CN104098316A - 一种耐高温加气砖及其制备方法 - Google Patents
一种耐高温加气砖及其制备方法 Download PDFInfo
- Publication number
- CN104098316A CN104098316A CN201410271956.5A CN201410271956A CN104098316A CN 104098316 A CN104098316 A CN 104098316A CN 201410271956 A CN201410271956 A CN 201410271956A CN 104098316 A CN104098316 A CN 104098316A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- steam
- high temperature
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种耐高温加气砖,由下列重量份的原料制成:钛渣3-5、沸腾炉渣7-9、聚四氟乙烯微粉0.5-1、葡萄糖酸钠0.4-0.7、三乙醇胺0.2-0.4、纯碱1-1.5、玻璃鳞片5-10、水泥9-12、生石灰12-15、改性稻壳9-11、石膏6-8、粉煤灰45-50、加气铝粉5-6、水适量;本发明加气砖通过使用钛渣、沸腾炉渣、玻璃鳞片,使得加气砖的强度高、而且耐高温、耐水性和耐火性好;通过使用改性稻壳,增强了隔热效果,耐水性好,减轻了重量,增加了抗震性能,同时减水效果好。
Description
技术领域
本发明属于砖领域,尤其涉及一种耐高温加气砖及其制备方法。
背景技术
加气砖也叫做加气混凝土砌块,应用非常的广泛,主要用在机械厂房和民用建筑中的墙体材料、填充墙、楼板和屋面板等承重墙材以及非承重材料和周围的填充围墙。
目前加气砖已成为建筑材料行业的主导产品,国家已经逐步禁止使用粘土实心砖,逐渐取而代之的就是加气混凝土砌块,蒸压砖。
加气砖具有重量轻、保温隔热性能好、抗震能力强、加工性能好、具有一定的耐高温性、隔音性能好、适应性强的特点,可根据当地不同原材料,不同条件来量身定造,原材料来源广泛,可选择河沙、粉煤灰、矿砂等,因地制宜,可以废物利用,有利环保,真正变废为宝。
但是随着建筑行业的发展,建筑物越来越高、造型越来越奇特,对加气砖的强度、密度、收缩值、抗冻性等要求都有所提高,另外随着人们生活水平的不断提高,对环境的要求也越来越高,对建筑物的保温性能、吸音性能、放射性都有更高的要求,甚至要求建筑物具有有益身体健康的性能,因此根据需要,研制更加性能优异的加气砖势在必行。
发明内容
本发明的目的在于提供一种耐高温加气砖及其制备方法,该加气砖强度高、而且耐高温、耐水性和耐火性好。
本发明的技术方案如下:
一种耐高温加气砖,其特征在于由下列重量份的原料制成:钛渣3-5、沸腾炉渣7-9、聚四氟乙烯微粉0.5-1、葡萄糖酸钠0.4-0.7、三乙醇胺0.2-0.4、纯碱1-1.5、玻璃鳞片5-10、水泥9-12、生石灰12-15、改性稻壳9-11、石膏6-8、粉煤灰45-50、加气铝粉5-6、水适量;
所述改性稻壳由下列重量份的原料制成:稻壳13-15、亚硫酸钠0.5-0.7、远红外陶瓷粉1-2、庚酸烯丙酯0.5-0.7、2-甲基咪唑0.1-0.2、芳香族聚氨酯丙烯酸酯1-2、丙烯酸羟乙酯1-2、聚羧酸高效减水剂1-2、玻璃粉1-2、过硫酸铵0.01-0.02、海藻酸钙0.4-0.7、霞石粉1-2、三丹油0.5-0.7、地沟油2-3;制作方法为:将稻壳粉碎成50-100目颗粒,边搅拌边喷入三丹油、地沟油,混合均匀后放置5-7个小时,再与其他剩余成分混合,加热至75-80℃,分散研磨30-40分钟,即得。
所述的耐高温加气砖的制备方法,其特征在于包括以下步骤:
(1)将水泥、生石灰、石膏、粉煤灰、钛渣、沸腾炉渣混合,送入球磨机中研磨成50-100目颗粒,再与除加气铝粉之外的成分混合,按水料比为0.57-0.58加入水,搅拌均匀,再加入加气铝粉,搅拌均匀得到浆料;
(2)将第(1)步得到的浆料倒入模具中,得到砖胚体;
(3)将砖胚体放入蒸养釜进行抽真空,然后在1.7-1.9小时内均匀地通入蒸汽,使蒸养室内的温度升至170-180℃,压力达到11-13MPa,保持恒定9-12小时;
(4)在1.7-1.9小时内均匀地放出蒸汽,使蒸养室内的温度降至70℃以下,出釜,放置28-30天即得。
本发明的有益效果
本发明加气砖通过使用钛渣、沸腾炉渣、玻璃鳞片,使得加气砖的强度高、而且耐高温、耐水性和耐火性好;通过使用改性稻壳,增强了隔热效果,耐水性好,减轻了重量,增加了抗震性能,同时减水效果好。
具体实施方式
一种耐高温加气砖,由下列重量份(公斤)的原料制成:钛渣4、沸腾炉渣8、聚四氟乙烯微粉0.8、葡萄糖酸钠0.5、三乙醇胺0.3、纯碱1.3、玻璃鳞片7、水泥11、生石灰14、改性稻壳10、石膏7、粉煤灰47、加气铝粉5.5、水适量;
所述改性稻壳由下列重量份(公斤)的原料制成:稻壳14、亚硫酸钠0.6、远红外陶瓷粉1.6、庚酸烯丙酯0.6、2-甲基咪唑0.1、芳香族聚氨酯丙烯酸酯1.5、丙烯酸羟乙酯1.5、聚羧酸高效减水剂1.5、玻璃粉1.5、过硫酸铵0.01、海藻酸钙0.6、霞石粉1.6、三丹油0.6、地沟油2.6;制作方法为:将稻壳粉碎成80目颗粒,边搅拌边喷入三丹油、地沟油,混合均匀后放置6个小时,再与其他剩余成分混合,加热至77℃,分散研磨35分钟,即得。
所述的耐高温加气砖的制备方法,包括以下步骤:
(1)将水泥、生石灰、石膏、粉煤灰、钛渣、沸腾炉渣混合,送入球磨机中研磨成70目颗粒,再与除加气铝粉之外的成分混合,按水料比为0.57加入水,搅拌均匀,再加入加气铝粉,搅拌均匀得到浆料;
(2)将第(1)步得到的浆料倒入模具中,得到砖胚体;
(3)将砖胚体放入蒸养釜进行抽真空,然后在1.8小时内均匀地通入蒸汽,使蒸养室内的温度升至175℃,压力达到12MPa,保持恒定11小时;
(4)在1.8小时内均匀地放出蒸汽,使蒸养室内的温度降至70℃,出釜,放置29天即得。
实验数据:
该加气砖的密度为600kg/m3,耐火温度为700℃,导热系数为0.12W /(m·℃),采用淋浴喷头分别向240mm厚的粘土砖墙和加气砖墙喷淋,粘土砖墙12小时后全部浸透,加气砖墙喷淋72小时后渗水深度为90mm,抗压强度为 6.7Mpa,吸声系数0.35。
Claims (2)
1.一种耐高温加气砖,其特征在于由下列重量份的原料制成:钛渣3-5、沸腾炉渣7-9、聚四氟乙烯微粉0.5-1、葡萄糖酸钠0.4-0.7、三乙醇胺0.2-0.4、纯碱1-1.5、玻璃鳞片5-10、水泥9-12、生石灰12-15、改性稻壳9-11、石膏6-8、粉煤灰45-50、加气铝粉5-6、水适量;
所述改性稻壳由下列重量份的原料制成:稻壳13-15、亚硫酸钠0.5-0.7、远红外陶瓷粉1-2、庚酸烯丙酯0.5-0.7、2-甲基咪唑0.1-0.2、芳香族聚氨酯丙烯酸酯1-2、丙烯酸羟乙酯1-2、聚羧酸高效减水剂1-2、玻璃粉1-2、过硫酸铵0.01-0.02、海藻酸钙0.4-0.7、霞石粉1-2、三丹油0.5-0.7、地沟油2-3;制作方法为:将稻壳粉碎成50-100目颗粒,边搅拌边喷入三丹油、地沟油,混合均匀后放置5-7个小时,再与其他剩余成分混合,加热至75-80℃,分散研磨30-40分钟,即得。
2.根据权利要求1所述的耐高温加气砖的制备方法,其特征在于包括以下步骤:
(1)将水泥、生石灰、石膏、粉煤灰、钛渣、沸腾炉渣混合,送入球磨机中研磨成50-100目颗粒,再与除加气铝粉之外的成分混合,按水料比为0.57-0.58加入水,搅拌均匀,再加入加气铝粉,搅拌均匀得到浆料;
(2)将第(1)步得到的浆料倒入模具中,得到砖胚体;
(3)将砖胚体放入蒸养釜进行抽真空,然后在1.7-1.9小时内均匀地通入蒸汽,使蒸养室内的温度升至170-180℃,压力达到11-13MPa,保持恒定9-12小时;
(4)在1.7-1.9小时内均匀地放出蒸汽,使蒸养室内的温度降至70℃以下,出釜,放置28-30天即得。