CN104197008A - Production technology for graphite gasket - Google Patents
Production technology for graphite gasket Download PDFInfo
- Publication number
- CN104197008A CN104197008A CN201410503364.1A CN201410503364A CN104197008A CN 104197008 A CN104197008 A CN 104197008A CN 201410503364 A CN201410503364 A CN 201410503364A CN 104197008 A CN104197008 A CN 104197008A
- Authority
- CN
- China
- Prior art keywords
- production technology
- temperature
- die
- graphite
- vulcanized
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production technology for a graphite gasket. The production technology comprises the following steps: (1) graphite powder, an accelerant and a plasticizer are uniformly mixed for use at the weight ratio of 3:1:1; (2) a die is preheated and the die is heated at the temperature of 180 DEG C-220 DEG C; (3) the mixture is put in the die, the mixture and the die are together put in a heating furnace with the temperature controlled below 300 DEG C at the beginning, and the temperature is increased to 500 DEG C and kept for 2-3 h; (4) the die is taken out and cooled to the indoor temperature; (5) a cylindrical blank is immersed into a vulcanized tank and a saponified tank in sequence, the vulcanized tank is filled with a zinc-calcium vulcanized liquid with the concentration of 6-9%, the temperature of the zinc-calcium vulcanized liquid is 45-65 DEG C, and the immersing time lasts for 25-30 min; (6) tap water is used for rinsing, and air inducing equipment is used for drying; (7) trimming, burr taking out, processing and cutting are conducted to obtain finished products. According to the invention, the production technology is simple in operation and skillful in technology, and sealing gaskets produced by the production technology have low probability of wearing and are durable.
Description
Technical field
The present invention relates to sealing material field, specifically, specially refer to a kind of Graphite pad production technology.
Background technique
Sealing material just draws and refers to that can bear seam displacement is called sealing material with the material that reaches airtight, watertight object and embed in building joint.Sealing member material has metallic material (aluminium, lead, indium, stainless steel etc.), also having nonmetallic material (rubber, plastics, pottery, graphite etc.), composite material (as rubber-asbestos slate, aerogel blanket-polyurethane), is rubber-like elastomeric material but use maximum.Existing gasket seal is not wear-resistant, and working life is shorter.
Summary of the invention
The object of the invention is to for deficiency of the prior art, provide a kind of Graphite pad production technology, to address the above problem.
Technical problem solved by the invention can realize by the following technical solutions:
Graphite pad production technology, comprises the steps:
1) weight proportion of powdered graphite, promoter and binder being pressed to 3:1:1 evenly mixes stand-by;
2) preheated mold, by mold heated 180-220 DEG C;
3) mixture is put into mould, then put into oven together with mould, charging temperature is controlled at below 300 DEG C, is warming up to 500 degrees Celsius, and keeps 2-3 hour;
4) take out, be cooled to room temperature;
4) cylindric blank is immersed successively in sulfuration pond and saponification pond, in phosphating pond, filling concentration is the zinc calcium sulfuration liquid of 6-9%, and the temperature of zinc calcium sulfuration liquid is 45-65 DEG C, and dip time is 25-30 minute;
5) use tap water to carry out rinsing, then use air inducing equipment to dry up;
6) deburring, takes out burr, and processing cutting, makes finished product.
Preferably, described step 2) in the optimum temperature of preheating be 200 DEG C.
Preferably, described zinc calcium sulfuration liquid optium concentration is 8%, and dipping Best Times is 25 minutes.
Compared with prior art, beneficial effect of the present invention is as follows:
Simple to operate, technique is ingenious, and the gasket seal of producing through the present invention is not easy to wear, durable in use.
Embodiment
For technological means, creation characteristic that the present invention is realized, reach object and effect is easy to understand, below in conjunction with embodiment, further set forth the present invention.
Embodiment 1
Graphite pad production technology, comprises the steps:
1) weight proportion of powdered graphite, promoter and binder being pressed to 3:1:1 evenly mixes stand-by;
2) preheated mold, by 180 DEG C of mold heated;
3) mixture is put into mould, then put into oven together with mould, charging temperature is controlled at below 300 DEG C, is warming up to 500 degrees Celsius, and keeps 2 hours;
4) take out, be cooled to room temperature;
4) cylindric blank is immersed successively in sulfuration pond and saponification pond, fill concentration and be 6% zinc calcium sulfuration liquid in phosphating pond, the temperature of zinc calcium sulfuration liquid is 65 DEG C, and dip time is 25 minutes;
5) use tap water to carry out rinsing, then use air inducing equipment to dry up;
6) deburring, takes out burr, and processing cutting, makes finished product.
Embodiment 2
Graphite pad production technology, comprises the steps:
1) weight proportion of powdered graphite, promoter and binder being pressed to 3:1:1 evenly mixes stand-by;
2) preheated mold, by 220 DEG C of mold heated;
3) mixture is put into mould, then put into oven together with mould, charging temperature is controlled at below 300 DEG C, is warming up to 500 degrees Celsius, and keeps 3 hours;
4) take out, be cooled to room temperature;
4) cylindric blank is immersed successively in sulfuration pond and saponification pond, fill concentration and be 9% zinc calcium sulfuration liquid in phosphating pond, the temperature of zinc calcium sulfuration liquid is 65 DEG C, and dip time is 30 minutes;
5) use tap water to carry out rinsing, then use air inducing equipment to dry up;
6) deburring, takes out burr, and processing cutting, makes finished product.
More than show and described basic principle of the present invention and major character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that in above-described embodiment and specification, describes just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (3)
1. Graphite pad production technology, is characterized in that, comprises the steps:
1) weight proportion of powdered graphite, promoter and binder being pressed to 3:1:1 evenly mixes stand-by;
2) preheated mold, by mold heated 180-220 DEG C;
3) mixture is put into mould, then put into oven together with mould, charging temperature is controlled at below 300 DEG C, is warming up to 500 degrees Celsius, and keeps 2-3 hour;
4) take out, be cooled to room temperature;
4) cylindric blank is immersed successively in sulfuration pond and saponification pond, in phosphating pond, filling concentration is the zinc calcium sulfuration liquid of 6-9%, and the temperature of zinc calcium sulfuration liquid is 45-65 DEG C, and dip time is 25-30 minute;
5) use tap water to carry out rinsing, then use air inducing equipment to dry up;
6) deburring, takes out burr, and processing cutting, makes finished product.
2. Graphite pad production technology according to claim 1, is characterized in that, described step 2) in the optimum temperature of preheating be 200 DEG C.
3. Graphite pad production technology according to claim 1, is characterized in that, described zinc calcium sulfuration liquid optium concentration is 8%, and dipping Best Times is 25 minutes.