CN104072203B - 一种电瓷灰釉修补釉组合物及其制备方法 - Google Patents
一种电瓷灰釉修补釉组合物及其制备方法 Download PDFInfo
- Publication number
- CN104072203B CN104072203B CN201410303295.XA CN201410303295A CN104072203B CN 104072203 B CN104072203 B CN 104072203B CN 201410303295 A CN201410303295 A CN 201410303295A CN 104072203 B CN104072203 B CN 104072203B
- Authority
- CN
- China
- Prior art keywords
- glaze
- colorant
- electroceramics
- reparation
- ash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种电瓷灰釉修补釉组合物及其制备方法,包括如下重量百分比的原料:钾长石8-16%,石英32-40%,氧化硼16-24%,水洗高岭土6-14%,滑石4-12%,石灰石2-10%,硅酸锆2-6%,色料4-10%。色料包括:氧化锌25-55%,氧化铬4-20%,氟化钠5-15%,氧化钴30-45%。首先将色剂原料经高温煅烧,磨细后再与基础釉按配好的比例进行湿法球磨,球磨至料浆细度达到325目筛筛余0.04-0.06%,即得到所述电瓷灰釉修补釉组合物。该配方生产的电瓷灰釉修补釉组合物,适用于各种瓷质坯体,瓷件釉面光滑,色泽白灰清透,表面无缺陷,提高了产品合格率,满足市场需求。
Description
技术领域
本发明属于电瓷技术领域,具体涉及一种电瓷灰釉修补釉组合物及其制备方法。
背景技术
电瓷制品在烧成过程中,坯釉料中的有机物、碳酸盐、硫酸盐等分解放出的气体在釉熔融之前未能充分排出,气泡上升到釉表面后破裂,会留下的凹坑不能自发封闭而形成缺陷,有针孔、圆形等形状。为了这些因釉面缺陷导致不合品变为成品,采取修补釉进行二次煅烧烧成修补是一种切实可行的方法。但是目前现有技术对电瓷灰釉修补方法少有报道。
发明内容
本发明的目的是提供一种电瓷灰釉修补釉后瓷质机械性能好,表面呈色效果好,无色差等缺陷的电瓷灰釉修补釉组合物及其制备方法。
为实现上述目的,本发明采用的技术方案为:一种电瓷灰釉修补釉组合物,所述修补釉组合物包括如下重量百分比的原料:钾长石8-16%,石英32-40%,氧化硼16-24%,水洗高岭土6-14%,滑石4-12%,石灰石2-10%,硅酸锆2-6%;色料4-10%。
所述色料为氧化锌、氧化铬、氟化钠、氧化钴的混合物,其中包含如下重量百分比:氧化锌25-55%,氧化铬4-20%,氟化钠5-15%,氧化钴30-45%。
其中,钾长石,石英,氧化硼,水洗高岭土,滑石,石灰石和硅酸锆的混合物称为基础釉。
本发明首先从工艺上改进,将色料的各组分按配好的比例混合,经过1100℃高温煅烧,磨细过325目,得到色料。再将原料和色料按配好的比例进行湿法球磨,直至料浆细度达到325目筛筛余0.04-0.06%,即得到所述电瓷灰釉修补釉组合物。基础釉烧成温度1200-1230℃,修补釉的烧成温度950-1050℃。
本发明的优点是:本发明电瓷灰釉修补釉组合物与灰釉结合良好。本发明确保了釉面质量,增加了成品率,降低了生产成本。同时,成色效果好,色泽白灰清透,无色差,电瓷产品的外观得到极大改善,填补此类电瓷釉的空白,值得应用推广。
具体实施方式
下面结合具体实施例对本发明作进一步的详细说明。
实施例1:
本实施例电瓷灰釉修补釉组合物,包括如下原料,按重量百分比计,分别为:钾长石12%,石英36%,氧化硼20%,水洗高岭土10%,滑石8%,石灰石6%,硅酸锆2%,色料6%。
色料为氧化锌、氧化铬、氟化钠、氧化钴的混合物,其中包含如下重量百分比:氧化锌35%,氧化铬15%,氟化钠10%,氧化钴40%。
上述电瓷灰釉修补釉组合物的制备方法为:首先将各种色剂的组分按配好的比例混合,经过1150℃高温煅烧,磨细过325目,得到色料。再将基础釉的各组分和色料按配好的比例进行湿法球磨,直至料浆细度达到325目筛筛余0.04-0.06%,即得到所述电瓷灰釉修补釉组合物。
采用本发明修补釉组合物补釉后的电瓷灰釉烧成最高温度1000℃。
本发明电瓷灰釉的化学成分及物理性能如下:
电瓷灰釉修补釉组合物的化学分析成分(%):
Si2O | Fe2O3 | Al2O3 | CaO | MgO | K2O | 烧失量 | ZrO2 | Co2O3 | B2O3 | ZnO | TiO2 |
40-60 | 0.1-0.6 | 1.5-6 | 2-5 | 2-6 | 0.5-3 | 4-7 | 1-3 | 0.03-1 | 15-25 | 0.1-1 | 0.4-1.0 |
电瓷灰釉修补釉组合物的物理性能:
按照本实施例的组分及重量百分比生产的电瓷灰釉修补釉组合物,上釉后电瓷性能及釉面质量光滑、明亮,色泽白灰清透,无色差。
实施例2:与实施例1基本相同,所不同的是配方,具体如下:钾长石8%,石英40%,氧化硼16%,水洗高岭土12%,滑石10%,石灰石6%,硅酸锆2%;色料6%。
其中色料包括如下组分:氧化锌35%,氧化铬20%,氟化钠15%,氧化钴30%。
实施例3:与实施例1基本相同,所不同的是配方,具体如下:钾长石16%,石英32%,氧化硼24%,水洗高岭土6%,滑石12%,石灰石2%,硅酸锆4%;色料4%。
其中色料包括如下组分:氧化锌25%,氧化铬20%,氟化钠15%,氧化钴40%。
实施例4:与实施例1基本相同,所不同的是配方,具体如下:钾长石10%,石英32%,氧化硼20%,水洗高岭土10%,滑石4%,石灰石8%,硅酸锆6%;色料10%。
其中色料包括如下组分:氧化锌55%,氧化铬4%,氟化钠11%,氧化钴30%。
实施例5:与实施例1基本相同,所不同的是配方,具体如下:钾长石11%,石英35%,氧化硼20%,水洗高岭土14%,滑石4%,石灰石10%,硅酸锆2%;色料4%。
其中色料包括如下组分:氧化锌35%,氧化铬15%,氟化钠5%,氧化钴45%。
本发明按照上述实施例进行了说明应当理解,上述实施例不以任何形式限定本发明,凡采用等同替换或等效变换方式所获得的技术方案,均落在本发明的保护范围之内。
Claims (3)
1.一种电瓷灰釉修补釉组合物,其特征在于,所述修补釉组合物包括如下重量百分比的原料:钾长石8-16%,石英32-40%,氧化硼16-24%,水洗高岭土6-14%,滑石4-12%,石灰石2-10%,硅酸锆2-6%;色料4-10%;所述的色料为氧化锌、氧化铬、氟化钠、氧化钴的混合物,其中包含如下重量百分比:氧化锌25-55%,氧化铬4-20%,氟化钠5-15%,氧化钴30-45%。
2.根据权利要求1所述的电瓷灰釉修补釉组合物的制备方法,其特征在于,该方法包括如下步骤:
(1)按照色料中各原料的配比进行混合,得到混合物色料,然后将混合物色料经过1100℃高温煅烧,粉碎磨细后得到所述色料;
(2)将色料与其他剩余原料按配好的比例进行湿法球磨,直至料浆细度达到325目筛筛余0.04-0.06%,即得到所述电瓷灰釉修补釉组合物。
3.根据权利要求2所述的电瓷灰釉修补釉组合物的制备方法,其特征在于,将高温煅烧后的色料过325目筛。