CN103952041A - Method for preparing antiseptic and mildew-proof water-based latex paint - Google Patents
Method for preparing antiseptic and mildew-proof water-based latex paint Download PDFInfo
- Publication number
- CN103952041A CN103952041A CN201410181836.6A CN201410181836A CN103952041A CN 103952041 A CN103952041 A CN 103952041A CN 201410181836 A CN201410181836 A CN 201410181836A CN 103952041 A CN103952041 A CN 103952041A
- Authority
- CN
- China
- Prior art keywords
- latex paint
- mildew
- agent
- fungus
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing an antiseptic and mildew-proof water-based latex paint, which is safe and environment-friendly, convenient to construct and quick to dry. According to the technical scheme, the method for preparing the antiseptic and mildew-proof water-based latex paint comprises the following operation steps: feeding the weighed titanium dioxide, talcum powder, kaoline, triple superphosphate and aluminum silicate to a disperse barrel according to the components; adding a proper amount of water, dispersing and stirring at a low speed; adding a styrene-acrylic emulsion, a biocide mildewcide and various assistants for paint mixing; dispersing the mixed solution prepared in the previous steps at a high speed; grinding and filtering the mixed solution obtained in the previous steps, so as to prepare the antiseptic and mildew-proof water-based latex paint product. The method can be used to produce the antiseptic and mildew-proof water-based latex paint which is environment-friendly, convenient to construct, quick to dry and good in using effect.
Description
Technical field
The present invention relates to water-miscible paint preparing technical field, relate in particular to a kind of preparation method of fungus and mildew resistance aqueous latex paint.
Background technology
Basic substance determines superstructure, and along with the raising of people's living standard, people's thought is also improving constantly, changing, and home environment is no longer object with " as long as expensive, not right ".A kind of environmental protection, healthy comfortable living environment are pursued by increasing family.Especially in house decoration, embodied significantly.
Summary of the invention
The object of this invention is to provide a kind of safety and environmental protection, easy construction, the dry preparation method of fungus and mildew resistance aqueous latex paint rapidly.
To achieve these goals, technical scheme of the present invention is achieved in that a kind of preparation method of fungus and mildew resistance aqueous latex paint, and its composition component and preparation manipulation step are as follows:
Title component
Titanium dioxide 15-25 part
Talcum powder 7-9 part
Kaolin 5-8 part
Coarse whiting 10-15 part
Pure aluminium silicate 1.5-2 part
Benzene emulsion 12-15 part
Biocide mildewcide 0.2-0.3 part
Other auxiliary agents 5-10 part
Water 15-50 part
1, according to above-mentioned components by weight percent, load weighted titanium dioxide, talcum powder, kaolin, coarse whiting, pure aluminium silicate are dropped into and disperse, in bucket, to add the water of formula ratio, with 350～800r/min low speed, disperse to stir 15～25min;
2, add again benzene emulsion, biocide mildewcide and various auxiliary agent to carry out paint;
3, the mixed solution described step 1,2 being made is with 1200～1500r/min high speed dispersion 20min～30min;
4, mixed solution above-mentioned steps 3 being obtained grinds, filters, and makes fungus and mildew resistance aqueous latex paint finished product.
Further, the auxiliary agent adding in step 2 comprises defoamer, wetting agent, fluorescent whitening agent VBL, ultramarine, titanium dioxide, Natvosol, flow agent, dispersion agent, Lauryl Alcohol ester, ethylene glycol.
Further, described auxiliary agent is aqueous promoter.
Further, kaolin particle degree is 4000 orders.
The present invention has following beneficial effect: enforcement of the present invention can provide a kind of environmental protection, easy construction, be dried the fungus and mildew resistance aqueous latex paint rapid, result of use is good.
Embodiment
The preparation method of a kind of fungus and mildew resistance aqueous latex paint of the present embodiment, its composition component and preparation manipulation step are as follows:
Embodiment 1
25 parts of titanium dioxides
9 parts of talcum powder
8 parts of kaolin
15 parts of coarse whitings
2 parts of pure aluminium silicate
15 parts of benzene emulsions
0.3 part of biocide mildewcide
911 0.8 parts of defoamers
0.1 part of wetting agent
0.7 part of fluorescent whitening agent VBL
0.9 part of thickening material
2.1 parts of Natvosols
1.5 parts of Lauryl Alcohol esters
1.5 parts of ethylene glycol
0.5 part of HT-612 flow agent
1 part, ultramarine
0.6 part of dispersion agent
0.3 part of HT-95 multifunctional assistant
15.7 parts, water
1, according to said components, load weighted titanium dioxide, talcum powder, kaolin, coarse whiting, pure aluminium silicate are dropped into and disperse, in bucket, to add the water of 15.7 parts, with 350～600r/min low speed, disperse to stir 20min;
2, add again benzene emulsion, biocide mildewcide and aqueous promoter: defoamer, wetting agent, Lauryl Alcohol ester, Natvosol, flow agent, dispersion agent, membrane-forming agent, ethylene glycol carry out paint, fluorescent whitening agent VBL, ultramarine, titanium dioxide;
3, the mixed solution described step 1,2 being made is with 1200～1500r/min high speed dispersion 30min;
4, mixed solution above-mentioned steps 3 being obtained grinds, filters, and makes fungus and mildew resistance aqueous latex paint finished product.
Embodiment 2
17.5 parts of titanium dioxides
8 parts of talcum powder
6.5 parts of kaolin
12.5 parts of coarse whitings
1.75 parts of pure aluminium silicate
13.5 parts of benzene emulsions
0.25 part of biocide mildewcide
911 0.6 parts of defoamers
0.1 part of wetting agent
0.5 part of fluorescent whitening agent VBL
0.7 part of thickening material
1.5 parts of Natvosols
1 part of Lauryl Alcohol ester
1 part of ethylene glycol
0.3 part of HT-612 flow agent
0.9 part, ultramarine
0.6 part of dispersion agent
0.3 part of HT-95 multifunctional assistant
32.5 parts, water
1, according to said components, load weighted titanium dioxide, talcum powder, kaolin, coarse whiting, pure aluminium silicate are dropped into and disperse, in bucket, to add the water of 32.5 parts, with 350 ~ 800r/min low speed, disperse to stir 20min;
2, add again benzene emulsion, biocide mildewcide and aqueous promoter: defoamer, wetting agent, Lauryl Alcohol ester, Natvosol, flow agent, dispersion agent, membrane-forming agent, ethylene glycol carry out paint, fluorescent whitening agent VBL, ultramarine, titanium dioxide;
3, the mixed solution described step 1,2 being made is with 1200～1500r/min high speed dispersion 25min;
4, mixed solution above-mentioned steps 3 being obtained grinds, filters, and makes fungus and mildew resistance aqueous latex paint finished product.
Embodiment 3
15 parts of titanium dioxides
7 parts of talcum powder
5 parts of kaolin
10 parts of coarse whitings
1.5 parts of pure aluminium silicate
12 parts of benzene emulsions
0.2 part of biocide mildewcide
911 0.4 parts of defoamers
0.05 part of wetting agent
0.35 part of fluorescent whitening agent VBL
0.45 part of thickening material
1.05 parts of Natvosols
0.75 part of Lauryl Alcohol ester
0.75 part of ethylene glycol
0.25 part of HT-612 flow agent
0.5 part, ultramarine
0.3 part of dispersion agent
0.15 part of HT-95 multifunctional assistant
44.3 parts, water
1, according to said components, load weighted titanium dioxide, talcum powder, kaolin, coarse whiting, pure aluminium silicate are dropped into and disperse, in bucket, to add the water of 44.3 parts, with 350 ~ 800r/min low speed, disperse to stir 20min;
2, add again benzene emulsion, biocide mildewcide and aqueous promoter: defoamer, wetting agent, Lauryl Alcohol ester, Natvosol, flow agent, dispersion agent, membrane-forming agent, ethylene glycol carry out paint, fluorescent whitening agent VBL, ultramarine, titanium dioxide;
3, the mixed solution described step 1,2 being made is with 1200～1500r/min high speed dispersion 20min;
4, mixed solution above-mentioned steps 3 being obtained grinds, filters, and makes fungus and mildew resistance aqueous latex paint finished product.
Finally explanation is, above embodiment is only unrestricted in order to technical scheme of the present invention to be described, other modifications that those of ordinary skills make technical scheme of the present invention or be equal to replacement, only otherwise depart from the spirit and scope of technical solution of the present invention, all should be encompassed in the middle of claim scope of the present invention.
Claims (4)
1. a preparation method for fungus and mildew resistance aqueous latex paint, is characterized in that, its composition component and preparation manipulation step are as follows:
Title component
Titanium dioxide 15-25 part
Talcum powder 7-9 part
Kaolin 5-8 part
Coarse whiting 10-15 part
Pure aluminium silicate 1.5-2 part
Benzene emulsion 12-15 part
Biocide mildewcide 0.2-0.3 part
Other auxiliary agents 5-10 part
Water 15-50 part
(1) according to above-mentioned components by weight percent, load weighted titanium dioxide, talcum powder, kaolin, coarse whiting, pure aluminium silicate are dropped into and disperse, in bucket, to add the water of formula ratio, with 350～800r/min low speed, disperse to stir 15～25min;
(2) add again benzene emulsion, biocide mildewcide and various auxiliary agent to carry out paint;
(3) mixed solution described step (1), (2) being made is with 1200～1500r/min high speed dispersion 20min～30min;
(4) mixed solution above-mentioned steps (3) being obtained grinds, filters, and makes fungus and mildew resistance aqueous latex paint finished product.
2. the preparation method of a kind of fungus and mildew resistance aqueous latex paint according to claim 1, it is characterized in that, the auxiliary agent adding in step (2) comprises defoamer, wetting agent, fluorescent whitening agent VBL, ultramarine, titanium dioxide, Natvosol, flow agent, dispersion agent, Lauryl Alcohol ester, ethylene glycol.
3. the preparation method of a kind of fungus and mildew resistance aqueous latex paint according to claim 1 and 2, is characterized in that, described auxiliary agent is aqueous promoter.
4. the preparation method of a kind of fungus and mildew resistance aqueous latex paint according to claim 1, is characterized in that, kaolin particle degree is 4000 orders.