A kind of environmentally-friendly acrylic ester grouting material and preparation method and application
Technical field
The present invention relates in a kind of Geotechnical Engineering antiseepage, leak stopping grouting material, and in particular to it is a kind of to be applied to ground
Foundation treatment engineering antiseepage and reinforcing, the sealing of movement joint leak and the environmentally-friendly acrylic ester grouting material and its preparation reinforced
Method and application.
Background technology
In dealing with foundation project seepage controlling with consolidation process, frequently with acrylates grouting material and modified epoxy tree
Fat grouting material carries out antiseepage and consolidation process as grouting material.But organic grouting material price is higher, causes to be constructed into
This height.For this purpose, unit in charge of construction wish by organic grouting material and routine inorganic grouting material for example cement mortar, clay cement grout,
Bentonite cement slurry etc. is mixed and is in the milk, and replaces organic chemistry grouting material to be filled with part inorganic grouting material
Slurry, can be greatly lowered construction material cost, improve the durability of material, simplify construction technology.But current has mechanical irrigation
Pulp material can not be mixed with inorganic grouting material, together carry out chemical grouting, such as acrylates grouting material and cement mortar
When liquid mixes, acrylates grouting material meets the silicate ion in cement, produces rapidly precipitation, loses concrete castability;Polyurethane
Grouting material meets the water in cement mortar, rapid to foam, and loses concrete castability;Modified epoxy grouting material is met in cement mortar
Water, in fact it could happen that situations such as not solidifying.
Meanwhile, the movement joint leak in underground space structure is also current one big difficult point of construction, existing organic injection material
Material can not effectively solving movement joint seepy question.Acrylates grouting material gelling time is difficult to, by temperature, initiation
The factors such as dosage, impurity affect larger, and accurate gelling time is difficult to control to;The solid content of acrylate grout is limited, it is impossible to
More than 40%, cause its gel low intensity, be similar to jelly colloid, after water swelling, gel intensity is very low, highly brittle, easily
Extrude from crack, the grouting to waterproof for not being suitable for movement joint is processed.Polyurethane grouting material is divided into oil-soluble and water-soluble filling
Two kinds of pulp material, the polyurethane grouting material for concrete crack crack are mainly soluble polyurethane grouting material.The material
Material meet Water blown, after foaming into crack micropore in, but foam after foams it is very soft, cause foam Hole compared with
It is many and be interconnected.Engineering practice is proved:Carried out after sealing using polyurethane grouting material, general effective time is that half a year is left
The right side, occurs the situation of leak after half a year again.Therefore, Shenzhen Metro, Guangzhou Underground are it has been specified that polyurethane mustn't be adopted
Grouting material carries out sealing, Anti-seeping technology to distress in concrete.Modified epoxy grouting material be a kind of viscosity it is low, solidification after
The high grouting material of intensity, is widely used in the improvement of various dry concrete diseases.But due to modified epoxy grouting material
It is oiliness, and the interface of the movement joint of leak is flooded profit, water-oil phase is unable to bonding, causes modified epoxy injection material
Expect that the repairing effect to leak movement joint is limited, treatment effect is bad.
The content of the invention
Technical problem solved by the invention is to provide a kind of environmentally-friendly acrylic ester grouting material and preparation method thereof
With application, to solve existing organic grouting material and can not mix with inorganic grouting material to be in the milk, and existing grouting material
The durability of presence is bad, and low intensity, water-soluble bad, water-swellable rate be not high, the high technical barrier of toxicity.
Technical problem solved by the invention employs the following technical solutions to realize:
A kind of environmentally-friendly acrylic ester grouting material, is mainly made up of with proportioning following components:
Host:100 parts of methacrylic acid-beta-hydroxy ethyl ester
Crosslinking agent:5~30 parts of the hydrophilic compounds of diallyl containing ether functional group
1~5 part of initiator
0.5~3 part of accelerator
Solvent:2~1000 parts of water
0~20 part of auxiliary agent.
In above-mentioned environmentally-friendly acrylic ester grouting material, it is preferred that the crosslinking agent is polyethylene glycol diallyl ether.
In above-mentioned environmentally-friendly acrylic ester grouting material, it is preferred that the crosslinking agent is polyethylene glycol diallyl ether
With the mixture of ethoxylated bisphenol A dual-allyl ethers in mass ratio 100: 1~50.
In above-mentioned environmentally-friendly acrylic ester grouting material, it is preferred that poly- second two in the polyethylene glycol diallyl ether
The molecular weight of alcohol is between 40~2000.
In above-mentioned environmentally-friendly acrylic ester grouting material, it is preferred that ethoxy in the ethoxylated bisphenol A dual-allyl ethers
The number for changing functional group is 5~15.
Wherein polyethylene glycol diallyl ether is non-toxic material, miscible with water, simultaneous with two allyl functionalities, i.e.,
As crosslinking agent, methacrylic acid-beta-hydroxy ethyl ester is promoted to form water-fast cubic network shape gel;Contain in molecule simultaneously
There is longer flexible chain, the toughness and elasticity of grouting material gel can be improved;Ethoxylated bisphenol A dual-allyl ethers are except with poly-
Beyond the feature performance benefit of ethylene glycol diallyl ether, also contain bisphenol-A functional group in molecular structure, with good weather-proof, resistance to
Corrosivity, cementability, while improve the rigidity of grouting material gel.
In above-mentioned environmentally-friendly acrylic ester grouting material, it is preferred that the initiator be potassium peroxydisulfate, ammonium persulfate,
It is a kind of in sodium peroxydisulfate, benzoyl peroxide, TBHP, methyl ethyl ketone peroxide or di-cyclohexylperoxy di-carbonate
Or several mixtures.
In above-mentioned environmentally-friendly acrylic ester grouting material, it is preferred that the accelerator be sodium acid carbonate, triethanolamine,
In stannous chloride, sodium thiosulfate, sodium dithionate, ferrous sulfate, cobalt naphthenate or β-dimethylaminopropionitrile one or more
Mixture.
In above-mentioned environmentally-friendly acrylic ester grouting material, it is preferred that the auxiliary agent be PAA, calcium acrylate, third
The mixture of one or more in olefin(e) acid magnesium, the potassium ferricyanide, the purpose of addition be further improve slurries water swelling and
Adjust the gel time of slurries.
Used as a total technology design, the present invention also provides a kind of system of above-mentioned environmentally-friendly acrylic ester grouting material
Preparation Method:First host, crosslinking agent, accelerator are well mixed, wherein can also add auxiliary agent or solvent, form solution A;Then
Second liquid is formed after initiator and solvent are well mixed, and solution A, second liquid are mixed to form into environmentally-friendly acrylic ester grouting during use
Slurries, final crosslinking curing.
Used as a total technology design, the present invention also provides a kind of answering for above-mentioned environmentally-friendly acrylic ester grouting material
With:The water-solid ratio for adding equal-volume ratio in the environmentally-friendly acrylic ester grouting material is 0.5~5:1 cement mortar, clay water
Mud or bentonite cement slurries, can form organic-inorganic grouting material after mixing and stirring.
Beneficial effects of the present invention are:
1)Using host monomer miscible with water, the hydrophilic compounds with dual-allyl ether functional group are crosslinking agent, with
Water is solvent, during raw material can be dissolved in a large amount of water and wraps up a large amount of free water cures.
2)After slurries crosslinking curing, the main chain in cross-linked network is carbon-carbon bond, and cross linked chain is carbon-carbon bond and ehter bond, is had
There are good hydrolytic resistance and resistance to ag(e)ing.
3)Slurries are host methacrylic acid-beta-hydroxy ethyl ester, and LD50 is 11200mg/kg, is micro- poison;And host only accounts for slurry
Within the 50% of liquid, after being configured to the aqueous solution, it is actual nontoxic type, with the construction feature of environmental protection.
4)Caused using oxidation-reduction system and solidified, hardening time is affected less by ambient temperature, water quality environment, gel
Time is easily controlled.
5)Viscosity is very low before curing for slurries, is first changed into rubbery state from liquid during solidification, completes to shrink, then switchs to solid
Body, therefore after pouring in crack, shrinkage factor very little.
6)The material solid content can be adjusted to more than 98% as needed, Gu sand body intensity is higher, reachable more than 1MPa, greatly
Amplitude improves the collapsoing strength of material, solves material strength problem, it is possible to achieve to stratum consolidation.
7)Gelling body elasticity is very good, and drawing stretches elongation up to more than 500%, is especially suitable for the elasticity change of deformation crack
Shape.
8)After grout curing, water-swellable rate reaches as high as 300% up to more than 30%, when 300 % is reached, still with one
Fixed elasticity and mechanical property, are that one kind has some strength and preferable elasticity, the big sealing material of water-swellable rate concurrently.
9)Slurries can directly be mixed with the inorganic grouting liquid such as cement mortar, bentonite slurry, cement clay slip, stir
It is latter to be in the milk together, the technical problem that chemical grout can not be blended grouting with inorganic particle injecting paste material is solved, is reduced
The cost of grouting material, simplifies grouting construction process flow process.
Specific embodiment
For the ease of understand the present invention, below in conjunction with specification preferred embodiment to the present invention make more comprehensively, it is careful
Ground description.
Embodiment 1
A kind of environmentally-friendly acrylic ester grouting material is made up of by quality proportioning following components:
Host:100 parts of methacrylic acid-beta-hydroxy ethyl ester;
Crosslinking agent:30 parts of polyethylene glycol diallyl ether;
Initiator:2 parts of ammonium persulfate;
Accelerator:1 part of triethanolamine;
Solvent:130 parts of water.
After methacrylic acid-beta-hydroxy ethyl ester, polyethylene glycol diallyl ether, triethanolamine are well mixed, first is formed
Liquid;Then second liquid is formed after being well mixed ammonium persulfate and water, and solution A, second liquid are mixed to form into environmental protection acrylic during use
Ester grouting slurries, final crosslinking curing.
In polyethylene glycol diallyl ether, the mean molecule quantity of polyethylene glycol is 160.
The physical property of slurries is as follows:
1)Slurries outward appearance:Colourless or light yellow clear homogeneous liquid;It is white solid after slurries final set;
2)Viscosity:7cP;
3)Density:1.03g/cm3;
3)Presetting period 13min, final setting time 16min.
The mechanical property of slurries is as follows:
1)The water-swellable rate 30% of pure colloid(7 days);
2)Tensile elongation is more than 350 %;
3)Gu sand body compression strength 0.6MPa;
4)Infiltration coefficient is less than 10-7cm/s。
Embodiment 2
A kind of environmentally-friendly acrylic ester grouting material is made up of by quality proportioning following components:
Host:100 parts of methacrylic acid-beta-hydroxy ethyl ester;
Crosslinking agent:10 parts of polyethylene glycol diallyl ether;
4 parts of ethoxylated bisphenol A dual-allyl ethers;
Initiator:3 parts of potassium peroxydisulfate;
Accelerator:0.5 part of sodium thiosulfate;
Auxiliary agent:15 parts of PAA
Auxiliary agent:0.02 part of the potassium ferricyanide
Solvent:25 parts of water.
Wherein, in polyethylene glycol diallyl ether, the mean molecule quantity of polyethylene glycol is 480, ethoxylated bisphenol A dienes third
Ji Mizhong ethoxyquins functional group number is 8.
By methacrylic acid-beta-hydroxy ethyl ester, polyethylene glycol diallyl ether, ethoxylated bisphenol A dual-allyl ethers, thio sulphur
After sour sodium, water, PAA, the potassium ferricyanide are well mixed, solution A is formed;Then will be potassium peroxydisulfate and the mixing of remaining water equal
Second liquid is formed after even, and solution A, second liquid are mixed to form into environmentally-friendly acrylic ester grouting slurries, final crosslinking curing during use.
The physical property of slurries is as follows:
1)Slurries outward appearance:Colourless or light yellow clear single-phase liquid;It is white solid after slurries final set;
2)Viscosity:12 cP;
3)Density:1.04 g/cm3;
3)34 min of presetting period, 47 min of final setting time.
The mechanical property of slurries is as follows:
1)230 % of water-swellable rate of pure colloid(7 days);
2)Tensile elongation is more than 30 %;
3)Gu 1.7 MPa of sand body compression strength;
4)Infiltration coefficient is less than 10-7 cm/s。
Embodiment 3
A kind of environmentally-friendly acrylic ester grouting material is made up of by quality proportioning following components:
Host:100 parts of methacrylic acid β hydroxyl ethyl esters;
Crosslinking agent:20 parts of polyethylene glycol diallyl ether;
4 parts of ethoxylated bisphenol A dual-allyl ethers;
Initiator:2 parts of potassium peroxydisulfate, ammonium persulfate;
Accelerator:0.9 part of sodium thiosulfate, sodium acid carbonate;
Solvent:200 parts of water.
In polyethylene glycol diallyl ether, the mean molecule quantity of polyethylene glycol is 1600, ethoxylated bisphenol A dual-allyl ethers
Middle ethoxyquin functional group number is 12.
By methacrylic acid-beta-hydroxy ethyl ester, polyethylene glycol diallyl ether, ethoxylated bisphenol A dual-allyl ethers, thio sulphur
After sour sodium, sodium acid carbonate, water are well mixed, solution A is formed;Then will be the mixing of potassium peroxydisulfate, ammonium persulfate and remaining water equal
Second liquid is formed after even.Solution A, second liquid are mixed to form into environmentally-friendly acrylic ester grouting material during use.
The ratio of mud for adding equal-volume ratio in environmentally-friendly acrylic ester grouting material is 1:1 cement grout, mixes
Organic-inorganic grouting material can be formed after uniform.
The physical property of slurries is as follows:24 min of presetting period, 33 min of final setting time.
The mechanical property of slurries is as follows:
1)2.5 MPa of organic-inorganic hybrid-type grouting material gel compression strength(28 days intensity);
2)Infiltration coefficient is less than 10-6 cm/s。
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not restricted to the described embodiments, the simply explanation described in above-described embodiment and specification this
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these changes
Change and improvement is both fallen within scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent thereof.