CN104178068A - Adhesive for construction - Google Patents
Adhesive for construction Download PDFInfo
- Publication number
- CN104178068A CN104178068A CN201410450676.0A CN201410450676A CN104178068A CN 104178068 A CN104178068 A CN 104178068A CN 201410450676 A CN201410450676 A CN 201410450676A CN 104178068 A CN104178068 A CN 104178068A
- Authority
- CN
- China
- Prior art keywords
- weight parts
- styrene
- butadiene
- weight
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an adhesive which is prepared from styrene-butadiene-styrene copolymer, terpene resin, cyclohexane, petroleum resin, trichloroethane, paraffin, a solvent, a reinforcer, an anti-aging agent and the like. The adhesive has high curing speed, and can enhance the construction speed and work efficiency. The adhesive has favorable water resistance and can not easily crack when meeting with water. The adhesive is suitable for connection among wood, stone, concrete, ceramics, glass, foam plastics and metals in construction.
Description
Technical field
The present invention relates to a kind of binding agent.Specifically, be the binding agent that connects use between timber, stone material, concrete, pottery, glass, porous plastics, metal.
Background technology
At building field, the binding agent of the use that bonds between timber, stone material, concrete, pottery, glass, porous plastics, metal is mainly polychloroprene-novolac type sizing agent at present.There is following shortcoming in this sizing agent, and the one, in construction process, curing speed is slower, thereby can affect construction speed; The 2nd, water resistance is poor, easy to crack with the water capacity.
Summary of the invention
The problem to be solved in the present invention is to provide a kind of binding agent for building.This binding agent for building, curing speed is fast, and water resistance is good.
For addressing the above problem, take following technical scheme:
Binding agent feature for building of the present invention is to be made up of the raw material of following parts by weight:
Styrene-butadiene-styrene 50 ~ 60 weight parts;
Terpine resin 20 ~ 23 weight parts;
Hexanaphthene 140 ~ 160 weight parts;
Petroleum resin 58 ~ 60 weight parts;
Trichloroethane 26 ~ 28 weight parts;
Paraffin 3 ~ 5 weight parts;
Solvent 70 ~ 80 weight parts;
Toughener 13 ~ 15 weight parts;
Anti-aging agent 0.2 ~ 0.3 weight part;
Wherein:
Described solvent is No. 97 gasoline;
The ethyl acetate solution that described toughener is is 20% by tolylene diisocyanate, TriMethylolPropane(TMP) and concentration, according to tolylene diisocyanate: TriMethylolPropane(TMP): the part by weight of ethyl acetate solution=1:1:1 that concentration is 20% mixes;
Preparation method is:
First styrene-butadiene-styrene, solvent, trichloroethane, hexanaphthene and paraffin are dropped in reactor, stir, styrene-butadiene-styrene is dissolved completely;
Add again terpine resin, petroleum resin, toughener, anti-aging agent, at the temperature of 38 ~ 42 degrees Celsius, stir 5 ~ 6 hours, material is dissolved completely, obtain binding agent for building.
Take above scheme, have the following advantages:
As can be seen from the above scheme, because binding agent of the present invention is made up of raw materials such as styrene-butadiene-styrene, terpine resin, hexanaphthene, petroleum resin, trichloroethane, paraffin, solvent, toughener, anti-aging agent, after testing, there is curing speed faster, can improve speed of application, increase work efficiency; There is good water resistance, not easy to crack with water.
Embodiment
Embodiment mono-
First choose the styrene-butadiene-styrene of 50 weight parts, the terpine resin of 20 weight parts, the hexanaphthene of 140 weight parts, the petroleum resin of 58 weight parts, the trichloroethane of 26 weight parts, the paraffin of 3 weight parts, the solvent of 70 weight parts, the toughener of 13 weight parts, the anti-aging agent of 13 weight parts.Wherein: described solvent is No. 97 gasoline; The ethyl acetate solution that described toughener is is 20% by tolylene diisocyanate, TriMethylolPropane(TMP) and concentration, according to tolylene diisocyanate: TriMethylolPropane(TMP): the part by weight of ethyl acetate solution=1:1:1 that concentration is 20% mixes.
Then styrene-butadiene-styrene, solvent, trichloroethane, hexanaphthene and paraffin are dropped in reactor, stir, styrene-butadiene-styrene is dissolved completely
Add again terpine resin, petroleum resin, toughener, anti-aging agent, at the temperature of 38 degrees Celsius, stir 5 hours, material is dissolved completely, obtain binding agent for building.
Embodiment bis-
First choose the styrene-butadiene-styrene of 55 weight parts, the terpine resin of 22 weight parts, the hexanaphthene of 150 weight parts, the petroleum resin of 59 weight parts, the trichloroethane of 27 weight parts, the paraffin of 4 weight parts, the solvent of 75 weight parts, the toughener of 14 weight parts, the anti-aging agent of 14 weight parts.Wherein: described solvent is No. 97 gasoline; The ethyl acetate solution that described toughener is is 20% by tolylene diisocyanate, TriMethylolPropane(TMP) and concentration, according to tolylene diisocyanate: TriMethylolPropane(TMP): the part by weight of ethyl acetate solution=1:1:1 that concentration is 20% mixes.
Then styrene-butadiene-styrene, solvent, trichloroethane, hexanaphthene and paraffin are dropped in reactor, stir, styrene-butadiene-styrene is dissolved completely
Add again terpine resin, petroleum resin, toughener, anti-aging agent, at the temperature of 40 degrees Celsius, stir 5.5 hours, material is dissolved completely, obtain binding agent for building.
Embodiment tri-
First choose the styrene-butadiene-styrene of 60 weight parts, the terpine resin of 23 weight parts, the hexanaphthene of 160 weight parts, the petroleum resin of 60 weight parts, the trichloroethane of 28 weight parts, the paraffin of 5 weight parts, the solvent of 80 weight parts, the toughener of 15 weight parts, the anti-aging agent of 15 weight parts.Wherein: described solvent is No. 97 gasoline; The ethyl acetate solution that described toughener is is 20% by tolylene diisocyanate, TriMethylolPropane(TMP) and concentration, according to tolylene diisocyanate: TriMethylolPropane(TMP): the part by weight of ethyl acetate solution=1:1:1 that concentration is 20% mixes.
Then styrene-butadiene-styrene, solvent, trichloroethane, hexanaphthene and paraffin are dropped in reactor, stir, styrene-butadiene-styrene is dissolved completely
Add again terpine resin, petroleum resin, toughener, anti-aging agent, at the temperature of 42 degrees Celsius, stir 6 hours, material is dissolved completely, obtain binding agent for building.
Claims (1)
1. binding agent for building, is characterized in that being made up of the raw material of following parts by weight:
Styrene-butadiene-styrene 50 ~ 60 weight parts;
Terpine resin 20 ~ 23 weight parts;
Hexanaphthene 140 ~ 160 weight parts;
Petroleum resin 58 ~ 60 weight parts;
Trichloroethane 26 ~ 28 weight parts;
Paraffin 3 ~ 5 weight parts;
Solvent 70 ~ 80 weight parts;
Toughener 13 ~ 15 weight parts;
Anti-aging agent 0.2 ~ 0.3 weight part;
Wherein:
Described solvent is No. 97 gasoline;
The ethyl acetate solution that described toughener is is 20% by tolylene diisocyanate, TriMethylolPropane(TMP) and concentration, according to tolylene diisocyanate: TriMethylolPropane(TMP): the part by weight of ethyl acetate solution=1:1:1 that concentration is 20% mixes;
Preparation method is:
First styrene-butadiene-styrene, solvent, trichloroethane, hexanaphthene and paraffin are dropped in reactor, stir, styrene-butadiene-styrene is dissolved completely;
Add again terpine resin, petroleum resin, toughener, anti-aging agent, at the temperature of 38 ~ 42 degrees Celsius, stir 5 ~ 6 hours, material is dissolved completely, obtain binding agent for building.