CN104060470A - Formula of finishing agent for wool fiber carpet and application thereof - Google Patents
Formula of finishing agent for wool fiber carpet and application thereof Download PDFInfo
- Publication number
- CN104060470A CN104060470A CN201410256398.5A CN201410256398A CN104060470A CN 104060470 A CN104060470 A CN 104060470A CN 201410256398 A CN201410256398 A CN 201410256398A CN 104060470 A CN104060470 A CN 104060470A
- Authority
- CN
- China
- Prior art keywords
- carpet
- finishing agent
- water
- formula
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of spinning, and particularly relates to a formula of a finishing agent for a wool fiber carpet and an application thereof. The formula of the finishing agent for the wool fiber carpet is characterized in that the finishing agent is prepared from an organic silicone softener, an antistatic agent and water; the ratio of the organic silicone softener to the antistatic agent to water in percent is 10-20% to 5-10% to 65-85%. Compared with the prior art, a polymethyl hydrogen polysiloxane structure contains an active hydrogen functional group, so that the polymer can react with a polar group on the fiber in a water medium under the catalytic action of organic metal, and can be subjected to crosslinking on the surface of the fiber or fabric, so as to form a mesh film with a three-dimensional space, thus the fabric has good water repellency and limpness, stearic amide propyl dimethyl-beta-hydroxyethyl ammonium dihydrogen phosphate can be widely applied to the antistatic agent of the fiber, and the finishing agent has a good antistatic effect.
Description
Technical field
The present invention relates to textile technology field, specifically a kind of formula and application thereof of the finishing agent for wool sense fiber carpet.
Background technology
Due to the costliness increasingly of wool carpet, a kind of operation of polyster fibre being utilized to acupuncture of now a lot of manufacturers' product is stung polyster fibre on nonwoven fabric, be made into mat, and therefore carry out the carpet of emulation wool feel, but polyster fibre and wool fibre are differentiated after all, and it is soft like that polyster fibre does not have wool fibre, therefore needs follow-up operation to process and just can reach desirable effect the carpet of polyster fibre.
Summary of the invention
The present invention is for overcoming the deficiencies in the prior art, a kind of finishing agent is provided, softener and antistatic additive are made according to a certain percentage, and process polyster fibre carpet, make to there is the same feel of wool carpet after polyster fibre carpet finished product, and reduce the situation of the static of self, well improved the quality of carpet.
For achieving the above object, design a kind of formula of the finishing agent for wool sense fiber carpet, it is characterized in that: described finishing agent is made up of silicone softening agent, antistatic additive and water, and the percentage of silicone softening agent, antistatic additive and water is 10 ~ 25%:5 ~ 10%:65 ~ 85%.
Adopt above-mentioned formula to be handled as follows step:
(a) in every premium on currency, adding 30 grams of finishing agents fully stirs;
(b) carpet is positioned in finish solution and soaks 15 ~ 20 minutes, and water temperature keeps 60 DEG C;
(c) carpet after soaking is well put into Water Extraction Machinery and dewater, the water retention rate of the carpet after dehydration reaches 20%;
(d) carpet after dehydration is put into dryer and dry, the temperature of oven dry keeps 120 DEG C;
(e) carpet after drying is paved, and by hand the hair on it is made in order with comb.
Described silicone softening agent is poly-methyl hydrogen-containing siloxane.
Described antistatic additive is stearamide propyl dimethyl-beta-hydroxyethyl ammonium dihydrogen orthophosphate.
The present invention compared with the existing technology, in poly-methyl hydrogen-containing siloxane structure, contain active hydrogen functional groups, make this polymer in aqueous medium, under organic metal catalytic action, can react with the polar group on fiber, occur to be cross-linked on the surface of fiber or fabric, form and there is three-dimensional reticulated film, give WATER REPELLENCY and flexibility that fabric is good; Stearamide propyl dimethyl-beta-hydroxyethyl ammonium dihydrogen orthophosphate is widely used in the antistatic additive of fiber, has good antistatic effect.
A kind of finishing agent is provided, softener and antistatic additive are made according to a certain percentage, and processed polyster fibre carpet, make to there is the same feel of wool carpet after polyster fibre carpet finished product, and reduce the situation of the static of self, well improved the quality of carpet.
Detailed description of the invention
Embodiment mono-
Finishing agent is made up of silicone softening agent, antistatic additive and water, and the percentage of silicone softening agent, antistatic additive and water is 10%:5%:85%.
Described silicone softening agent is poly-methyl hydrogen-containing siloxane.
Described antistatic additive is stearamide propyl dimethyl-beta-hydroxyethyl ammonium dihydrogen orthophosphate
Adopt above-mentioned formula to be handled as follows step:
(a) in every premium on currency, adding 30 grams of finishing agents fully stirs;
(b) carpet is positioned in finish solution and soaks 15 ~ 20 minutes, and water temperature keeps 60 DEG C;
(c) carpet after soaking is well put into Water Extraction Machinery and dewater, the water retention rate of the carpet after dehydration reaches 20%;
(d) carpet after dehydration is put into dryer and dry, the temperature of oven dry keeps 120 DEG C;
(e) carpet after drying is paved, and by hand the hair on it is made in order with comb.
Embodiment bis-
Finishing agent is made up of silicone softening agent, antistatic additive and water, and the percentage of silicone softening agent, antistatic additive and water is 25%:10%:65%.
Described silicone softening agent is poly-methyl hydrogen-containing siloxane.
Described antistatic additive is stearamide propyl dimethyl-beta-hydroxyethyl ammonium dihydrogen orthophosphate
Adopt above-mentioned formula to be handled as follows step:
(a) in every premium on currency, adding 30 grams of finishing agents fully stirs;
(b) carpet is positioned in finish solution and soaks 15 ~ 20 minutes, and water temperature keeps 60 DEG C;
(c) carpet after soaking is well put into Water Extraction Machinery and dewater, the water retention rate of the carpet after dehydration reaches 20%;
(d) carpet after dehydration is put into dryer and dry, the temperature of oven dry keeps 120 DEG C;
(e) carpet after drying is paved, and by hand the hair on it is made in order with comb.
Claims (4)
1. for a formula for the finishing agent of wool sense fiber carpet, it is characterized in that: described finishing agent is made up of silicone softening agent, antistatic additive and water, and the percentage of silicone softening agent, antistatic additive and water is 10 ~ 25%:5 ~ 10%:65 ~ 85%.
2. for an application for the finishing agent of wool sense fiber carpet, it is characterized in that adopting the formula described in claim 1 to be handled as follows step:
(a) in every premium on currency, adding 30 grams of finishing agents fully stirs;
(b) carpet is positioned in finish solution and soaks 15 ~ 20 minutes, and water temperature keeps 60 DEG C;
(c) carpet after soaking is well put into Water Extraction Machinery and dewater, the water retention rate of the carpet after dehydration reaches 20%;
(d) carpet after dehydration is put into dryer and dry, the temperature of oven dry keeps 120 DEG C;
(e) carpet after drying is paved, and by hand the hair on it is made in order with comb.
3. the formula of a kind of finishing agent for wool sense fiber carpet according to claim 1, is characterized in that: described silicone softening agent is poly-methyl hydrogen-containing siloxane.
4. the formula of a kind of finishing agent for wool sense fiber carpet according to claim 1, is characterized in that: described antistatic additive is stearamide propyl dimethyl-beta-hydroxyethyl ammonium dihydrogen orthophosphate.