CN104130613A - 一种塑料板用高附着力涂料及其制备方法 - Google Patents

一种塑料板用高附着力涂料及其制备方法 Download PDF

Info

Publication number
CN104130613A
CN104130613A CN201410367183.0A CN201410367183A CN104130613A CN 104130613 A CN104130613 A CN 104130613A CN 201410367183 A CN201410367183 A CN 201410367183A CN 104130613 A CN104130613 A CN 104130613A
Authority
CN
China
Prior art keywords
parts
plastic plate
high adhesion
portions
adhesion paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410367183.0A
Other languages
English (en)
Inventor
张金龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU JUKANG NEW MATERIAL TECHNOLOGY Co Ltd
Original Assignee
SUZHOU JUKANG NEW MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU JUKANG NEW MATERIAL TECHNOLOGY Co Ltd filed Critical SUZHOU JUKANG NEW MATERIAL TECHNOLOGY Co Ltd
Priority to CN201410367183.0A priority Critical patent/CN104130613A/zh
Publication of CN104130613A publication Critical patent/CN104130613A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种塑料板用高附着力涂料及其制备方法，该涂料以质量份计含有以下成分：甲基丙烯酸甲酯8～20份，甲基丙烯酸羟乙酯2～6份，三羟甲基丙烷三丙烯酸酯1.5～2.5份，安息香双甲醚0.2～0.6份，三乙胺1.5～4.5份，羟乙基纤维素0.05～0.015份，硼酸锌1～2.2份，乙二醇0.8～1.5份，水1.5～2.5份。本发明提供的涂料对塑料板的附着力高，贮存稳定性好，涂膜的耐划痕性、阻燃性都较好，对塑料板具有很好的涂覆和装饰作用。

Description

一种塑料板用高附着力涂料及其制备方法
技术领域
 本发明涉及涂料领域，尤其涉及一种塑料板用高附着力涂料及其制备方法。
背景技术
 塑料板就是用塑料做成的板材，塑料为合成的高分子化合物，可以自由改变形体样式，因此其具有优美的形状，并且应用范围很广。为了是塑料板具有优美的外观，我们可以在塑料板上涂覆涂料，使其更具有美观和实用价值。但是，目前现有的塑料板用涂料的附着力、耐划痕性、阻燃性不高。
发明内容
解决的技术问题：针对现有塑料板用涂料附着力、耐划痕性、阻燃性不高的缺点，本发明提供一种塑料板用高附着力涂料及其制备方法。
技术方案：一种塑料板用高附着力涂料，以质量份计含有以下成分：甲基丙烯酸甲酯8～20份，甲基丙烯酸羟乙酯2～6份，三羟甲基丙烷三丙烯酸酯1.5～2.5份，安息香双甲醚0.2～0.6份，三乙胺1.5～4.5份，羟乙基纤维素0.05～0.015份，硼酸锌1～2.2份，乙二醇0.8～1.5份，水1.5～2.5份。
上述所述的一种塑料板用高附着力涂料，以质量份计含有以下成分：甲基丙烯酸甲酯10～15份，甲基丙烯酸羟乙酯3～4份，三羟甲基丙烷三丙烯酸酯1.8～2份，安息香双甲醚0.3～0.4份，三乙胺2～3份，羟乙基纤维素0.08～0.01份，硼酸锌1.2～1.6份，乙二醇1～1.2份，水1.7～2份。
上述所述的一种塑料板用高附着力涂料的制备步骤如下：将乙二醇加热至70～80℃，然后加入甲基丙烯酸甲酯、甲基丙烯酸羟乙酯、三羟甲基丙烷三丙烯酸酯和安息香双甲醚，保持温度为70～80℃，保温4～5h，然后加入三乙胺和水，混合均匀后加入羟乙基纤维素和硼酸锌，混合均匀即得成品。
有益效果：本发明提供的一种塑料板用高附着力涂料及其制备方法，该涂料对塑料板的附着力高，贮存稳定性好，涂膜的耐划痕性、阻燃性都较好，对塑料板具有很好的涂覆和装饰作用。
具体实施方式
实施例1
本实施例提供一种塑料板用高附着力涂料，以质量份计含有以下成分：甲基丙烯酸甲酯8份，甲基丙烯酸羟乙酯2份，三羟甲基丙烷三丙烯酸酯1.5份，安息香双甲醚0.2份，三乙胺1.5份，羟乙基纤维素0.05份，硼酸锌1份，乙二醇0.8份，水1.5份。
一种塑料板用高附着力涂料的制备步骤如下：将乙二醇加热至70℃，然后加入甲基丙烯酸甲酯、甲基丙烯酸羟乙酯、三羟甲基丙烷三丙烯酸酯和安息香双甲醚，保持温度为70℃，保温4h，然后加入三乙胺和水，混合均匀后加入羟乙基纤维素和硼酸锌，混合均匀即得成品。
实施例2
本实施例提供一种塑料板用高附着力涂料，以质量份计含有以下成分：甲基丙烯酸甲酯10份，甲基丙烯酸羟乙酯3份，三羟甲基丙烷三丙烯酸酯1.8份，安息香双甲醚0.3份，三乙胺2份，羟乙基纤维素0.08份，硼酸锌1.2份，乙二醇1份，水1.7份。
一种塑料板用高附着力涂料的制备步骤如下：将乙二醇加热至80℃，然后加入甲基丙烯酸甲酯、甲基丙烯酸羟乙酯、三羟甲基丙烷三丙烯酸酯和安息香双甲醚，保持温度为80℃，保温5h，然后加入三乙胺和水，混合均匀后加入羟乙基纤维素和硼酸锌，混合均匀即得成品。
实施例3
本实施例提供一种塑料板用高附着力涂料，以质量份计含有以下成分：甲基丙烯酸甲酯15份，甲基丙烯酸羟乙酯4份，三羟甲基丙烷三丙烯酸酯2份，安息香双甲醚0.4份，三乙胺3份，羟乙基纤维素0.01份，硼酸锌1.6份，乙二醇1.2份，水2份。
一种塑料板用高附着力涂料的制备步骤如下：将乙二醇加热至75℃，然后加入甲基丙烯酸甲酯、甲基丙烯酸羟乙酯、三羟甲基丙烷三丙烯酸酯和安息香双甲醚，保持温度为75℃，保温4.5h，然后加入三乙胺和水，混合均匀后加入羟乙基纤维素和硼酸锌，混合均匀即得成品。
上述实施例1～实施例3的一种塑料板用高附着力涂料的技术性能指标，其检测结果如下：
检测结果
以上对本发明实施例进行了详细介绍，对于本领域的一般技术人员，依据本发明实施例的思想，在具体实施方式及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。

Claims (3)

1.一种塑料板用高附着力涂料，其特征在于以质量份计含有以下成分：甲基丙烯酸甲酯8～20份，甲基丙烯酸羟乙酯2～6份，三羟甲基丙烷三丙烯酸酯1.5～2.5份，安息香双甲醚0.2～0.6份，三乙胺1.5～4.5份，羟乙基纤维素0.05～0.015份，硼酸锌1～2.2份，乙二醇0.8～1.5份，水1.5～2.5份。
2.根据权利要求1所述的一种塑料板用高附着力涂料，其特征在于以质量份计含有以下成分：甲基丙烯酸甲酯10～15份，甲基丙烯酸羟乙酯3～4份，三羟甲基丙烷三丙烯酸酯1.8～2份，安息香双甲醚0.3～0.4份，三乙胺2～3份，羟乙基纤维素0.08～0.01份，硼酸锌1.2～1.6份，乙二醇1～1.2份，水1.7～2份。
3.如权利要求1所述的一种塑料板用高附着力涂料的制备方法，其特征在于该方法的制备步骤如下：将乙二醇加热至70～80℃，然后加入甲基丙烯酸甲酯、甲基丙烯酸羟乙酯、三羟甲基丙烷三丙烯酸酯和安息香双甲醚，保持温度为70～80℃，保温4～5h，然后加入三乙胺和水，混合均匀后加入羟乙基纤维素和硼酸锌，混合均匀即得成品。
CN201410367183.0A 2014-07-30 2014-07-30 一种塑料板用高附着力涂料及其制备方法 Pending CN104130613A (zh)