CN104059207A - Acrylic acid and polyactic acid (PAA) contained functional polymer material - Google Patents
Acrylic acid and polyactic acid (PAA) contained functional polymer material Download PDFInfo
- Publication number
- CN104059207A CN104059207A CN201410321031.7A CN201410321031A CN104059207A CN 104059207 A CN104059207 A CN 104059207A CN 201410321031 A CN201410321031 A CN 201410321031A CN 104059207 A CN104059207 A CN 104059207A
- Authority
- CN
- China
- Prior art keywords
- lactic acid
- paa
- poly
- star
- pla
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an acrylic acid and polyactic acid (PAA) contained functional polymer material which is prepared through the following steps of with L-lactide as a raw material, synthesizing three-arm or multi-arm star-shaped polylactic acid (PLA) by using a classical stannous octoate catalyzed ring-opening method, and due to the existence of hydroxyl at the terminal of a polymer, enabling three-arm or multi-arm star-shaped PLA to react with bromoisobutyryl bromide in ice bath to obtain a star-shaped macroinitiator SPLA-Br of a bromo-terminal functional group; carrying out ring opening polymerization on the macroinitiator and AA (Acrylic Acid) according to a certain ratio to obtain a star-shaped PAA block polymer with PLA as a core, then, adding N-isopropylacrylamide, and carrying out ATRP (Atom Transfer Radical Polymerization) to obtain a triblock copolymer; adding PAA with low-molecular weight, and dissolving the PAA with water by means of the amphipathicity of the block copolymer to form a nanoporous material. The block copolymer is of a hexagonal prism shaped structure, contains PLA as a continuous phase and is provided with nano-grade micropores. The material has the advantages that the material is provided with the nano-grade micropores; the defect of poor processability of the traditional linear PLA material is overcome; no toxic or side effect is generated; the material can be used as a drug carrier material, a medical implant material and an in-vivo continuous dosing device part material.
Description
Affiliated technical field
The present invention relates to a kind of degradable poly lactate material, particularly relate to a kind of preparation method with nanometer level microporous block macromolecular material.Belong to polymer chemistry and technical field of polymer.
Background technology
Poly(lactic acid) (Polylactic acid, PLA) be that a new generation of developing rapidly the nineties in 20th century can degradable macromolecular material, it has good biocompatibility, class bio-medical material and environment-friendly materials of food and drug administration (Food and Drug Adiministration, FDA) accreditation.From the sixties in 20th century, scientific worker starts to pay close attention to the degradation property of poly-lactic acid material, and first using poly-lactic acid material as degradable operation stitching wire material.1966, (the Kricheldorf H. R. such as Kulkarni
chemospherein 2001,43,49-54., propose first: low-molecular-weight PLA can degradation in vivo, and final meta-bolites is CO
2and H
2o, harmless, environmentally safe.Simultaneously, find by the research to poly(lactic acid) vivo degradation process, the intermediate product lactic acid of degraded is the product of eubolism in body, can not accumulate in vivo, therefore PLA can not produce detrimentally affect to organism after degrading in vivo, has caused thus the beginning using this class material as bio-medical material.In recent years, it in medicine sustained and controlled release system, has more and more received the concern of scientists as pharmaceutical carrier.
But common line style poly(lactic acid) (Linear polylactic acid, LPLA) there are some shortcomings, for example its solution and bulk viscosity are higher, degree of crystallinity is large, material fragility is high, thermostability is low and low degradation speed, limit to a certain extent its widespread use in fields such as medical, agricultural and packagings, particularly at the application aspect Thermosensitive Material Used for Controlled Releasing of Medicine (Wang L., Dong C. M.
j. Polym. Sci. Part A:Polym. Chem.2006,44 (7), 2226-2236.).Star-like poly(lactic acid) (Star-shaped polylactic acids, SPLA) there is the short and molecular weight advantages of higher of side chain, its solution and bulk viscosity are more much lower than same molecular amount LPLA, mobility and solubility property improve, and its degradation speed is but fast than same molecular amount LPLA, thermostability is higher, is conducive to its processed and applied in the bio-medical materials such as medicament slow release.
No matter although line style or star-like poly-lactic acid material have been widely used in Thermosensitive Material Used for Controlled Releasing of Medicine and tissue engineering material aspect, but due to the restriction of himself hydrophobic structure, also part comes with some shortcomings, for example its wetting ability is not good, degradation rate is slower, degradation cycle is difficult to regulation and control, and implant inner posterior quadrant easily adheres to material surface etc.Scientists has been carried out the research of the modification of structure aspects to PLA material for these problems.In order to increase the wetting ability of PLA, common material modified have polyoxyethylene glycol (Polyethylene glycol, PEG) (Moffatt S., Cristiano R.
j. Int. J. Pharm.2006,317,10-13.), polyvinyl alcohol (Poly vinyl alcohol, PVA), dextran (dextran), chitosan and polypeptide (polypeptide) etc.Because polypeptide (also referred to as polyamino acid) is the biodegradable polymer of a class, have low toxicity, good biocompatibility, biodegradable, easily absorbed by body and the advantage such as metabolism, Amino Acid Unit structure can be selected, hydrophilicity and hydrophobicity is adjustable, started to be applied in the study on the modification of poly(lactic acid), but only had little report.
On the other hand, multiporous biological degradable material is the brand-new material system that development in recent years is got up, and is a kind of material with network structure being made up of mutual perforation or blind hole hole, and the border of hole or surface are made up of pillar or flat board.It has regularly arranged and big or small adjustable pore passage structure, relative density is low, specific tenacity is high, porosity and surface-area large, perviousness and excellent adsorption and good biocompatibility, the features such as environmental friendliness, in bulky molecular catalysis, absorption and separate, the field such as nanomaterial assembly, biological chemistry, molecular recognition and pharmaceutical carrier is all with a wide range of applications.To the consulting of documents and materials, also there is no so far that a kind of poly-lactic acid material has that processing characteristics is high simultaneously, the feature such as wetting ability, good biodegradability, nanometer level microporous, high Drug loading capacity by us.
Summary of the invention
The object of the invention is to set up a kind of preparation method of degradable multiporous poly(lactic acid), this polymer materials has the following advantages: good processability, wetting ability, good biodegradability, nanometer level microporous, high Drug loading capacity.
This poly-lactic acid material is a kind of star-like poly(lactic acid)/PAA segmented copolymer; Taking L-rac-Lactide as raw material, utilize stannous octoate catalysis open loop method to synthesize three arm poly(lactic acid); Prepare macromole evocating agent; Carry out atom transfer radical polymerization with vinylformic acid (AA) and obtain the star block copolymer taking PLA as core PAA as arm, then add NIPA, again carry out ATRP polymerization, obtain triblock copolymer; Add lower molecular weight PAA, utilize the amphiphilic water of segmented copolymer to be dissolved, form nanoscale porous material.
The technology of preparing scheme of porous poly-lactic acid material is as follows:
1) star-like poly(lactic acid) is synthetic
2) macromole evocating agent is synthetic
3) preparation of star block copolymer
By above technical scheme, tool of the present invention has the following advantages: 1) degradable multiporous poly(lactic acid) has nano micropore structure capable;
2) degradable multiporous poly(lactic acid) has hexagonal columnar structure;
3) degradable multiporous poly(lactic acid) has high drug loading amount, and good biocompatibility;
4) degradable multiporous poly(lactic acid) has pharmaceutical carrier function and discharges pharmic function, can effectively reduce medicine normal tissue organ toxic side effect.
Brief description of the drawings
Fig. 1 is the vesicular structure schematic diagram of this polymer materials;
Fig. 2 is the electron photomicrograph of this polymer materials.
Embodiment
Provide embodiment below so that the present invention is specifically described; but it is worthy of note that following examples are only used to further illustrate the present invention; can not be interpreted as limiting the scope of the invention, some nonessential improvement that the person skilled in the art in this field makes the present invention according to the invention described above content and adjustment still belong to protection scope of the present invention.
Embodiment 1:
1. prepare star block copolymer
Taking L-rac-Lactide as raw material, utilize classical stannous octoate catalysis open loop method to synthesize three arms or multi-arm star-shaped poly(lactic acid), due to the existence of the hydroxyl of polymer ends, react in ice territory with bromo isobutyl acylbromide, obtain the star-like macromole evocating agent SPLA-Br of bromine terminal functionality.Macromole evocating agent and AA are carried out to ATRP polymerization by a certain percentage, obtain the star block copolymer taking PLA as core PAA.
2. the sign of star block copolymer material self-assembled structures and performance
The chemical structure of polymkeric substance and shape characteristic are the bases of the every character of Study Polymer Melts.This problem intends utilizing gel permeation chromatography (GPC), Fourier transform infrared spectroscopy (FTIR) and nucleus magnetic resonance (NMR) method detect chemical structure and the polymerization degree of polymkeric substance, utilize thermogravimetric analyzer (TGA) to study the thermal characteristics of polymkeric substance, the transformation mutually, the liquid crystal behavior that use differential scanning calorimeter (DSC) research segmented copolymer, utilize one dimension, two-dimentional wide-angle x-ray diffraction instrument (WAXD) to determine the phase structure of each segment in segmented copolymer.The star block copolymer proposing in this problem more easily forms micro phase separation structure, can utilize atomic force microscope (AFM) and transmission electron microscope (TEM) to observe the self-assembled structures of star block copolymer at substrate surface, utilize little angle one dimension, two-dimentional x-ray diffractometer (SAXS) to study the micro phase separation structure of star block copolymer.
3. the preparation of porous material
Obtain after required poly(lactic acid)/PAA star block copolymer, we will observe its body self-assembly behavior, mainly study its micro phase separation structure.Because the body microphase-separated self-assembled structures of segmented copolymer is relevant with the relative proportion of composition component, by research block component the phase of the factor such as content, molecular weight on micro phase separation structure and the impact of size, we can determine may be applicable segmented copolymer to carry out aftertreatment.Particularly for the segmented copolymer that forms (six sides) column phase or co-continuous double helix phase, when material forms nano pore, and micro phase separation structure is arranged when even, material is higher for the release efficiency of medicine, during as embedded material and the contact area of body fluid increase, be conducive to improve the degradation speed of material.We as the impact on material micro phase separation structure such as solvent species, solvent evaporates speed, make the PAA block in polymkeric substance outside form column or double-spiral structure to obtain top condition research material preparation condition.
The synthetic PLA-b-PAA star block copolymer obtaining in a certain amount of lower molecular weight PAA homopolymer and above-mentioned route is carried out to blend, can obtain the hexagonal columnar phase micro phase separation structure that we need, phase structure can be by the confirmation such as low-angle scattering of X-rays and high-resolution electron microscope.The phase of composition etc. by research blend on micro phase separation structure and the impact of size, we can select suitable blend to carry out aftertreatment.On the other hand, if multipolymer forms co-continuous double helix phase, also may be used as porous material.Then we,, by having the film water treatment of column phase or co-continuous double helix phase structure, dissolve PGA homopolymer, just obtain the star-like polylactic acid modified porous material containing hydrophilic nano duct, can be used as the carrier of pharmaceutical model compound.
4. porous star block copolymer is as the research of pharmaceutical carrier
This experiment is intended by existence form and the concentration of steady-state fluorescence spectral characterization and mensuration pyrene, with prove this based block copolymer whether can be in water solution system stable micro-molecular compound, and then discharge in EPC liposome, thereby explore the potential application of this type of macromolecular material as pharmaceutical carrier from the complex body of high-molecular block copolymer-pyrene.Main employing steady-state fluorescence spectroscopic analysis: the spectrum of all samples all records by right angle light path in 4 mL cuvettes.The spectrum of solid-state pyrene crystal is measured by solid support.While doing fluorescence emission spectrum mensuration, emission spectrum wavelength region is 350~650 nm, and excitation wavelength is 336 nm.Excitation spectrum records at emission wavelength 374 nm and 470 nm that represent pyrene monomer and excimer transmitting respectively.All scanning exciting light slits are made as 5 nm, and utilizing emitted light slit is made as 2.5 nm, and PMT voltage is all made as 400 volts, and sweep velocity is 240 nm/min, and spectrum correction is all made as the wavelength dependency of opening to eliminate grating and monitor response.Each Sample Scan is averaged for three times.Be determined at 25
ounder C, carry out.
Finally it should be noted that, above embodiment is only unrestricted in order to technical scheme of the present invention to be described, although the present invention is had been described in detail with reference to preferred embodiment, those of ordinary skill in the art should understand, can a point technical scheme for invention be modified or be replaced on an equal basis, and not departing from the spirit and scope of technical solution of the present invention, it all should be encompassed in the middle of claim scope of the present invention.
Claims (7)
1. a degradable multiporous poly(lactic acid), its constitutional features is: described macromolecular material is the star-like type multipolymer being formed by hydrophobicity polylactic acid chain segment and the coupling of wetting ability PAA segment.
2. a method of preparing degradable multiporous poly(lactic acid) claimed in claim 1 is carried out as follows:
1), taking L-rac-Lactide as raw material, utilize stannous octoate catalysis open loop method to synthesize three arm poly(lactic acid);
2) prepare macromole evocating agent;
3) carry out by a certain percentage ATRP polymerization with AA, obtain the star block copolymer taking PLA as core PAA;
4) add lower molecular weight PAA, utilize the amphiphilic water of segmented copolymer to be dissolved, form nanoscale porous material.
3. the preparation method of a kind of degradable multiporous poly(lactic acid) according to claim 2, is characterized in that the catalyzer that in aforesaid method, star-type polymer that step 1) is closed uses is stannous octoate.
4. the preparation method of a kind of degradable multiporous poly(lactic acid) according to claim 2, is further characterized in that the polymerization single polymerization monomer that in aforesaid method, step 3) is used is AA.
5. the preparation method of a kind of degradable multiporous poly(lactic acid) according to claim 2, is further characterized in that in the ring-opening polymerization that in aforesaid method, step 3) is carried out and uses isobutyl bromide to carry out polyreaction as initiator.
6. the degradable multiporous poly(lactic acid) of one according to claim 2, is further characterized in that: this macromolecular material is the porous material that poly(lactic acid) and PAA form.
7. the degradable multiporous poly(lactic acid) of one according to claim 2, is further characterized in that: described porous polymer materials has hexagonal columnar structure clearly.