CN104262823A - High-wear-resistance polyvinyl chloride foamed shoe sole material and manufacturing method thereof - Google Patents
High-wear-resistance polyvinyl chloride foamed shoe sole material and manufacturing method thereof Download PDFInfo
- Publication number
- CN104262823A CN104262823A CN201410448774.0A CN201410448774A CN104262823A CN 104262823 A CN104262823 A CN 104262823A CN 201410448774 A CN201410448774 A CN 201410448774A CN 104262823 A CN104262823 A CN 104262823A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- sole
- shoe
- high abrasion
- chloride material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a high-wear-resistance polyvinyl chloride foamed shoe sole material which is prepared from the following components in parts by weight: 50-60 parts of polyvinyl chloride, 5-10 parts of nano silicon carbide, 30-40 parts of plasticizer, 0.5-1 part of foaming agent, 0.1-0.5 part of coupling agent, 1-4 parts of ACR, 1.5-3 parts of stabilizer and 0.5-1 part of lubricant. The invention also provides a manufacturing method of the high-wear-resistance polyvinyl chloride foamed shoe sole material. The polyvinyl chloride foamed shoe sole material provided by the invention has favorable wear resistance.
Description
Technical field:
The present invention relates to a kind of material for sole of shoe, particularly relate to a kind of foam polyvinyl chloride material for sole of shoe and manufacture method thereof of high abrasion.
Background technology:
Foam polyvinyl chloride material for sole of shoe is matrix with polyvinyl chloride (PVC) RESINS, adds the auxiliary agents such as appropriate whipping agent, stablizer, and through mediating granulation, injection moulding obtains.More soft than common polyvinyl chloride material for sole of shoe, quality lightens, and elasticity is better, and various aspects of performance is close to urethane-PU material for sole of shoe, and cost is low a lot.But, while pliability raising, weight reduce, the wear resistance of foam polyvinyl chloride material for sole of shoe is also weakened much, shortens its work-ing life.
Summary of the invention:
The technical problem to be solved in the present invention is to provide a kind of foam polyvinyl chloride material for sole of shoe of high abrasion, has good wear resisting property.
For solving the problems of the technologies described above, technical scheme of the present invention is:
A foam polyvinyl chloride material for sole of shoe for high abrasion, its weight part consists of:
Preferably, softening agent of the present invention is at least one in n-butyl phthalate, dinoctyl phthalate, Phthalic acid, diallyl ester, diethyl phthalate.
Preferably, whipping agent of the present invention is Cellmic C 121, the sub-methyne tetramine of dinitroso or Diisopropyl azodicarboxylate.
Preferably, coupling agent of the present invention is titanate coupling agent.
Preferably, stablizer of the present invention is dibasic lead stearate, second base lead sulfate or dibasic lead phosphite.
Preferably, lubricant of the present invention is calcium stearate, lead stearate, barium stearate, Zinic stearas or cadmium stearate.
Another technical problem that the present invention will solve is to provide the manufacture method of the foam polyvinyl chloride material for sole of shoe of above-mentioned high abrasion.
For solving the problems of the technologies described above, technical scheme is:
A manufacture method for the foam polyvinyl chloride material for sole of shoe of high abrasion, comprises the following steps:
(1) nanometer silicon carbide is dissolved in the aqueous solution of coupling agent, high-speed stirring 5 minutes, is placed in baking oven and dries 3 hours at 130 DEG C, obtain modified Nano silicon carbide;
(2) the modified Nano silicon nitride that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2.5 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 35 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains the foam polyvinyl chloride material for sole of shoe of high abrasion.
Therefore compared with prior art, the present invention has following beneficial effect:
Nanometer silicon carbide density is low, hardness is high, there is excellent thermodynamic stability, wear resisting property and chemical proofing, fill nanometer silicon carbide in polyvinyl-chloride foam material after, improve its ultimate compression strength, hardness and creep-resistant property, when rubbing with other materials, nanometer silicon carbide can play carrying effect, therefore improves the wear resisting property of this material for sole of shoe, affinity between nanometer silicon carbide and PVC base system is poor, interface bond strength is lower, therefore the present invention has carried out modification by coupling agent to nanometer silicon carbide, after process its dispersiveness in PVC base system be improved significantly, reunion smaller volume and being evenly distributed, its intrinsic wetting ability is also changed, significantly improve with the interface bond strength of polyvinyl chloride, in friction process, nanometer silicon carbide not easily comes off from resin, reduce the abrasive wear of material, thus reduce abrasion loss and the rubbing factor of whole material for sole of shoe, significantly improve its wear resisting property.
Embodiment:
Describe the present invention in detail below in conjunction with specific embodiment, be used for explaining the present invention in this illustrative examples of the present invention and explanation, but not as a limitation of the invention.
Embodiment 1
A foam polyvinyl chloride material for sole of shoe for high abrasion, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nanometer silicon carbide is dissolved in the aqueous solution of coupling agent, high-speed stirring 5 minutes, is placed in baking oven and dries 3 hours at 130 DEG C, obtain modified Nano silicon carbide;
(2) the modified Nano silicon nitride that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2.5 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 35 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains the foam polyvinyl chloride material for sole of shoe of high abrasion.
Embodiment 2
A foam polyvinyl chloride material for sole of shoe for high abrasion, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nanometer silicon carbide is dissolved in the aqueous solution of coupling agent, high-speed stirring 5 minutes, is placed in baking oven and dries 3 hours at 130 DEG C, obtain modified Nano silicon carbide;
(2) the modified Nano silicon nitride that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2.5 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 35 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains the foam polyvinyl chloride material for sole of shoe of high abrasion.
Embodiment 3
A foam polyvinyl chloride material for sole of shoe for high abrasion, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nanometer silicon carbide is dissolved in the aqueous solution of coupling agent, high-speed stirring 5 minutes, is placed in baking oven and dries 3 hours at 130 DEG C, obtain modified Nano silicon carbide;
(2) the modified Nano silicon nitride that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2.5 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 35 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains the foam polyvinyl chloride material for sole of shoe of high abrasion.
Embodiment 4
A foam polyvinyl chloride material for sole of shoe for high abrasion, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nanometer silicon carbide is dissolved in the aqueous solution of coupling agent, high-speed stirring 5 minutes, is placed in baking oven and dries 3 hours at 130 DEG C, obtain modified Nano silicon carbide;
(2) the modified Nano silicon nitride that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2.5 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 35 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains the foam polyvinyl chloride material for sole of shoe of high abrasion.
Embodiment 5
A foam polyvinyl chloride material for sole of shoe for high abrasion, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nanometer silicon carbide is dissolved in the aqueous solution of coupling agent, high-speed stirring 5 minutes, is placed in baking oven and dries 3 hours at 130 DEG C, obtain modified Nano silicon carbide;
(2) the modified Nano silicon nitride that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2.5 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 35 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains the foam polyvinyl chloride material for sole of shoe of high abrasion.
Embodiment 6
A foam polyvinyl chloride material for sole of shoe for high abrasion, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nanometer silicon carbide is dissolved in the aqueous solution of coupling agent, high-speed stirring 5 minutes, is placed in baking oven and dries 3 hours at 130 DEG C, obtain modified Nano silicon carbide;
(2) the modified Nano silicon nitride that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2.5 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 35 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains the foam polyvinyl chloride material for sole of shoe of high abrasion.
Above-described embodiment is illustrative principle of the present invention and effect thereof only, but not for limiting the present invention.Any person skilled in the art scholar all without prejudice under spirit of the present invention and category, can modify above-described embodiment or changes.Therefore, such as have in art usually know the knowledgeable do not depart from complete under disclosed spirit and technological thought all equivalence modify or change, must be contained by claim of the present invention.
Claims (7)
1. a foam polyvinyl chloride material for sole of shoe for high abrasion, is characterized in that: its weight part consists of:
2. the foam polyvinyl chloride material for sole of shoe of a kind of high abrasion according to claim 1, is characterized in that: described softening agent is at least one in n-butyl phthalate, dinoctyl phthalate, Phthalic acid, diallyl ester, diethyl phthalate.
3. the foam polyvinyl chloride material for sole of shoe of a kind of high abrasion according to claim 1, is characterized in that: described whipping agent is Cellmic C 121, the sub-methyne tetramine of dinitroso or Diisopropyl azodicarboxylate.
4. the foam polyvinyl chloride material for sole of shoe of a kind of high abrasion according to claim 1, is characterized in that: described coupling agent is titanate coupling agent.
5. the foam polyvinyl chloride material for sole of shoe of a kind of high abrasion according to claim 1, is characterized in that: described stablizer is dibasic lead stearate, second base lead sulfate or dibasic lead phosphite.
6. the foam polyvinyl chloride material for sole of shoe of a kind of high abrasion according to claim 1, is characterized in that: described lubricant is calcium stearate, lead stearate, barium stearate, Zinic stearas or cadmium stearate.
7. the manufacture method of the foam polyvinyl chloride material for sole of shoe of a kind of high abrasion according to claim 1 ~ 6 any one, is characterized in that: comprise the following steps:
(1) nanometer silicon carbide is dissolved in the aqueous solution of coupling agent, high-speed stirring 5 minutes, is placed in baking oven and dries 3 hours at 130 DEG C, obtain modified Nano silicon carbide;
(2) the modified Nano silicon nitride that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2.5 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 35 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains the foam polyvinyl chloride material for sole of shoe of high abrasion.