CN104157861A - Mesoporous carbon material, elemental sulfur and preparation method for mesoporous carbon composite material - Google Patents
Mesoporous carbon material, elemental sulfur and preparation method for mesoporous carbon composite material Download PDFInfo
- Publication number
- CN104157861A CN104157861A CN201310177637.3A CN201310177637A CN104157861A CN 104157861 A CN104157861 A CN 104157861A CN 201310177637 A CN201310177637 A CN 201310177637A CN 104157861 A CN104157861 A CN 104157861A
- Authority
- CN
- China
- Prior art keywords
- carbon
- mixed
- mesoporous carbon
- preparation
- matrix precursor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Provided is a preparation method for a mesoporous carbon material. The preparation method comprises the following steps: pore forming agents and carbon precursors are mixed uniformly and a mixture is obtained, the mixture is processed for 2-3h at the temperature of 120-160 DEG C, and mesoporous carbon precursors are obtained, and the mass ratio of the pore forming agents to the carbon precursors is 4:6-6:4; the mesoporous carbon precursors are subjected to heat treatment at the temperature of 600-900 DEG C and under protection gases, and the mesoporous carbon material is obtained after separation and purification. In the preparation method, a hard template method is employed for preparation of the mesoporous carbon material, the operation is simple, good pore size distribution is achieved, and the mesoporous carbon material facilitates high dispersion of sulfur. In addition, the strong adsorptivity of the material can inhibit dissolution and loss of polysulfides effectively, and the mesoporous carbon material is helpful to raise the utilization rate of active sulfur.
Description
Technical field
The present invention relates to electrode material field, particularly relate to the preparation method of a kind of meso-porous carbon material, elemental sulfur and mesoporous carbon composite material.
Background technology
Along with human society the constant growth of productivity, people sharply increase the demand of the energy in daily production and life.For the day by day serious global energy shortage of reply, traditional primary cell is substituted by reusable secondary cell gradually.Meanwhile, the fast development of the aspects such as current communication, portable electric appts, electric automobile and space technology, the performance of battery has been proposed to more and more higher requirement, traditional secondary cell is because capacity is low, and poor safety performance and volume heaviness are unfavorable for carrying and are replaced by novel lithium secondary battery gradually.Development has high-energy-density, low cost and eco-friendly Novel lithium secondary cell and has very important significance.
The close height of energy, self discharge are little owing to having for lithium ion battery, memory-less effect, operating temperature range are wide, have extended cycle life and the advantage such as environmentally friendly, it is the best new green environment protection high-energy secondary battery of current combination property, it is one of optimal electrical source of power, be widely used in national defence, space flight, the every aspect in production and daily life.In lithium rechargeable battery system, positive electrode is the important component part in lithium battery system, and positive electrode is the bottleneck of restriction battery development always, and its price, specific capacity and cycle performance all need to be optimized.Therefore,, since lithium battery comes out, the scientists of various countries does not always stop exploring and improving the step of anode material of lithium battery.The research and development of positive electrode and improvement are the links of the developing core of lithium battery.Traditional transition metal oxide base anode material is as LiCoO
2, LiNiO
2and LiMn
2o
4deng containing lithium metal compounds, but the equal capacity of these materials is lower and can cause certain pollution to environment.Therefore, new high-energy-density, long circulation life, the exploitation of energy storage material are cheaply particularly important.
In new energy storage system, taking lithium metal as negative pole elemental sulfur as the theoretical specific energy of anodal lithium-sulfur cell can reach 2600Wh/kg (theoretical specific capacity of lithium and sulphur is respectively 3860mAh/g and 1675mAh/g), the commercialization secondary cell using much larger than present stage. meet the requirement of electric automobile to battery, also meet the requirement of portable type electronic product to battery " light, thin, little "; And sulphur has the features such as wide material sources (cost is low), nontoxic (pollution-free).The advantages such as therefore, sulfur-bearing composite positive pole is with its high power capacity, low cost, and hypotoxicity, cycle performance are better, become and have one of positive electrode of development prospect most at present, and being has exploitation to be worth and the secondary power anode material of lithium battery of application prospect.But its weak point is, lithium anode and sulfenyl positive electrode all exist cycle performance poor, have restricted the development of lithium-sulfur rechargeable battery, and this is also the emphasis of current lithium-sulfur rechargeable battery research.For sulfenyl positive pole, the key issue of existence is as follows: (1) elemental sulfur is at room temperature electronics and ion insulator, while making electrode, need add a large amount of conductive agent (as acetylene black), causes the energy density of electrode system to reduce; (2) elemental sulfur can be reduced into the polysulfide of Yi Rong in discharge process, cause active material to run off, and polysulfide is dissolved in after electrolyte, can increase concentration of electrolyte, worsens its ionic conductivity; (3) be dissolved in the direct contacting metal cathode of lithium of polysulfide of electrolyte, self discharge reaction occurs; (4) in charge and discharge process can there is corresponding pucker & bloat in sulfur electrode, destroys to a certain extent the physical structure of electrode.These problems have all restricted the chemical property of sulfenyl positive pole, cause that sulphur active material utilization is low, electrochemical reversibility is poor and capacity attenuation fast etc.Therefore, improve sulphur positive electrode conductivity, reduce or the solvent solubility that overcomes active sulfur is the key of dealing with problems.Preparing a kind of elemental sulfur and mesoporous carbon composite material is one of way addressing these problems.
Summary of the invention
Based on this, provide the preparation method of a kind of meso-porous carbon material, elemental sulfur and mesoporous carbon composite material.
A preparation method for meso-porous carbon material, comprises the following steps:
After pore creating material and carbon matrix precursor are mixed, obtain mixture, described mixture is processed to 2～3h at 120～160 DEG C, obtain mesoporous carbon presoma, wherein, the mass ratio of described pore creating material and described carbon matrix precursor is 4:6～6:4;
Under temperature is 600～900 DEG C, protective gas atmosphere, by described mesoporous carbon presoma heat treatment 2～3h, after separation and purification, obtain described meso-porous carbon material.
Therein in an embodiment, describedly after being mixed, pore creating material and carbon matrix precursor obtain being operating as of mixture:
Described pore creating material is dissolved in and in the first solvent, is mixed with pore creating material solution, described carbon matrix precursor is dissolved in and in the second solvent, is mixed with carbon matrix precursor solution, after described pore creating material solution and described carbon matrix precursor solution are mixed, obtain mixed liquor, obtain described mixture after described mixed liquor is dry.
In an embodiment, described pore creating material is nano-calcium carbonate, nano aluminium oxide or mesoporous silicon oxide therein.
In an embodiment, described carbon matrix precursor is sucrose, glucose or furfuryl alcohol therein.
In an embodiment, described protective gas is nitrogen or argon gas therein.
A preparation method for elemental sulfur and mesoporous carbon composite material, comprises the following steps:
After pore creating material and carbon matrix precursor are mixed, obtain mixture, described mixture is processed to 2～3h at 120～160 DEG C, obtain mesoporous carbon presoma, wherein, the mass ratio of described pore creating material and described carbon matrix precursor is 4:6～6:4;
Under temperature is 600～900 DEG C, protective gas atmosphere, by described mesoporous carbon presoma heat treatment 2～3h, after purifying, obtain described meso-porous carbon material;
Sodium thiosulfate, described meso-porous carbon material and surfactant are mixed with to mixed solution, wherein, the concentration of described sodium thiosulfate is 0.3～0.6mol/L, and the concentration of described meso-porous carbon material is 1～3g/L, and the concentration of described surfactant is 4～8mmol/L;
To described mixed solution and dripping acid solution, filter after completely until precipitation and retain filter residue, described residue washing, be dried after, be described elemental sulfur and mesoporous carbon composite material.
Therein in an embodiment, describedly after being mixed, pore creating material and carbon matrix precursor obtain being operating as of mixture:
Described pore creating material is dissolved in and in the first solvent, is mixed with pore creating material solution, described carbon matrix precursor is dissolved in and in the second solvent, is mixed with carbon matrix precursor solution, after described pore creating material solution and described carbon matrix precursor solution are mixed, obtain mixed liquor, obtain described mixture after described mixed liquor is dry.
In an embodiment, described pore creating material is nano-calcium carbonate, nano aluminium oxide or mesoporous silicon oxide therein;
Described carbon matrix precursor is sucrose, glucose or furfuryl alcohol;
Described protective gas is nitrogen or argon gas.
In an embodiment, described surfactant is softex kw, sodium cetanesulfonate or neopelex therein;
The concentration of described acid solution is 1～3mol/L, and the solute of described acid solution is formic acid, acetic acid or hydrochloric acid.
In an embodiment, be also included in and obtain after described elemental sulfur and mesoporous carbon composite material therein, under 150～160 DEG C and atmosphere of inert gases, by the operation of described elemental sulfur and mesoporous carbon composite material heat treatment 10～15h.
The preparation method of above-mentioned mesoporous carbon adopts hard template method to prepare meso-porous carbon material, simple to operate, and has good pore-size distribution, is conducive to the high degree of dispersion of sulphur; Meanwhile, the strong absorption property of the meso-porous carbon material making can effectively suppress dissolving and the loss of polysulfide, is conducive to improve the utilance of active sulfur.
Brief description of the drawings
Fig. 1 is the mesoporous carbon preparation method's of an execution mode flow chart;
Fig. 2 is the elemental sulfur of an execution mode and mesoporous carbon composite material preparation method's flow chart;
Fig. 3 is the elemental sulfur that makes of the mesoporous carbon that makes of embodiment 3 and embodiment 4 and scanning electron microscope (SEM) photograph and the TEM (transmission electron microscope) analysis figure of mesoporous carbon composite material, Fig. 3 (a) and Fig. 3 (b) are respectively SEM figure and the TEM figure of the mesoporous carbon that embodiment 3 makes, and the SEM that Fig. 3 (c) and Fig. 3 (d) are respectively elemental sulfur that embodiment 4 makes and mesoporous carbon composite wood schemes and TEM schemes;
Fig. 4 is the N of the mesoporous carbon that makes of embodiment 3
2adsorption and desorption isotherms, illustration is mesoporous carbon pore size distribution curve;
Fig. 5 is the thermogravimetric analysis curve of embodiment 4 elemental sulfur, elemental sulfur and the mesoporous carbon composite material that make;
Figure 6 shows that the XRD figure of elemental sulfur, mesoporous carbon, elemental sulfur and the mesoporous carbon composite material of the embodiment of the present invention 2;
Fig. 7 is that elemental sulfur and the mesoporous carbon composite material that embodiment 4 makes forms anodal cyclic voltammetry curve;
Fig. 8 is that elemental sulfur and the mesoporous carbon composite material that embodiment 4 makes forms anodal charging and discharging curve;
Fig. 9 is that elemental sulfur and the mesoporous carbon composite material that embodiment 4 makes forms anodal cycle life figure;
Figure 10 is that elemental sulfur and the mesoporous carbon composite material that embodiment 4 makes forms anodal high rate performance figure.
Embodiment
For above-mentioned purpose of the present invention, feature and advantage can be become apparent more, below in conjunction with accompanying drawing, the specific embodiment of the present invention is described in detail.A lot of details are set forth in the following description so that fully understand the present invention.But the present invention can implement to be much different from alternate manner described here, and those skilled in the art can do similar improvement without prejudice to intension of the present invention in the situation that, and therefore the present invention is not subject to the restriction of following public concrete enforcement.
Refer to Fig. 1, the preparation method of the meso-porous carbon material of an execution mode, comprises the following steps:
Step S101: obtain mixture after pore creating material and carbon matrix precursor are mixed, mixture is processed to 2～3h at 120～160 DEG C, obtain mesoporous carbon presoma, wherein, the mass ratio of pore creating material and carbon matrix precursor is 4:6～6:4.
After being mixed, pore creating material and carbon matrix precursor obtain being operating as of mixture: pore creating material is dissolved in and in the first solvent, is mixed with pore creating material solution, carbon matrix precursor is dissolved in and in the second solvent, is mixed with carbon matrix precursor solution, after being mixed, pore creating material solution and carbon matrix precursor solution obtains mixed liquor, after mixed liquor is dry, remove unnecessary moisture, obtain mixture.For example by mixed liquor under magnetic agitation in 80 DEG C of heating evaporation 6h, remove unnecessary moisture.The first solvent is preferably ethanol, methyl alcohol or other alcohols, and the second solvent is preferably deionized water.
Pore creating material is mixed with to pore creating material solution, and carbon matrix precursor mixes after being mixed with carbon matrix precursor solution, and carbon matrix precursor and pore creating material particle are more fine and closely woven, mixes more evenly, and after pore-forming, distribution of pores is more even, and aperture is less.
The mass ratio of pore creating material and carbon matrix precursor is 4:6～6:4.Pore creating material is preferably calcium carbonate, nano aluminium oxide, mesoporous silicon oxide.Carbon matrix precursor is preferably sucrose, glucose, furfuryl alcohol.
By mixture dry 2h at 160 DEG C, mixture is carried out to pre-carbonization.
Step S102: under temperature is 600～900 DEG C, protective gas atmosphere, by mesoporous carbon presoma heat treatment 2～3h, obtain meso-porous carbon material after separation and purification.
Mesoporous carbon presoma heat treatment mode is the earthenware of mesoporous carbon presoma being put into tube furnace, 800 DEG C of carbonization 2h.Protective gas is preferably nitrogen, argon gas.
Mesoporous carbon presoma washing after purification process can adopt watery hydrochloric acid, dilute sulfuric acid or other acids to heat treatment.
The preparation method of above-mentioned meso-porous carbon material adopts hard template method to prepare meso-porous carbon material, simple to operate, and has good pore-size distribution, is conducive to the high degree of dispersion of sulphur; Meanwhile, the strong absorption property of this material can effectively suppress dissolving and the loss of polysulfide, is conducive to improve the utilance of active sulfur.
Elemental sulfur as shown in Figure 2 and the preparation method of mesoporous carbon composite material, comprise the following steps:
Step S201: obtain mixture after pore creating material and carbon matrix precursor are mixed, mixture is processed to 2～3h at 120～160 DEG C, obtain mesoporous carbon presoma, wherein, the mass ratio of pore creating material and carbon matrix precursor is respectively 4:6～6:4.
After being mixed, pore creating material and carbon matrix precursor obtain being operating as of mixture: pore creating material is dissolved in and in the first solvent, is mixed with pore creating material solution, carbon matrix precursor is dissolved in and in the second solvent, is mixed with carbon matrix precursor solution, after being mixed, pore creating material solution and carbon matrix precursor solution obtains mixed liquor, after mixed liquor is dry, remove unnecessary moisture, obtain mixture.For example by mixed liquor under magnetic agitation in 80 DEG C of heating evaporation 6h, remove unnecessary moisture.The first solvent is preferably ethanol, methyl alcohol or other alcohols, and the second solvent is preferably deionized water.
Pore creating material is mixed with to pore creating material solution, and carbon matrix precursor mixes after being mixed with carbon matrix precursor solution, and carbon matrix precursor and pore creating material particle are more fine and closely woven, mixes more evenly, and after pore-forming, distribution of pores is more even, and aperture is less.
The mass ratio of pore creating material and carbon matrix precursor is 4:6～6:4.Pore creating material is preferably calcium carbonate, nano aluminium oxide, mesoporous silicon oxide.Carbon matrix precursor is preferably sucrose, glucose, furfuryl alcohol.
By mixture dry 2h at 160 DEG C, mixture is carried out to pre-carbonization.
Step S202: under temperature is 600～900 DEG C, protective gas atmosphere, by mesoporous carbon presoma heat treatment 2～3h, obtain meso-porous carbon material after purifying.
Mesoporous carbon presoma heat treatment mode is the earthenware of mesoporous carbon presoma being put into tube furnace, 800 DEG C of carbonization 2h.Protective gas is preferably nitrogen, argon gas.
Mesoporous carbon presoma washing after purification process can adopt watery hydrochloric acid, dilute sulfuric acid or other acids to heat treatment.
Step S203: sodium thiosulfate, meso-porous carbon material and surfactant are mixed with to mixed solution, and wherein, the concentration of sodium thiosulfate is 0.3～0.6mol/L, and the concentration of meso-porous carbon material is 1～3g/L, and the concentration of surfactant is 4～8mmol/L.
Sodium thiosulfate, meso-porous carbon material and surfactant are dissolved in deionized water, and ultrasonic agitation obtains mixed solution.The concentration of sodium thiosulfate is 0.3～0.6mol/L, and the concentration of meso-porous carbon material is 1～3g/L, and the concentration of surfactant is 4～8mmol/L.Surfactant is preferably the one of softex kw (CTAB), sodium cetanesulfonate (SDS), neopelex (SDBS).
Step S204: to mixed solution and dripping acid solution, filter after completely until precipitation and retain filter residue, residue washing, be dried after, be elemental sulfur and mesoporous carbon composite material.
The mode that adds of acid solution is preferably dropping, drips speed control built in 30～40/min.The concentration of acid solution is preferably 1～3mol/L, and the solute of acid solution is preferably formic acid, acetic acid or hydrochloric acid.
The washing of filter residue can respectively be washed 3 times with acetone and deionized water.The dry of filter residue can be dried 72 hours at 50 DEG C.
Obtaining after elemental sulfur and mesoporous carbon composite material, can also be included under 150～160 DEG C and atmosphere of inert gases, by the operation of elemental sulfur and mesoporous carbon composite material heat treatment 10～15h, this operation is immersed in the loose structure of meso-porous carbon material sulphur simple substance more uniformly.
Above-mentioned elemental sulfur and the preparation method of mesoporous carbon composite material, adopt chemical codeposition legal system for elemental sulfur and mesoporous carbon composite material, and technique is simple, not harsh to operation and environmental requirement, for technology is provided by the simple and easy to do condition that provides.Because mesoporous carbon is a kind of high conductivity high-ratio surface active carbon material, not only there is good conductivity but also can keep the stability of electrode material structure; Therefore the good stability taking elemental sulfur and mesoporous carbon composite material as the lithium ion cell electrode interface of anodal preparation.Make electrode slice have splendid crosslinked network structure adding of meso-porous carbon material, for the migration of lithium ion provides a passage easily, the ionic conductivity of sulfur electrode improves greatly simultaneously, thereby the cycle performance of lithium-sulfur cell also obtains larger raising.
Describe below in conjunction with specific embodiment.
Embodiment 1
The preparation of meso-porous carbon material
What the present embodiment adopted is that hard template method is prepared meso-porous carbon material, and nano-calcium carbonate used is nano-calcium carbonate (specialty minerals company of the U.S.).Specifically comprise the following steps:
By nano-calcium carbonate and carbon precursor sucrose in mass ratio 4:6 mix, specifically 8g nano-calcium carbonate is dissolved in and is distributed in 20ml ethanol, then mix with 0.2L 0.175mol/L sucrose solution.Mixed liquor under magnetic agitation in 80 DEG C of heating evaporation 6h to remove the moisture of the inside, then dryly at 160 DEG C carry out the pre-carbonization of 2h.
Finally in tube furnace under blanket of nitrogen in 800 DEG C of carbonization 2h.High temperature cabonization product is placed in to watery hydrochloric acid and removes nano-calcium carbonate, after being dried, obtain 3g meso-porous carbon material, productive rate is about 25%.
Embodiment 2
The preparation of meso-porous carbon material
What the present embodiment adopted is that hard template method is prepared meso-porous carbon material, and nano aluminium oxide used is nano aluminium oxide (specialty minerals company of the U.S.).Specifically comprise the following steps:
By nano aluminium oxide and carbon precursor glucose in mass ratio 6:4 mix, specifically 12g nano aluminium oxide is dissolved in and is distributed in 20ml ethanol, then mix with 0.2L 0.12mol/L glucose solution.Mixed liquor under magnetic agitation in 80 DEG C of heating evaporation 6h to remove the moisture of the inside, then dryly at 120 DEG C carry out the pre-carbonization of 2.5h.
Finally in tube furnace under blanket of nitrogen in 600 DEG C of carbonization 2.5h.High temperature cabonization product is placed in to watery hydrochloric acid and removes nano aluminium oxide, after being dried, obtain 2g meso-porous carbon material, productive rate is about 25%.
Embodiment 3
The preparation of meso-porous carbon material
What the present embodiment adopted is that hard template method is prepared meso-porous carbon material, and mesoporous silicon oxide used is mesoporous silicon oxide (specialty minerals company of the U.S.).Specifically comprise the following steps:
By mesoporous silicon oxide and carbon precursor furfuryl alcohol in mass ratio 1:1 mix, specifically 10g meso-porous titanium dioxide silico-calcium is dissolved in and is distributed in 20mL ethanol, then mix with 0.2L 0.15mol/L furfuryl alcohol solution.Mixed liquor under magnetic agitation in 80 DEG C of heating evaporation 6h to remove the moisture of the inside, then dryly at 150 DEG C carry out the pre-carbonization of 3h.
Finally in tube furnace under blanket of nitrogen in 900 DEG C of carbonization 3h.High temperature cabonization product is placed in to watery hydrochloric acid and removes mesoporous silicon oxide, after being dried, obtain 2.5g meso-porous carbon material, productive rate is about 25%.
Embodiment 4
The preparation of elemental sulfur and mesoporous carbon composite material.
The elemental sulfur of the present embodiment and the preparation of mesoporous carbon composite material comprise the following steps:
25.12g sodium thiosulfate is dissolved in 150ml deionized water, makes hypo solution.The meso-porous carbon material that hypo solution and 0.5g embodiment 3 are made joins in the solution of 0.1L 10mmol/L softex kw (CTAB) simultaneously, and ultrasonic agitation 2h obtains mixed solution;
Preparation 100mL concentration is 2mol/L formic acid solution; Under agitation, formic acid solution is splashed in mixed solution, speed is controlled at 30～40/min, dropwises rear continuation and stirs 2h.By solution filter, get precipitation, respectively wash 3 times with acetone and deionized water, at 50 DEG C dry 72 hours, finally obtain 1.25g elemental sulfur/mesoporous carbon composite material, productive rate is 35.7%.By the heat treatment 12 hours at 155 DEG C in argon gas of elemental sulfur and mesoporous carbon composite material, so that sulphur is immersed in the loose structure of mesoporous carbon more uniformly.
Embodiment 5
The preparation of elemental sulfur and mesoporous carbon composite material
The elemental sulfur of the present embodiment and the preparation of mesoporous carbon composite material comprise the following steps:
18.62g sodium thiosulfate is dissolved in 150ml deionized water, makes hypo solution.The meso-porous carbon material that hypo solution and 0.25g embodiment 3 are made joins in the solution of 0.1L 15mmol/L sodium cetanesulfonate (SDS) simultaneously, and ultrasonic agitation 2h obtains mixed solution.
Preparation 100mL concentration is 2mol/L acetic acid solution; Under agitation, acetic acid solution is splashed in mixed solution, speed is controlled at 30～40/min, dropwises rear continuation and stirs 2h.By solution filter, get precipitation, respectively wash 3 times with acetone and deionized water, at 50 DEG C dry 72 hours, finally obtain 1g elemental sulfur/mesoporous carbon composite material, productive rate is 33.3%.By the heat treatment 10 hours at 155 DEG C in argon gas of elemental sulfur and mesoporous carbon composite material, so that sulphur is immersed in the loose structure of mesoporous carbon more uniformly.
The preparation of embodiment 6 elemental sulfurs and mesoporous carbon composite material
The elemental sulfur of the present embodiment and the preparation of mesoporous carbon composite material comprise the following steps:
37.24g sodium thiosulfate is dissolved in 150ml deionized water, make hypo solution. the meso-porous carbon material that hypo solution and 0.5g embodiment 3 are made joins in the solution of 0.1L20mmol/L neopelex (SDBS) simultaneously, and ultrasonic agitation 2h obtains mixed solution.
Preparation 100mL concentration is 2mol/L hydrochloric acid solution; Under agitation, hydrochloric acid solution is splashed in mixed solution, speed is controlled at 30～40/min, dropwises rear continuation and stirs 2h.By solution filter, get precipitation, respectively wash 3 times with acetone and deionized water, at 50 DEG C dry 72 hours, finally obtain 1.6g elemental sulfur/mesoporous carbon composite material, productive rate is 37%.By the heat treatment 15 hours at 150 DEG C in argon gas of elemental sulfur and mesoporous carbon composite material, so that sulphur is immersed in the loose structure of mesoporous carbon more uniformly.
Embodiment 7
Characterize and performance test experiment.
eSEM and TEM (transmission electron microscope) analysis
The mesoporous carbon respectively embodiment 3 and embodiment 4 being made and elemental sulfur and mesoporous carbon composite material carry out ESEM and TEM (transmission electron microscope) analysis, and the SEM figure and the TEM that obtain scheme, as shown in Figure 3.
As shown in Figure 3, gained meso-porous carbon material has tremelloid loose structure, and sulphur is evenly distributed in its meso-hole structure.
the sign of specific surface area and pore structure
The meso-porous carbon material that embodiment 3 is made carries out the sign of specific area and pore structure, and the nitrogen adsorption desorption curve of the meso-porous carbon material obtaining and graph of pore diameter distribution are as shown in Figure 4.
As shown in Figure 4, the meso-porous carbon material that embodiment 3 makes has larger specific area and more uniform meso-hole structure, and hole is mainly distributed in 3.6 and about 40nm, and the carrier that is suitable as nano-sulfur is prepared elemental sulfur and mesoporous carbon composite material.Deposition and electrolyte that the loose structure of mesoporous carbon is conducive to nano-sulfur infiltrate in meso-hole structure, and can suppress lithium sulfide and be dissolved in electrolyte.
thermogravimetric analysis
Elemental sulfur, elemental sulfur and mesoporous carbon composite material that embodiment 4 is made carry out thermogravimetric analysis, and the thermogravimetric curve obtaining as shown in Figure 5.
As shown in Figure 5, elemental sulfur is volatilization completely between 150-280 DEG C, and the percentage composition that can determine thus elemental sulfur and the mesoporous carbon composite material sulphur before heat treatment is 59.7%.
xRD analysis
Elemental sulfur, mesoporous carbon, sulphur/mesoporous carbon composite positive pole that embodiment 4 is made carry out XRD analysis, and the XRD spectra obtaining as shown in Figure 6
As shown in Figure 6, spectral line a explanation elemental sulfur is the good crystal of crystallinity, and spectral line c is at 24 ° and the 45 ° characteristic diffraction peaks of locating to occur indefinite form carbon.Spectral line b is similar to the peak type of spectral line a, but intensity weakens to some extent, illustrate elemental sulfur uniform deposition in the hole of meso-porous carbon material.
cyclic voltammetric and charge-discharge test
Embodiment 4 gained elemental sulfurs and mesoporous carbon composite material composition positive pole are carried out to cyclic voltammetric and charge-discharge test, and the cyclic voltammetry curve obtaining and charging and discharging curve are as shown in Figure 7 and Figure 8.
As shown in Figure 7, the redox reaction of elemental sulfur in electrolyte is that polyelectron transmits consecutive steps, so oxidation peak and the reduction peak of different potentials value appear in its cyclic voltammetry curve.Having there are 2 obvious reduction peak at voltage 2.25V and 2.05V place respectively in first Zhou Fang electricity, corresponds respectively to S
8to many sulphions Li
2s
xconversion and many sulphions to Li
2s
2, Li
2the further reduction of S.When reverse scan, cyclic voltammetry curve occurs that one by two oxidation peak that oxidation peak is overlapping, and spike potential is in 2.4V left and right, and peak shape is narrow.As shown in Figure 8, discharge curve shows two stable discharge platforms first, corresponds respectively to S
8to many sulphions Li
2s
xconversion and many sulphions to Li
2the further reduction process of S, result and Fig. 7 cyclic voltammetric result match.Taking elemental sulfur and mesoporous carbon composite material as anodal lithium battery first discharge capacity up to 1380mAh/g, there is reasonable discharge capacity first.More than illustrate that mesoporous carbon has good conductive structure, make nano-sulfur there is good dispersiveness, and there is the polysulfide that stronger adsorption capacity can effectively suppress to produce in charge and discharge process and dissolve in electrolyte.
charge and discharge cycles test
The elemental sulfur that embodiment 4 is made and mesoporous carbon composite material composition positive pole carry out charge and discharge cycles test, and the cyclic curve obtaining as shown in Figure 9.
As shown in Figure 9, battery under 0.1C first discharge capacity be 1013mAh/g, more than the capacity after 100 weeks still remains 758mAh/g, and coulombic efficiency remains on 96% left and right.This explanation has good cyclical stability taking elemental sulfur and mesoporous carbon composite material as anodal lithium battery.Mesoporous carbon not only can provide effective conductive channel for sulfur electrode, and can cushion the change in volume causing in sulfur electrode charge and discharge process, in addition the loose structure in mesoporous carbon can effectively suppress the dissolving in electrolyte of the polysulfide that produces in charge and discharge process, and therefore battery capacity conservation rate is greatly improved.
high rate performance test
Embodiment 4 gained elemental sulfurs and mesoporous carbon composite material composition positive pole are carried out to the test of high rate performance, and the high rate performance curve obtaining as shown in figure 10.
As shown in Figure 10, battery capacity under 0.02C is 1380mAh/g, and under different multiplying, after 20 circulations, under 0.5C, discharge capacity still reaches 630mAh/g, the conductivity of the raising sulfur electrode that this explanation meso-porous carbon material can be larger.
The above embodiment has only expressed several execution mode of the present invention, and it describes comparatively concrete and detailed, but can not therefore be interpreted as the restriction to the scope of the claims of the present invention.It should be pointed out that for the person of ordinary skill of the art, without departing from the inventive concept of the premise, can also make some distortion and improvement, these all belong to protection scope of the present invention.Therefore, the protection range of patent of the present invention should be as the criterion with claims.
Claims (10)
1. a preparation method for meso-porous carbon material, is characterized in that, comprises the following steps:
After pore creating material and carbon matrix precursor are mixed, obtain mixture, described mixture is processed to 2～3h at 120～160 DEG C, obtain mesoporous carbon presoma, wherein, the mass ratio of described pore creating material and described carbon matrix precursor is 4:6～6:4;
Under temperature is 600～900 DEG C, protective gas atmosphere, by described mesoporous carbon presoma heat treatment 2～3h, after separation and purification, obtain described meso-porous carbon material.
2. the preparation method of meso-porous carbon material as claimed in claim 1, is characterized in that, describedly obtains being operating as of mixture after pore creating material and carbon matrix precursor are mixed:
Described pore creating material is dissolved in and in the first solvent, is mixed with pore creating material solution, described carbon matrix precursor is dissolved in and in the second solvent, is mixed with carbon matrix precursor solution, after described pore creating material solution and described carbon matrix precursor solution are mixed, obtain mixed liquor, obtain described mixture after described mixed liquor is dry.
3. the preparation method of meso-porous carbon material as claimed in claim 1, is characterized in that, described pore creating material is nano-calcium carbonate, nano aluminium oxide or mesoporous silicon oxide.
4. the preparation method of meso-porous carbon material as claimed in claim 1, is characterized in that, described carbon matrix precursor is sucrose, glucose or furfuryl alcohol.
5. the preparation method of meso-porous carbon material as claimed in claim 1, is characterized in that, described protective gas is nitrogen or argon gas.
6. a preparation method for elemental sulfur and mesoporous carbon composite material, is characterized in that, comprises the following steps:
After pore creating material and carbon matrix precursor are mixed, obtain mixture, described mixture is processed to 2～3h at 120～160 DEG C, obtain mesoporous carbon presoma, wherein, the mass ratio of described pore creating material and described carbon matrix precursor is 4:6～6:4;
Under temperature is 600～900 DEG C, protective gas atmosphere, by described mesoporous carbon presoma heat treatment 2～3h, after purifying, obtain described meso-porous carbon material;
Sodium thiosulfate, described meso-porous carbon material and surfactant are mixed with to mixed solution, wherein, the concentration of described sodium thiosulfate is 0.3～0.6mol/L, and the concentration of described meso-porous carbon material is 1～3g/L, and the concentration of described surfactant is 4～8mmol/L;
To described mixed solution and dripping acid solution, filter after completely until precipitation and retain filter residue, described residue washing, be dried after, be described elemental sulfur and mesoporous carbon composite material.
7. the preparation method of elemental sulfur as claimed in claim 6 and mesoporous carbon composite material, is characterized in that, describedly obtains being operating as of mixture after pore creating material and carbon matrix precursor are mixed:
Described pore creating material is dissolved in and in the first solvent, is mixed with pore creating material solution, described carbon matrix precursor is dissolved in and in the second solvent, is mixed with carbon matrix precursor solution, after described pore creating material solution and described carbon matrix precursor solution are mixed, obtain mixed liquor, obtain described mixture after described mixed liquor is dry.
8. the preparation method of elemental sulfur as claimed in claim 6 and mesoporous carbon composite material, is characterized in that, described pore creating material is nano-calcium carbonate, nano aluminium oxide or mesoporous silicon oxide;
Described carbon matrix precursor is sucrose, glucose or furfuryl alcohol;
Described protective gas is nitrogen or argon gas.
9. the preparation method of elemental sulfur as claimed in claim 6 and mesoporous carbon composite material, is characterized in that, described surfactant is softex kw, sodium cetanesulfonate or neopelex;
The concentration of described acid solution is 1～3mol/L, and the solute of described acid solution is formic acid, acetic acid or hydrochloric acid.
10. the preparation method of elemental sulfur as claimed in claim 6 and mesoporous carbon composite material, it is characterized in that, also be included in and obtain after described elemental sulfur and mesoporous carbon composite material, under 150～160 DEG C and atmosphere of inert gases, by the operation of described elemental sulfur and mesoporous carbon composite material heat treatment 10～15h.