CN104087099A - Healthy indoor anion paint - Google Patents
Healthy indoor anion paint Download PDFInfo
- Publication number
- CN104087099A CN104087099A CN201410348654.3A CN201410348654A CN104087099A CN 104087099 A CN104087099 A CN 104087099A CN 201410348654 A CN201410348654 A CN 201410348654A CN 104087099 A CN104087099 A CN 104087099A
- Authority
- CN
- China
- Prior art keywords
- healthy indoor
- parts
- coating according
- indoor coating
- anion healthy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to healthy indoor anion paint. The paint is characterized by comprising the following components in parts by weight: 30-60 parts of water-borne emulsion, 10-30 parts of tourmaline powder, 1-10 parts of nanometer TiO2, 1-5 parts of thickener, 1-5 parts of coalescing agent, 1-5 parts of pigment, 1-5 parts of dispersing agents and 1-5 parts of waterproof impermeable additive. The healthy indoor anion paint provided by the invention can effectively release anions indoors and meanwhile the performance of the paint is ensured, the cracking can be prevented and the paint is washable.
Description
Technical field
The present invention relates to a kind of indoor paint, relate in particular to a kind of anion healthy indoor coating.
Background technology
Along with growth in the living standard, people more and more pay close attention to the feature of environmental protection of indoor paint, and the impact that HUMAN HEALTH is produced.Various wholesome indoor paints arise at the historic moment.In prior art, also the example of negative ion releasable material is added in oriented coating the inside.But directly to existing coating products, add the performance that negative ion releasable material can affect coating itself, cause the problems such as chapping, not water-fastness easily appears in coating.
Summary of the invention
The invention provides a kind of anion healthy indoor coating, can guarantee the performance of coating own at indoor effective anion releasing, can prevent be full of cracks, water-fastness simultaneously.
The present invention is that the technical scheme that technical solution problem adopts is:
An anion healthy indoor coating, is characterized in that comprising by weight:
Preferably, dispersion agent is polyacrylate and/or polymaleic acid salt.
Preferably, thickening material is one or more in methylcellulose gum, Vltra tears, Xylo-Mucine, Natvosol.
Preferably, water-based emulsion is aqueous acrylic emulsion or aqueous polyurethane emulsion.
Preferably, the component of water proof anti-seepage additive and weight proportion be, silicon-dioxide 62%-89%, hydroxycarboxylate 1%-12%, Tai-Ace S 150 7%-21%, sodium alkyl benzene sulfonate 3%-5%.
Preferably, film coalescence aid is ethylene glycol phenyl ether or propylene glycol.
Preferably, pigment is one or more in ultramarine, phthalocyanine blue, chrome yellow and chrome red.
Anion healthy indoor coating provided by the invention, can guarantee the performance of coating own at indoor effective anion releasing simultaneously, can prevent coating be full of cracks, also water-fastness.
Embodiment
Below by specific embodiment, the present invention is described in detail, but the content of describing should not be considered as limitation of the present invention, and any change and the modification according to inventive concept, made, should be considered as belonging to protection scope of the present invention.
Embodiment 1
An anion healthy indoor coating, is characterized in that comprising by weight:
Wherein, dispersion agent is polyacrylate;
Thickening material is methylcellulose gum;
Water-based emulsion is aqueous acrylic emulsion;
The component of water proof anti-seepage additive and weight proportion be, silicon-dioxide 62%, hydroxycarboxylate 12%, Tai-Ace S 150 21%, sodium alkyl benzene sulfonate 5%;
Film coalescence aid is ethylene glycol phenyl ether;
Pigment is ultramarine.
Embodiment 2
An anion healthy indoor coating, is characterized in that comprising by weight:
Wherein, dispersion agent is polyacrylate;
Thickening material is Vltra tears;
Water-based emulsion is aqueous polyurethane emulsion;
The component of water proof anti-seepage additive and weight proportion be, silicon-dioxide 80%, hydroxycarboxylate 8%, Tai-Ace S 150 7%, sodium alkyl benzene sulfonate 5%;
Film coalescence aid be ethylene glycol phenyl ether or;
Pigment is ultramarine and chrome red.
Embodiment 3
An anion healthy indoor coating, is characterized in that comprising by weight:
Dispersion agent is polyacrylate and polymaleic acid salt;
Thickening material is Xylo-Mucine;
Water-based emulsion is aqueous acrylic emulsion;
The component of water proof anti-seepage additive and weight proportion be, silicon-dioxide 80%, hydroxycarboxylate 8%, Tai-Ace S 150 7%, sodium alkyl benzene sulfonate 5%;
Film coalescence aid is propylene glycol;
Pigment is chrome red.
Embodiment 4
An anion healthy indoor coating, is characterized in that comprising by weight:
Dispersion agent is polyacrylate and polymaleic acid salt.
Excellent thickening material is Xylo-Mucine;
Water-based emulsion is aqueous acrylic emulsion;
The component of water proof anti-seepage additive and weight proportion be, silicon-dioxide 80%, hydroxycarboxylate 8%, Tai-Ace S 150 7%, sodium alkyl benzene sulfonate 5%;
Film coalescence aid is propylene glycol;
Pigment is chrome red.
Claims (7)
1. an anion healthy indoor coating, is characterized in that comprising by weight:
2. anion healthy indoor coating according to claim 1, is characterized in that, described dispersion agent is polyacrylate and/or polymaleic acid salt.
3. anion healthy indoor coating according to claim 1, is characterized in that, described thickening material is one or more in methylcellulose gum, Vltra tears, Xylo-Mucine, Natvosol.
4. a kind of anion healthy indoor coating according to claim 1, is characterized in that described water-based emulsion is aqueous acrylic emulsion or aqueous polyurethane emulsion.
5. a kind of anion healthy indoor coating according to claim 1, the component and the weight proportion that it is characterized in that described water proof anti-seepage additive be, silicon-dioxide 62%-89%, hydroxycarboxylate 1%-12%, Tai-Ace S 150 7%-21%, sodium alkyl benzene sulfonate 3%-5%.
6. a kind of anion healthy indoor coating according to claim 1, is characterized in that described film coalescence aid is ethylene glycol phenyl ether or propylene glycol.
7. a kind of anion healthy indoor coating according to claim 1, is characterized in that described pigment is one or more in ultramarine, phthalocyanine blue, chrome yellow and chrome red.