CN104211328A - 环保砖 - Google Patents

环保砖 Download PDF

Info

Publication number
CN104211328A
CN104211328A CN201310207859.5A CN201310207859A CN104211328A CN 104211328 A CN104211328 A CN 104211328A CN 201310207859 A CN201310207859 A CN 201310207859A CN 104211328 A CN104211328 A CN 104211328A
Authority
CN
China
Prior art keywords
waste
brick
materials
protection brick
environmental protection
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310207859.5A
Other languages
English (en)
Inventor
张飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ningxia Xinhang Energy And Environment Technology Co Ltd
Original Assignee
Ningxia Xinhang Energy And Environment Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningxia Xinhang Energy And Environment Technology Co Ltd filed Critical Ningxia Xinhang Energy And Environment Technology Co Ltd
Priority to CN201310207859.5A priority Critical patent/CN104211328A/zh
Publication of CN104211328A publication Critical patent/CN104211328A/zh
Pending legal-status Critical Current

Abstract

一种变废为宝的环保砖，用80%的煤粉、煤渣、废砖瓦、废混凝土块等作为主料，用20%的水泥、河淤泥、粘土等辅料制成，各种原料占原料总重量的百分比分别为80%的工业垃圾和建筑垃圾，20%的胶结材料。其中工业垃圾和建筑垃圾的原料的组合分配是：煤粉15%～25%，煤渣25%～35%，废砖瓦15%～20%，废混凝土块30%～50%，胶结材料的原料组合分配是煤矸石4%～12%，水泥47%～54%，河淤泥（粘土）34%～49%。经过加工粉碎后，用砖机挤压成型，再经过高温高压蒸汽养护而制成。本发明的环保砖硬度好，抗压性强，外形美观，且工艺简单，综合利用了废弃物资源，有效的减少了工业垃圾、建筑垃圾带来的污染，变废为宝，改善了原料的级配，成本降低。

Description

环保砖
所属技术领域
本发明涉及一种将煤粉、煤渣、废砖瓦、废混凝土块等工业垃圾和建筑垃圾经过粉碎挤压成能够用于建筑和铺路使用的环保砖。属于建筑材料领域。
背景技术
目前的建筑用砖多以粘土砖为主，但是由于就地取材，大量的生产，不仅大面积的耕地被破坏，也导致土层地下水的流失，加重了土质的沙化，严重破坏了环境。同时工业上产生的大量的工业废料煤粉、煤渣和建筑垃圾废砖瓦、废混凝土块等对环境造成了第二次污染。
发明内容
为了解决上述问题，本发明提供了一种可以将工业垃圾和建筑垃圾变废为宝的建筑用砖即环保砖。有效的节约了资源，避免了对环境的第二次污染。
实现本发明所采取的技术方案为：一种环保砖，其制备原料煤粉、煤渣、废砖瓦、废混凝土块以及少量的煤矸石、水泥、河淤泥、粘土等胶结材料。各种原料占原料总重量的百分比分别为80%的工业垃圾和建筑垃圾，20%的胶结材料。其中工业垃圾和建筑垃圾的原料的组合分配是：煤粉15%～25%，煤渣25%～35%，废砖瓦15%～20%，废混凝土块30%～50%，胶结材料的原料组合分配是煤矸石4%～12%，水泥47%～54%，河淤泥（粘土）34%～49%。将这几种原料混合搅拌均匀后，用砖机挤压成各类型和形状的环保砖。成型后砖坯放到高温养生室，用300℃～320℃的水蒸气对砖坯进行高温养生1～1.5小时，养生后的砖坯放到环境温度20℃～30℃、相对湿度65±20%rh晾晒棚中，避免暴晒，自然干燥48小时以上即可成品。广泛用于建筑与铺路。
本发明的特点是，可以制成各种形状的砖，利用工业垃圾和建筑垃圾制作环保砖，进行了废物利用，节约了资源，制作工艺简单，为建筑业提供了原材料，成本低。
具体实施方式
以下结合实例对本发明作进一步的说明
实施例1
用15%煤粉、25%煤渣、15%废砖瓦、45%废混凝土组合的混合物作为主料，用4%煤矸石、54%的300#水泥、42%粘土组合的混合物作为辅料，取80%的主料和20%的辅料在水泥搅拌机中搅拌均匀，用砖机挤压成所需的长方形，成型后砖坯放到高温养生室，用300℃～320℃的水蒸气对砖坯进行高温养生1～1.5小时，养生后的砖坯放到环境温度20℃～30℃、相对湿度65±20%rh晾晒棚中，避免暴晒，自然干燥48小时以上即可成品。广泛用于建筑。
实施例2
用25%煤粉、30%煤渣、15%废砖瓦、30%废混凝土组合的混合物作为主料，用12%煤矸石、47%水泥、41%河淤泥组合的混合物作为辅料，取80%的主料和20%的辅料在水泥搅拌机中搅拌均匀，用砖机挤压成所需的长方形，成型后砖坯放到高温养生室，用300℃～320℃的水蒸气对砖坯进行高温养生1～1.5小时，养生后的砖坯放到环境温度20℃～30℃、相对湿度65±20%rh晾晒棚中，避免暴晒，自然干燥48小时以上即可成品。广泛用于铺路。

Claims (2)

1.一种环保砖将各类的垃圾集中起来，经过加工粉碎之后，其特征是：取80%煤粉、煤渣、废砖瓦、废混凝土块等作为主料，取20%的水泥、河淤泥、粘土等辅料。其中工业垃圾和建筑垃圾的原料的组合分配是：煤粉15%～25%，煤渣25%～35%，废砖瓦15%～20%，废混凝土块30%～50%，胶结材料的原料组合分配是煤矸石4%～12%，水泥47%～54%，河淤泥（粘土）34%～49%。将这几种原料混合搅拌均匀后，用砖机挤压成各类型和形状的环保砖。将成型后砖坯放到高温养生室，用300℃～320℃的水蒸气对砖坯进行高温养生1～1.5小时，养生后的砖坯放到环境温度20℃～30℃、相对湿度65±20%rh晾晒棚中，避免暴晒，自然干燥48小时以上即可成品。
2.根据权利要求1所述的环保砖，其特征在于，制成的环保砖比普通砖的硬度高，耐磨性好，透水性好。
CN201310207859.5A 2013-05-30 2013-05-30 环保砖 Pending CN104211328A (zh)