CN104004450A - Switch cabinet spraying priming paint and preparation method thereof - Google Patents
Switch cabinet spraying priming paint and preparation method thereof Download PDFInfo
- Publication number
- CN104004450A CN104004450A CN201410170340.9A CN201410170340A CN104004450A CN 104004450 A CN104004450 A CN 104004450A CN 201410170340 A CN201410170340 A CN 201410170340A CN 104004450 A CN104004450 A CN 104004450A
- Authority
- CN
- China
- Prior art keywords
- parts
- hour
- priming paint
- alum
- switch cabinet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a switch cabinet spraying priming paint. The switch cabinet spraying priming paint is prepared by using the following raw materials, by weight, 40-45 parts of polyurethane acrylate, 23-28 parts of epoxy acrylate, 3-4 parts of titanium dioxide, 2-3 parts of hydrophobic silica, 2-3 parts of zinc cyanurate, 3-4 parts of zinc oxide, 2-3 parts of alum powder, 1-2 parts of isopropyl thioxanthone, 3-4 parts of benzoin bis-methyl ether, 1-2 parts of methyl methacrylate, 3-5 parts of ethylene glycol ethyl ether acetate, 8-10 parts of dipentaerythritol hexaacrylate, 7-9 parts of ethyl acetate and 3-4 parts of a dispersion assistant. The dispersion assistant improves the optical performance, makes the paint uniformly dispersed and maintains the stability of the paint. The switch cabinet spraying priming paint has the advantages of sagging resistance, abundant films, strong adhesion, rapid solidification, and substantial improvement of the work efficiency.
Description
Technical field
The present invention relates to a kind of paint and preparation method thereof, particularly a kind of switching cabinet spraying priming paint and preparation method thereof.
Background technology
Switching cabinet (switch cabinet) is a kind of electric equipment, and outside line is introduced into master switch in cabinet, then enters sub-control switch, and each shunt needs to arrange by it.As instrument, automatic control, electric motor magnetic switch, various alternating current contactors etc., what have also establishes pressurizing chamber and low-pressure chamber switching cabinet, is provided with high voltage bus, and as power station etc., what have is also provided with the low-frequency load reduction into protecting major equipment.Switching cabinet work under bad environment, surface scribbles enamelled coating, and with high temperature resistant, cold-resistant, UV resistant, corrosion-resistant etc., but existing paint cannot meet the different requirements of switching cabinet.
Summary of the invention
The object of this invention is to provide switching cabinet spraying priming paint that a kind of paint film enriches, is uniformly dispersed, wear resistance is good, sticking power is good and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
A kind of switching cabinet spraying priming paint, is made up of the raw material of following weight part: urethane acrylate 40-45, epoxy acrylate 23-28, titanium dioxide 3-4, water drain silica 2-3, cyanuric acid zinc 2-3, zinc oxide 3-4, alum powder 2-3, isopropyl thioxanthone 1-2, benzoin dimethylether 3-4, methyl methacrylate 1-2, ethylene glycol ether acetate 3-5, double pentaerythritol methacrylate 8-10, ethyl acetate 7-9, dispersing auxiliary 3-4;
Described dispersing auxiliary makes by the following method: the weight part of its each feed composition is: kaolin 300-310, clay 10-12, aluminium nitride 5-6, jade 1-2, N-2-(aminoethyl)-3-aminopropyl trimethoxysilane 1-2, linking agent TAC1-2, alum 8-10, trolamine 2-3, Flos Rosae Rugosae quintessence oil 1-2, tea-polyphenol 1-2; Preparation method adds kaolin, clay in 12-15% hydrochloric acid soln and soaks 3-4 hour, takes out, and cleans with clear water, calcines 3-4 hour with sending in calcining furnace at 530-550 DEG C, cooling, merges and grinds to form 300-400 order powder with jade; Adding N-2-(aminoethyl)-3-aminopropyl trimethoxysilane, linking agent TAC, alum continue grinding distribution 2-3 hour, then add other remaining component to be ground to fully to disperse to obtain 300-400 order powder, to obtain final product.
Switching cabinet spraying priming paint of the present invention, made by following concrete steps:
(1) urethane acrylate, epoxy acrylate, titanium dioxide, water drain silica, cyanuric acid zinc, zinc oxide, alum powder are added in reactor and stirred, temperature of reaction is controlled at below 40-60 DEG C, stirs 0.5-1 hour;
(2) in reactor, add isopropyl thioxanthone, benzoin dimethylether, methyl methacrylate, ethylene glycol ether acetate, double pentaerythritol methacrylate again, temperature of reaction is controlled at below 70-80 DEG C, stirs 0.5-1 hour;
(3) finally add all the other remaining components, mix, stir, grind, obtain the slurry of 20-40 μ m, filter and get final product.
Dispersing auxiliary of the present invention has improved optical property, and paint is uniformly dispersed, and has maintained the stability of paint; Sag prevention of the present invention, film is abundant, and strong adhesion can fast setting, has greatly improved working efficiency.
Specific embodiments
Below by specific examples, the present invention is described in detail.
A kind of switching cabinet spraying priming paint, by following weight part (kilogram) raw material make: urethane acrylate 40, epoxy acrylate 23, titanium dioxide 3, water drain silica 2, cyanuric acid zinc 2, zinc oxide 3, alum powder 2, isopropyl thioxanthone 1, benzoin dimethylether 3, methyl methacrylate 1, ethylene glycol ether acetate 3, double pentaerythritol methacrylate 8, ethyl acetate 7, dispersing auxiliary 3;
Described dispersing auxiliary makes by the following method: the weight part of its each feed composition (kilogram) be: kaolin 300, clay 10, aluminium nitride 5, jade 1, N-2-(aminoethyl)-3-aminopropyl trimethoxysilane 1, linking agent TAC1, alum 8, trolamine 2, Flos Rosae Rugosae quintessence oil 1, tea-polyphenol 1; Preparation method adds kaolin, clay in 12-15% hydrochloric acid soln and soaks 3-4 hour, takes out, and cleans with clear water, calcines 3-4 hour with sending in calcining furnace at 530-550 DEG C, cooling, merges and grinds to form 300-400 order powder with jade; Adding N-2-(aminoethyl)-3-aminopropyl trimethoxysilane, linking agent TAC, alum continue grinding distribution 2-3 hour, then add other remaining component to be ground to fully to disperse to obtain 300-400 order powder, to obtain final product.
Switching cabinet spraying priming paint of the present invention, made by following concrete steps:
(1) urethane acrylate, epoxy acrylate, titanium dioxide, water drain silica, cyanuric acid zinc, zinc oxide, alum powder are added in reactor and stirred, temperature of reaction is controlled at below 40-60 DEG C, stirs 0.5-1 hour;
(2) in reactor, add isopropyl thioxanthone, benzoin dimethylether, methyl methacrylate, ethylene glycol ether acetate, double pentaerythritol methacrylate again, temperature of reaction is controlled at below 70-80 DEG C, stirs 0.5-1 hour;
(3) finally add all the other remaining components, mix, stir, grind, obtain the slurry of 20-40 μ m, filter and get final product.
Product performance index of the present invention:
1, snappiness mm≤1
2, hardness >=2H
3, high temperature resistant (130 DEG C) >=490h
4, shock-resistance 50
5, salt spray resistance (120h level) >=3
6, water tolerance (29 ± 1 DEG C of 240h): non-foaming, do not come off
7, oil resistant (90# gasoline, 56h): non-foaming, do not come off
8, alkali resistance (GB/T9755-2001): by 48 hours
9, artificial weathering ageing resistance (GB/T9755-2001): by 1200 hours.
Claims (2)
1. a switching cabinet spraying priming paint, it is characterized in that, made by the raw material of following weight part: urethane acrylate 40-45, epoxy acrylate 23-28, titanium dioxide 3-4, water drain silica 2-3, cyanuric acid zinc 2-3, zinc oxide 3-4, alum powder 2-3, isopropyl thioxanthone 1-2, benzoin dimethylether 3-4, methyl methacrylate 1-2, ethylene glycol ether acetate 3-5, double pentaerythritol methacrylate 8-10, ethyl acetate 7-9, dispersing auxiliary 3-4;
Described dispersing auxiliary makes by the following method: the weight part of its each feed composition is: kaolin 300-310, clay 10-12, aluminium nitride 5-6, jade 1-2, N-2-(aminoethyl)-3-aminopropyl trimethoxysilane 1-2, linking agent TAC1-2, alum 8-10, trolamine 2-3, Flos Rosae Rugosae quintessence oil 1-2, tea-polyphenol 1-2; Preparation method adds kaolin, clay in 12-15% hydrochloric acid soln and soaks 3-4 hour, takes out, and cleans with clear water, calcines 3-4 hour with sending in calcining furnace at 530-550 DEG C, cooling, merges and grinds to form 300-400 order powder with jade; Adding N-2-(aminoethyl)-3-aminopropyl trimethoxysilane, linking agent TAC, alum continue grinding distribution 2-3 hour, then add other remaining component to be ground to fully to disperse to obtain 300-400 order powder, to obtain final product.
2. switching cabinet sprays priming paint according to claim 1, it is characterized in that, is made up of following concrete steps:
(1) urethane acrylate, epoxy acrylate, titanium dioxide, water drain silica, cyanuric acid zinc, zinc oxide, alum powder are added in reactor and stirred, temperature of reaction is controlled at below 40-60 DEG C, stirs 0.5-1 hour;
(2) in reactor, add isopropyl thioxanthone, benzoin dimethylether, methyl methacrylate, ethylene glycol ether acetate, double pentaerythritol methacrylate again, temperature of reaction is controlled at below 70-80 DEG C, stirs 0.5-1 hour;
(3) finally add all the other remaining components, mix, stir, grind, obtain the slurry of 20-40 μ m, filter and get final product.