CN104164100A - 一种具有吸音效果的改性膨润土及其制备方法 - Google Patents
一种具有吸音效果的改性膨润土及其制备方法 Download PDFInfo
- Publication number
- CN104164100A CN104164100A CN201410335848.XA CN201410335848A CN104164100A CN 104164100 A CN104164100 A CN 104164100A CN 201410335848 A CN201410335848 A CN 201410335848A CN 104164100 A CN104164100 A CN 104164100A
- Authority
- CN
- China
- Prior art keywords
- parts
- sound
- stir
- powder
- absorbing effect
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种具有吸音效果的改性膨润土,其特征在于,由下列重量份的原料制备制成:膨润土90-95、耐火纤维棉2-4、丁苯乳液5-6、玉米芯碎片3-4、丙烯酸乳液4-6、硫基乙酸异辛酯3.5-4.5、纸浆废液4-5、矿渣棉2.5-4、聚酯纤维2-3、改性硅藻土3-4;本发明通过添加高分子聚合物进行改性,使得本发明具有良好的结合力,制成的材料韧性好,力学性能优异,通过加入耐火纤维棉、玉米芯碎片、矿渣棉、聚酯纤维等孔隙大,比表面积大的物质,增加了原料的吸音效果,本发明适合用于建筑用吸音棉、吸音板、吸附剂等。
Description
技术领域
本发明涉及工业填料领域,特别是一种具有吸音效果的改性膨润土及其制备方法。
背景技术
中国的膨润土矿资源非常丰富,储量居世界首位,占世界总量的60%,预测资源量在70亿吨以上,并以分布广、埋藏浅、易采掘及品种齐全为特点。膨润土及其提纯改型产品都不同程度地具有一些优越的特性,这些特性主要有膨胀性、亲水性(或亲油性,如有机膨润土)、吸附性、阳离子交换性、催化活性、分散性、悬浮性、粘接性、触变性、稳定性、无毒性。随着科学技术的发展,人们对膨润土结晶特性和物理化学性质的了解逐渐加深,膨润土在工农业生产和科学研究方面的使用日益广泛。它作为粘结剂、悬浮剂、增稠剂、触变剂、絮凝剂、稳定剂、净化脱色剂、充填剂、催化剂以及催化剂载体在冶金、机械铸造、钻探、石油化工、轻工、农林牧、建筑工程、环保等领域有着十分广泛的应用前景。
发明内容
本发明的目的是提供一种具有吸音效果的改性膨润土及其制备方法。
为了实现本发明的目的,本发明通过以下方案实施:
一种具有吸音效果的改性膨润土,由下列重量份的原料制备制成:膨润土90-95、耐火纤维棉2-4、丁苯乳液5-6、玉米芯碎片3-4、丙烯酸乳液4-6、硫基乙酸异辛酯3.5-4.5、纸浆废液4-5、矿渣棉2.5-4、聚酯纤维2-3、改性硅藻土3-4;
所述改性硅藻土由以下重量份的原料制成:硅藻土50-60、沸石分子筛4-7、锆英粉3-5、聚乙烯醇2-4、季戊四醇4-6、液体松香树脂4-7、丙烯酸乙酯5-7、乙酰柠檬酸三乙酯4-5、水50-60;制备方法是首先加入硅藻土、丙烯酸乙酯、聚乙烯醇、水搅拌均匀,形成悬浮液,然后立即加入季戊四醇、液体松香树脂、乙酰柠檬酸三乙酯混合搅拌25-35分钟,然后加入其余剩余成分,在1200-1500转/分条件下搅拌,在50-60℃下烘干,粉碎成200-400目粉末即得。
本发明所述一种具有吸音效果的改性膨润土,由以下具体步骤制成:
(1)将膨润土、耐火纤维棉、玉米芯碎片、矿渣棉、聚酯纤维混合均匀加入研磨机内,以1500-2000转/分钟 的速度研磨 15-20 分钟,取出烘干,粉碎研细,过 100-200目筛,得混合粉末待用;
(2)将丁苯乳液、丙烯酸乳液放入混料桶中,升温至80-90℃之间,搅拌半小时,继续加入硫基乙酸异辛酯、纸浆废液,继续升温至130-160℃,搅拌15-20分钟后倒出,烘干,得胶粉;
(3)将混合粉末与胶粉混合均匀,加入适量水,搅拌并研磨2-3小时,形成混悬液待用;
(4)将混悬液与改性硅藻土混合,800-1000转/分下搅拌10-15分钟,烘干、粉碎成200-400目粉末即得。
本发明的有益效果是:本发明通过添加高分子聚合物进行改性,使得本发明具有良好的结合力,制成的材料韧性好,力学性能优异,通过加入耐火纤维棉、玉米芯碎片、矿渣棉、聚酯纤维等孔隙大,比表面积大的物质,增加了原料的吸音效果,本发明适合用于建筑用吸音棉、吸音板、吸附剂等。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种具有吸音效果的改性膨润土,由下列重量份(公斤)的原料制备制成:膨润土90、耐火纤维棉2、丁苯乳液5、玉米芯碎片3、丙烯酸乳液4、硫基乙酸异辛酯3.5、纸浆废液4、矿渣棉2.5、聚酯纤维2、改性硅藻土3;
所述改性硅藻土由以下重量份(公斤)的原料制成:硅藻土50、沸石分子筛4、锆英粉3、聚乙烯醇2、季戊四醇4、液体松香树脂4、丙烯酸乙酯5、乙酰柠檬酸三乙酯4、水50;制备方法是首先加入硅藻土、丙烯酸乙酯、聚乙烯醇、水搅拌均匀,形成悬浮液,然后立即加入季戊四醇、液体松香树脂、乙酰柠檬酸三乙酯混合搅拌25-35分钟,然后加入其余剩余成分,在1200-1500转/分条件下搅拌,在50-60℃下烘干,粉碎成200-400目粉末即得。
本发明所述一种具有吸音效果的改性膨润土,由以下具体步骤制成:
(1)将膨润土、耐火纤维棉、玉米芯碎片、矿渣棉、聚酯纤维混合均匀加入研磨机内,以1500-2000转/分钟 的速度研磨 15-20 分钟,取出烘干,粉碎研细,过 100-200目筛,得混合粉末待用;
(2)将丁苯乳液、丙烯酸乳液放入混料桶中,升温至80-90℃之间,搅拌半小时,继续加入硫基乙酸异辛酯、纸浆废液,继续升温至130-160℃,搅拌15-20分钟后倒出,烘干,得胶粉;
(3)将混合粉末与胶粉混合均匀,加入适量水,搅拌并研磨2-3小时,形成混悬液待用;
(4)将混悬液与改性硅藻土等混合,800-1000转/分下搅拌10-15分钟,烘干、粉碎成200-400目粉末即得。
对本发明的改性膨润土和普通膨润土的性能检测比较如下 :
首先测量改性前、后膨润土的堆积密度,然后将改性好的膨润土和未改性的膨润土钙加入到橡胶制品中,制成样品,分别测试两者的力学性能,对比结果见下表 :
由上表可以看出,改性后的膨润土的松散堆积密度变小,说明膨润土分体充分分散,还可以看出改性后膨润土的各项力学性能都得到提高。
Claims (2)
1.一种具有吸音效果的改性膨润土,其特征在于,由下列重量份的原料制备制成:膨润土90-95、耐火纤维棉2-4、丁苯乳液5-6、玉米芯碎片3-4、丙烯酸乳液4-6、硫基乙酸异辛酯3.5-4.5、纸浆废液4-5、矿渣棉2.5-4、聚酯纤维2-3、改性硅藻土3-4;
所述改性硅藻土由以下重量份的原料制成:硅藻土50-60、沸石分子筛4-7、锆英粉3-5、聚乙烯醇2-4、季戊四醇4-6、液体松香树脂4-7、丙烯酸乙酯5-7、乙酰柠檬酸三乙酯4-5、水50-60;制备方法是首先加入硅藻土、丙烯酸乙酯、聚乙烯醇、水搅拌均匀,形成悬浮液,然后立即加入季戊四醇、液体松香树脂、乙酰柠檬酸三乙酯混合搅拌25-35分钟,然后加入其余剩余成分,在1200-1500转/分条件下搅拌,在50-60℃下烘干,粉碎成200-400目粉末即得。
2.根据权利要求1所述一种具有吸音效果的改性膨润土,其特征在于,由以下具体步骤制成:
(1)将膨润土、耐火纤维棉、玉米芯碎片、矿渣棉、聚酯纤维混合均匀加入研磨机内,以1500-2000转/分钟 的速度研磨 15-20 分钟,取出烘干,粉碎研细,过 100-200目筛,得混合粉末待用;
(2)将丁苯乳液、丙烯酸乳液放入混料桶中,升温至80-90℃之间,搅拌半小时,继续加入硫基乙酸异辛酯、纸浆废液,继续升温至130-160℃,搅拌15-20分钟后倒出,烘干,得胶粉;
(3)将混合粉末与胶粉混合均匀,加入适量水,搅拌并研磨2-3小时,形成混悬液待用;
(4)将混悬液与改性硅藻土混合,800-1000转/分下搅拌10-15分钟,烘干、粉碎成200-400目粉末即得。