CN104042460B - 一种应用西华红粘土制备的矿物泥面膜及其制备方法 - Google Patents
一种应用西华红粘土制备的矿物泥面膜及其制备方法 Download PDFInfo
- Publication number
- CN104042460B CN104042460B CN201410327412.6A CN201410327412A CN104042460B CN 104042460 B CN104042460 B CN 104042460B CN 201410327412 A CN201410327412 A CN 201410327412A CN 104042460 B CN104042460 B CN 104042460B
- Authority
- CN
- China
- Prior art keywords
- xihua
- admaic earth
- admaic
- powder
- adjuvant component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种应用西华红粘土制备的矿物泥面膜及其制备方法，属于化妆品技术领域。其特征在于按重量百分含量计由如下组分组成西华红粘土50%～75%；甘油1.5%～4%；月桂酰胺丙基甜菜碱0.2%～2%；氨基酸保湿剂0.5%～5%；透明质酸2%～7%；助剂组分1%～3%；余量为去离子水，能够保湿补水，去皱除污，使肌肤细腻爽滑，使用后易清洗，具有成本低，工艺简单，生产效率高，不污染环境，无毒无刺激，适合所有人使用的特点。
Description
【技术领域】
本发明涉及一种应用西华红粘土制备的矿物泥面膜及其制备方法，属于化妆品技术领域。
【背景技术】
泥疗是古代养生文化的重要内容，历史记载远在两千年前，人类开始利用泥土祛邪，治病和养生保养。传统养生学在数千年漫长的历史进程中，不但形成了自己独特的理论体系，而且也积累了一整套实用、同时又充满古代人聪明睿智的实践方法。在古代医学中，如晋洪的《肘后备急方》、孙思邈的《干金要方》等，都有泥疗的记载。李时珍的《本草纲目》中曾说及泥与人体的关系，曰：“诸土皆能胜湿补脾。”中医认为，脾属土，自然界的泥土敷于人体，皆于人体的脾“同气相召”，凡因脾引起的疾病，用泥疗疗效明显。当代，西方人喜欢用火山泥进行泥疗或者制作化妆品，也证明了泥土是有疗效的。现有的泥疗和化妆品多采用火山泥，没有采用红粘土的，因此发明一种应用红粘土制备的化妆品就成为人们一直渴求的愿望。
西华红粘土，属积钙红粘土亚类火红土土属。分布于甘肃省天水、临夏、平凉、定西、庆阳、陇南、兰州、白银等地水土流失严重的丘陵、残塬、梁、峁及山坡地上。面积约271．8万亩。其主要性状：土种母质为第三纪红土，剖面发育较弱，为A11一AC一C型，耕层厚15cm左右，多呈浊红棕色粒状结构，其下为亮红棕色块状结构。通体石灰反应强烈，碳酸钙含量8％一11％。土壤pH8．0一8．5，呈微碱性。据119个剖面样分析结果统计：A11层有机质含量0．95％，全氮0．063％，速效磷6ppm、速效钾171ppm；有效微量元素含量（n＝18）：锌0．7ppm、铜1．05ppm、硼0．77ppm、钼0．09ppm、铁13ppm、锰11ppm。红粘土粉末是一种矿物泥，颗粒细小，常在胶体尺寸范围内，因其富含红色氧化铁而呈现出特有的红色，不溶于水、醇及有机溶剂，但很容易分散于去离子水中，并形成具有一定黏度的泥浆。根据范德华力分子间的作用原理，物质的吸附能力决定于单位表面积的大小，单位面积大，吸附能力就强，即吸附质的数量随着吸附剂表面的增大而增大的。而红粘土粉末为极其细小的粉体，300目过筛大于95%，粒径约为48μm，具有很高的比表面积和表面活性，是一种良好的天然净化基质，能彻底清除肌肤深层污垢及油脂，起到清洁皮肤的功效。同时,它含有大量的钙、镁以及硅等为人体所必需的矿物质元素。并且红粘土的性质非常稳定，无刺激性，适合各种皮肤。因此发明一种使用西华红粘土制备的化妆品就显得很有必要，人们一直渴望一种应用西华红粘土的化妆品。并且，西华红粘土储备量极大，获取容易，价格极低，容易加工，开发成化妆品，能取得巨大的经济效益。
申请号为201210383729.2的发明公布了一种矿物泥浆和矿物精华水的制备方法，申请号为201210383655.2的发明公布了一种矿物泥浆水洗面膜，这两个发明都使用石胆为原料，经百度百科查证和《神农本草经》中的记载，均揭示石胆是铜盐，中国古代五毒之一,药性：酸、辛、寒、有毒；不适合做化妆品使用；并且其生产工艺中有风化、预浸泡、初沉二沉、陈化等步骤，步骤繁琐工艺复杂，并且采用物理加工工艺，既不能去除石胆的毒性，又加工工艺复杂，不利于生产，且危害健康。申请号为200710018373.1的发明公开了一种高原红土的处理方法及在生产美容用品中的应用，其加工工艺复杂，使用酸洗碱洗工艺，很污染环境，不利于生产普及。
申请号为200710065259的发明公布了一种用于皮肤护理保健的矿物黑泥干粉及其制备方法，其选用山西运城盐湖湖底表层泥土剥去1—3米后的天然黑泥制成，其效果确实，但其制备工艺中没有消毒杀菌工艺；众所周知，很多动植物和浮游生物腐烂后产生的有机物和残骸，均沉积到湖底的黑泥中，导致黑泥含有很多细菌等微生物，并且有很重的异味；虽然其说明书中强调选用表层泥土剥去1—3米后的天然黑泥，但是其中仍含有多种细菌和微生物，以及动植物残骸等有害物质；这些细菌等微生物直接危害人体健康，特别是有青春痘或小的创口时，很容易导致细菌感染，极其危险；所以消毒杀菌很有必要。
【发明内容】
为解决上述现有技术的不足，本发明提供一种应用西华红粘土制备的矿物泥面膜，能够保湿补水，去皱除污，使肌肤细腻爽滑，使用后易清洗，具有成本低，工艺简单，生产效率高，不污染环境，无毒无刺激，适合所有人使用的特点。
本发明的另一目的是提供一种上述应用西华红粘土制备的矿物泥面膜的制备方法。
为实现上述目的，本发明采用以下技术方案：
一种应用西华红粘土制备的矿物泥面膜，其特征在于按重量百分含量计由以下组分组成：
西华红粘土 50%～75% 甘油 1.5%～4% 月桂酰胺丙基甜菜碱0.2%～2% 氨基酸保湿剂0.5%～5% 透明质酸2%～7% 助剂组分1%～3% 余量为去离子水
所述的西华红粘土，为甘肃省定西市陇西县菜子镇采集的西华红粘土。
所述的助剂组分为香精、防腐剂中的一种或两种混合物。
一种制备上述应用西华红粘土制备的矿物泥面膜的方法，其特征在于包括以下步骤：
（1）选取干净的西华红粘土土块，使用粉碎机等机械设备，粉碎成300~450目的西华红粘土粉末，待用；
（2）进行高压蒸气灭菌：将上步制得的红粘土粉末，在压力为98.066kPa，温度121～126℃，处理15～25分钟即可，干燥后待用；
（3）按照上述配方中的重量百分含量称取西华红粘土粉末，将西华红粘土粉末加入到去离子水中，在不停地搅拌中加热到65～90℃，加入甘油、月桂酰胺丙基甜菜碱搅拌均匀，降温到40～60℃，加入透明质酸、氨基酸保湿剂和助剂组分，搅拌均匀，均质，即可。
本发明的设计思路：西华红粘土经过粉碎机粉碎时，在粘土颗粒表面产生的高温可以杀灭粘土中的细菌和微生物，此步骤实现了粉碎和杀菌两个功效，避免细菌和微生物危害人体皮肤，防止皮肤过敏；红粘土粉末为极其细小的粉体，具有很高的比表面积和表面活性，是一种良好的天然净化基质，能彻底清除肌肤深层污垢及油脂，起到清洁皮肤的功效，同时,它含有大量的钙、镁以及硅等为人体所必需的矿物质元素，并且红粘土的性质非常稳定，无刺激性，适合各种皮肤。甘油具有滋润皮肤的效果；月桂酰胺丙基甜菜碱是表面活性剂，方便使用后，清洗掉残留的面膜矿泥；透明质酸是天然的保湿润滑剂，使皮肤光滑湿润；氨基酸保湿剂具有保湿、柔肤、抗皱的效果。
本发明的有益效果：能够高效保湿补水、舒展皱纹，使肌肤细腻爽滑；去除皮肤深层的污垢和油脂；使用后易清洗；可以滋润肌肤、延缓衰老；不使用酸洗碱洗工艺，不污染环境，生产工艺简单；原材料不使用石胆，无毒无刺激，适合长期使用；生产工艺不使用风化、预浸泡、初沉二沉、陈化等步骤，工艺简单，生产效率高；西华红粘土储备量大，开采加工成本低，生产效率高，能够取得很好的经济效益。
【具体实施方式】
下面结合具体实施例对本发明作进一步说明：
实施例1：
本发明一种应用西华红粘土制备的矿物泥面膜，其按重量百分含量计由以下组分组成：
西华红粘土 55% 甘油3% 月桂酰胺丙基甜菜碱1.8% 氨基酸保湿剂4% 透明质酸5% 助剂组分3% 余量为去离子水
所述的西华红粘土，为甘肃省定西市陇西县菜子镇采集的西华红粘土。
所述的助剂组分为香精1.3%、防腐剂1.7%。
本实施例的制备是通过一下步骤实现的：
（1）选取干净的西华红粘土土块，使用粉碎机等机械设备，粉碎成400目的西华红粘土粉末，待用；
（2）进行高压蒸气灭菌：将上步制得的红粘土粉末，在压力为98.066kPa，温度121℃，处理20分钟即可，干燥后待用；
（3）按照上述配方中的重量百分含量称取西华红粘土粉末，将西华红粘土粉末加入到去离子水中，在不停地搅拌中加热到90℃时，加入甘油、月桂酰胺丙基甜菜碱搅拌均匀，降温到56℃时，加入透明质酸、氨基酸保湿剂和助剂组分，搅拌均匀，均质，即可。
实施例2：
本发明一种应用西华红粘土制备的矿物泥面膜，其按重量百分含量计由以下组分组成：
西华红粘土75% 甘油 1.5% 月桂酰胺丙基甜菜碱0.5% 氨基酸保湿剂2% 透明质酸3% 助剂组分1% 余量为去离子水
所述的西华红粘土，为甘肃省定西市陇西县菜子镇采集的西华红粘土。
所述的助剂组分为防腐剂。
本实施例的制备是通过一下步骤实现的：
（1）选取干净的西华红粘土土块，使用粉碎机等机械设备，粉碎成350目的西华红粘土粉末，待用；
（2）进行高压蒸气灭菌：将上步制得的红粘土粉末，在压力为98.066kPa，温度126℃，处理15分钟即可，干燥后待用；
（3）按照上述配方中的重量百分含量称取西华红粘土粉末，将西华红粘土粉末加入到去离子水中，在不停地搅拌中加热到77℃时，加入甘油、月桂酰胺丙基甜菜碱搅拌均匀，降温到50℃时，加入透明质酸、氨基酸保湿剂和助剂组分，搅拌均匀，均质，即可。
实施例3：
本发明一种应用西华红粘土制备的矿物泥面膜，其按重量百分含量计由以下组分组成：
西华红粘土67% 甘油2.3% 月桂酰胺丙基甜菜碱1.2% 氨基酸保湿剂1% 透明质酸6% 助剂组分2% 余量为去离子水
所述的西华红粘土，为甘肃省定西市陇西县菜子镇采集的西华红粘土。
所述的助剂组分为香精1%、防腐剂1%。
本实施例的制备是通过一下步骤实现的：
（1）选取干净的西华红粘土土块，使用粉碎机等机械设备，粉碎成300目的西华红粘土粉末，待用；
（2）进行高压蒸气灭菌：将上步制得的红粘土粉末，在压力为98.066kPa，温度124℃，处理25分钟即可，干燥后待用；
（3）按照上述配方中的重量百分含量称取西华红粘土粉末，将西华红粘土粉末加入到去离子水中，在不停地搅拌中加热到65℃时，加入甘油、月桂酰胺丙基甜菜碱搅拌均匀，降温到44℃时，加入透明质酸、氨基酸保湿剂和助剂组分，搅拌均匀，均质，即可。
本发明的实验研究：
征集面部皮肤粗糙、多油、毛孔粗大、有皱纹的试用者40名，其中男16名，女24名，平均年龄26.7岁。实验时间1个月。试用者晚上彻底洁面后，使用实施例2制备的面膜，敷10分钟，然后彻底清洗干净，每两天使用一次。1个月后，所有试用者的皮肤多油症状均消失，皮肤细腻有弹性，其中33人皮肤细腻红润、细微皱纹减小或消失。经试验得出本发明除油效果显著，效率可达100%；补水保湿、嫩肤去皱纹效果良好，可达82.5%。
Claims (4)
1.一种应用西华红粘土制备的矿物泥面膜，其特征在于由以下方法制成：
按重量百分含量计由以下组分组成：西华红粘土50％～75％、甘油1.5％～4％、月桂酰胺丙基甜菜碱0.2％～2％、氨基酸保湿剂0.5％～5％、透明质酸2％～7％、助剂组分1％～3％、余量为去离子水；
所述的西华红粘土，为甘肃省定西市陇西县菜子镇采集的西华红粘土；所述的助剂组分为香精、防腐剂中的一种或两种混合物；
本面膜的制备是通过以下步骤实现的：
(1)选取干净的西华红粘土土块，使用粉碎机，粉碎成300～450目的西华红粘土粉末，待用；
(2)进行高压蒸气灭菌：将上步制得的红粘土粉末，在压力为98.066kPa，温度121～126℃，处理15～25分钟即可，干燥后待用；
(3)按照上述配方中的重量百分含量称取西华红粘土粉末，将西华红粘土粉末加入到去离子水中，在不停地搅拌中加热到65～90℃，加入甘油、月桂酰胺丙基甜菜碱搅拌均匀，降温到40～60℃，加入透明质酸、氨基酸保湿剂和助剂组分，搅拌均匀，均质，即可。
2.一种应用西华红粘土制备的矿物泥面膜，其特征在于采用以下方法制成，按重量百分含量计由以下组分组成：西华红粘土55％、甘油3％、月桂酰胺丙基甜菜碱1.8％、氨基酸保湿剂4％、透明质酸5％、助剂组分3％、余量为去离子水；所述的西华红粘土，为甘肃省定西市陇西县菜子镇采集的西华红粘土；所述的助剂组分为香精1.3％、防腐剂1.7％；本面膜的制备是通过以下步骤实现的：(1)选取干净的西华红粘土土块，使用粉碎机，粉碎成400目的西华红粘土粉末，待用；(2)进行高压蒸气灭菌：将上步制得的红粘土粉末，在压力为98.066kPa，温度121℃，处理20分钟即可，干燥后待用；(3)按照上述配方中的重量百分含量称取西华红粘土粉末，将西华红粘土粉末加入到去离子水中，在不停地搅拌中加热到90℃时，加入甘油、月桂酰胺丙基甜菜碱搅拌均匀，降温到56℃时，加入透明质酸、氨基酸保湿剂和助剂组分，搅拌均匀，均质，即可。
3.一种应用西华红粘土制备的矿物泥面膜，其特征在于采用以下方法制成，按重量百分含量计由以下组分组成：西华红粘土75％、甘油1.5％、月桂酰胺丙基甜菜碱0.5％、氨基酸保湿剂2％、透明质酸3％、助剂组分1％、余量为去离子水；所述的西华红粘土，为甘肃省定西市陇西县菜子镇采集的西华红粘土；所述的助剂组分为防腐剂；本面膜的制备是通过以下步骤实现的：(1)选取干净的西华红粘土土块，使用粉碎机，粉碎成350目的西华红粘土粉末，待用；(2)进行高压蒸气灭菌：将上步制得的红粘土粉末，在压力为98.066kPa，温度126℃，处理15分钟即可，干燥后待用；(3)按照上述配方中的重量百分含量称取西华红粘土粉末，将西华红粘土粉末加入到去离子水中，在不停地搅拌中加热到77℃时，加入甘油、月桂酰胺丙基甜菜碱搅拌均匀，降温到50℃时，加入透明质酸、氨基酸保湿剂和助剂组分，搅拌均匀，均质，即可。
4.一种应用西华红粘土制备的矿物泥面膜，其特征在于采用以下方法制成，按重量百分含量计由以下组分组成：西华红粘土67％、甘油2.3％、月桂酰胺丙基甜菜碱1.2％、氨基酸保湿剂1％、透明质酸6％、助剂组分2％、余量为去离子水；所述的西华红粘土，为甘肃省定西市陇西县菜子镇采集的西华红粘土；所述的助剂组分为香精1％、防腐剂1％；本面膜的制备是通过以下步骤实现的：(1)选取干净的西华红粘土土块，使用粉碎机，粉碎成300目的西华红粘土粉末，待用；(2)进行高压蒸气灭菌：将上步制得的红粘土粉末，在压力为98.066kPa，温度124℃，处理25分钟即可，干燥后待用；(3)按照上述配方中的重量百分含量称取西华红粘土粉末，将西华红粘土粉末加入到去离子水中，在不停地搅拌中加热到65℃时，加入甘油、月桂酰胺丙基甜菜碱搅拌均匀，降温到44℃时，加入透明质酸、氨基酸保湿剂和助剂组分，搅拌均匀，均质，即可。