CN103951370B - 一种反射远红外线保温防火板及其制备方法 - Google Patents
一种反射远红外线保温防火板及其制备方法 Download PDFInfo
- Publication number
- CN103951370B CN103951370B CN201410121855.XA CN201410121855A CN103951370B CN 103951370 B CN103951370 B CN 103951370B CN 201410121855 A CN201410121855 A CN 201410121855A CN 103951370 B CN103951370 B CN 103951370B
- Authority
- CN
- China
- Prior art keywords
- add
- fire plate
- magnesium
- insulated fire
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种反射远红外线保温防火板,由下列重量份的原料制成:氧化镁100-120、石油磺酸钠1-2、活性白土10-15、聚磷酸铵3-5、硼酸锌3-5、硫酸镁10-15、无水氯化镁10-15、硫酸钙晶须3-5、糯米粉10-15、玻璃棉5-8、二氧化钛2-4、聚四氟乙烯微粉3-5、聚丙烯腈微球2-3、咖啡酸1-2、耐火材料25-30、二氧化锰3-5、α-Al2O3微粉3-5、松香酸钠1-2、甲酸钙1-2、纸浆废液10-13、水?120-140;本发明的保温防火板燃点高,阻燃效果好,隔热效果好,防火效果好;而且该板材还具有红外线反射性能,不仅保温效果好,而且有益人体健康。
Description
技术领域
本发明属于建筑材料领域,尤其涉及一种反射远红外线保温防火板及其制备方法。
背景技术
防火板又名耐火板,学名为热固性树脂浸渍纸高压层积板,是表面装饰用耐火建材,广泛用于室内装饰、家具、厨柜、实验室枱面、外墙等领域。
玻镁防火板具有耐高温、阻燃、吸声、防震、防虫、轻质防腐、无毒无味无污染、可直接上油漆、直接贴面,可用气钉、直接上瓷砖,表面有较好的着色性,强度高、耐弯曲有韧性、可钉、可锯、可粘,装修方便。还可以与多种保温材料复合制成复合保温板材。
目前的玻镁防火板还是存在保温性能不够好,不能达到国家节能环保的目标,而且存在强度和耐磨性不够高,防水性能不够好,使用寿命不够长的缺点,需要进一步提高板材的性能。
发明内容
本发明的目的在于提供一种反射远红外线保温防火板及其制备方法,该防火板具有燃点高、阻燃效果好、有益人体健康、抗菌、保温、自洁、防火性能好的特点,而且节约成本,减少了环境污染。
本发明的技术方案如下:
一种反射远红外线保温防火板,其特征在于由下列重量份的原料制成:氧化镁100-120、石油磺酸钠1-2、活性白土10-15、聚磷酸铵3-5、硼酸锌3-5、硫酸镁10-15、无水氯化镁10-15、硫酸钙晶须3-5、糯米粉10-15、玻璃棉5-8、二氧化钛2-4、聚四氟乙烯微粉3-5、聚丙烯腈微球2-3、咖啡酸1-2、耐火材料25-30、二氧化锰3-5、α-Al2O3微粉3-5、松香酸钠1-2、甲酸钙1-2、纸浆废液10-13、水120-140;
所述耐火材料由下列重量份的原料制成:轻质碳酸钙10-15、膨胀石墨5-10、硅酸铝纤维10-15、莫来石粉10-15、氧化锆4-6、硅线石粉4-7、硅溶胶12-16、三氧化二锑2-4、粉煤灰空心微珠10-20;制备方法为:将轻质碳酸钙、膨胀石墨、三氧化二锑、氧化锆、硅酸铝纤维、莫来石粉、硅线石粉、粉煤灰空心微珠混合,边搅拌边加入硅溶胶,分散研磨成颗粒,即得;
所述的反射远红外线保温防火板的制备方法,其特征在于包括以下步骤:
(1)、将氧化镁、耐火材料、活性白土、硫酸钙晶须、玻璃棉、二氧化钛、聚丙烯腈微球、二氧化锰混合,再加入混合物总质量30-40%的水搅拌均匀,再加入α-Al2O3微粉、松香酸钠、聚四氟乙烯微粉,搅拌20-30分钟,得到混合物;
(2)、将无水氯化镁、硫酸镁加入剩余水中,再加入石油磺酸钠、纸浆废液,搅拌均匀后加入第(1)步得到的混合物,搅拌20-30分钟,再加入其他剩余成分,在10000-12000转/分搅拌下加入二氧化碳气体,且每1000千克搅拌物中二氧化碳气体的加入量为2-3立方米;
(3)、将第(2)所得搅拌物放入板材模具中,在70-90℃下固化24-48小时后脱模,在室温下继续固化10-15天即得。
本发明的有益效果
本发明的反射远红外线保温防火板通过添加多种耐火材料,燃点高,阻燃效果好,而且添加了粉煤灰空心微珠,隔热效果好,防火效果好;而且该板材添加了硫酸钙晶须,增加了板材的强度、韧性、绝缘性、耐磨耗、耐高温、耐酸碱、抗腐蚀的性能,还具有红外线反射性能,不仅保温效果好,而且有益人体健康;该板材还具有良好的抗菌、保温、自洁、防火性能;通过使用纸浆废液,增加了发泡性能,节约了成本,减少了环境污染。
具体实施方式
一种反射远红外线保温防火板,由下列重量份(公斤)的原料制成:氧化镁110、石油磺酸钠1.5、活性白土13、聚磷酸铵4、硼酸锌4、硫酸镁13、无水氯化镁13、硫酸钙晶须4、糯米粉13、玻璃棉6、二氧化钛3、聚四氟乙烯微粉4、聚丙烯腈微球2.5、咖啡酸1.5、耐火材料27、二氧化锰4、α-Al2O3微粉4、松香酸钠1.5、甲酸钙1.5、纸浆废液12、水130;
所述耐火材料由下列重量份(公斤)的原料制成:轻质碳酸钙13、膨胀石墨7、硅酸铝纤维13、莫来石粉13、氧化锆5、硅线石粉6、硅溶胶14、三氧化二锑3、粉煤灰空心微珠15;制备方法为:将轻质碳酸钙、膨胀石墨、三氧化二锑、氧化锆、硅酸铝纤维、莫来石粉、硅线石粉、粉煤灰空心微珠混合,边搅拌边加入硅溶胶,分散研磨成3mm的颗粒,即得;
所述的反射远红外线保温防火板的制备方法,包括以下步骤:
(1)、将氧化镁、耐火材料、活性白土、硫酸钙晶须、玻璃棉、二氧化钛、聚丙烯腈微球、二氧化锰混合,再加入混合物总质量35%的水搅拌均匀,再加入α-Al2O3微粉、松香酸钠、聚四氟乙烯微粉,搅拌25分钟,得到混合物;
(2)、将无水氯化镁、硫酸镁加入剩余水中,再加入石油磺酸钠、纸浆废液,搅拌均匀后加入第(1)步得到的混合物,搅拌25分钟,再加入其他剩余成分,在11000转/分搅拌下加入二氧化碳气体,且每1000千克搅拌物中二氧化碳气体的加入量为2.5立方米;
(3)、将第(2)所得搅拌物放入板材模具中,在80℃下固化38小时后脱模,在室温下继续固化13天即得。
试验数据:
试验项目 | 试验数据 |
压缩强度(Mpa) | 10.28 |
垂直于版面方向的抗拉强度(MPa) | 9.26 |
导热系数(W/(MK)) | 0.025 |
燃烧性能级别,GB24-2006标准检验(级) | A1 |
吸水率(VOL)(%) | 5.3 |
从表中可以看出,该反射远红外线保温防火板强度、防火性能和保温性能都很优异,符合国家标准。
Claims (2)
1.一种反射远红外线保温防火板,其特征在于:由下列重量份的原料制成:氧化镁100-120、石油磺酸钠1-2、活性白土10-15、聚磷酸铵3-5、硼酸锌3-5、硫酸镁10-15、无水氯化镁10-15、硫酸钙晶须3-5、糯米粉10-15、玻璃棉5-8、二氧化钛2-4、聚四氟乙烯微粉3-5、聚丙烯腈微球2-3、咖啡酸1-2、耐火材料25-30、二氧化锰3-5、α-Al2O3微粉3-5、松香酸钠1-2、甲酸钙1-2、纸浆废液10-13、水120-140;所述耐火材料由下列重量份的原料制成:轻质碳酸钙10-15、膨胀石墨5-10、硅酸铝纤维10-15、莫来石粉10-15、氧化锆4-6、硅线石粉4-7、硅溶胶12-16、三氧化二锑2-4、粉煤灰空心微珠10-20;所述耐火材料的制备方法为:将轻质碳酸钙、膨胀石墨、三氧化二锑、氧化锆、硅酸铝纤维、莫来石粉、硅线石粉、粉煤灰空心微珠混合,边搅拌边加入硅溶胶,分散研磨成颗粒,即得。
2.根据权利要求1所述的反射远红外线保温防火板的制备方法,其特征在于包括以下步骤:
(1)、将氧化镁、耐火材料、活性白土、硫酸钙晶须、玻璃棉、二氧化钛、聚丙烯腈微球、二氧化锰混合,再加入混合物总质量30-40%的水搅拌均匀,再加入α-Al2O3微粉、松香酸钠、聚四氟乙烯微粉,搅拌20-30分钟,得到混合物;
(2)、将无水氯化镁、硫酸镁加入剩余水中,再加入石油磺酸钠、纸浆废液,搅拌均匀后加入第(1)步得到的混合物,搅拌20-30分钟,再加入其他剩余成分,在10000-12000转/分搅拌下加入二氧化碳气体,且每1000千克搅拌物中二氧化碳气体的加入量为2-3立方米;
(3)、将第(2)所得搅拌物放入板材模具中,在70-90℃下固化24-48小时后脱模,在室温下继续固化10-15天即得。