CN104140647B - 一种导电pbt材料 - Google Patents

一种导电pbt材料 Download PDF

Info

Publication number
CN104140647B
CN104140647B CN201410340793.1A CN201410340793A CN104140647B CN 104140647 B CN104140647 B CN 104140647B CN 201410340793 A CN201410340793 A CN 201410340793A CN 104140647 B CN104140647 B CN 104140647B
Authority
CN
China
Prior art keywords
raw material
mixed
pbt
add
oil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410340793.1A
Other languages
English (en)
Other versions
CN104140647A (zh
Inventor
孟勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan City Winter Yu new materials Limited by Share Ltd
Original Assignee
CHUZHOU YOUSHENG HIGH POLYMER MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHUZHOU YOUSHENG HIGH POLYMER MATERIAL Co Ltd filed Critical CHUZHOU YOUSHENG HIGH POLYMER MATERIAL Co Ltd
Priority to CN201410340793.1A priority Critical patent/CN104140647B/zh
Publication of CN104140647A publication Critical patent/CN104140647A/zh
Application granted granted Critical
Publication of CN104140647B publication Critical patent/CN104140647B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种导电pbt材料，它是由下述重量份的原料组成的：聚对苯二甲酸丁二醇酯72-80、二甲基丙烯酸乙二醇酯2-3、茶皂素1-2、石墨烯5-10、溴化聚苯乙烯2-3、全氟丁基磺酸钾0.8-1、环氧大豆油3-4、1-羟乙基-2-油基咪唑啉1-2、过硫酸钠0.1-0.2、聚乙二醇1000？2-3、聚酰亚胺0.6-1、加工助剂1-2，本发明的pbt材料加入了石墨烯，可以有效的降低了成品基体的表面电阻率，导电性能优越，特别适用于汽车、电子电器、机械零部件等。

Description

一种导电pbt材料
技术领域
本发明主要涉及材料领域，尤其涉及一种导电pbt材料。
背景技术
聚对苯二甲酸丁二醇酯，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但体积电阻、介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。缺点是缺口冲击强度低，成型收缩率大。故大部分采用玻璃纤维增强或无机填充改性，其拉伸强度、弯曲强度可提高一倍以上，热变形温度也大幅提高。可以在140℃下长期工作，玻纤增强后制品纵、横向收缩率不一致，易使制品发生翘曲。
PBT结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。
PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气***零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套。
另外还有运输机械零件，缝纫机和纺织机械零件、钟表外壳、镜筒、电熨斗罩、水银灯罩、烘烤炉部件、电动工具零件、屏蔽套。
发明内容
本发明目的就是提供一种导电pbt材料。
本发明是通过以下技术方案实现的：
一种导电pbt材料，它是由下述重量份的原料组成的：
聚对苯二甲酸丁二醇酯72-80、二甲基丙烯酸乙二醇酯2-3、茶皂素1-2、石墨烯5-10、溴化聚苯乙烯2-3、全氟丁基磺酸钾0.8-1、环氧大豆油3-4、1-羟乙基-2-油基咪唑啉1-2、过硫酸钠0.1-0.2、聚乙二醇10002-3、聚酰亚胺0.6-1、加工助剂1-2；
所述的加工助剂是由下述重量份的原料组成的：
硅酸三钙1-2、罗望子胶2-3、硅酮母粒1-2、癸二酸二辛酯2-3、牡蛎壳粉2-3、钨酸铵0.1-0.3、8-羟基喹啉0.2-0.4、聚二甲基硅氧烷1-2；
将牡蛎壳粉、硅酮母粒混合，搅拌均匀后加入癸二酸二辛酯，在50-60℃下加热混合2-4分钟，加入聚二甲基硅氧烷，200-300转/分搅拌分散7-10分钟，得预混料；
将硅酸三钙与钨酸铵混合球磨，加入上述预混料和剩余各原料，搅拌均匀，得所述加工助剂。
一种导电pbt材料的制备方法，包括以下步骤：
将石墨烯、溴化聚苯乙烯混合，搅拌均匀后加入二甲基丙烯酸乙二醇酯，50-60℃下搅拌混合3-7分钟，加入聚乙二醇1000，搅拌至常温；
将茶皂素、1-羟乙基-2-油基咪唑啉、环氧大豆油混合，搅拌混合均匀；
将上述处理后的各原料与剩余各原料混合，高速搅拌均匀，送入双螺杆挤出机挤出，经过拉条、冷却、切粒、干燥处理，即得所述导电pbt材料。
本发明的优点是：
本发明的pbt材料加入了石墨烯，可以有效的降低了成品基体的表面电阻率，导电性能优越，特别适用于汽车、电子电器、机械零部件等。
具体实施方式
实施例1
一种导电pbt材料，它是由下述重量份（公斤）的原料组成的：
聚对苯二甲酸丁二醇酯80、二甲基丙烯酸乙二醇酯3、茶皂素1、石墨烯5-10、溴化聚苯乙烯2、全氟丁基磺酸钾0.8、环氧大豆油4、1-羟乙基-2-油基咪唑啉1、过硫酸钠0.2、聚乙二醇10002、聚酰亚胺0.6、加工助剂2；
所述的加工助剂是由下述重量份的原料组成的：
硅酸三钙2、罗望子胶3、硅酮母粒1、癸二酸二辛酯2、牡蛎壳粉3、钨酸铵0.3、8-羟基喹啉0.4、聚二甲基硅氧烷1；
将牡蛎壳粉、硅酮母粒混合，搅拌均匀后加入癸二酸二辛酯，在60℃下加热混合2分钟，加入聚二甲基硅氧烷，300转/分搅拌分散10分钟，得预混料；
将硅酸三钙与钨酸铵混合球磨，加入上述预混料和剩余各原料，搅拌均匀，得所述加工助剂。
一种导电pbt材料的制备方法，包括以下步骤：
将石墨烯、溴化聚苯乙烯混合，搅拌均匀后加入二甲基丙烯酸乙二醇酯，60℃下搅拌混合3分钟，加入聚乙二醇1000，搅拌至常温；
将茶皂素、1-羟乙基-2-油基咪唑啉、环氧大豆油混合，搅拌混合均匀；
将上述处理后的各原料与剩余各原料混合，高速搅拌均匀，送入双螺杆挤出机挤出，经过拉条、冷却、切粒、干燥处理，即得所述导电pbt材料。
本实施方法中所得的导电pbt材料的具体性能为：
拉伸强度为93MPa；
缺口冲击强度（KJ/m2）9.56；
垂直燃烧(1.6mm)FV-O。

Claims (2)

1.一种导电pbt材料，其特征在于它是由下述重量份的原料组成的：
聚对苯二甲酸丁二醇酯72-80、二甲基丙烯酸乙二醇酯2-3、茶皂素1-2、石墨烯5-10、溴化聚苯乙烯2-3、全氟丁基磺酸钾0.8-1、环氧大豆油3-4、1-羟乙基-2-油基咪唑啉1-2、过硫酸钠0.1-0.2、聚乙二醇10002-3、聚酰亚胺0.6-1、加工助剂1-2；
所述的加工助剂是由下述重量份的原料组成的：
硅酸三钙1-2、罗望子胶2-3、硅酮母粒1-2、癸二酸二辛酯2-3、牡蛎壳粉2-3、钨酸铵0.1-0.3、8-羟基喹啉0.2-0.4、聚二甲基硅氧烷1-2；
将牡蛎壳粉、硅酮母粒混合，搅拌均匀后加入癸二酸二辛酯，在50-60℃下加热混合2-4分钟，加入聚二甲基硅氧烷，200-300转/分搅拌分散7-10分钟，得预混料；
将硅酸三钙与钨酸铵混合球磨，加入上述预混料和剩余各原料，搅拌均匀，得所述加工助剂。
2.一种如权利要求1所述的导电pbt材料的制备方法，其特征在于包括以下步骤：
将石墨烯、溴化聚苯乙烯混合，搅拌均匀后加入二甲基丙烯酸乙二醇酯，50-60℃下搅拌混合3-7分钟，加入聚乙二醇1000，搅拌至常温；
将茶皂素、1-羟乙基-2-油基咪唑啉、环氧大豆油混合，搅拌混合均匀；
将上述处理后的各原料与剩余各原料混合，高速搅拌均匀，送入双螺杆挤出机挤出，经过拉条、冷却、切粒、干燥处理，即得所述导电pbt材料。
CN201410340793.1A 2014-07-17 2014-07-17 一种导电pbt材料 Active CN104140647B (zh)