Electrode material internal resistance method of testing
Technical field
The present invention relates to a kind of electrode material internal resistance method of testing.
Background technology
The internal resistance of battery is one of of paramount importance characterisitic parameter of battery, and it is the important parameter of characterizing battery life-span and battery operation state, is the outstanding feature that measurement electronics and ion transmit complexity in electrode.The accurate detection internal resistance of cell particularly ohmic internal resistance is also the objective requirement of battery management and practical application.
Present stage only tests the monitoring of the internal resistance of cell after cell package completes, and for causing batch bad situation of the property internal resistance of cell because electrode material is abnormal, now battery has completed the assembling process of product, and loss has caused, and cannot retrieve.Find after deliberation, after project organization sizing, the size of core component electrode material self internal resistance is depended in the internal resistance of battery to a great extent, by the internal resistance of monitoring electrode material self, judge starting material quality, the situation that can predict the internal resistance of cell after putting into production, notes abnormalities early, reduces the loss.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of method that can the internal resistance of Validity Test electrode material, so that can before cell package completes, predict the situation of the internal resistance of cell, or raw-material internal resistance situation is done to a judge.
The technical solution adopted for the present invention to solve the technical problems is: a kind of electrode material internal resistance method of testing, comprises the steps: electrode material and auxiliary material that a, preparation will be tested; B, electrode material and auxiliary material are put into stirring machine stir into slurry; C, take out slurry and put into baking oven and dry, make powder; D, some part that powder is divided into equivalent are pressed into respectively flaky material in sheeter; E, be evenly coated with and spread silver powder in each flaky material both sides; F, the flaky material of respectively smearing silver powder is put into baking oven, dry the organic solvent in silver powder; G, each flaky material both sides after the oven dry copper conductor of respectively burn-oning; H, the resistance value of directly reading each flaky material with resistance tester by described copper conductor; I, calculating mean value are electrode material internal resistance value.
In described steps d, need use same sheeter when pressed powder moulding, powder weight, forming pressure, time need consistent.
It is corresponding that the silver powder of described each flaky material both sides is smeared position, and need smear with same mould.
The length of described all wires is consistent.
Described flaky material is coin shapes.
Described resistance tester is universal meter.
Beneficial effect: the invention solves the defect existing in background technology, can before cell package completes, measure electrode material internal resistance and have or not extremely, thereby prediction cell package complete after the situation of the internal resistance of cell, note abnormalities early, reduce the loss.Also can be used as electrode starting material detection method, whether unanimously detect starting material batch property simultaneously.
Embodiment
A kind of electrode material internal resistance method of testing, comprises the steps: electrode material and auxiliary material that a, preparation will be tested; B, electrode material and auxiliary material are put into stirring machine stir into slurry; C, take out slurry and put into baking oven and dry, make powder; D, some part that powder is divided into equivalent are pressed into respectively coin-shaped flaky material in sheeter; E, be evenly coated with and spread silver powder in each flaky material both sides; F, the flaky material of respectively smearing silver powder is put into baking oven, dry the organic solvent in silver powder; G, each flaky material both sides after the oven dry copper conductor of respectively burn-oning; H, the resistance value of directly reading each flaky material with universal meter by described copper conductor; The mean value of i, all effective resistance values of calculating gained, is electrode material internal resistance value.
In order to ensure the accuracy of test, in steps d, need use same sheeter when pressed powder moulding, powder weight, forming pressure, time need unanimously.The silver powder of each flaky material both sides is smeared position need be corresponding, and need smear with same mould.The length of all wires needs consistent.
Should be appreciated that specific embodiment described above, only for explaining the present invention, is not intended to limit the present invention.The apparent variation of being extended out by spirit of the present invention or variation are still among protection scope of the present invention.