CN104194638A - 抗结晶松香的制备方法 - Google Patents
抗结晶松香的制备方法 Download PDFInfo
- Publication number
- CN104194638A CN104194638A CN201410358218.4A CN201410358218A CN104194638A CN 104194638 A CN104194638 A CN 104194638A CN 201410358218 A CN201410358218 A CN 201410358218A CN 104194638 A CN104194638 A CN 104194638A
- Authority
- CN
- China
- Prior art keywords
- rosin
- crystallization
- reactor
- weight part
- sodium phosphate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种抗结晶松香的制备方法,属于松香深加工技术领域。本发明包括将松香放入反应器中,加热熔解,然后加入磷酸氢二钠,在185℃~215℃的温度下,进行搅拌;当所述磷酸氢二钠溶解完全时,停止搅拌,静置10分钟~15分钟,出料。本发明制得的抗结晶松香具有很好的抗结晶作用,使其在凝固时不致于形成晶体。
Description
技术领域
本发明属于松香深加工技术领域,尤其涉及一种抗结晶松香的制备方法。
背景技术
松香是重要的化工原料,广泛应用于肥皂、造纸、油漆、橡胶等行业。然而,由于松香具有结晶倾向,松香结晶会使透明度、溶解度降低,松香结晶熔点可高达110℃~135℃,并且松香在溶剂中还有再结晶的趋势,降低使用价值。此时,需要对松香进行相应的处理来尽防止其结晶。
一般,防止松香结晶的方法普遍是采用加强通风冷却、防止水分进入、避免震动等方式,但这些方法难度系数大,难以达到稳定的控制,所以松香仍然会出现不同程度的结晶。
发明内容
本发明解决的技术问题是提供一种具有抗结晶作用的抗结晶松香的制备方法,该方法能解决现有防止松香结晶的方法难度系数大,难以达到稳定的控制以及仍会出现不同程度结晶的问题。
为了解决上述技术问题,本发明所采用的技术方案是:
一种抗结晶松香的制备方法是:
先将0.8重量份~0.1重量份的松香放入反应器中,加热熔解,然后向所述反应器中加入0.0001重量份~0.0005重量份的磷酸氢二钠,在185℃~215℃的温度下,进行搅拌;当所述磷酸氢二钠溶解完全时,停止搅拌,静置10分钟~15分钟后,出料。
由于采用上述技术方案,本发明得到的有益效果是:
本发明采用在松香晶体的生长面上生成一层与其晶格排列不同的分子,从而破坏松香晶面上后续晶格的发育,阻碍晶体成长,从而有效地阻止和延缓松香结晶,使松香在凝固时不致于形成晶体,从而达到抗结晶的目的。
具体实施方式
以下结合具体实施例对本发明作进一步详述,而本发明的保护范围并非仅仅局限于以下实施例。
实施例1
本抗结晶松香的制备方法是:
先将0.8kg松香放入反应器中,加热熔解,然后向所述反应器中加入0.0001kg磷酸氢二钠,在185℃的温度下,进行搅拌;当所述磷酸氢二钠溶解完全时,停止搅拌,静置10分钟后,出料。
实施例2
本抗结晶松香的制备方法是:
先将0.9kg松香放入反应器中,加热熔解,然后向所述反应器中加入0.0003kg磷酸氢二钠,在200℃的温度下,进行搅拌;当所述磷酸氢二钠溶解完全时,停止搅拌,出料,静置13分钟后,出料。
实施例3
本抗结晶松香的制备方法是:
先将0.1kg松香放入反应器中,加热熔解,然后向所述反应器中加入0.0005kg磷酸氢二钠,在215℃的温度下,进行搅拌;当所述磷酸氢二钠溶解完全时,停止搅拌,静置15分钟后,出料。
将实施例1~3制得的抗结晶松香进行性能检测,其结果如表1。
表1
从上述表1中可以看出,本发明制得的抗结晶松香不仅具备抗结晶的作用,而且很好的保留了原料松香的性能。
Claims (1)
1.一种抗结晶松香的制备方法,其特征在于包括以下步骤:
先将0.8重量份~0.1重量份的松香放入反应器中,加热熔解,然后向所述反应器中加入0.0001重量份~0.0005重量份的磷酸氢二钠,在185℃~215℃的温度下,进行搅拌;当所述磷酸氢二钠溶解完全时,停止搅拌,静置10分钟~15分钟后,出料。