CN104262544A - Environment-friendly high-strength acrylate grouting material and using method thereof - Google Patents
Environment-friendly high-strength acrylate grouting material and using method thereof Download PDFInfo
- Publication number
- CN104262544A CN104262544A CN201410450719.5A CN201410450719A CN104262544A CN 104262544 A CN104262544 A CN 104262544A CN 201410450719 A CN201410450719 A CN 201410450719A CN 104262544 A CN104262544 A CN 104262544A
- Authority
- CN
- China
- Prior art keywords
- liquid
- acrylate
- parts
- injection material
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an environment-friendly high-strength acrylate grouting material and a using method thereof. The grouting material comprises liquid A and liquid B, wherein the liquid A comprises the following components in parts by weight: 30-50 parts of main agent acrylate, 2-15 parts of cross-linking agent: bisallyl ether functional group-containing hydrophilic compound and 50-100 parts of water; and the liquid B comprises the following components in parts by weight: 1-5 parts of initiators, 0.5-4 parts of accelerant and 80-150 parts of water. The using method of the acrylate grouting material comprises the following steps: firstly preparing the liquid A and the liquid B, and respectively grouting the liquid A and the liquid B into a crack to be processed according to a volume ratio of 1:(0.3-3.0) by using different grouting pipes one the scene, wherein the grouting is carried out at a normal temperature. According to the environment-friendly high-strength acrylate grouting material and the using method thereof, the technical problem that the acrylate grouting materials at present consist of a plurality of components, have high toxicity, have no resistance to hydrolysis and have low gel strength is solved.
Description
Technical field
The present invention relates to the injection material of building concrete antiseepage, ground and Foundation Anti-seepage and reinforcing, be specifically related to a kind ofly be applicable to dealing with foundation project seepage controlling, the acrylate injection material of leak stopping and reinforcing and using method thereof.
Background technology
In dealing with foundation project seepage controlling and consolidation process, the normal acrylate injection material that adopts carries out Anti-seeping technology.At present, the acrylate injection material on market is primarily of host Magnesium Acrylate Prepared, calcium acrylate, and linking agent N, N '-methyne bisacrylamide, initiator ammonium persulfate, promotor trolamine and aqueous solvent form.In these components, easily there is chemical reaction in promotor and host, initiator, product is gone bad, therefore three can not mix common storage between two, cause when transporting and prepare, transport must be stored separately, be prepared by more than three components and just can construct, bring inconvenience to material produce, construction; The linking agent N adopted, N '-methyne bisacrylamide toxicity is comparatively large, limits the range of application of material.The gelling thing formed after adopting said components mixing, intensity is lower, and after water-swellable, anti-plasticating capacity significantly reduces.
China Patent Publication No. CN101265048A, publication date on September 17th, 2008, denomination of invention is acrylate grouting liquid and preparation method thereof, for reducing the toxicity of acrylate injection material, acrylate is adopted to replace N, N '-methyne bisacrylamide as linking agent, reduce the toxicity of acrylate injection material, but acrylate cross linked dose utilizes ester bond to connect, ester bond is easily hydrolyzed at acid or alkaline condition, causes the weather resistance of material to be under suspicion.
Summary of the invention
The invention provides a kind of environmental protection and high-strength acrylate grouting material, be made up of multiple component to solve existing acrylate injection material, the technical problems such as injection material toxicity is high, not hydrolysis, and injection material gel intensity is low.
Technical problem solved by the invention realizes by the following technical solutions:
A kind of environment-friendly type high intensity acrylate injection material, comprise first liquid and second liquid, the component of above-mentioned first liquid and second liquid is as follows with the proportioning of listed as parts by weight:
First liquid: host: acrylate 30 ~ 50 parts
Linking agent: the hydrophilic compounds of diallyl containing ether functional group 2 ~ 15 parts
50 ~ 100 parts, water
Second liquid: initiator 1 ~ 5 part
Promotor 0.5 ~ 4 part
80 ~ 150 parts, water.
In above-mentioned acrylate injection material, preferably, described acrylate host is the mixture of calcium acrylate, vinylformic acid copper, Magnesium Acrylate Prepared and a small amount of sodium acrylate.In the present invention, add vinylformic acid copper, with calcium acrylate and Magnesium Acrylate Prepared jointly as the host of injection material, the ultimate compression strength of the gel of acrylate injection material can be increased substantially.Using calcium acrylate and Magnesium Acrylate Prepared as host, its gel strength is low, Gu sand body ultimate compression strength is usually within 300KPa.After adding vinylformic acid copper, Gu sand body ultimate compression strength improves more than 50%, can more than 500KPa be reached, maximumly reach 550KPa.
In above-mentioned acrylate injection material, preferably, the weight part of described calcium acrylate, vinylformic acid copper, sodium acrylate and Magnesium Acrylate Prepared is respectively: 1 ~ 5 part, 10 ~ 25 parts, 0 ~ 3 part, 10 ~ 25 parts.
In above-mentioned acrylate injection material, preferably, described linking agent is one or both mixture in polyoxyethylene glycol diallyl ether, ethoxylated bisphenol A dual-allyl ether.In the present invention, one or both mixture in polyoxyethylene glycol diallyl ether, ethoxylated bisphenol A dual-allyl ether is adopted to replace conventional linking agent acrylate, N, N '-methyne bisacrylamide.Toxicity comparatively N, the N '-methyne bisacrylamide of polyoxyethylene glycol diallyl ether, ethoxylated bisphenol A dual-allyl ether is much lower, solves raw-material toxicity problem; Based on ehter bond and C-C in polyoxyethylene glycol diallyl ether, ethoxylated bisphenol A dual-allyl ether, the ester bond in more acrylate cross linked dose, its hydrolytic resistance is much better than, has therefore increased substantially the weather resistance of injection material gel.
In above-mentioned acrylate injection material, preferably, in described polyoxyethylene glycol diallyl ether, the molecular weight of polyoxyethylene glycol is between 40 ~ 2000, and in described ethoxylated bisphenol A dual-allyl ether, the number of ethoxy functional groups is 5 ~ 15.
In above-mentioned acrylate injection material, preferably, described initiator is one or more mixture in Potassium Persulphate, Sodium Persulfate, ammonium persulphate.
In above-mentioned acrylate injection material, preferably, described promotor is ammoniacal liquor.Described ammoniacal liquor is the industrial ammonia that market is bought.In the present invention, ammoniacal liquor is adopted to replace conventional trolamine as promotor, ammoniacal liquor can mix with initiator potassium persulfate, ammonium persulphate, sodium persulfate aqueous solution, storage time can reach more than three months, the longlyest reach 6 ~ 8 months, initiator and promotor can be made to mix, decrease a component.In Material Manufacturing Process, by initiator and promotor blended formation second liquid, by host and linking agent blended formation first liquid.In construction process, 1: 0.3 ~ 3.0 mixing by volume of first liquid, second liquid are injected into and specify stratum; Three components are weighed mixing and becomes two components, simplify constructing operation.
As a total technical conceive, the present invention also provides a kind of using method of above-mentioned acrylate injection material, method is in the past generally first prepare first liquid and second liquid, at the scene by first liquid and second liquid by volume 1:0.3 ~ 3.0 normal temperature mix gel, then by grout pipe, mixed gel is filled in pending crack; In the present invention, the method of special employing comprises the following steps: first prepare first liquid and second liquid, then different grout pipes is used to be filled in pending crack respectively by first liquid and second liquid at the scene respectively, make first liquid and second liquid enter into crack by the volume ratio of 1:0.3 ~ 3.0 by the grouting flow of controlled grouting pipe and pressure during perfusion, and perfusion carries out at normal temperatures.
In the using method of aforesaid propylene hydrochlorate injection material, preferably, in described second liquid, add the retardant Tripotassium iron hexacyanide of 0 ~ 0.08% before perfusion, the application operability of slurries can be improved, make slurries gel time adjustable between several minutes to a few hours.
Beneficial effect of the present invention is:
1) add vinylformic acid copper in host, increased substantially the ultimate compression strength of injection material glue sand body, improve mechanical property.
2) polyoxyethylene glycol diallyl ether, ethoxylated bisphenol A dual-allyl ether (LD is adopted
50all being greater than 5000mg/kg, is actual nontoxicity) in one or both mixture replace conventional linking agent acrylate, N, N '-methyne bisacrylamide (LD
50390mg/kg is moderate toxicity), the toxicity of material has been fallen generation; Adopt the linking agent of ether-containing key to replace containing the linking agent of ester bond, improve the weather resistance of material.
3) adopt ammoniacal liquor to replace conventional promotor, can coexist with initiator, improve the application operability in filling process.
Embodiment
For the ease of understanding the present invention, hereafter will do to describe more comprehensively, meticulously to the present invention in conjunction with preferred embodiment, but protection scope of the present invention is not limited to following specific embodiment.
Unless otherwise defined, hereinafter used all technical terms are identical with the implication that those skilled in the art understand usually.The object of technical term used herein just in order to describe specific embodiment is not be intended to limit the scope of the invention.
embodiment 1
A kind of environment-friendly type high intensity acrylate injection material, comprise first liquid and second liquid, the proportioning that first liquid is calculated by weight by following component mixes:
Host:
Calcium acrylate 2 parts;
Vinylformic acid copper 18 parts;
Magnesium Acrylate Prepared 13 parts;
Sodium acrylate 1 part;
Linking agent: polyoxyethylene glycol diallyl ether 6 parts;
Solvent: 51 parts, water.
The proportioning that second liquid is calculated by weight by following component mixes:
Initiator: ammonium persulphate 2 parts;
Promotor: ammoniacal liquor 2 parts;
Solvent: 96 parts, water.
The molecular weight of the polyoxyethylene glycol wherein in polyoxyethylene glycol diallyl ether is 1600, and ammoniacal liquor is the industrial ammonia that market is bought, containing ammonia 25% ~ 28%.
The using method of aforesaid propylene hydrochlorate injection material is: first prepare first liquid and second liquid, then different grout pipes is used to be filled in pending crack respectively by first liquid and second liquid at the scene respectively, make first liquid and second liquid enter into crack by the volume ratio of 1:0.5 by the grouting flow of controlled grouting pipe and pressure during perfusion, and perfusion carries out at normal temperatures.
With reference to JC/T 2037-2010 " acrylate injection material " specification, record material property as follows:
The physicals of slurries is as follows:
1) slurries outward appearance: colourless or dark brown clear homogeneous liquid; It is white solid after slurries final set;
2) viscosity: 10cP;
3) density: 1.099g/cm after slurry mixing
3;
3) presetting period 2min, final setting time 6min.
The mechanical property of slurries is as follows:
1) the water-swellable rate 50%(7 days of pure colloid);
2) anti-ly intensity 600KPa is extruded;
3) solid sand body ultimate compression strength 0.65MPa;
4) permeability coefficient is less than 10
-7cm/s.
embodiment 2
A kind of environment-friendly type high intensity acrylate injection material, comprise first liquid and second liquid, the proportioning that first liquid is calculated by weight by following component mixes:
Host:
Calcium acrylate 5 parts;
Vinylformic acid copper 11 parts;
Magnesium Acrylate Prepared 20 parts;
Linking agent: polyoxyethylene glycol diallyl ether 3 parts;
Ethoxylated bisphenol A dual-allyl ether 3 parts;
Solvent: 58 parts, water.
The proportioning that second liquid is calculated by weight by following component mixes:
Initiator: Potassium Persulphate 4 parts;
Promotor: ammoniacal liquor 3 parts;
Solvent: 92.5 parts, water.
Molecular weight polyethylene glycol wherein in polyoxyethylene glycol diallyl ether is 800, and the number of the ethoxy functional groups in ethoxylated bisphenol A dual-allyl ether is 8, and the industrial ammonia that ammoniacal liquor taste market is bought, containing ammonia 25% ~ 28%.
The using method of aforesaid propylene hydrochlorate injection material is: first prepare first liquid and second liquid, and in second liquid, add the Tripotassium iron hexacyanide of 0.06%, then different grout pipes is used to be filled in pending crack respectively by first liquid and second liquid at the scene respectively, make first liquid and second liquid enter into crack by the volume ratio of 1:2.5 by the grouting flow of controlled grouting pipe and pressure during perfusion, and perfusion carries out at normal temperatures.
With reference to JC/T 2037-2010 " acrylate injection material " specification, record material property as follows:
The physicals of slurries is as follows:
1) slurries outward appearance: colourless or dark brown clear homogeneous liquid; It is white solid after slurries final set;
2) viscosity: 4cP;
3) density: 1.035g/cm after slurry mixing
3;
3) presetting period 63min, final setting time 93min.
The mechanical property of slurries is as follows:
1) the water-swellable rate 60%(7 days of pure colloid);
2) anti-ly intensity 400KPa is extruded;
3) solid sand body ultimate compression strength 0.35MPa;
4) permeability coefficient is less than 10
-7cm/s.
Claims (9)
1. an environment-friendly type high intensity acrylate injection material, comprises first liquid and second liquid, it is characterized in that, the component of above-mentioned first liquid and second liquid is as follows with the proportioning of listed as parts by weight:
First liquid: host: acrylate 30 ~ 50 parts
Linking agent: the hydrophilic compounds of diallyl containing ether functional group 2 ~ 15 parts
50 ~ 100 parts, water
Second liquid: initiator 1 ~ 5 part
Promotor 0.5 ~ 4 part
80 ~ 150 parts, water.
2. a kind of environment-friendly type high intensity acrylate injection material according to claim 1, is characterized in that, described acrylate host is the mixture of calcium acrylate, vinylformic acid copper, sodium acrylate and Magnesium Acrylate Prepared.
3. a kind of environment-friendly type high intensity acrylate injection material according to claim 2, it is characterized in that, the weight part of described calcium acrylate, vinylformic acid copper, sodium acrylate and Magnesium Acrylate Prepared is respectively: 1 ~ 5 part, 10 ~ 25 parts, 0 ~ 3 part, 10 ~ 25 parts.
4. according to a kind of environment-friendly type high intensity acrylate injection material in claims 1 to 3 described in any one, it is characterized in that, described linking agent is one or both mixture in polyoxyethylene glycol diallyl ether, ethoxylated bisphenol A dual-allyl ether.
5. a kind of environment-friendly type high intensity acrylate injection material according to claim 4, it is characterized in that, in described polyoxyethylene glycol diallyl ether, the molecular weight of polyoxyethylene glycol is between 40 ~ 2000, and in described ethoxylated bisphenol A dual-allyl ether, the number of ethoxy functional groups is 5 ~ 15.
6. according to a kind of environment-friendly type high intensity acrylate injection material in claims 1 to 3 described in any one, it is characterized in that, described initiator is one or more mixture in Potassium Persulphate, Sodium Persulfate, ammonium persulphate.
7., according to a kind of environment-friendly type high intensity acrylate injection material in claims 1 to 3 described in any one, it is characterized in that, described promotor is ammoniacal liquor.
8. the using method as the acrylate injection material in claim 1 ~ 7 as described in any one, comprise the following steps, first prepare first liquid and second liquid, then different grout pipes is used to be filled in pending crack respectively by first liquid and second liquid at the scene respectively, make first liquid and second liquid enter into crack by the volume ratio of 1:0.3 ~ 3.0 by the grouting flow of controlled grouting pipe and pressure during perfusion, and perfusion carries out at normal temperatures.
9. the using method of acrylate injection material according to claim 8, is characterized in that, adds the retardant Tripotassium iron hexacyanide of 0 ~ 0.08% before perfusion in described second liquid.