CN104059252A - Rubber resisting thermal ageing - Google Patents
Rubber resisting thermal ageing Download PDFInfo
- Publication number
- CN104059252A CN104059252A CN201410291283.XA CN201410291283A CN104059252A CN 104059252 A CN104059252 A CN 104059252A CN 201410291283 A CN201410291283 A CN 201410291283A CN 104059252 A CN104059252 A CN 104059252A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- thermal ageing
- resistant performance
- ageing resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of rubbers, and particularly relates to a rubber resisting thermal ageing. The rubber resisting thermal ageing comprises the following components in parts by weight: 80-220 parts of natural rubber, 50-220 parts of hydrogenated acrylonitrile butadiene rubber, 3-10 parts of nano zinc oxide, 2-4 parts of sodium stearate, 15-65 parts of carbon black N100, 5-12 parts of a softener, 5-15 parts of reinforcing powder, 5-10 parts of sulphur, 2-5 parts of an antiager, 2-8 parts of calcium carbonate, 2-6 parts of a tackifier, 2-5 parts of naphthenic oil, 2-5 parts of white carbon black, 2-5 parts of a scorch retarder, 2-4 parts of phthalic acid dibutyl ester, 2-4 parts of diethyl dithiocarbamic acid, 2-4 parts of 2-thiol imidazoline, and 2-10 parts of a plasticizer. Compared with common rubber, the rubber resisting thermal ageing has the beneficial effects of good thermal ageing resistance and dynamic fatigue resistance, and is used as rubber products in fatigue state for long.
Description
Technical field
The present invention relates to a kind of rubber with thermal ageing resistant performance, belong to rubber materials.
Background technology
When rubber is taken on alternative cycle stress or strain, caused local structure changes and the growth process of subsurface defect, is called the fatigue of rubber.Under dynamic tensile, compression, distortion and shearing action, the performance of rubber item and structure can produce and change or damage, and this is so-called tired breaking-up.It reduces the mechanical property of material, and finally causes be full of cracks or fracture completely.The tired essence of rubber is that aging presentation occurs the stressed and hot used time rubber of doing, and has covered flexing fatigue and aging fatigue.It is a lot of to there is tired condition in rubber, and analogy is extended or compression; Periodic External Force Acting etc.Fatigue-resisting rubber we daily life and industrial production in be widely used, there is high practical value.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of rubber with thermal ageing resistant performance.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of rubber with thermal ageing resistant performance, this rubber with thermal ageing resistant performance comprises the component of following portions by weight: natural rubber 80-220 part, hydrogenated nitrile-butadiene rubber 50-220 part, nano zine oxide 3-10 part, sodium stearate 2-4 part, carbon black N10015-65 part, tenderizer 5-12 part, strengthening powder 5-15 part, sulphur 5-10 part, anti-aging agent 2-5 part, calcium carbonate 2-8 part, tackifier 2-6 part, naphthenic oil 2-5 part, white carbon black 2-5 part, scorch retarder 2-5 part, dibutyl phthalate 2-4 part, zinc diethyldithiocarbamate 2-4 part, 2-thiol group tetrahydroglyoxaline 2-4 part, softening agent 2-10 part.
Preferably, above-mentioned conductive rubber comprises the component of following portions by weight:
Natural rubber 40-80 part silicon rubber 40-90 part
Nano zine oxide 2-9 part conductive particle 1-4 part
Carbon black N300 15-45 part electrically conductive graphite 2-5 part
Coumarone indene resin 4-13 part Sulfur 2-9 part
Anti-aging agent 1-5 part rosin 1-5 part
Hydroxy silicon oil 1-6 part vulcanizing agent 1-5 part
White carbon black 1-5 part dimethyl silicone oil 1-5 part
Tetramethylthiuram monosulfide 0.5-2 part 4,4 '-dithio morpholine 0.5-2 part
The N-tertiary butyl-2 benzothiazole sulphenamide 0.5-2 part.
Above-mentioned natural rubber is at least one in rubber smoked sheet, white crepe, pearl glue, the clear crepe of glue, chlorinated natural rubber, hydrochlorinate natural rubber, epoxy natural rubber, guayule, gutta-percha, Ba Lata glue, gutta-percha, Qi Geer glue, the logical glue of gill.
Above-mentioned anti-aging agent is 6-oxyethyl group-2,2,4-trimethylammonium-1,2 dihyaroquinolines, 2,2,4-trimethylammonium 1, at least one in 2-dihydro quinoline polymer, diaryl secondary amine antioxidant, Ursol D class.
Above-mentioned anti-aging agent is at least one of N-phenyl-α-aniline, N-phenyl-N '-sec.-propyl-Ursol D, N-N '-phenylbenzene-Ursol D, antioxidant 4020.
Above-mentioned anti-aging agent is N-phenyl-α-aniline, N-N '-phenylbenzene-Ursol D, and both ratios of weight and number are 1-3:1.
Above-mentioned anti-aging agent is N-phenyl-α-aniline, N-N '-phenylbenzene-Ursol D, and both ratios of weight and number are 2:1.
Above-mentioned process oil is naphthenic oil and aromatic hydrocarbon oil.
Above-mentioned tenderizer is at least one in ointment, stearic acid, oleic acid;
Softening agent is any in dioctyl phthalate (DOP), dibutyl phthalate, Tritolyl Phosphate, trioctyl phosphate, dioctyl sebacate, Octyl adipate.
According to antifatigue physical disturbance, can utilize tenderizer or softening agent control fatigue of materials weathering process, from the power-chemical theory of fatigue aging, add tenderizer and softening agent can make rubber molecule mobility strengthen, stress relaxation is accelerated, stress activation-deterioration by oxidation habituation, material antifatigue aging improves.
The selected tenderizer of the present invention can increase plasticity, mobility, is convenient to processing; Reduce the viscosity of melting temperature and sizing material, be conducive to Synergist S-421 95 and disperse, reach energy-conservation object; Can also make elongation, the rebound resilience of cross-linked rubber improve, low-temperature performance is good, and heat-dissipating is little; Except above-mentioned effect, the resistance to fatigue of all right Reinforced Rubber.
In the present invention, add suitable tenderizer and softening agent, can improve the antifatigue life-span of rubber, this can not simply from strengthening rubber molecule mobility, this explains on the one hand, but because softening agent is distributed in supramolecular structure interfacial layer, has improved rubber molecule mobility and caused.
The fatigure failure of material occurs under long-time loop cycle, in its fatigue process, inevitably to contact with oxygen, ozone, ultraviolet ray, microorganism and corrosive deposit etc., thereby because of the antifatigue destructive characteristics of aging or infection material, therefore in rubber components, add suitable anti-aging agent can effectively reduce the destruction to sizing material fatigue performance such as oxygen, ozone, light and heat.Different anti-aging agent prevents the chemical degradation reaction of sizing material by different protective mechanisms; Wax can migrate to sizing material surface; between objectionable impurities in rubber and environment, form one deck physical protection film; other anti-aging agent by directly with cause degradation material or with other, necessary material generation of DeR chemical reaction occur, thereby the protective effect of playing.
Beneficial effect of the present invention is, rubber of the present invention and common rubber phase ratio, have good heat-proof aging, anti-dynamic fatigue property, can be used as needing the long-time rubber item in fatigue state.
Embodiment
Embodiment 1
120 parts of 150 parts of hydrogenated nitrile-butadiene rubbers of rubber smoked sheet
2 parts of 6 parts of sodium stearate of nano zine oxide
7 parts of 25 parts of ointment of carbon black N100
6 parts, 12 parts of sulphur of strengthening powder
6 parts, 4 parts of calcium carbonate of N-phenyl-α-aniline
4 parts of 5 parts of naphthenic oils of cobalt naphthenate
4 parts of 3 parts of scorch retarder of white carbon black
3 parts of 3 parts of zinc diethyldithiocarbamates of dibutyl phthalate
7 parts of 3 parts of dibutyl phthalates of 2-thiol group tetrahydroglyoxaline.
2 parts of embodiment
50 parts of 80 parts of hydrogenated nitrile-butadiene rubbers of epoxy natural rubber
1 part of 2 parts of sodium stearate of nano zine oxide
2 parts of 15 parts of stearic acid of carbon black N100
2 parts, 4 parts of sulphur of strengthening powder
6-oxyethyl group-2,2,4-trimethylammonium-1,21 part of dihyaroquinoline
1 part, calcium carbonate
1 part of 1 part of naphthenic oil of titanate coupling agent
1 part of 1 part of scorch retarder of white carbon black
1 part of 1 part of zinc diethyldithiocarbamate of dibutyl phthalate
1 part of 1 part of Octyl adipate of 2-thiol group tetrahydroglyoxaline.
Certain above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example, those skilled in the art, and in essential scope of the present invention, variation, change, interpolation or the replacement made, all should belong to protection scope of the present invention.
Claims (6)
1. one kind has the rubber of thermal ageing resistant performance, it is characterized in that, the described rubber with thermal ageing resistant performance comprises the component of following portions by weight: natural rubber 80-220 part, hydrogenated nitrile-butadiene rubber 50-220 part, nano zine oxide 3-10 part, sodium stearate 2-4 part, carbon black N10015-65 part, tenderizer 5-12 part, strengthening powder 5-15 part, sulphur 5-10 part, anti-aging agent 2-5 part, calcium carbonate 2-8 part, tackifier 2-6 part, naphthenic oil 2-5 part, white carbon black 2-5 part, scorch retarder 2-5 part, dibutyl phthalate 2-4 part, zinc diethyldithiocarbamate 2-4 part, 2-thiol group tetrahydroglyoxaline 2-4 part, softening agent 2-10 part.
2. a kind of rubber with thermal ageing resistant performance as claimed in claim 1, it is characterized in that, described natural rubber is at least one in rubber smoked sheet, white crepe, pearl glue, the clear crepe of glue, chlorinated natural rubber, hydrochlorinate natural rubber, epoxy natural rubber, guayule, gutta-percha, Ba Lata glue, gutta-percha, Qi Geer glue, the logical glue of gill.
3. a kind of rubber with thermal ageing resistant performance as claimed in claim 1, it is characterized in that, described anti-aging agent is 6-oxyethyl group-2,2,4-trimethylammonium-1,2 dihyaroquinolines, 2,2,4-trimethylammonium 1, at least one in 2-dihydro quinoline polymer, diaryl secondary amine antioxidant, Ursol D class.
4. a kind of rubber with thermal ageing resistant performance as claimed in claim 1, it is characterized in that, described anti-aging agent is at least one of N-phenyl-α-aniline, N-phenyl-N '-sec.-propyl-Ursol D, N-N '-phenylbenzene-Ursol D, antioxidant 4020.
5. a kind of rubber with thermal ageing resistant performance as claimed in claim 1, is characterized in that, described anti-aging agent is N-phenyl-α-aniline, N-N '-phenylbenzene-Ursol D, and both ratios of weight and number are 1-3:1.
6. a kind of rubber with thermal ageing resistant performance as claimed in claim 3, is characterized in that, described anti-aging agent is N-phenyl-α-aniline, N-N '-phenylbenzene-Ursol D, and both ratios of weight and number are 2:1.