CN104231839A - Jade powder-containing powdered coating with high wear resistance - Google Patents
Jade powder-containing powdered coating with high wear resistance Download PDFInfo
- Publication number
- CN104231839A CN104231839A CN201410416861.8A CN201410416861A CN104231839A CN 104231839 A CN104231839 A CN 104231839A CN 201410416861 A CN201410416861 A CN 201410416861A CN 104231839 A CN104231839 A CN 104231839A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- wear resistance
- jade powder
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a jade powder-containing powdered coating with high wear resistance. The coating is prepared from the following raw materials in parts by weight: 1-2 parts of dicyandiamide, 4-6 parts of jade powder, 0.1-0.2 part of nigrosine, 3-5 parts of barium sulfate, 30-50 parts of phenolic resin, 2-4 parts of glass fibers, 4-6 parts of light calcium carbonate, 1-2 parts of glycerin monostearate, 3-6 parts of EVA (ethylene-vinyl acetate) resin, 0.1-0.2 part of diacetone alcohol, 10-15 parts of polyester resin, 1-2 parts of isocyanate, 1-2 parts of sodium hydroxide, 1-2 parts of nano magnesium oxide, 0.1-0.2 part of polyvinyl alcohol, 1-2 parts of ethanediamine, 1-2 parts of montmorillonite powder and 3-6 parts of a compound adhesive. The obtained powered coating contains raw materials such as jade powder, and after being reasonably compounded and extruded, the coating is excellent in wear resistance and impact resistance, stable in chemical property, durable and excellent in performance.
Description
Technical field
The present invention relates to art of powder coatings, is exactly a kind of powder coating containing jade powder with high-wear resistance.
Background technology
Powder coating is a kind of novel not containing solvent 100% solid powdery coating.There is solvent-free, pollution-free, recyclable, environmental protection, the saving energy and resource, reduce labor intensity and film physical strength high.And Mierocrystalline cellulose must apply in coating is a lot, the effect of coating toughness can be played.
Summary of the invention
The object of the present invention is to provide a kind of powder coating containing jade powder with high-wear resistance.
Above-mentioned purpose is realized by following scheme:
There is containing jade powder a powder coating for high-wear resistance, it is characterized in that: it is obtained by the raw material of following weight parts:
Dyhard RU 100 1-2, jade powder 4-6, nigrosine 0.1-0.2, barium sulfate 3-5, resol 30-50, glass fibre 2-4, light calcium carbonate 4-6, glyceryl monostearate 1-2, EVA resin 3-6, diacetone alcohol 0.1-0.2, vibrin 10-15, isocyanic ester 1-2, sodium hydroxide 1-2, nano magnesia 1-2, polyvinyl alcohol 0.1-0.2, quadrol 1-2, montmorillonite powder 1-2, composite sizing agent 3-6;
Composite sizing agent is obtained by the raw material of following weight parts:
Styrene-butadiene rubber(SBR) 4-6; st-yrax 0.1-0.5, acetone 1-2, pine tar 1-2, resol 0.8-0.9, Hydroxylated acrylic resin 1-2, zinc powder 0.1-0.2, silica 1-2, uric acid 0.1-0.5, Walocel MT 20.000PV 1-2, antioxidant 1076 1-2, polyether-ether-ketone 1-2;
The preparation method of composite sizing agent is: after each raw material blending, in 80-90 DEG C of mixing 10-20min, after taking-up, pulverizes, crosses 100-200 mesh sieve, to obtain final product.
Described a kind of powder coating containing jade powder with high-wear resistance, is characterized in that:
Preparation method comprises the following steps:
(1) all materials take by proportioning, are placed in high-speed mixer, 700-900 rev/min of mixing 20-25min;
(2) twin screw extruder is adopted, in 130-140
oabout C extrudes;
(3) extruding tablet through pulverizing, crossing 300-400 mesh sieve, to obtain final product.
Beneficial effect of the present invention is:
Gained powder coating contains the raw materials such as jade powder, by rationally composite, after extruding, has excellent wear resisting property and shock resistance, stable chemical nature, durable in use, superior performance.
Embodiment
Have a powder coating for high-wear resistance containing jade powder, it is obtained by the raw material of following weight (kg):
Dyhard RU 100 2, jade powder 5, nigrosine 0.2, barium sulfate 5, resol 50, glass fibre 2, light calcium carbonate 6, glyceryl monostearate 2, EVA resin 6, diacetone alcohol 0.2, vibrin 15, isocyanic ester 2, sodium hydroxide 1, nano magnesia 2, polyvinyl alcohol 0.2, quadrol 2, montmorillonite powder 2, composite sizing agent 5;
Composite sizing agent is obtained by the raw material of following weight (kg):
Styrene-butadiene rubber(SBR) 4, st-yrax 0.1, acetone 1, pine tar 1, resol 0.9, Hydroxylated acrylic resin 2, zinc powder 0.2, silicon-dioxide 2, uric acid 0.5, Walocel MT 20.000PV 2, antioxidant 1076 1, polyether-ether-ketone 2;
The preparation method of composite sizing agent is: after each raw material blending, in 80 DEG C of mixing 10min, after taking-up, pulverizes, crosses 100 mesh sieves, to obtain final product.
Described a kind of powder coating containing jade powder with high-wear resistance,
Preparation method comprises the following steps:
(1) all materials take by proportioning, are placed in high-speed mixer, 900 revs/min of mixing 25min;
(2) twin screw extruder is adopted, in 140
oabout C extrudes;
(3) extruding tablet through pulverizing, crossing 400 mesh sieves, to obtain final product.
The coating process of the present embodiment product is general electrostatic spraying, condition of cure: 200
oc/10-15min, gained coating is level and smooth, complete, and the artificial accelerated aging time is>=1700h.
Claims (2)
1. there is containing jade powder a powder coating for high-wear resistance, it is characterized in that: it is obtained by the raw material of following weight parts:
Dyhard RU 100 1-2, jade powder 4-6, nigrosine 0.1-0.2, barium sulfate 3-5, resol 30-50, glass fibre 2-4, light calcium carbonate 4-6, glyceryl monostearate 1-2, EVA resin 3-6, diacetone alcohol 0.1-0.2, vibrin 10-15, isocyanic ester 1-2, sodium hydroxide 1-2, nano magnesia 1-2, polyvinyl alcohol 0.1-0.2, quadrol 1-2, montmorillonite powder 1-2, composite sizing agent 3-6;
Composite sizing agent is obtained by the raw material of following weight parts:
Styrene-butadiene rubber(SBR) 4-6; st-yrax 0.1-0.5, acetone 1-2, pine tar 1-2, resol 0.8-0.9, Hydroxylated acrylic resin 1-2, zinc powder 0.1-0.2, silica 1-2, uric acid 0.1-0.5, Walocel MT 20.000PV 1-2, antioxidant 1076 1-2, polyether-ether-ketone 1-2;
The preparation method of composite sizing agent is: after each raw material blending, in 80-90 DEG C of mixing 10-20min, after taking-up, pulverizes, crosses 100-200 mesh sieve, to obtain final product.
2. a kind of powder coating containing jade powder with high-wear resistance according to claim 1, is characterized in that:
Preparation method comprises the following steps:
(1) all materials take by proportioning, are placed in high-speed mixer, 700-900 rev/min of mixing 20-25min;
(2) twin screw extruder is adopted, in 130-140
oabout C extrudes;
(3) extruding tablet through pulverizing, crossing 300-400 mesh sieve, to obtain final product.