CN104087201A - 一种乙烯-醋酸乙烯热熔胶 - Google Patents
一种乙烯-醋酸乙烯热熔胶 Download PDFInfo
- Publication number
- CN104087201A CN104087201A CN201410293067.9A CN201410293067A CN104087201A CN 104087201 A CN104087201 A CN 104087201A CN 201410293067 A CN201410293067 A CN 201410293067A CN 104087201 A CN104087201 A CN 104087201A
- Authority
- CN
- China
- Prior art keywords
- parts
- add
- vinyl acetate
- hot melt
- melt adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种乙烯-醋酸乙烯热熔胶,它是由下述重量份的原料组成的:乙烯-醋酸乙烯共聚物64-71、三萜皂苷1-2、磷酸钠0.1-0.3、甲苯基二苯基磷酸酯1-2、蓖麻油酸锌0.2-0.4、聚马来酸酐1-2、钼酸铵1-2、液体石蜡10-13、甘油聚氧乙烯醚椰油酸酯0.3-1、双巯基乙酸异辛酯二正辛基锡0.1-0.2、双十二碳醇酯2-3、粘结助剂7-10;本发明制备的热熔胶基本没有污染和挥发物,具有适中的弹性、良好的耐油迁移、间隔后易剥离、易喷胶等优点。
Description
技术领域
本发明主要涉及一种热熔胶粉末,尤其涉及一种乙烯-醋酸乙烯热熔胶。
背景技术
热熔胶是一种可塑性的粘合剂,在一定温度范围内其物理状态随温度改变而改变,而化学特性不变,其无毒无味,属环保型化学产品。
发明内容
本发明目的就是提供一种乙烯-醋酸乙烯热熔胶。
本发明是通过以下技术方案实现的:
一种乙烯-醋酸乙烯热熔胶,它是由下述重量份的原料组成的:
乙烯-醋酸乙烯共聚物64-71、三萜皂苷1-2、磷酸钠0.1-0.3、甲苯基二苯基磷酸酯1-2、蓖麻油酸锌0.2-0.4、聚马来酸酐1-2、钼酸铵1-2、液体石蜡10-13、甘油聚氧乙烯醚椰油酸酯0.3-1、双巯基乙酸异辛酯二正辛基锡0.1-0.2、双十二碳醇酯2-3、粘结助剂7-10;
所述的增粘结助剂是由下述重量份的原料组成的:
液体石蜡24-30、亚麻籽胶2-3、氟化石墨1-2、EVA树脂4-5、马来酸二丁酯3-4、油酸钾皂0.6-2、丙基三甲氧基硅烷0.2-0.5;
将EVA树脂加热软化,加入马来酸二丁酯,搅拌均匀,加入丙基三甲氧基硅烷,在50-60℃下保温搅拌10-15分钟,加入到液体石蜡中,搅拌均匀,得粘结液;
将亚麻籽胶与油酸钾皂混合,搅拌均匀后加入氟化石墨,球磨均匀,加入到上述粘结液中,60-80转/分搅拌分散3-4分钟,即得所述粘结助剂。
一种乙烯-醋酸乙烯热熔胶的制备方法,其特征在于包括以下步骤:
将钼酸铵、蓖麻油酸锌混合加入到液体石蜡中,搅拌均匀后加入三萜皂苷, 100-120转/分搅拌混合5-10分钟,加入甲苯基二苯基磷酸酯、双巯基乙酸异辛酯二正辛基锡,在50-60℃下搅拌混合10-16分钟,加入双十二碳醇酯,搅拌至常温,加入除了粘结助剂以外的各原料,在25-30℃下保温静置1-2小时,加入粘结助剂,送入混炼机,加热升温至90-100℃,混炼20-30min;将混炼均匀后的产物经过真空脱泡后加入到双螺杆挤出机,挤出产物经冷却、造粒,即得所述乙烯-醋酸乙烯热熔胶。
本发明的优点是:
本发明制备的热熔胶基本没有污染和挥发物,具有适中的弹性、良好的耐油迁移、间隔后易剥离、易喷胶等优点。
具体实施方式
实施例1
一种乙烯-醋酸乙烯热熔胶,它是由下述重量份(公斤)的原料组成的:
乙烯-醋酸乙烯共聚物71、三萜皂苷1、磷酸钠0.3、甲苯基二苯基磷酸酯1、蓖麻油酸锌0.2、聚马来酸酐2、钼酸铵2、液体石蜡13、甘油聚氧乙烯醚椰油酸酯0.3、双巯基乙酸异辛酯二正辛基锡0.2、双十二碳醇酯3、粘结助剂10;
所述的增粘结助剂是由下述重量份的原料组成的:
液体石蜡30、亚麻籽胶2、氟化石墨1、EVA树脂4、马来酸二丁酯4、油酸钾皂0.6、丙基三甲氧基硅烷0.5;
将EVA树脂加热软化,加入马来酸二丁酯,搅拌均匀,加入丙基三甲氧基硅烷,在60℃下保温搅拌15分钟,加入到液体石蜡中,搅拌均匀,得粘结液;
将亚麻籽胶与油酸钾皂混合,搅拌均匀后加入氟化石墨,球磨均匀,加入到上述粘结液中,80转/分搅拌分散4分钟,即得所述粘结助剂。
一种乙烯-醋酸乙烯热熔胶的制备方法,包括以下步骤:
将钼酸铵、蓖麻油酸锌混合加入到液体石蜡中,搅拌均匀后加入三萜皂苷, 120转/分搅拌混合10分钟,加入甲苯基二苯基磷酸酯、双巯基乙酸异辛酯二正辛基锡,在60℃下搅拌混合16分钟,加入双十二碳醇酯,搅拌至常温,加入除了粘结助剂以外的各原料,在30℃下保温静置2小时,加入粘结助剂,送入混炼机,加热升温至100℃,混炼30min;将混炼均匀后的产物经过真空脱泡后加入到双螺杆挤出机,挤出产物经冷却、造粒,即得所述乙烯-醋酸乙烯热熔胶。
性能测试
软化点94℃;
剥离强度:92N/25mm。
Claims (2)
1.一种乙烯-醋酸乙烯热熔胶,其特征在于它是由下述重量份的原料组成的:
乙烯-醋酸乙烯共聚物64-71、三萜皂苷1-2、磷酸钠0.1-0.3、甲苯基二苯基磷酸酯1-2、蓖麻油酸锌0.2-0.4、聚马来酸酐1-2、钼酸铵1-2、液体石蜡10-13、甘油聚氧乙烯醚椰油酸酯0.3-1、双巯基乙酸异辛酯二正辛基锡0.1-0.2、双十二碳醇酯2-3、粘结助剂7-10;
所述的增粘结助剂是由下述重量份的原料组成的:
液体石蜡24-30、亚麻籽胶2-3、氟化石墨1-2、EVA树脂4-5、马来酸二丁酯3-4、油酸钾皂0.6-2、丙基三甲氧基硅烷0.2-0.5;
将EVA树脂加热软化,加入马来酸二丁酯,搅拌均匀,加入丙基三甲氧基硅烷,在50-60℃下保温搅拌10-15分钟,加入到液体石蜡中,搅拌均匀,得粘结液;
将亚麻籽胶与油酸钾皂混合,搅拌均匀后加入氟化石墨,球磨均匀,加入到上述粘结液中,60-80转/分搅拌分散3-4分钟,即得所述粘结助剂。
2.一种如权利要求1所述的乙烯-醋酸乙烯热熔胶的制备方法,其特征在于包括以下步骤:
将钼酸铵、蓖麻油酸锌混合加入到液体石蜡中,搅拌均匀后加入三萜皂苷, 100-120转/分搅拌混合5-10分钟,加入甲苯基二苯基磷酸酯、双巯基乙酸异辛酯二正辛基锡,在50-60℃下搅拌混合10-16分钟,加入双十二碳醇酯,搅拌至常温,加入除了粘结助剂以外的各原料,在25-30℃下保温静置1-2小时,加入粘结助剂,送入混炼机,加热升温至90-100℃,混炼20-30min;将混炼均匀后的产物经过真空脱泡后加入到双螺杆挤出机,挤出产物经冷却、造粒,即得所述乙烯-醋酸乙烯热熔胶。