CN104058791A - Special metal glaze for ceramic - Google Patents
Special metal glaze for ceramic Download PDFInfo
- Publication number
- CN104058791A CN104058791A CN201410305897.9A CN201410305897A CN104058791A CN 104058791 A CN104058791 A CN 104058791A CN 201410305897 A CN201410305897 A CN 201410305897A CN 104058791 A CN104058791 A CN 104058791A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal glaze
- nano
- glaze
- ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses special metal glaze for ceramic. The special metal glaze comprises 30-50 parts of zinc silicates, 30-60 parts of brown iron ore, 20-30 parts of nanometer zinc oxide, 20-30 parts of nanocrystalline iron oxide, 15-25 parts of silicon dioxide, 5-10 parts of calcium hydroxide, 10-20 parts of sodium sulfate, 10-20 parts of phosphorus pentoxide and 15-30 parts of piperonyl butoxide. The special metal glaze for the ceramic has the advantages of being high in smoothness, good in glaze quality, high in brightness and attractiveness and the like and can meet the high requirement and standard for high brightness of people.
Description
Technical field
The present invention relates to a kind of technical field of ceramic metal glaze, relate in particular to a kind of pottery special and there is the ceramic metal glaze of altitude response.
Background technology
Pottery smooth surface, wear resisting property is good, but the ceramic luminance brightness of prior art is general, along with the raising of people's living standard, people are not meeting existing ceramic luminance brightness, therefore, necessary on the basis of prior art, a kind of glaze of research and development design is smooth, enamel is good, especially luminance brightness is high, and aesthetics is good, can meet the highlighted ceramic glaze of high request standard.
Summary of the invention
The object of the invention is the shortcoming in order to overcome above-mentioned prior art, provide a kind of pottery special ceramic metal glaze, the special ceramic metal glaze of this pottery has that glaze slickness is good, enamel is good, especially high brightness is high, the advantages such as aesthetics is good, can meet the highlighted ceramic metal glaze of people's high request standard.
The technical solution adopted for the present invention to solve the technical problems is: the ceramic metal glaze that a kind of pottery is special, is made up of the feed composition of following umber: 30-50 part zinc silicate, 30-60 part limonite, 20-30 part nano zine oxide, 20-30 part nano-sized iron oxide, 15-25 part silicon-dioxide, 5-10 part calcium hydroxide, 10-20 part sodium sulfate, 10-20 part Vanadium Pentoxide in FLAKES, 15-30 part piperonyl butoxide.
Further, the umber of each feed composition is: 30 parts of zinc silicates, 30 parts of limonites, 20 parts of nano zine oxides, 20 parts of nano-sized iron oxides, 15 parts of silicon-dioxide, 5 parts of calcium hydroxides, 10 parts of sodium sulfate, 10 parts of Vanadium Pentoxide in FLAKESs, 15 parts of piperonyl butoxides.
Or the umber of each feed composition is: 50 parts of zinc silicates, 60 parts of limonites, 30 parts of nano zine oxides, 30 parts of nano-sized iron oxides, 25 parts of silicon-dioxide, 10 parts of calcium hydroxides, 20 parts of sodium sulfate, 20 parts of Vanadium Pentoxide in FLAKESs, 30 parts of piperonyl butoxides.
In sum, the special ceramic metal glaze of pottery of the present invention has the advantages such as glaze slickness is good, enamel is good, and especially high brightness is high, and aesthetics is good, can meet the highlighted ceramic metal glaze of people's high request standard.
Embodiment
Embodiment 1
The ceramic metal glaze that the described a kind of pottery of the present embodiment 1 is special, is made up of the feed composition of following umber: 30 parts of zinc silicates, 30 parts of limonites, 20 parts of nano zine oxides, 20 parts of nano-sized iron oxides, 15 parts of silicon-dioxide, 5 parts of calcium hydroxides, 10 parts of sodium sulfate, 10 parts of Vanadium Pentoxide in FLAKESs, 15 parts of piperonyl butoxides.
Embodiment 2
The ceramic metal glaze that the described a kind of pottery of the present embodiment 2 is special, is made up of the feed composition of following umber: 50 parts of zinc silicates, 60 parts of limonites, 30 parts of nano zine oxides, 30 parts of nano-sized iron oxides, 25 parts of silicon-dioxide, 10 parts of calcium hydroxides, 20 parts of sodium sulfate, 20 parts of Vanadium Pentoxide in FLAKESs, 30 parts of piperonyl butoxides.
The above, be only preferred embodiment of the present invention, not technical scheme of the present invention done to any pro forma restriction.Any simple modification, equivalent variations and modification that every foundation technical spirit of the present invention is done above embodiment, all still belong in the scope of technical scheme of the present invention.
Claims (3)
1. the ceramic metal glaze that pottery is special, it is characterized in that, formed by the feed composition of following umber: 30-50 part zinc silicate, 30-60 part limonite, 20-30 part nano zine oxide, 20-30 part nano-sized iron oxide, 15-25 part silicon-dioxide, 5-10 part calcium hydroxide, 10-20 part sodium sulfate, 10-20 part Vanadium Pentoxide in FLAKES, 15-30 part piperonyl butoxide.
2. the special ceramic metal glaze of a kind of pottery according to claim 1, it is characterized in that, the umber of each feed composition is: 30 parts of zinc silicates, 30 parts of limonites, 20 parts of nano zine oxides, 20 parts of nano-sized iron oxides, 15 parts of silicon-dioxide, 5 parts of calcium hydroxides, 10 parts of sodium sulfate, 10 parts of Vanadium Pentoxide in FLAKESs, 15 parts of piperonyl butoxides.
3. the special ceramic metal glaze of a kind of pottery according to claim 1, it is characterized in that, the umber of each feed composition is: 50 parts of zinc silicates, 60 parts of limonites, 30 parts of nano zine oxides, 30 parts of nano-sized iron oxides, 25 parts of silicon-dioxide, 10 parts of calcium hydroxides, 20 parts of sodium sulfate, 20 parts of Vanadium Pentoxide in FLAKESs, 30 parts of piperonyl butoxides.