CN104213053A - Hot-working die alloy - Google Patents
Hot-working die alloy Download PDFInfo
- Publication number
- CN104213053A CN104213053A CN201410465091.6A CN201410465091A CN104213053A CN 104213053 A CN104213053 A CN 104213053A CN 201410465091 A CN201410465091 A CN 201410465091A CN 104213053 A CN104213053 A CN 104213053A
- Authority
- CN
- China
- Prior art keywords
- hot
- die alloy
- percent
- working die
- work die
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses hot-working die alloy, which comprises the following ingredients in percentage by weight: 0.3 to 0.35 percent of carbon, 0.02 to 0.2 percent of silicon, 0.3 to 0.36 percent of nickel, 0.09 to 0.12 percent of potassium, 0.05 to 0.09 percent of phosphorus, 0.3 to 0.5 percent of manganese, 0.01 to 0.03 percent of titanium and the balance ferrum. The hot-working die alloy has the beneficial effects that the ingredients of the hot-working die alloy are scientific and reasonable; the performance is stable; and the service life is long.
Description
Technical field
The present invention relates to a kind of hot-work die alloy.
Background technology
At present, hot-work die alloy material realizes one of the modern basis of production and core technology, and its developmental level is the leading indicator of the national production level height of measurement one.Hot-work die alloy generally operates under suitable complex work condition, and the performance requriements for die steel material is also quite strict.And the hot-work die alloy of domestic production, the tropism such as grade of steel is lower, and homogeneity of structure is poor, and the mould synthetic performance examination produced is lower, seriously limits work-ing life.
Therefore, for solving the problem, spy provides a kind of new technical scheme to satisfy the demands.
Summary of the invention
The invention provides a kind of hot-work die alloy.
The technical solution used in the present invention is:
A kind of hot-work die alloy, comprises the component composition of following weight percent:
Carbon 0.3-0.35%;
Silicon 0.02-0.2%;
Nickel 0.3-0.36%;
Potassium 0.09-0.12%;
Phosphorus 0.05-0.09%;
Manganese 0.3-0.5%;
Titanium 0.01-0.03%;
Surplus is iron.
The antimony that weight percent is 0.07-0.1% can also be added.
The tin that weight percent is 0.02-0.06% can also be added.
The invention has the beneficial effects as follows: this kind of hot-work die alloy compositions is scientific and reasonable, stable performance, long service life.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only for explaining the present invention, does not form limiting the scope of the present invention.
Embodiment 1
A kind of hot-work die alloy, comprises the component composition of following weight percent:
Carbon 0.3%;
Silicon 0.02%;
Nickel 0.3%;
Potassium 0.09%;
Phosphorus 0.05%;
Manganese 0.3%;
Titanium 0.01%;
Surplus is iron.
Embodiment 2
A kind of hot-work die alloy, comprises the component composition of following weight percent:
Carbon 0.32%;
Silicon 0.15%;
Nickel 0.32%;
Potassium 0.1%;
Phosphorus 0.079%;
Manganese 0.4%;
Titanium 0.02%;
Tin 0.06%;
Surplus is iron.
Embodiment 3
A kind of hot-work die alloy, comprises the component composition of following weight percent:
Carbon 0.35%;
Silicon 0.2%;
Nickel 0.36%;
Potassium 0.12%;
Phosphorus 0.09%;
Manganese 0.5%;
Titanium 0.03%;
Antimony 0.1%;
Surplus is iron.
The invention has the beneficial effects as follows: this kind of hot-work die alloy compositions is scientific and reasonable, stable performance, long service life.
The above is only preferred embodiment of the present invention, is not restriction the present invention being made to any other form, and any amendment done according to technical spirit of the present invention or equivalent variations, still belong to the present invention's scope required for protection.
Claims (3)
1. a hot-work die alloy, is characterized in that: the component composition comprising following weight percent:
Carbon 0.3-0.35%;
Silicon 0.02-0.2%;
Nickel 0.3-0.36%;
Potassium 0.09-0.12%;
Phosphorus 0.05-0.09%;
Manganese 0.3-0.5%;
Titanium 0.01-0.03%;
Surplus is iron.
2. a kind of hot-work die alloy according to claim 1, is characterized in that: can also add the antimony that weight percent is 0.07-0.1%.
3. a kind of hot-work die alloy according to claim 1, is characterized in that: can also add the tin that weight percent is 0.02-0.06%.