB高物性复合型注塑橡胶材料。
为达到上述目的,本发明的技术方案为:一种TRB高物性复合型注塑橡胶材料,所述材料是由以下重量份比的原料加工而成:SBS 50-60份;SEBS 10-20份;丁腈橡胶 20-30 份;聚苯乙烯 15-20份;软化油 15-20 份;白炭黑 4-8份;纳米碳酸钙 5-7份;低温发泡剂 4-5 份;高分子耐磨油 1.5-2 份;接枝物质 5-10份。
进一步,所述接枝物质由填充剂、橡胶助剂和润滑剂混合制成。
其中,上述的SBS为苯乙烯-丁二烯-苯乙烯嵌段共聚物的简称,SEBS为苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物的简称,该两种物质及其简称均为本领域技术人员所知。
本发明的有益效果为,本发明提供的一种TRB高物性复合型注塑橡胶材料,具有以下优点:
其一,本发明的高物性复合型注塑橡胶材料以热塑性橡胶为主材料,传统橡胶为辅助材料对传统热塑橡胶进行改性,有可塑性、高弹性、耐应力开裂性、耐磨性和密度低等优点;
其二,本发明的配方加入了纳米碳酸钙作为活性剂,其颗粒细小具有很大的表面积,具有良好的分散性与良好的吸附性,因而能促进复合型注塑橡胶的硫化、活化和补强防老化作用,达到稳定性、加工安全性提高、大幅度降低不良率,提高橡胶制品耐撕裂性、耐磨性;
其三,在进行成型加工时,可通过直接注塑,挤出等方式加工成型,而无需象常规橡胶那样,需要硫化模压成型,从而大大缩短了加工时间,并且注塑加工后产生的水口边角料可加工后重复使用,既简化加工过程,又降低加工成本。
具体实施方式
为了便于本领域技术人员的理解,下面将结合具体实施例对本发明所要求保护的技术方案作进一步详细描述 :
实施例一
本实施例中,高物性复合型注塑橡胶材料的原料重量份比为:SBS 50份;SEBS 10份;丁腈橡胶 20份;聚苯乙烯 15份;软化油 17份;白炭黑 4份;纳米碳酸钙 5份;低温发泡剂 4份;高分子耐磨油 1.5份;接枝物质 5份。
其中,接枝物质由填充剂、橡胶助剂和润滑剂混合制成。
实施例二
本实施例中,高物性复合型注塑橡胶材料的原料重量份比为:SBS 60份;SEBS 20份;丁腈橡胶:30份;聚苯乙烯20份;软化油17份;白炭黑8份;纳米碳酸钙7份;低温发泡剂5份;高分子耐磨油2份;接枝物质10份。
其中,接枝物质由填充剂、橡胶助剂和润滑剂混合制成。
以上两个实施例为制备一种TRB高物性复合型注塑橡胶材料的具体配方,其范围皆在本发明专利所要求保护的技术方案中,可采用同样的工艺将其制备为一种高物性复合型注塑橡胶材料,现列举一种工艺进行说明供技术人员参考。
该工艺包括以下步骤:先将丁腈橡胶塑炼压成厚度为0.5-0.8mm的薄片并进行切割使每片薄片的重量为0.5kg,然后将其投入搅拌桶内加乳化油浸泡30分钟,再加入SBS和SEBS搅拌30-40分钟,下搅拌桶静置6小时自然冷却;
把冷却后的材料投入密炼机并加入聚苯乙烯、软化油、白炭黑、纳米碳酸钙、高分子耐磨油密炼3-4分钟再加入填充剂、橡胶助剂以及润滑剂进行密炼6-7分钟;
材料密炼完毕后经过双轴挤出机出料,再经冷却及造粒后获得颗粒,颗粒经射出管注入模具内,在温度为150-160℃,压力10-15mpa下注压4-8分钟,可获得成品。
其中,在丁腈橡胶薄片与SBS和SEBS混合搅拌并冷却的步骤中,可先将SBS和SEBS陆续投入搅拌桶中加软化油搅拌,再将塑丁腈橡胶薄片陆续放入搅拌桶内搅拌30-70分钟,下搅拌桶靜置6小时自然冷却。
以上实施例仅是本发明的一些优选实施方式,但本发明的保护范围并不仅限于此。本领域技术人员应该理解,所有未背离本发明精神和范围的任何修改或局部替换都在本发明保护范围之内。
Claims (2)
1.一种TRB高物性复合型注塑橡胶材料,其特征在于;所述材料是由以下重量份比的原料加工而成:SBS 50-60份;SEBS 10-20份;丁腈橡胶 20-30 份;聚苯乙烯 15-20份;软化油 15-20 份;白炭黑 4-8份;纳米碳酸钙 5-7份;低温发泡剂 4-5 份;高分子耐磨油 1.5-2 份;接枝物质 5-10份。
2.根据权利要求1所述的一种TRB高物性复合型注塑橡胶材料,其特征在于;所述接枝物质由填充剂、橡胶助剂和润滑剂混合制成。