CN104244600B - 一种笔记本电脑用柔性线路板板面平整度工艺 - Google Patents
一种笔记本电脑用柔性线路板板面平整度工艺 Download PDFInfo
- Publication number
- CN104244600B CN104244600B CN201410359569.7A CN201410359569A CN104244600B CN 104244600 B CN104244600 B CN 104244600B CN 201410359569 A CN201410359569 A CN 201410359569A CN 104244600 B CN104244600 B CN 104244600B
- Authority
- CN
- China
- Prior art keywords
- fpc
- baking
- technique
- plate face
- notebook computer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种笔记本电脑用柔性线路板板面平整度工艺,包括以下几个步骤:(1)准备工作:准备好平整用的柔性电路板、检查烘箱是否符合安全使用规则、若干白纸(阻燃)、两块烧付铁板;(2)预烘烤:把待烘烤的柔性电路板竖立放到烘箱层架里;(3)二次烘烤:对已经完成预烘烤的柔性电路板进行二次烘烤;(4)烘烤后检查:对完成以上流程的柔性电路板进行检查,其平整度是否达到工艺要求。本发明通过对柔性电路板的两次烘烤,利用烧付铁板的重力加紧柔性电路板,通过烘箱高温烘烤作用,达到柔性电路板板面平整度高,最终板翘均小于6mm的目的。
Description
【技术领域】
本发明属于柔性线路板制作技术领域,更具体地说,涉及笔记本电脑用柔性线路板板面平整度工艺。
【背景技术】
随着键盘发光均匀度要求越来越高,对柔性线路板板面平整度要求也越来越高。从柔性线路板制作制程看,影响柔性线路板平整度的制程为白色感光油墨的烘烤。白色感光油墨烘烤时,由于油墨固化产生的应力会导致柔性线路板板翘。其它方式为用白色覆盖膜替代白色感光油墨,但因白色覆盖膜成本较高且制程公差(±0.1mm)比白色感光油墨制程公差(±0.03mm)大,影响产品的良品率,一般不使用。
因此,有必要提供一种新型工艺来解决上述问题。
【发明内容】
本发明所要解决的技术问题是,提供一种笔记本电脑用柔性线路板屏板面平整度工艺,解决现有成型工艺中柔性线路板板翘过高的问题。
为解决上述技术问题,本发明采用如下技术方案,包括以下步骤。
(1)准备工作:准备好平整用的柔性线路板、检查烘箱是否符合安全使用规则、若干白纸(阻燃)、两块烧付铁板;
(2)预烘烤:把待烘烤的柔性线路板竖立放到烘箱层架里;
(3)二次烘烤:对已经完成预烘烤的柔性线路板进行二次烘烤;
(4)烘烤后检查:对完成以上流程的柔性线路板进行检查,其平整度是否达到工艺要求。
进一步的,所述步骤(2)中,白纸是具有阻燃性质的。
进一步的,所述步骤(2)中,烘干温度为100℃,时间为30min。
进一步的,所述步骤(3)中,每一块柔性线路板夹在两张白纸中间。
进一步的,所述步骤(3)中,最上端与最下端的白纸夹杂在烧付铁板与柔性线路板中间。
进一步的,所述步骤(3)中,其余白纸夹杂在两张柔性线路板中间。
进一步的,所述步骤(3)中,两块烧付铁板分别位于夹层的最外端。
进一步的,所述步骤(3)中,烘干温度为150℃,时间为50min。
本发明的有益效果是:通过对柔性线路板的两次烘烤,利用烧付铁板的重力加紧柔性线路板,通过烘箱高温烘烤作用,达到柔性线路板板面平整度高,最终板翘均小于6mm的目的。
【附图说明】
图1为本发明的夹层结构示意图。
图中:1、柔性线路板;2、白纸;3、烧付铁板。
【具体实施方式】
下面结合具体实施例对本发明做进一步进行描述。
请参阅图1,本发明笔记本电脑用柔性线路板板面平整度工艺方法,包括烘箱(未标出),包括如下步骤:(1)准备工作:准备好平整用的柔性线路板1、检查烘箱是否符合安全使用规则、若干白纸2(阻燃)、两块烧付铁板3;(2)预烘烤:把待烘烤的柔性线路板1竖立放到烘箱层架里,打开烘箱电源,设置烘干温度为100℃,时间为30min。烘烤完成后将柔性线路板1拉出烤箱;(3)二次烘烤:对已经完成预烘烤的柔性线路板1进行二次烘烤。如图1所示,二次烘烤时,每一块柔性线路板1夹在两张白纸2中间,最上端与最下端的白纸2夹杂在烧付铁板3与柔性线路板1中间,其余白纸2夹杂在两张柔性线路板1中间,两块烧付铁板3分别位于夹层的最外端,烧付铁板3的重力将夹杂在其中间的柔性线路板1压紧,确保柔性线路板1的板面平整度。将准备好的夹层100水平放到烘箱层架里,打开烘箱电源,设置烘干温度为150℃,时间为50min;(4)烘烤后检查:对完成以上流程的柔性线路板1进行检查,其平整度是否达到工艺要求(板翘<6mm)。
在一个实施例中,所述夹层100种夹有5块柔性线路板1,在其他实施例中对柔性线路板1的数量并不仅限于此。
本发明通过对柔性线路板1的两次烘烤,利用烧付铁板3的重力加紧柔性线路板1,通过烘箱高温烘烤作用,达到柔性线路板1板面平整度高,板翘低的目的。
区别于现有技术的柔性线路板平整度工艺,通过本工艺加工的柔性线路板1板翘均控制在6mm以下,相比使用旧工艺(板翘均为8mm以上)取得很大进步。
以上示意性的对本发明及其实施方式进行了描述,该描述没有限制性,附图中所示的也只是本发明的实施方式之一,实际的结构并不局限于此。所以,如果本领域的普通技术人员受其启示,在不脱离本发明创造宗旨的情况下,不经创造性的设计出与该技术方案相似的结构方式及实施例,均应属于本发明的保护范围。
Claims (6)
1.一种笔记本电脑用柔性线路板板面平整度工艺,包括烘箱,其特征在于,包括有以下步骤:
(1)准备工作:准备好平整用的柔性线路板、若干白纸、两块烧付铁板;
(2)预烘烤:把待烘烤的柔性线路板竖立放到烘箱层架里,所述预烘烤中烘干温度为100℃,时间为30min;
(3)二次烘烤:对已经完成预烘烤的柔性线路板进行二次烘烤,所述二次烘烤中,烘干温度为150℃,时间为50min;
(4)烘烤后检查:对完成以上流程的柔性线路板进行检查,其平整度是否达到工艺要求。
2.如权利要求1所述的笔记本电脑用柔性线路板板面平整度工艺,其特征在于:所述纸是具有阻燃性质的。
3.如权利要求1所述的笔记本电脑用柔性线路板板面平整度工艺,其特征在于:所述二次烘烤中,每一块柔性线路板夹在两张白纸中间。
4.如权利要求1所述的笔记本电脑用柔性线路板板面平整度工艺,其特征在于:所述二次烘烤中,最上端与最下端的白纸夹杂在烧付铁板与柔性线路板中间。
5.如权利要求1所述的笔记本电脑用柔性线路板板面平整度工艺,其特征在于:所述二次烘烤中,剩余白纸夹杂在两张柔性线路板中间。
6.如权利要求1所述的笔记本电脑用柔性线路板板面平整度工艺,其特征在于:所述二次烘烤中,两块烧付铁板分别位于夹层的最外端。