CN104047099B - The production technology of health blended knitted fabric - Google Patents
The production technology of health blended knitted fabric Download PDFInfo
- Publication number
- CN104047099B CN104047099B CN201410286870.XA CN201410286870A CN104047099B CN 104047099 B CN104047099 B CN 104047099B CN 201410286870 A CN201410286870 A CN 201410286870A CN 104047099 B CN104047099 B CN 104047099B
- Authority
- CN
- China
- Prior art keywords
- minutes
- health
- production technology
- knitted fabric
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the production technology of health blended knitted fabric, fabric is Chloranthus glaber fiber, moral suede becomes fineness degree to be that the blended yarn of 30 ~ 50S is weaved and formed with viscose fiber blending, in fabric, each Ingredients Weight ratio is that Chloranthus glaber fiber accounts for 30 ~ 50%, moral suede accounts for 30 ~ 40%, viscose accounts for 10 ~ 40%, and its production technology is as follows: weave → dye → dewater → cut open width → oven dry → sizing → finished product; In dyeing, adopt two one-bath two-step process to dye, the first step uses cation dyes to dye to moral suede, and second step uses REACTIVE DYES to dye to Chloranthus glaber fiber and viscose; In oven dry, bake out temperature is 100 ~ 120 DEG C, and speed is 15 ~ 25m/min; In sizing, setting temperature is 130 ~ 150 DEG C, and speed is 16 ~ 26m/min.Its advantage is: gained fabric of the present invention has the functions such as heat generating and retention, ecological, environmental protective and health care.
Description
Technical field
The present invention relates to the production technology of fabric, refer more particularly to a kind of production technology of blended yarn woven fabric.
Background technology
In recent years, along with the development of science and technology and the raising of living standards of the people, people more focus on healthy, so wish that garment material is while having heat generating and retention function, also there is the function such as environmental protection and health care, but traditional dress fabric function singleness, can not meet people to the polyfunctional requirement of garment material.
Summary of the invention
Technical problem to be solved by this invention is: provide a kind of production technology to make fabric have the functions such as heat generating and retention, ecological, environmental protective and health care.
For solving the problem, the technical solution used in the present invention is: the production technology of health blended knitted fabric, fabric to become fineness degree to be that the blended yarn of 30 ~ 50S is weaved and formed with viscose fiber blending by Chloranthus glaber fiber, moral suede, in fabric, each Ingredients Weight ratio is that Chloranthus glaber fiber accounts for 30 ~ 50%, moral suede accounts for 30 ~ 40%, viscose accounts for 10 ~ 40%, the production process of fabric is as follows: weave → dye → dewater → cut open width → oven dry → sizing → finished product, its feature is as follows.
(1) dyeing course adopts two one-bath two-step process, specific as follows.
First be first step dyeing, technical process is as follows:
A. dye vat enters water, is warming up to 35 ~ 45 DEG C, enters cloth; Then 65 ~ 75 DEG C are directly warming up to, insulation operation 4 ~ 6 minutes, select following material: cloth heavy 2.2 ~ 2.8% glacial acetic acid, cloth heavy 0.7 ~ 1.3% sodium acetate, cloth heavy 0 ~ 8% glauber salt, cloth weigh 0.2 ~ 0.5% the levelling agent for cation dyes, after above four kinds of materials are diluted respectively, then join in dye vat, the joining day is 4 ~ 6 minutes simultaneously;
B. with the speed of 1.2 ~ 1.8 DEG C/minute, temperature is risen to 80 ~ 90 DEG C from 65 ~ 75 DEG C, get cloth heavy 0.1 ~ 4% cation dyes join in dye vat, the joining day is 25 ~ 35 minutes, adds rear insulation operation 10 ~ 20 minutes;
C. with the speed of 0.8 ~ 1.2 DEG C/minute, temperature is risen to 95 ~ 105 DEG C from 80 ~ 90 DEG C, insulation operation, after 30 ~ 50 minutes, is cooled to 55 ~ 65 DEG C with the speed of 1.2 ~ 1.7 DEG C/minute, then discharge opeing, finally again through washing, hot water wash.
Then be second step dyeing, technical process is as follows:
A. dye vat enters water, is warming up to 35 ~ 45 DEG C, insulation operation 4 ~ 6 minutes; At the temperature of 35 ~ 45 DEG C, in dye vat, add chelated dispersants 0.5 ~ 1g/L, the joining day is 4 ~ 6 minutes;
B. get cloth heavy 0.1 ~ 4% REACTIVE DYES join in dye vat, the joining day is 25 ~ 35 minutes, rear insulation operation 8 ~ 12 minutes of having fed in raw material;
C. add glauber salt 5 ~ 60g/L, the joining day is 35 ~ 45 minutes, rear insulation operation 15 ~ 25 minutes of having fed in raw material; Then with ramp to 55 ~ 65 DEG C of 0.8 ~ 1.2 DEG C/minute, insulation operation 8 ~ 12 minutes; Then add soda ash 5 ~ 18g/L, the joining day is 45 ~ 55 minutes, rear insulation 30 ~ 60 minutes of having fed in raw material;
D. discharge opeing, hot water wash, pickling, 70 ~ 90 DEG C of low temperature soapings, hot water wash, cold wash.
(2) in oven dry, bake out temperature is 100 ~ 120 DEG C, and speed is 15 ~ 25m/min.
(3) in sizing, setting temperature is 130 ~ 150 DEG C, and speed is 16 ~ 26m/min.
Further, the production technology of aforesaid health blended knitted fabric, wherein: the fineness degree of described blended yarn is one in 32S, 40S or 50S.
Further, the production technology of aforesaid health blended knitted fabric, wherein: in health blended knitted fabric, each Ingredients Weight ratio is that Chloranthus glaber fiber accounts for 30%, moral suede accounts for 30%, viscose accounts for 40%.
Further, the production technology of aforesaid health blended knitted fabric, wherein: in first step dyeing course, glacial acetic acid be cloth heavy 2.5%, sodium acetate be cloth heavy 1.0%.
Further, the production technology of aforesaid health blended knitted fabric, wherein: in second step dyeing course, the consumption of chelated dispersants is 0.5g/L, and low temperature soaping temperature is 80 DEG C.
Further, the production technology of aforesaid health blended knitted fabric, wherein: bake out temperature is 110 DEG C, drying rate is 20m/min.
Further, the production technology of aforesaid health blended knitted fabric, wherein: setting temperature is 140 DEG C, sizing speed is 22m/min.
Further, the production technology of aforesaid health blended knitted fabric, wherein: by glacial acetic acid, sodium acetate, glauber salt, be used for the levelling agent of cation dyes, after above four kinds of materials dilute 5 ~ 10 times respectively, then join in dye vat simultaneously.
The invention has the advantages that: gained fabric of the present invention has the functions such as heat generating and retention, ecological, environmental protective and health care, improves the class of taking of fabric, more meets the pursuit of consumer to multi-functional fabric.
Detailed description of the invention
Be described in further detail below by the production technology of preferred embodiment to health blended knitted fabric of the present invention.
Embodiment 1
The production technology of health blended knitted fabric, fabric to become fineness degree to be that the blended yarn of 32S is weaved and formed with viscose fiber blending by Chloranthus glaber fiber, moral suede, and in fabric, each Ingredients Weight ratio is that Chloranthus glaber fiber accounts for 40%, moral suede accounts for 40%, viscose accounts for 20%; In the present embodiment, Chloranthus glaber fiber joins blended fibroblast in rayon spinning liquid by the active ingredient extracted in Chloranthus glaber to make, and moral suede is researched and developed by Bayer A.G, and Chloranthus glaber fiber and moral suede can commercially be purchased; The production process of fabric is as follows: weave → dye → dewater → cut open width → oven dry → sizing → finished product, its feature is as follows.
(1) weave to reach on large circle machine in the routine profit of Singapore's import and carry out.
(2) dyeing course adopts two one-bath two-step process, specific as follows.
First be first step dyeing, first step dyeing is mainly dyeed to moral suede, and technical process is as follows:
A. dye vat enters water according to the bath raio of 1:15, is warming up to 35 DEG C, enters cloth; Then 65 DEG C are directly warming up to, insulation operation 4 minutes, select following material: cloth heavy 2.2% glacial acetic acid, cloth heavy 0.7% sodium acetate, cloth weigh 0.2% for the levelling agent of cation dyes, above three kinds of materials are diluted 5 times respectively, then evenly join in dye vat, the joining day is 6 minutes simultaneously; When cation dyes consumption be less than or equal to cloth heavy 0.5% time, can not glauber salt be added during dyeing; In actual production, the model of being produced by Hai'an, Jiangsu petrochemical plant can be used to be the levelling agent of 1227;
B. with the speed of 1.8 DEG C/minute, temperature is risen to 90 DEG C from 65 DEG C, get cloth heavy 0.3% cation dyes evenly join in dye vat, the joining day is 25 minutes, adds rear insulation operation 10 minutes; In actual production, cation dyes can use cationic yellow X-GL;
C. with the speed of 0.8 DEG C/minute, temperature is risen to 105 DEG C from 90 DEG C, insulation operation, after 30 minutes, is cooled to 65 DEG C with the speed of 1.7 DEG C/minute, then discharge opeing, finally by washing, 60 DEG C of hot water wash.
Then be second step dyeing, second step dyeing is mainly dyeed to Chloranthus glaber fiber and viscose, and technical process is as follows:
A. dye vat enters water according to the bath raio of 1:10, is warming up to 35 DEG C, insulation operation 6 minutes; At the temperature of 35 DEG C, in dye vat, evenly add chelated dispersants 1g/L, the joining day is 4 minutes; In actual production, the model of being produced by Zhejiang Province Chuanhua Co., Ltd can be used to be the chelated dispersants of TF-510;
B. get cloth heavy 4% REACTIVE DYES evenly join in dye vat, the joining day is 35 minutes, rear insulation operation 12 minutes of having fed in raw material; In actual production, REACTIVE DYES can use active yellow 3 R S;
C. evenly add glauber salt 60g/L, the joining day is 45 minutes, rear insulation operation 15 minutes of having fed in raw material; Then with the ramp to 55 DEG C of 0.8 DEG C/min, insulation operation 8 minutes; Then evenly add soda ash 18g/L, the joining day is 55 minutes, rear insulation 60 minutes of having fed in raw material;
D. discharge opeing, 60 DEG C of hot water wash, pickling, 90 DEG C of low temperature soapings, 60 DEG C of hot water wash, cold wash.
In second step dyeing course, too fastly causing look flower, have employed low temperature and adding dyestuff, the bright powder craft of Canadian dollar in order to avoid painting, the time adding dye well auxiliary agent is also suitable extends about 10 minutes.
(3) in actual production, dewater and cut open width can Italy produce CORINO squezzing, cut open on width all-in-one and carry out.
(4) in oven dry, bake out temperature is 100 DEG C, and speed is 15m/min; There is Chloranthus glaber composition in gained fabric of the present invention, long-time high-temperature process easily weakens the antibiotic and sterilizing ability of Chloranthus glaber, so adopt low temperature drying; In actual production, dry and can carry out on the dryer of dyeing and finishing machinery Co., Ltd of Shandong Taida production.
(5) in sizing, setting temperature is 150 DEG C, and speed is 26m/min; Setting temperature is the same with bake out temperature, also unsuitable too high; In actual production, sizing can be carried out on German Bruckner setting machine.
Embodiment 2
The production technology of health blended knitted fabric, fabric to become fineness degree to be that the blended yarn of 32S is weaved and formed with viscose fiber blending by Chloranthus glaber fiber, moral suede, and in fabric, each Ingredients Weight ratio is that Chloranthus glaber fiber accounts for 40%, moral suede accounts for 40%, viscose accounts for 20%; In the present embodiment, Chloranthus glaber fiber joins blended fibroblast in rayon spinning liquid by the active ingredient extracted in Chloranthus glaber to make, and moral suede is researched and developed by Bayer A.G, and Chloranthus glaber fiber and moral suede can commercially be purchased; The production process of fabric is as follows: weave → dye → dewater → cut open width → oven dry → sizing → finished product, its feature is as follows.
(1) weave to reach on large circle machine in the routine profit of Singapore's import and carry out.
(2) dyeing course adopts two one-bath two-step process, specific as follows.
First be first step dyeing, first step dyeing is mainly dyeed to moral suede, and technical process is as follows:
A. dye vat enters water according to the bath raio of 1:15, is warming up to 35 DEG C, enters cloth; Then 65 DEG C are directly warming up to, insulation operation 4 minutes, select following material: cloth heavy 2.3% glacial acetic acid, cloth heavy 0.8% sodium acetate, cloth heavy 1.5% glauber salt, cloth weigh 0.3% for the levelling agent of cation dyes, above four kinds of materials are diluted 5 times respectively, then evenly join in dye vat, the joining day is 6 minutes simultaneously; In actual production, the model of being produced by Hai'an, Jiangsu petrochemical plant can be used to be the levelling agent of 1227;
B. with the speed of 1.8 DEG C/minute, temperature is risen to 90 DEG C from 65 DEG C, get cloth heavy 1% cation dyes evenly join in dye vat, the joining day is 25 minutes, adds rear insulation operation 10 minutes; In actual production, cation dyes can use cationic yellow X-GL;
C. with the speed of 0.8 DEG C/minute, temperature is risen to 105 DEG C from 90 DEG C, insulation operation, after 30 minutes, is cooled to 65 DEG C with the speed of 1.7 DEG C/minute, then discharge opeing, finally by washing, 60 DEG C of hot water wash.
Then be second step dyeing, second step dyeing is mainly dyeed to Chloranthus glaber fiber and viscose, and technical process is as follows:
A. dye vat enters water according to the bath raio of 1:10, is warming up to 35 DEG C, insulation operation 6 minutes; At the temperature of 35 DEG C, in dye vat, evenly add chelated dispersants 1g/L, the joining day is 4 minutes; In actual production, the model of being produced by Zhejiang Province Chuanhua Co., Ltd can be used to be the chelated dispersants of TF-510;
B. get cloth heavy 4% REACTIVE DYES evenly join in dye vat, the joining day is 35 minutes, rear insulation operation 12 minutes of having fed in raw material; In actual production, REACTIVE DYES can use active yellow 3 R S;
C. evenly add glauber salt 60g/L, the joining day is 45 minutes, rear insulation operation 15 minutes of having fed in raw material; Then with the ramp to 55 DEG C of 0.8 DEG C/min, insulation operation 8 minutes; Then evenly add soda ash 18g/L, the joining day is 55 minutes, rear insulation 60 minutes of having fed in raw material;
D. discharge opeing, 60 DEG C of hot water wash, pickling, 90 DEG C of low temperature soapings, 60 DEG C of hot water wash, cold wash.
In second step dyeing course, too fastly causing look flower, have employed low temperature and adding dyestuff, the bright powder craft of Canadian dollar in order to avoid painting, the time adding dye well auxiliary agent is also suitable extends about 10 minutes.
(3) in actual production, dewater and cut open width can Italy produce CORINO squezzing, cut open on width all-in-one and carry out.
(4) in oven dry, bake out temperature is 100 DEG C, and speed is 15m/min; There is Chloranthus glaber composition in gained fabric of the present invention, long-time high-temperature process easily weakens the antibiotic and sterilizing ability of Chloranthus glaber, so adopt low temperature drying; In actual production, dry and can carry out on the dryer of dyeing and finishing machinery Co., Ltd of Shandong Taida production.
(5) in sizing, setting temperature is 150 DEG C, and speed is 26m/min; Setting temperature is the same with bake out temperature, also unsuitable too high; In actual production, sizing can be carried out on German Bruckner setting machine.
Embodiment 3
The production technology of health blended knitted fabric, fabric to become fineness degree to be that the blended yarn of 40S is weaved and formed with viscose fiber blending by Chloranthus glaber fiber, moral suede, and in fabric, each Ingredients Weight ratio is that Chloranthus glaber fiber accounts for 30%, moral suede accounts for 30%, viscose accounts for 40%; In the present embodiment, Chloranthus glaber fiber joins blended fibroblast in rayon spinning liquid by the active ingredient extracted in Chloranthus glaber to make, and moral suede is researched and developed by Bayer A.G, and Chloranthus glaber fiber and moral suede can commercially be purchased; The production process of fabric is as follows: weave → dye → dewater → cut open width → oven dry → sizing → finished product, its feature is as follows.
(1) weave to reach on large circle machine in the routine profit of Singapore's import and carry out.
(2) dyeing course adopts two one-bath two-step process, specific as follows.
First be first step dyeing, first step dyeing is mainly dyeed to moral suede, and technical process is as follows:
A. dye vat enters water according to the bath raio of 1:15, is warming up to 40 DEG C, enters cloth; Then 70 DEG C are directly warming up to, insulation operation 5 minutes, select following material: cloth heavy 2.5% glacial acetic acid, cloth heavy 1.0% sodium acetate, cloth heavy 4% glauber salt, cloth weigh 0.35% for the levelling agent of cation dyes, above four kinds of materials are diluted 8 times respectively, then evenly join in dye vat, the joining day is 5 minutes simultaneously; In actual production, the model of being produced by Hai'an, Jiangsu petrochemical plant can be used to be the levelling agent of 1227;
B. with the speed of 1.5 DEG C/minute, temperature is risen to 85 DEG C from 70 DEG C, get cloth heavy 2% cation dyes evenly join in dye vat, the joining day is 30 minutes, adds rear insulation operation 15 minutes; In actual production, cation dyes can use Cationic Red X-GRL;
C. with the speed of 1 DEG C/minute, temperature is risen to 100 DEG C from 85 DEG C, insulation operation, after 40 minutes, is cooled to 60 DEG C with the speed of 1.5 DEG C/minute, then discharge opeing, finally by washing, 60 DEG C of hot water wash.
Then be second step dyeing, second step dyeing is mainly dyeed to Chloranthus glaber fiber and viscose, and technical process is as follows:
A. dye vat enters water according to the bath raio of 1:10, is warming up to 40 DEG C, insulation operation 5 minutes; At the temperature of 40 DEG C, in dye vat, evenly add chelated dispersants 0.5g/L, the joining day is 5 minutes; In actual production, the model of being produced by Zhejiang Province Chuanhua Co., Ltd can be used to be the chelated dispersants of TF-510;
B. get cloth heavy 2% REACTIVE DYES evenly join in dye vat, the joining day is 30 minutes, rear insulation operation 10 minutes of having fed in raw material; In actual production, REACTIVE DYES can use active red 3BS;
C. evenly add glauber salt 30g/L, the joining day is 40 minutes, rear insulation operation 20 minutes of having fed in raw material; Then with the ramp to 60 DEG C of 1 DEG C/min, insulation operation 10 minutes; Then evenly add soda ash 12g/L, the joining day is 50 minutes, rear insulation 45 minutes of having fed in raw material;
D. discharge opeing, 60 DEG C of hot water wash, pickling, 80 DEG C of low temperature soapings, 60 DEG C of hot water wash, cold wash.
In second step dyeing course, too fastly causing look flower, have employed low temperature and adding dyestuff, the bright powder craft of Canadian dollar in order to avoid painting, the time adding dye well auxiliary agent is also suitable extends about 10 minutes.
(3) in actual production, dewater and cut open width can Italy produce CORINO squezzing, cut open on width all-in-one and carry out.
(4) in oven dry, bake out temperature is 110 DEG C, and speed is 20m/min; There is Chloranthus glaber composition in gained fabric of the present invention, long-time high-temperature process easily weakens the antibiotic and sterilizing ability of Chloranthus glaber, so adopt low temperature drying; In actual production, dry and can carry out on the dryer of dyeing and finishing machinery Co., Ltd of Shandong Taida production.
(5) in sizing, setting temperature is 140 DEG C, and speed is 22m/min; Setting temperature is the same with bake out temperature, also unsuitable too high; In actual production, sizing can be carried out on German Bruckner setting machine.
Embodiment 4
The production technology of health blended knitted fabric, fabric to become fineness degree to be that the blended yarn of 50S is weaved and formed with viscose fiber blending by Chloranthus glaber fiber, moral suede, and in fabric, each Ingredients Weight ratio is that Chloranthus glaber fiber accounts for 50%, moral suede accounts for 35%, viscose accounts for 15%; In the present embodiment, Chloranthus glaber fiber joins blended fibroblast in rayon spinning liquid by the active ingredient extracted in Chloranthus glaber to make, and moral suede is researched and developed by Bayer A.G, and Chloranthus glaber fiber and moral suede can commercially be purchased; The production process of fabric is as follows: weave → dye → dewater → cut open width → oven dry → sizing → finished product, its feature is as follows.
(1) weave to reach on large circle machine in the routine profit of Singapore's import and carry out.
(2) dyeing course adopts two one-bath two-step process, specific as follows.
First be first step dyeing, first step dyeing is mainly dyeed to moral suede, and technical process is as follows:
A. dye vat enters water according to the bath raio of 1:15, is warming up to 45 DEG C, enters cloth; Then 75 DEG C are directly warming up to, insulation operation 6 minutes, select following material: cloth heavy 2.8% glacial acetic acid, cloth heavy 1.3% sodium acetate, cloth heavy 8% glauber salt, cloth weigh 0.5% for the levelling agent of cation dyes, above four kinds of materials are diluted 10 times respectively, then evenly join in dye vat, the joining day is 4 minutes simultaneously; In actual production, the model of being produced by Hai'an, Jiangsu petrochemical plant can be used to be the levelling agent of 1227;
B. with the speed of 1.2 DEG C/minute, temperature is risen to 80 DEG C from 75 DEG C, get cloth heavy 4% cation dyes evenly join in dye vat, the joining day is 35 minutes, adds rear insulation operation 20 minutes; In actual production, cation dyes can use cationic blue X-BL;
C. with the speed of 1.2 DEG C/minute, temperature is risen to 95 DEG C from 80 DEG C, insulation operation, after 50 minutes, is cooled to 55 DEG C with the speed of 1.2 DEG C/minute, then discharge opeing, finally by washing, 60 DEG C of hot water wash.
Then be second step dyeing, second step dyeing is mainly dyeed to Chloranthus glaber fiber and viscose, and technical process is as follows:
A. dye vat enters water according to the bath raio of 1:10, is warming up to 45 DEG C, insulation operation 4 minutes; At the temperature of 45 DEG C, in dye vat, evenly add chelated dispersants 0.8g/L, the joining day is 6 minutes; In actual production, the model of being produced by Zhejiang Province Chuanhua Co., Ltd can be used to be the chelated dispersants of TF-510;
B. get cloth heavy 0.1% REACTIVE DYES evenly join in dye vat, the joining day is 25 minutes, rear insulation operation 8 minutes of having fed in raw material; In actual production, REACTIVE DYES can use reactive blue B;
C. evenly add glauber salt 8g/L, the joining day is 35 minutes, rear insulation operation 25 minutes of having fed in raw material; Then with the ramp to 65 DEG C of 1.2 DEG C/min, insulation operation 12 minutes; Then evenly add soda ash 5g/L, the joining day is 45 minutes, rear insulation 30 minutes of having fed in raw material;
D. discharge opeing, 60 DEG C of hot water wash, pickling, 70 DEG C of low temperature soapings, 60 DEG C of hot water wash, cold wash.
In second step dyeing course, too fastly causing look flower, have employed low temperature and adding dyestuff, the bright powder craft of Canadian dollar in order to avoid painting, the time adding dye well auxiliary agent is also suitable extends about 10 minutes.
(3) in actual production, dewater and cut open width can Italy produce CORINO squezzing, cut open on width all-in-one and carry out.
(4) in oven dry, bake out temperature is 120 DEG C, and speed is 25m/min; There is Chloranthus glaber composition in gained fabric of the present invention, long-time high-temperature process easily weakens the antibiotic and sterilizing ability of Chloranthus glaber, so adopt low temperature drying; In actual production, dry and can carry out on the dryer of dyeing and finishing machinery Co., Ltd of Shandong Taida production.
(5) in sizing, setting temperature is 130 DEG C, and speed is 16m/min; Setting temperature is the same with bake out temperature, also unsuitable too high; In actual production, sizing can be carried out on German Bruckner setting machine.
Beneficial effect of the present invention is: the Chloranthus glaber fiber one, in gained fabric of the present invention has stronger anti-microbial property, " test of JISL1902-2002 textile fabrics antibacterial activity and the efficiency " method of employing, and with undressed white cotton knitted cloth for control sample, gained fabric of the present invention is tested, show that the bacteriostatic activity value of gained fabric of the present invention to Staphylococcus aureus is 2.3, be 2.8 to colibacillary bacteriostatic activity value, belong to antibacterial deodourizing fabricated product; Medicinal ingredient simultaneously in Chloranthus glaber fiber also has the health cares such as clearing heat and detoxicating, expelling wind and activating blood flow, swelling and pain relieving.Two, the blended yarn in gained fabric of the present invention, nontoxic, to human body skin without anaphylaxis and carcinogenic, and have good biodegradability and Environmental compatibility, therefore gained fabric of the present invention is a ecological, environmental protective fabric.Three, gained fabric of the present invention adopts Chloranthus glaber fiber, moral suede, viscose fiber blended yarn to be made into, and do not use containing formaldehyde, forbidding azo auxiliary agent or raw material, environmental protection, the indexs such as fiber content of formaldehyde, poisonous and harmful substances all meet national standard.Four, Chloranthus glaber fiber and viscose have moisture absorption and put thermal property, can promote human body temperature 2 ~ 3 DEG C taking in process; Moral Down Fiber uses unique ultra-fine profiled-cross-section technology of dry-spinning, and fabric bulk degree is higher than other allied fibers by 10%; In addition, its exclusive moisture wicking function, makes fabric can dredge the moisture that health produces to external quickly, and heat indwelling in body, thus reach warming function.The mensuration of thermal resistance and dampness " under the GB/T11048-2008 textiles physiological comfort limit " method is adopted to test gained fabric of the present invention, show that the insulation rate of fabric is 71.2%, clo value is 0.23, therefore show that gained fabric of the present invention has good heat generating and retention characteristic from theory and practice.Five, the index such as COLOR FASTNESS, content of formaldehyde, pH value of gained fabric of the present invention is all up to state standards, examination criteria adopts: GB18401-2010 " National Textile technical specification of security " category-B, GB/T3921.3-1997 " textile color stability test color fastness to washing: test 3 ", and result is as shown in table 1:
Claims (8)
1. the production technology of health blended knitted fabric, fabric to become fineness degree to be that the blended yarn of 30 ~ 50S is weaved and formed with viscose fiber blending by Chloranthus glaber fiber, moral suede, in fabric, each Ingredients Weight ratio is that Chloranthus glaber fiber accounts for 30 ~ 50%, moral suede accounts for 30 ~ 40%, viscose accounts for 10 ~ 40%, the production process of fabric is as follows: weave → dye → dewater → cut open width → oven dry → sizing → finished product, it is characterized in that:
(1) dyeing course adopts two one-bath two-step process, specific as follows:
First be first step dyeing, technical process is as follows:
A. dye vat enters water, is warming up to 35 ~ 45 DEG C, enters cloth; Then 65 ~ 75 DEG C are directly warming up to, insulation operation 4 ~ 6 minutes, select following material: cloth heavy 2.2 ~ 2.8% glacial acetic acid, cloth heavy 0.7 ~ 1.3% sodium acetate, cloth heavy 0 ~ 8% glauber salt, cloth weigh 0.2 ~ 0.5% the levelling agent for cation dyes, after above four kinds of materials are diluted respectively, then join in dye vat, the joining day is 4 ~ 6 minutes simultaneously;
B. with the speed of 1.2 ~ 1.8 DEG C/minute, temperature is risen to 80 ~ 90 DEG C from 65 ~ 75 DEG C, get cloth heavy 0.1 ~ 4% cation dyes join in dye vat, the joining day is 25 ~ 35 minutes, adds rear insulation operation 10 ~ 20 minutes;
C. with the speed of 0.8 ~ 1.2 DEG C/minute, temperature is risen to 95 ~ 105 DEG C from 80 ~ 90 DEG C, insulation operation, after 30 ~ 50 minutes, is cooled to 55 ~ 65 DEG C with the speed of 1.2 ~ 1.7 DEG C/minute, then discharge opeing, finally again through washing, hot water wash;
Then be second step dyeing, technical process is as follows:
A. dye vat enters water, is warming up to 35 ~ 45 DEG C, insulation operation 4 ~ 6 minutes; At the temperature of 35 ~ 45 DEG C, in dye vat, add chelated dispersants 0.5 ~ 1g/L, the joining day is 4 ~ 6 minutes;
B. get cloth heavy 0.1 ~ 4% REACTIVE DYES join in dye vat, the joining day is 25 ~ 35 minutes, rear insulation operation 8 ~ 12 minutes of having fed in raw material;
C. add glauber salt 5 ~ 60g/L, the joining day is 35 ~ 45 minutes, rear insulation operation 15 ~ 25 minutes of having fed in raw material; Then with ramp to 55 ~ 65 DEG C of 0.8 ~ 1.2 DEG C/minute, insulation operation 8 ~ 12 minutes; Then add soda ash 5 ~ 18g/L, the joining day is 45 ~ 55 minutes, rear insulation 30 ~ 60 minutes of having fed in raw material;
D. discharge opeing, hot water wash, pickling, 70 ~ 90 DEG C of low temperature soapings, hot water wash, cold wash;
(2) in oven dry, bake out temperature is 100 ~ 120 DEG C, and speed is 15 ~ 25m/min;
(3) in sizing, setting temperature is 130 ~ 150 DEG C, and speed is 16 ~ 26m/min.
2. the production technology of health blended knitted fabric according to claim 1, is characterized in that: the fineness degree of described blended yarn is one in 32S, 40S or 50S.
3. the production technology of health blended knitted fabric according to claim 1, is characterized in that: in health blended knitted fabric, each Ingredients Weight ratio is that Chloranthus glaber fiber accounts for 30%, moral suede accounts for 30%, viscose accounts for 40%.
4. the production technology of health blended knitted fabric according to claim 1, is characterized in that: in first step dyeing course, glacial acetic acid be cloth heavy 2.5%, sodium acetate be cloth heavy 1.0%.
5. the production technology of health blended knitted fabric according to claim 1, is characterized in that: in second step dyeing course, and the consumption of chelated dispersants is 0.5g/L, and low temperature soaping temperature is 80 DEG C.
6. the production technology of health blended knitted fabric according to claim 1, is characterized in that: bake out temperature is 110 DEG C, and drying rate is 20m/min.
7. the production technology of health blended knitted fabric according to claim 1, is characterized in that: setting temperature is 140 DEG C, and sizing speed is 22m/min.
8. the production technology of health blended knitted fabric according to claim 1, it is characterized in that: by glacial acetic acid, sodium acetate, glauber salt, be used for the levelling agent of cation dyes, after above four kinds of materials dilute 5 ~ 10 times respectively, then join in dye vat simultaneously.