CN103951319A - 一种添加焙烧煤矸石的复合吸音板材料及其制备方法 - Google Patents
一种添加焙烧煤矸石的复合吸音板材料及其制备方法 Download PDFInfo
- Publication number
- CN103951319A CN103951319A CN201410157602.8A CN201410157602A CN103951319A CN 103951319 A CN103951319 A CN 103951319A CN 201410157602 A CN201410157602 A CN 201410157602A CN 103951319 A CN103951319 A CN 103951319A
- Authority
- CN
- China
- Prior art keywords
- parts
- plate material
- coal gangue
- composite sound
- absorbing plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种添加焙烧煤矸石的复合吸音板材料,由下列重量份的原料制成:焙烧煤矸石100-120、河砂35-40、蛭石粉45-50、膨胀珍珠岩15-25、坚果壳20-25、醋丙乳液78-83、环氧乙烯基树脂20-25、PVC树脂粉25-30、十溴二苯乙烷3-4、硬脂酸1-2、甘油三醋酸酯5-7、助剂2-3;本发明焙烧煤矸石,质轻、孔隙大、来源广泛、防腐防潮;添加河沙、蛭石粉等,是板材料坚韧耐磨;添加坚果壳等天然植物纤维,增加材料的韧性,增加了吸收噪声的效果;而且本发明吸声频带宽,吸声系数高、抗压强度大,且防火、无毒性。
Description
技术领域
本发明涉及一种吸音板材料,具体涉及一种添加焙烧煤矸石的复合吸音板材料及其制备方法。
背景技术
随着工业生产、交通运输、城市建筑的发展,以及人口密度的增加,家庭设施(音响、空调、电视机等)的增多,环境噪声日益严重,它已成为污染人类社会环境的一大公害。一般人在日常生活中都会有机会暴露在各种不同程度的噪音中,可能发生各种不同程度的听力丧失,噪音也会影响心脏血管的健康,睡眠的品质,甚至胎儿的发育。
吸音板是指板状的具有吸音减噪作用的材料,主要应用于影剧院、音乐厅、博物馆、展览馆、图书馆、审讯室、画廊、拍卖厅、体育馆、报告厅、多功能厅、酒店大堂、医院、商场、学校、琴房、会议室、演播室、录音室、KTV 包房、酒吧、工业厂房、机房、家庭降噪等对声学环境要求较高及高档装修的场所。现有吸音板材料也有复合型的,但是无机物料与有机物料复合的性能指标优异的较少。因此,目前急需研究开发一种具有防潮阻燃、柔韧质轻、透气性好、能循环利用、无毒无害、吸音效果好并且制造成本低等优点的新型吸音板材料。
发明内容
本发明的目的在于,提供一种添加焙烧煤矸石的复合吸音板材料,使其施工方便、吸音隔噪,为了实现上述目的,本发明采用的技术方案如下:
一种添加焙烧煤矸石的复合吸音板材料,由下列重量份的原料制成:焙烧煤矸石100-120、河砂35-40、蛭石粉45-50、膨胀珍珠岩15-25、坚果壳20-25、醋丙乳液78-83、环氧乙烯基树脂20-25、PVC树脂粉25-30、十溴二苯乙烷3-4、硬脂酸1-2、甘油三醋酸酯5-7、助剂2-3;
所述的助剂由以下重量份的原料制成:亚麻全株8-10、椰子壳10-12、栗子壳5-7;制备方法是将亚麻全株切成2-3厘米的小段与椰子壳、栗子壳混合均匀,用球磨机磨成250-300目粉末;然后加入1%-2%磷酸溶液,搅拌均匀,浸泡30-40分钟;再加入1%-2%碳酸钠溶液中,搅拌20-30分钟,然后过滤取出;用去离子水反复清洗3-4次,烘干后再粉碎成细粉即得。
本发明所述的一种添加焙烧煤矸石的复合吸音板材料,由以下方法制得:
(1)将坚果壳送入炭化炉中,在530-620℃下炭化处理3-4小时,取出,粉碎成粉末;
(2)将步骤(1)物料加入到搅拌混合机中,再加入焙烧煤矸石、河砂、蛭石粉、膨胀珍珠岩、助剂高速混合搅拌均匀3-4分钟得到混合粉末;
(3)将环氧乙烯基树脂、PVC树脂粉、十溴二苯乙烷、硬脂酸、甘油三醋酸酯混合,边搅拌边加热,初混3-4分钟,然后进入高速混合机中加入步骤(2)混合粉末以及其余剩余成分,在110-120℃下以1600-1800转/分钟的速度搅拌3-5min,物料冷却至常温待用;
(4)将冷却过的物料加入双螺杆混合挤出机中进行处理,然后将挤出的物料投入造粒机造粒,即得吸音板材料。
本发明的有益效果在于:本发明焙烧煤矸石,质轻、孔隙大、来源广泛、防腐防潮;添加河沙、蛭石粉等,是板材料坚韧耐磨;添加坚果壳等天然植物纤维,增加材料的韧性,增加了吸收噪声的效果;而且本发明吸声频带宽,吸声系数高、抗压强度大,且防火、无毒性。
具体实施方式
一种添加焙烧煤矸石的复合吸音板材料,由下列重量份(公斤)的原料制成:焙烧煤矸石100、河砂35、蛭石粉45、膨胀珍珠岩15、坚果壳20、醋丙乳液78、环氧乙烯基树脂20、PVC树脂粉25、十溴二苯乙烷3、硬脂酸1、甘油三醋酸酯5、助剂2;
所述的助剂由以下重量份(公斤)的原料制成:亚麻全株8、椰子壳10、栗子壳5;制备方法是将亚麻全株切成2-3厘米的小段与椰子壳、栗子壳混合均匀,用球磨机磨成250-300目粉末;然后加入1%-2%磷酸溶液,搅拌均匀,浸泡30-40分钟;再加入1%-2%碳酸钠溶液中,搅拌20-30分钟,然后过滤取出;用去离子水反复清洗3-4次,烘干后再粉碎成细粉即得。
本发明所述的一种添加焙烧煤矸石的复合吸音板材料,由以下方法制得:
(1)将坚果壳送入炭化炉中,在530-620℃下炭化处理3-4小时,取出,粉碎成粉末;
(2)将步骤(1)物料加入到搅拌混合机中,再加入焙烧煤矸石、河砂、蛭石粉、膨胀珍珠岩、助剂高速混合搅拌均匀3-4分钟得到混合粉末;
(3)将环氧乙烯基树脂、PVC树脂粉、十溴二苯乙烷、硬脂酸、甘油三醋酸酯混合,边搅拌边加热,初混3-4分钟,然后进入高速混合机中加入步骤(2)混合粉末以及其余剩余成分,在110-120℃下以1600-1800转/分钟的速度搅拌3-5min,物料冷却至常温待用;
(4)将冷却过的物料加入双螺杆混合挤出机中进行处理,然后将挤出的物料投入造粒机造粒,即得吸音板材料。
本发明吸音板材料的性能测试结果为:吸声系数0.81-1.07。
Claims (2)
1.一种添加焙烧煤矸石的复合吸音板材料,由下列重量份的原料制成:焙烧煤矸石100-120、河砂35-40、蛭石粉45-50、膨胀珍珠岩15-25、坚果壳20-25、醋丙乳液78-83、环氧乙烯基树脂20-25、PVC树脂粉25-30、十溴二苯乙烷3-4、硬脂酸1-2、甘油三醋酸酯5-7、助剂2-3;
所述的助剂由以下重量份的原料制成:亚麻全株8-10、椰子壳10-12、栗子壳5-7;制备方法是将亚麻全株切成2-3厘米的小段与椰子壳、栗子壳混合均匀,用球磨机磨成250-300目粉末;然后加入1%-2%磷酸溶液,搅拌均匀,浸泡30-40分钟;再加入1%-2%碳酸钠溶液中,搅拌20-30分钟,然后过滤取出;用去离子水反复清洗3-4次,烘干后再粉碎成细粉即得。
2.如权利要求1所述的一种添加焙烧煤矸石的复合吸音板材料,其特征在于,由以下方法制得:
(1)将坚果壳送入炭化炉中,在530-620℃下炭化处理3-4小时,取出,粉碎成粉末;
(2)将步骤(1)物料加入到搅拌混合机中,再加入焙烧煤矸石、河砂、蛭石粉、膨胀珍珠岩、助剂高速混合搅拌均匀3-4分钟得到混合粉末;
(3)将环氧乙烯基树脂、PVC树脂粉、十溴二苯乙烷、硬脂酸、甘油三醋酸酯混合,边搅拌边加热,初混3-4分钟,然后进入高速混合机中加入步骤(2)混合粉末以及其余剩余成分,在110-120℃下以1600-1800转/分钟的速度搅拌3-5min,物料冷却至常温待用;
(4)将冷却过的物料加入双螺杆混合挤出机中进行处理,然后将挤出的物料投入造粒机造粒,即得吸音板材料。