CN104195870A - Ceramic fiber paper - Google Patents
Ceramic fiber paper Download PDFInfo
- Publication number
- CN104195870A CN104195870A CN201410433453.3A CN201410433453A CN104195870A CN 104195870 A CN104195870 A CN 104195870A CN 201410433453 A CN201410433453 A CN 201410433453A CN 104195870 A CN104195870 A CN 104195870A
- Authority
- CN
- China
- Prior art keywords
- ceramic fiber
- fiber paper
- hydroxide powder
- ceramic
- sizing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses ceramic fiber paper. The ceramic fiber paper comprises the following components in percentage by weight: 20-40% of ceramic fibers, 20-30% of graphite fibers, 20-40% of paper pulp, 10-12% of a sizing agent and 5-7% of additives. Compared with the prior art, the ceramic fiber paper is higher in flame retardant property, abrasive resistance, insulation property and heat insulation property, longer in service life in the actual production and better in effect.
Description
Technical field
The invention belongs to ceramic material field, be specifically related to a kind of ceramic fiber paper.
Background technology
Ceramic material is with a class Inorganic Non-metallic Materials natural or that synthetic compound process is shaped and high temperature sintering is made.It has the advantages such as high-melting-point, high rigidity, high-wearing feature, resistance to oxidation.Can be used as structural material, cutter material, because pottery also has some special performance, can be used as again functional material.In the whole world, be all study hotspot instantly for the exploitation of new ceramic material and ceramic material function.
Ceramic fiber paper is a large focus of current ceramic material area research.Ceramic fiber paper has heat insulation, and good insulating is fire-retardant, and the advantage such as wear-resisting, is now widely used in wheel, in lathe as base band or scrape slurry carrier.
Summary of the invention
Goal of the invention: the object of this invention is to provide the ceramic fiber paper that a kind of practicality is good, to solve existing ceramic material problem such as poor durability in actual production.
Technical scheme: a kind of ceramic fiber paper, comprises the component of following percentage by weight:
Wherein, ceramic fibre is without asbestos deposit fibres.
Wherein, auxiliary agent is the mixture of aluminium-hydroxide powder, sodium hydroxide powder and calcium sulphate powders; Wherein the weight ratio of aluminium-hydroxide powder, sodium hydroxide powder and calcium sulphate powders consumption is 1.5～2.5:1:1.
Wherein, paper pulp is wood pulp or straw pulp.
Wherein, sizing agent is any one in gum rosin, wax size or synthetic sizing agent.
Above-mentioned material is buied by market.
Beneficial effect: compared with prior art, its remarkable advantage is in the present invention: there is better anti-flammability, ABRASION RESISTANCE, insulating properties and thermal insulation, in actual production service time longer, better effects if.
Detailed description of the invention
Embodiment 1
Component and weight ratio thereof: without asbestos deposit fibres 30%, graphite fibre 25%, wood pulp 28%, gum rosin 12%, aluminium-hydroxide powder 2.5%, sodium hydroxide powder 1.25%, calcium sulphate powders 1.25%.
Preparation method: after ceramic fibre and graphite fibre are pulverized and paper pulp add in stirring pool, then add the water of 2 times of volumes; After being dissolved in to 1mol/L dilute hydrochloric acid solution, auxiliary agent adds in stirring pool; The most backward stirring pool adds sizing agent, stirs 1h; Finally copy and get, dry moulding.
Embodiment 2
Component and weight ratio thereof: without asbestos deposit fibres 23%, graphite fibre 20%, wood pulp 40%, wax size 10%, aluminium-hydroxide powder 3%, sodium hydroxide powder 2%, calcium sulphate powders 2%.
Preparation method: after ceramic fibre and graphite fibre are pulverized and paper pulp add in stirring pool, then add the water of 3 times of volumes; After being dissolved in to 1mol/L dilute hydrochloric acid solution, auxiliary agent adds in stirring pool; The most backward stirring pool adds sizing agent, stirs 2h; Finally copy and get, dry moulding.
Embodiment 3
Component and weight ratio thereof: without asbestos deposit fibres 37%, graphite fibre 28%, paper pulp 20%, synthetic sizing agent 10%, aluminium-hydroxide powder 2.5%, sodium hydroxide powder 1.25%, calcium sulphate powders 1.25%.
Preparation method: after ceramic fibre and graphite fibre are pulverized and paper pulp add in stirring pool, then add the water of 2 times of volumes; After being dissolved in to 1mol/L dilute hydrochloric acid solution, auxiliary agent adds in stirring pool; The most backward stirring pool adds sizing agent, stirs 1.5h; Finally copy and get, dry moulding.
Claims (5)
1. a ceramic fiber paper, is characterized in that, it comprises the component of following percentage by weight:
2. ceramic fiber paper according to claim 1, is characterized in that, described ceramic fibre is without asbestos deposit fibres.
3. ceramic fiber paper according to claim 1, is characterized in that, described auxiliary agent is the mixture of aluminium-hydroxide powder, sodium hydroxide powder and calcium sulphate powders; Wherein, the weight ratio of aluminium-hydroxide powder, sodium hydroxide powder and calcium sulphate powders consumption is 1.5～2.5:1:1.
4. ceramic fiber paper according to claim 1, is characterized in that, described paper pulp is wood pulp or straw pulp.
5. ceramic fiber paper according to claim 1, is characterized in that, described sizing agent is any one in gum rosin, wax size or synthetic sizing agent.