CN104046304A - Adhesive and preparation method thereof - Google Patents
Adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN104046304A CN104046304A CN201410271426.0A CN201410271426A CN104046304A CN 104046304 A CN104046304 A CN 104046304A CN 201410271426 A CN201410271426 A CN 201410271426A CN 104046304 A CN104046304 A CN 104046304A
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive
- stearic acid
- tackiness agent
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an adhesive which comprises the following components in parts by weight: 50-80 parts of a chloroprene rubber adhesive, 20-50 parts of methylcellulose, 20-40 parts of vinylidene chloride resin, 100-150 parts of ethylene glycol acetate-diethyl ether, 100-120 parts of stearic acid, 10-14 parts of phenolic resin and 5-10 parts of butyl acetate. A preparation method of the adhesive comprises the following steps: putting the chloroprene rubber adhesive, the methylcellulose, the vinylidene chloride resin, ethylene glycol acetate-diethyl ether, stearic acid, the phenolic resin and butyl acetate into an enameled reaction kettle, stirring, subsequently placing for 40-60 minutes, pouring into a crystallization tank to stand for 10 hours, and stirring again at the temperature of 30 DEG C to obtain a jelly substance. The adhesive disclosed by the invention is good in adhesive effect, good in adhesive strength, nontoxic, flavorless, environment-friendly and healthy.
Description
Technical field
The present invention relates to chemical technology field, be specifically related to a kind of tackiness agent.
Background technology
In shoemaking process, can use in a large number tackiness agent, tackiness agent is sticking and the interior poly-effect that waits by interface, can make two or more product or natural or synthetic, the organic or inorganic class material that links together of material, be referred to as tackiness agent, be again tamanori, traditionally referred to as glue.In brief, tackiness agent is exactly by adhesive effect, the material that can make to be sticked thing and combine.
Current some tackiness agent on the market, in viscose glue process, can produce certain toxic gas, and with irritating smell, not environmental protection.
Summary of the invention
Object of the present invention provides a kind of tackiness agent and preparation method thereof, solves one or more in above-mentioned prior art problem.
According to an aspect of the present invention, a kind of tackiness agent, the component that comprises following weight part: 50~80 parts of neoprene latexs, 20~50 parts of methylcellulose gum, 20~40 parts of supervinyi chloride resins, 100~150 parts of acetic acid glycol monoethyl ethers, 100~120 parts of stearic acid, 10~14 parts, resol, 5~10 parts of N-BUTYL ACETATEs.
A kind of preparation method of tackiness agent, by neoprene latex, methylcellulose gum, supervinyi chloride resin, acetic acid glycol monoethyl ether, stearic acid, resol, N-BUTYL ACETATE is placed in enamel reaction still, after stirring, place again 40~60min, pour standing 10h in crystallizer tank into, at the temperature of 30 ℃, continue to stir, become jelly.
A kind of tackiness agent provided by the invention, gluing effective, bond strength is high, nonpoisonous and tasteless, environment protection health.
Embodiment
Embodiment 1
A tackiness agent, comprises the component of following weight part: 50 parts of neoprene latexs, 20 parts of methylcellulose gum, 20 parts of supervinyi chloride resins, 100 parts of acetic acid glycol monoethyl ethers, 100 parts of stearic acid, 10 parts, resol, 5 parts of N-BUTYL ACETATEs.
The preparation method of tackiness agent, by neoprene latex, methylcellulose gum, supervinyi chloride resin, acetic acid glycol monoethyl ether, stearic acid, resol, N-BUTYL ACETATE is placed in enamel reaction still, after stirring, place again 40min, pour standing 10h in crystallizer tank into, at the temperature of 30 ℃, continue to stir, become jelly.
Embodiment 2
A tackiness agent, is characterized in that, comprises the component of following weight part: 65 parts of neoprene latexs, 35 parts of methylcellulose gum, 30 parts of supervinyi chloride resins, 125 parts of acetic acid glycol monoethyl ethers, 110 parts of stearic acid, 12 parts, resol, 8 parts of N-BUTYL ACETATEs.
The preparation method of tackiness agent, by neoprene latex, methylcellulose gum, supervinyi chloride resin, acetic acid glycol monoethyl ether, stearic acid, resol, N-BUTYL ACETATE is placed in enamel reaction still, after stirring, place again 40~60min, pour standing 10h in crystallizer tank into, at the temperature of 30 ℃, continue to stir, become jelly.
Embodiment 3
A tackiness agent, is characterized in that, comprises the component of following weight part: 80 parts of neoprene latexs, 50 parts of methylcellulose gum, 40 parts of supervinyi chloride resins, 150 parts of acetic acid glycol monoethyl ethers, 120 parts of stearic acid, 14 parts, resol, 10 parts of N-BUTYL ACETATEs.
The preparation method of tackiness agent, by neoprene latex, methylcellulose gum, supervinyi chloride resin, acetic acid glycol monoethyl ether, stearic acid, resol, N-BUTYL ACETATE is placed in enamel reaction still, after stirring, place again 60min, pour standing 10h in crystallizer tank into, at the temperature of 30 ℃, continue to stir, become jelly.
The above is only optimal way of the present invention; it should be pointed out that to those skilled in the art, without departing from the concept of the premise of the invention; can also make some similar distortion and improvement, within these also should be considered as protection scope of the present invention.
Claims (2)
1. a tackiness agent, is characterized in that, comprises the component of following weight part: 50~80 parts of neoprene latexs, 20~50 parts of methylcellulose gum, 20~40 parts of supervinyi chloride resins, 100~150 parts of acetic acid glycol monoethyl ethers, 100~120 parts of stearic acid, 10~14 parts, resol, 5~10 parts of N-BUTYL ACETATEs.
2. the preparation method of a kind of tackiness agent according to claim 1, is characterized in that, by neoprene latex, methylcellulose gum, supervinyi chloride resin, acetic acid glycol monoethyl ether, stearic acid, resol, N-BUTYL ACETATE is placed in enamel reaction still, places 40~60min after stirring again, pours standing 10h in crystallizer tank into, at the temperature of 30 ℃, continue to stir, become jelly.