CN104059590A - Room-temperature-curing toughened epoxy resin adhesive and preparation method thereof - Google Patents
Room-temperature-curing toughened epoxy resin adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN104059590A CN104059590A CN201410251510.6A CN201410251510A CN104059590A CN 104059590 A CN104059590 A CN 104059590A CN 201410251510 A CN201410251510 A CN 201410251510A CN 104059590 A CN104059590 A CN 104059590A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- parts
- resin adhesive
- vulcanizing
- self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a room-temperature-curing toughened epoxy resin adhesive and a preparation method thereof, belonging to the field of high polymer materials. The epoxy resin adhesive is prepared from the following raw materials in parts by weight: 40-60 parts of epoxy resin, 30-50 parts of curing agent, 10-20 parts of epoxy polybutadiene, 10-18 parts of dioctyl terephthalate, 3-5 parts of silane coupling agent and 30-50 parts of calcium carbonate. The prepared epoxy resin adhesive can be cured at room temperature, has excellent toughness, and has wide application range. The toughener is added into the room-temperature-curing epoxy resin to perform toughening modification on the epoxy resin, so that the epoxy resin can be well used for preparing various room-temperature-curing epoxy resin adhesives for different techniques and different application targets, and can be better applied to aramid fiber composite materials.
Description
Technical field
The present invention relates to a kind of epoxyn and preparation method thereof, more particularly, the present invention relates to a kind of self-vulcanizing toughened epoxy resin adhesive and preparation method thereof, belong to technical field of polymer materials.
Background technology
Epoxy resin is a kind of thermosetting resin, because having the characteristics such as excellent cementability, physical strength and electrical insulating property, and is widely used in the aspects such as tackiness agent, high-performance-light weight fibre reinforced composites, coating and matrices of composite material.In addition, epoxyn is because its good performance is widely used in sqtructural adhesive.But the ability that its obvious fragility and poor weathering resistance, resistance to fatigue, thermotolerance, water absorbability and shock resistance make it bear applied external force under heavily stressed is poor, is its unavoidable shortcoming.Therefore, need to carry out modification to epoxy resin.In addition, because epoxy resin viscosity is higher, to the feature such as the wetting property of aramid fiber is poor, epoxy resin to be performed well in to the preparation of aramid fiber reinforced composite, must carry out necessary modification to epoxy resin, make prepared aramid fiber/epoxy resin composite material there is best over-all properties.
It is CN101157835 that State Intellectual Property Office discloses a publication number in 2008.4.9, name is called the patent of invention of " a kind of modified epoxide resin adhesive and application thereof ", the tackiness agent that this patent provides a kind of effectively fixing spring, makes spring be not easy to come off from spring groove.The present invention provides the application of this tackiness agent aspect fixing spring simultaneously.Modified epoxide resin adhesive of the present invention, comprises the component of following mass parts: epoxy resin 100; Poly-sulphur glue 50 ~ 200; White carbon black 5 ~ 15; Coupling agent 1 ~ 5; Amine curing agent 2 ~ 10.Compared with ordinary epoxy resin: the present invention adopts thiorubber to carry out modification to epoxy resin, it is a kind of toughness reinforcing method of reactive liquid polymerization, after thiorubber mixes with epoxy resin, thiol group and epoxy group(ing) in poly-sulphur glue react, identify oneself with in curing epoxy resin structural, give the snappiness that epoxy resin is good.Therefore modified epoxide resin adhesive of the present invention effectively fixing spring, make spring be not easy to come off from spring groove, kept again other effective performances of epoxy resin simultaneously.
Epoxyn in above-mentioned patent has certain snappiness, but over-all properties is not good, cannot be advantageously applied to aramid fiber reinforced composite.
Summary of the invention
The present invention is intended to solve the problems of the technologies described above, and a kind of self-vulcanizing toughened epoxy resin adhesive is provided, and improves its over-all properties, can be advantageously applied to aramid fiber reinforced composite.
In order to realize foregoing invention object, its concrete technical scheme is as follows:
A kind of self-vulcanizing toughened epoxy resin adhesive, is characterized in that: comprise following according to the raw material of parts by weight meter:
Epoxy resin 40-60 part
Solidifying agent 30-50 part
Epoxidized polybutadiene 10-20 part
Dioctyl terephthalate 10-18 part
Silane coupling agent 3-5 part
Calcium carbonate 30-50 part.
A kind of self-vulcanizing toughened epoxy resin adhesive, is characterized in that: comprise following according to the raw material of parts by weight meter:
Epoxy resin 45-55 part
Solidifying agent 35-43 part
Epoxidized polybutadiene 12-17 part
Dioctyl terephthalate 11-15 part
Silane coupling agent 4-4.5 part
Calcium carbonate 35-40 part.
Epoxy resin of the present invention is E-44 epoxy resin.
Solidifying agent of the present invention is 554 solidifying agent.
Silane coupling agent of the present invention is KH-550 silane coupling agent.
A preparation method for self-vulcanizing toughened epoxy resin adhesive, is characterized in that: comprise following processing step:
A, by formula requirement take epoxy resin, epoxidized polybutadiene, silane coupling agent and calcium carbonate, be uniformly mixed;
B, on two rollers or three-roller, further mix as A component, for subsequent use;
C, by formula requirement take solidifying agent and dioctyl terephthalate, after mixing, obtain B component, for subsequent use;
D, get the B component that A component that step B obtains and step C obtain, mix, under room temperature, solidify, obtain epoxyn.
The useful technique effect that the present invention brings:
The invention solves existing epoxyn over-all properties not good, cannot be advantageously applied to the problem of aramid fiber reinforced composite, epoxyn prepared by the present invention, can self-vulcanizing, has again preferably toughness, has application comparatively widely.This patent carries out toughening modifying by the technological approaches that adds toughner in room temperature curing epoxy to epoxy resin, can be applied to preferably the preparation of various preparation technology's differences, room temperature curing epoxy adhesive that application purpose is different, can be advantageously applied to aramid fiber reinforced composite.
Embodiment
embodiment 1
A kind of self-vulcanizing toughened epoxy resin adhesive, comprises following according to the raw material of parts by weight meter:
40 parts of epoxy resin
30 parts, solidifying agent
10 parts of epoxidized polybutadienes
10 parts of dioctyl terephthalates
3 parts of silane coupling agents
30 parts, calcium carbonate.
embodiment 2
A kind of self-vulcanizing toughened epoxy resin adhesive, comprises following according to the raw material of parts by weight meter:
60 parts of epoxy resin
50 parts, solidifying agent
20 parts of epoxidized polybutadienes
18 parts of dioctyl terephthalates
5 parts of silane coupling agents
50 parts, calcium carbonate.
embodiment 3
A kind of self-vulcanizing toughened epoxy resin adhesive, comprises following according to the raw material of parts by weight meter:
50 parts of epoxy resin
40 parts, solidifying agent
15 parts of epoxidized polybutadienes
14 parts of dioctyl terephthalates
4 parts of silane coupling agents
40 parts, calcium carbonate.
embodiment 4
A kind of self-vulcanizing toughened epoxy resin adhesive, comprises following according to the raw material of parts by weight meter:
46 parts of epoxy resin
33 parts, solidifying agent
19 parts of epoxidized polybutadienes
15 parts of dioctyl terephthalates
3.5 parts of silane coupling agents
48 parts, calcium carbonate.
embodiment 5
A kind of self-vulcanizing toughened epoxy resin adhesive, comprises following according to the raw material of parts by weight meter:
45 parts of epoxy resin
35 parts, solidifying agent
12 parts of epoxidized polybutadienes
11 parts of dioctyl terephthalates
4 parts of silane coupling agents
35 parts, calcium carbonate.
embodiment 6
A kind of self-vulcanizing toughened epoxy resin adhesive, comprises following according to the raw material of parts by weight meter:
55 parts of epoxy resin
43 parts, solidifying agent
17 parts of epoxidized polybutadienes
15 parts of dioctyl terephthalates
4.5 parts of silane coupling agents
40 parts, calcium carbonate.
embodiment 7
A kind of self-vulcanizing toughened epoxy resin adhesive, comprises following according to the raw material of parts by weight meter:
50 parts of epoxy resin
39 parts, solidifying agent
14.5 parts of epoxidized polybutadienes
13 parts of dioctyl terephthalates
4.25 parts of silane coupling agents
37.5 parts, calcium carbonate.
embodiment 8
A kind of self-vulcanizing toughened epoxy resin adhesive, comprises following according to the raw material of parts by weight meter:
47 parts of epoxy resin
36 parts, solidifying agent
16.5 parts of epoxidized polybutadienes
14.5 parts of dioctyl terephthalates
4.2 parts of silane coupling agents
38 parts, calcium carbonate.
embodiment 9
On the basis of embodiment 1-9, preferred:
Described epoxy resin is E-44 epoxy resin.
Described solidifying agent is 554 solidifying agent.
Described silane coupling agent is KH-550 silane coupling agent.
embodiment 10
A preparation method for self-vulcanizing toughened epoxy resin adhesive, comprises following processing step:
A, by formula requirement take epoxy resin, epoxidized polybutadiene, silane coupling agent and calcium carbonate, be uniformly mixed;
B, on two rollers or three-roller, further mix as A component, for subsequent use;
C, by formula requirement take solidifying agent and dioctyl terephthalate, after mixing, obtain B component, for subsequent use;
D, get the B component that A component that step B obtains and step C obtain, mix, under room temperature, solidify, obtain epoxyn.
Claims (6)
1. a self-vulcanizing toughened epoxy resin adhesive, is characterized in that: comprise following according to the raw material of parts by weight meter:
Epoxy resin 40-60 part
Solidifying agent 30-50 part
Epoxidized polybutadiene 10-20 part
Dioctyl terephthalate 10-18 part
Silane coupling agent 3-5 part
Calcium carbonate 30-50 part.
2. a kind of self-vulcanizing toughened epoxy resin adhesive according to claim 1, is characterized in that: comprise following according to the raw material of parts by weight meter:
Epoxy resin 45-55 part
Solidifying agent 35-43 part
Epoxidized polybutadiene 12-17 part
Dioctyl terephthalate 11-15 part
Silane coupling agent 4-4.5 part
Calcium carbonate 35-40 part.
3. a kind of self-vulcanizing toughened epoxy resin adhesive according to claim 1 and 2, is characterized in that: described epoxy resin is E-44 epoxy resin.
4. a kind of self-vulcanizing toughened epoxy resin adhesive according to claim 1 and 2, is characterized in that: described solidifying agent is 554 solidifying agent.
5. a kind of self-vulcanizing toughened epoxy resin adhesive according to claim 1 and 2, is characterized in that: described silane coupling agent is KH-550 silane coupling agent.
6. the preparation method of a kind of self-vulcanizing toughened epoxy resin adhesive according to claim 1 and 2, is characterized in that: comprise following processing step:
A, by formula requirement take epoxy resin, epoxidized polybutadiene, silane coupling agent and calcium carbonate, be uniformly mixed;
B, on two rollers or three-roller, further mix as A component, for subsequent use;
C, by formula requirement take solidifying agent and dioctyl terephthalate, after mixing, obtain B component, for subsequent use;
D, get the B component that A component that step B obtains and step C obtain, mix, under room temperature, solidify, obtain epoxyn.