CN104109311A - Wallpaper foaming pulp - Google Patents
Wallpaper foaming pulp Download PDFInfo
- Publication number
- CN104109311A CN104109311A CN201410325134.0A CN201410325134A CN104109311A CN 104109311 A CN104109311 A CN 104109311A CN 201410325134 A CN201410325134 A CN 201410325134A CN 104109311 A CN104109311 A CN 104109311A
- Authority
- CN
- China
- Prior art keywords
- agent
- wallpaper
- resin powder
- dioxide
- dop
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wallpaper foaming pulp comprising the following components in percentage by weight: 25-45% of PVC resin powder, 20-35% of DOP, 5-15% of titanium dioxide, 10-20% of calcium carbonate, 2-5% of a foaming agent, 2-5% of a viscosity reducer, 0.5-1.5% of a stabilizing agent, 1-3% of a fire-proofing agent, 0.2-0.5% of a sterilizing agent and 1-3% of silicon dioxide. The wallpaper foaming pulp disclosed by the invention can be used for ensuring that foaming wallpaper is high in durability, good in moisture absorption effect and longer in service life.
Description
Technical field
The present invention relates to a kind of wallpaper foaming slurry.
Technical background
The flexible ridge design in foaming wallpaper surface, has decoration and sound-absorbing etc. multi-functional, and the surperficial ridge design figure that can impress out different color, and pattern is true to nature, and stereoscopic sensation is strong, and good decorating effect is applicable to the decorations such as indoor dado, parlor and building inside corridor.But foaming wallpaper on the market causes not wear-resisting because foaming slurry quality is not good, easily scratch, moisture absorption weak effect, causes work-ing life too short.
Summary of the invention
The technical problem that the present invention solves provides a kind of wallpaper foaming slurry, and the wallpaper durability degree that makes to foam is high, and the moisture absorption is effective, and the life-span is longer.
For solving the problems of the technologies described above, the present invention adopts following technical scheme: a kind of wallpaper foaming slurry, comprises that the weight percent of following component and each component is: polyvinyl chloride resin powder: 25~45%, DOP:20~35%, titanium dioxide: 5~15%, calcium carbonate: 10~20%, whipping agent: 2~5%, viscosity-depression agent: 2~5%, stablizer: 0.5~1.5%, fireproofing agent: 1~3%, antiseptic-germicide: 0.2~0.5%, silicon-dioxide: 1~3%.
Preferably, the weight percent of each component is: polyvinyl chloride resin powder: 40%, DOP:30%, titanium dioxide: 10%, calcium carbonate: 10%, whipping agent: 3%, viscosity-depression agent: 2%, stablizer: 0.5%, fireproofing agent: 2%, antiseptic-germicide: 0.5%, silicon-dioxide: 2%.
Preferably, the weight percent of each component is: polyvinyl chloride resin powder: 25%, DOP:35%, titanium dioxide: 9%, calcium carbonate: 15%, whipping agent: 2%, viscosity-depression agent: 2%, stablizer: 0.5%, fireproofing agent: 2%, antiseptic-germicide: 0.5%, silicon-dioxide: 3%.
Preferably, the weight percent of each component is: polyvinyl chloride resin powder: 45%, DOP:20%, titanium dioxide: 10%, calcium carbonate: 14%, whipping agent: 5%, viscosity-depression agent: 2%, stablizer: 0.5%, fireproofing agent: 2%, antiseptic-germicide: 0.5%, silicon-dioxide: 1%.
Preferably, described whipping agent is modification AC whipping agent, and described modification AC whipping agent is made up of AC whipping agent and zinc oxide.
Preferably, the granularity of described polyvinyl chloride resin powder is 1~2 μ m.
Beneficial effect of the present invention is: adopt polyvinyl chloride resin powder and DOP to be mixed to form PVC thickener as major ingredient, add calcium carbonate as weighting agent, cost is low and make wallpaper have good surface property and intensity, and the addition of calcium carbonate is less mix with polyvinyl chloride resin powder and DOP after, foaming slurry slurry has good foaming effect, make wallpaper there is better pore, moisture absorption ability gets a promotion, add silicon-dioxide, improve foaming slurry and be coated to the wear resistance after wallpaper, be not easy scratch loss, improved work-ing life.
Embodiment
Wallpaper foaming slurry of the present invention, comprises that the weight percent of following component and each component is: polyvinyl chloride resin powder: 25~45%, DOP:20~35%, titanium dioxide: 5~15%, calcium carbonate: 10~20%, whipping agent: 2~5%, viscosity-depression agent: 2~5%, stablizer: 0.5~1.5%, fireproofing agent: 1~3%, antiseptic-germicide: 0.2~0.5%, silicon-dioxide: 1~3%.
Embodiment 1: the weight percent of each component is: polyvinyl chloride resin powder: 40%, DOP:30%, titanium dioxide: 10%, calcium carbonate: 10%, whipping agent: 3%, viscosity-depression agent: 2%, stablizer: 0.5%, fireproofing agent: 2%, antiseptic-germicide: 0.5%, silicon-dioxide: 2%.
Embodiment 2: the weight percent of each component is: polyvinyl chloride resin powder: 25%, DOP:35%, titanium dioxide: 9%, calcium carbonate: 15%, whipping agent: 2%, viscosity-depression agent: 2%, stablizer: 0.5%, fireproofing agent: 2%, antiseptic-germicide: 0.5%, silicon-dioxide: 3%.
Embodiment 3: the weight percent of each component is: polyvinyl chloride resin powder: 45%, DOP:20%, titanium dioxide: 10%, calcium carbonate: 14%, whipping agent: 5%, viscosity-depression agent: 2%, stablizer: 0.5%, fireproofing agent: 2%, antiseptic-germicide: 0.5%, silicon-dioxide: 1%.
Described whipping agent is modification AC whipping agent, and described modification AC whipping agent is made up of AC whipping agent and zinc oxide.Zinc oxide can regulate activation temperature as activator, and the foaming effect of AC whipping agent is got a promotion, and described zinc oxide possesses associating anti-microbial effect as antiseptic-germicide simultaneously.
The granularity of described polyvinyl chloride resin powder is 1~2 μ m.Described viscosity-depression agent is polyether glycol.Described stablizer is azodicarbonic acid amine potassium formiate, has the large dual-use function with stoping DOP thermal destruction of gas production rate.Described fireproofing agent is trichloroethyl phosphate, simultaneously as ignition dope and softening agent.
Claims (6)
1. a wallpaper foaming slurry, is characterized in that: the weight percent that comprises following component and each component is: polyvinyl chloride resin powder: 25~45%, DOP:20~35%, titanium dioxide: 5~15%, calcium carbonate: 10~20%, whipping agent: 2~5%, viscosity-depression agent: 2~5%, stablizer: 0.5~1.5%, fireproofing agent: 1~3%, antiseptic-germicide: 0.2~0.5%, silicon-dioxide: 1~3%.
2. wallpaper foaming slurry according to claim 1, is characterized in that: the weight percent of each component is: polyvinyl chloride resin powder: 40%, DOP:30%, titanium dioxide: 10%, calcium carbonate: 10%, whipping agent: 3%, viscosity-depression agent: 2%, stablizer: 0.5%, fireproofing agent: 2%, antiseptic-germicide: 0.5%, silicon-dioxide: 2%.
3. wallpaper foaming slurry according to claim 1, is characterized in that: the weight percent of each component is: polyvinyl chloride resin powder: 25%, DOP:35%, titanium dioxide: 9%, calcium carbonate: 15%, whipping agent: 2%, viscosity-depression agent: 2%, stablizer: 0.5%, fireproofing agent: 2%, antiseptic-germicide: 0.5%, silicon-dioxide: 3%.
4. wallpaper foaming slurry according to claim 1, is characterized in that: the weight percent of each component is: polyvinyl chloride resin powder: 45%, DOP:20%, titanium dioxide: 10%, calcium carbonate: 14%, whipping agent: 5%, viscosity-depression agent: 2%, stablizer: 0.5%, fireproofing agent: 2%, antiseptic-germicide: 0.5%, silicon-dioxide: 1%.
5. according to the wallpaper foaming slurry described in claim 1 to 4 any one, it is characterized in that: described whipping agent is modification AC whipping agent, described modification AC whipping agent is made up of AC whipping agent and zinc oxide.
6. according to the wallpaper foaming slurry described in claim 1 to 4 any one, it is characterized in that: the granularity of described polyvinyl chloride resin powder is 1~2 μ m.