CN104240597A - Manufacturing method of flat-burning aluminum plate - Google Patents
Manufacturing method of flat-burning aluminum plate Download PDFInfo
- Publication number
- CN104240597A CN104240597A CN201310246515.5A CN201310246515A CN104240597A CN 104240597 A CN104240597 A CN 104240597A CN 201310246515 A CN201310246515 A CN 201310246515A CN 104240597 A CN104240597 A CN 104240597A
- Authority
- CN
- China
- Prior art keywords
- plate
- water
- glue
- manufacturing
- flat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a manufacturing method of a flat-burning aluminum plate and belongs to the technical field of plate manufacturing. According to the technical scheme, the method includes: feeding blank material 5mm larger than plate making size; polishing, drawing and oxidizing the blank material; fast immerging the processed plate into water after deoiling and film removing; adding glue into the water according to the weight ration of (2-2.3):100, boiling for 2 hours to allow the glue solution to dissolve sufficiently, adding (0.25-0.30)g of ammonium dichromate to each 100g of water after the temperature falls to 30-50 DEG C, evenly coating the metal plate with the glue solution, and dying; performing photosensitive plate burning with a 60-90cm lamp for 40-80 seconds, developing for one minute in warm water, and dyeing in color solution; coating the dyed plate with light keeping lacquer through a brush or a spraying gun after the plate is dried. The method is simple in plate making process, fast, timely in delivery and low in rejection rate.
Description
?
Technical field
The invention belongs to sign manufacturing technical field, particularly relate to a kind of method for making of flat solarization aluminium label.
Background technology
Metal tag refers to have the nameplate that operation instruction, trademark, making product nameplate, switch instruction, equipment nameplate, handicraft, metallic data plate, mechanical nameplate, electrical equipment nameplate, number etc. have body surface character by the nameplate product that several non-ferrous metal plates such as adopting copper, iron, aluminium, zinc, stainless steel uses different sign manufacturing processes to make.
The flat aluminium label that shines is the method adopting photosensitive lithographic, enters inside glued membrane, makes its word, pattern presents on a metal plate, thus reach the marking nameplate with descriptive sense by different pigment.
Summary of the invention
The invention provides a kind of method for making of flat solarization aluminium label.The present invention equals the method for making of shining aluminium label, is realized by following technical proposals:
(1) by woollen under the size of 5mm larger than plate-making size;
(2) woollen is carried out polishing, wire drawing and oxidation processes;
(3) plank will handled well, through deoiling, after membrane removal, is immersed in the water rapidly;
(4) by glue by (2-2.3): the weight ratio of 100 is added to the water, and boiling water boiling makes glue fully dissolve in 2 hours, after every 100 grams of water add heavy butyric acid ammonium (0.25-0.30) gram when temperature is down to 30-50 DEG C, is coated with uniformly on a metal plate by glue, dries;
(5) carry out photosensitive printing down, lamp 60-90cm, after time 40-80 gets second, being placed on development in warm water and within 1 minute, putting into look liquid and dye;
(6), through hyperchromatic plate, after airing, guarantor's lac varnish is coated with brush or spray gun.
The present invention puts down the obtained flat solarization label of the method for making of shining aluminium label, and be generally used on equipment that indoor article, small household appliances and non-weather extremes affect, the present invention equals the method for making of shining aluminium label, mask-making technology is simple, speed is fast, timely delivery guaranteed, takes defect rate and low.
Embodiment
Below by specific embodiment, the present invention is further illustrated.
The flat aluminium label that shines is the method adopting photosensitive lithographic, enters inside glued membrane, makes its word, pattern presents on a metal plate, thus reach the marking nameplate with descriptive sense by different pigment.
One, blanking: require that woollen size is generally greater than plate-making size (more than 5mm), plate face flat smooth, recessed without hole.
Two, pre-treatment: 1. polishing 2. wire drawing (Gao Guang) 3. processes and is 4. oxidized several methods such as (corrosion).
Three, water seal: by the plank handled well, through deoiling, after membrane removal, being immersed in the water and can not contacting with air rapidly.
Four, glue is played: the configuration of glue.
A, glue: 200-230 gram
Water: 1000ml
Boiling water boiling makes glue fully dissolve in 2 hours, is coated with uniformly on a metal plate by glue, dries stand-by when making temperature be down to 30-50 DEG C after adding photosensitizer (heavy butyric acid ammonium) 25-30 gram.
Five, printing down: SB750 type vacuum can be utilized to shine format machine and carry out photosensitive printing down, lamp 60-90cm, after time 40-80 gets second, being placed on development in warm water and within 1 minute, putting into look liquid and dye.
Six, protect light: through the plate of fully dyeing, after airing, coat with brush or spray gun and protect lac varnish (general eyes board baking vanish or exempt from baking guarantor lac varnish).
Seven, shear forming.
The flat label that shines is generally used on the equipment that indoor article, small household appliances and non-weather extremes affect.Advantage is that mask-making technology is simple, and speed is fast, timely delivery guaranteed, takes defect rate and low.Shortcoming is through exposing to the sun and rain, and easily fades.Outdoor sign can not be done.
Claims (1)
1. a flat method for making of shining aluminium label, is characterized in that comprising the following steps:
(1) by woollen under the size of 5mm larger than plate-making size;
(2) woollen is carried out polishing, wire drawing and oxidation processes;
(3) plank will handled well, through deoiling, after membrane removal, is immersed in the water rapidly;
(4) by glue by (2-2.3): the weight ratio of 100 is added to the water, and boiling water boiling makes glue fully dissolve in 2 hours, after every 100 grams of water add heavy butyric acid ammonium (0.25-0.30) gram when temperature is down to 30-50 DEG C, is coated with uniformly on a metal plate by glue, dries;
(5) carry out photosensitive printing down, lamp 60-90cm, after time 40-80 gets second, being placed on development in warm water and within 1 minute, putting into look liquid and dye;
(6), through hyperchromatic plate, after airing, guarantor's lac varnish is coated with brush or spray gun.