CN103937376A - 防腐蚀性涂料及其制备方法 - Google Patents
防腐蚀性涂料及其制备方法 Download PDFInfo
- Publication number
- CN103937376A CN103937376A CN201410107297.1A CN201410107297A CN103937376A CN 103937376 A CN103937376 A CN 103937376A CN 201410107297 A CN201410107297 A CN 201410107297A CN 103937376 A CN103937376 A CN 103937376A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- bisphenol
- component
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种防腐蚀性涂料,由下列重量份的原料制成:双酚A环氧树脂36-40、双酚F环氧树脂10-15、芳香胺8-12、丁氧基甲基环氧乙烷9-13、脂肪醇2-3、氯醋树脂16-20、茶树精油1-2、苯甲醇7-9、乙酸乙酯7-9、1,6-已二醇二缩水甘油醚8-10、甲酸钙3-5、缩水甘油醚氧丙基三甲氧基硅烷1-3、醋酸正丁酯4-6、聚醚改性聚硅氧烷0.1-0.3、聚酯树脂1-3、附着助剂4-6;本发明涂料通过氯醋树脂和环氧树脂为基料,形成互穿网络赋予涂层致密性,大大增加了其防腐性能和附着力,通过使用茶树精油和甲酸钙,增加了防腐防霉效果,能保持长时间的不起泡、不生锈、不褪色、不长霉斑、不脱落;而且该涂料对各种材质均有良好的附着性能,漆膜平整,外观靓丽。
Description
技术领域
本发明属于涂料领域,尤其涉及防腐蚀性涂料及其制备方法。
背景技术
现在涂料的使用领域很多,由于经常暴露在大气之中,受到氧气、水分等的侵蚀,容易造成金属锈蚀、木材腐朽、水泥风化等现象,随着人们生活水平的提高,对涂料各方面的要求都有所提高,尤其是对涂料的硬度、耐磨性、丰满度、耐冲击性、耐老化性、防腐、防水、防油、耐化学品、耐光、耐温等性能等方面的要求越来越高,因此需要研究更加进步的涂料以满足人们的需要。
发明内容
本发明的目的在于提供防腐蚀性涂料及其制备方法,该涂料能保持长时间的不起泡、不生锈、不褪色、不长霉斑、不脱落;而且对各种材质均有良好的附着性能,漆膜平整,外观靓丽。
本发明的技术方案如下:
一种防腐蚀性涂料,其特征在于由下列重量份的原料制成:双酚A环氧树脂36-40、双酚F环氧树脂10-15、芳香胺8-12、丁氧基甲基环氧乙烷9-13、脂肪醇2-3、氯醋树脂16-20、茶树精油1-2、苯甲醇7-9、乙酸乙酯7-9、1,6-已二醇二缩水甘油醚8-10、甲酸钙3-5、缩水甘油醚氧丙基三甲氧基硅烷 1-3、醋酸正丁酯4-6、聚醚改性聚硅氧烷0.1-0.3、聚酯树脂1-3、附着助剂4-6;
所述附着助剂由下列重量份的原料制成:烯丙基硫脲 0.2-0.3、硅烷偶联剂KH5500.4-0.6、丙烯酸丁酯3-5、1,6-己二醇二丙烯酸酯4-7、聚氨酯树脂6-8、氯化聚丙烯树脂7-9、没食子酸丙酯2-3、三聚磷酸钠2-3、过氧化二异丙苯0.1-0.2、丙烯酸异辛酯5-7、乙酸乙酯10-15、正丁醇10-15、亚麻油1-2、乳母果油1-2、琥珀酸0.2-0.3;制作方法为:将乙酸乙酯、正丁醇、亚麻油、乳母果油混合,在3000-4000转/分下加入聚氨酯树脂、氯化聚丙烯树脂,溶解后再加入丙烯酸丁酯、1,6-己二醇二丙烯酸酯,搅拌20-30分钟,加入其他剩余成分,加热至80-90℃,搅拌反应30-50分钟,即得。
所述的防腐蚀性涂料的制备方法,其特征在于包括以下步骤:
(1)制备 A 组份 :将双酚A环氧树脂、乙酸乙酯、苯甲醇、1,6-已二醇二缩水甘油醚、双酚F环氧树脂混合,在5000-7000转/分下搅拌20-30分钟,再加入氯醋树脂、聚酯树脂,继续搅拌1-2个小时,超声分散5-10分钟,制得A组份;
(2)制备 B 组份 :在密闭的搅拌器中,将芳香胺、脂肪醇、茶树精油混合,在4000-5000转/分下加入缩水甘油醚氧丙基三甲氧基硅烷,搅拌20-30分钟,制得B组份;
(3)将其他剩余成分混合均匀,加入A组份和B组份,搅拌均匀研磨成浆料即得。
本发明的有益效果
本发明涂料通过氯醋树脂和环氧树脂为基料,形成互穿网络赋予涂层致密性,大大增加了其防腐性能和附着力,通过使用茶树精油和甲酸钙,增加了防腐防霉效果,能保持长时间的不起泡、不生锈、不褪色、不长霉斑、不脱落;而且该涂料对各种材质均有良好的附着性能,漆膜平整,外观靓丽。
具体实施方式
一种防腐蚀性涂料,由下列重量份(公斤)的原料制成:双酚A环氧树脂38、双酚F环氧树脂13、芳香胺10、丁氧基甲基环氧乙烷10、脂肪醇2.5、氯醋树脂18、茶树精油1.5、苯甲醇8、乙酸乙酯8、1,6-已二醇二缩水甘油醚9、甲酸钙4、缩水甘油醚氧丙基三甲氧基硅烷 2、醋酸正丁酯5、聚醚改性聚硅氧烷0.2、聚酯树脂2、附着助剂5;
所述附着助剂由下列重量份(公斤)的原料制成:烯丙基硫脲 0.2、硅烷偶联剂KH5500.5、丙烯酸丁酯4、1,6-己二醇二丙烯酸酯5、聚氨酯树脂7、氯化聚丙烯树脂8、没食子酸丙酯2.5、三聚磷酸钠2.5、过氧化二异丙苯0.1、丙烯酸异辛酯6、乙酸乙酯13、正丁醇13、亚麻油1.5、乳母果油1.5、琥珀酸0.2;制作方法为:将乙酸乙酯、正丁醇、亚麻油、乳母果油混合,在3500转/分下加入聚氨酯树脂、氯化聚丙烯树脂,溶解后再加入丙烯酸丁酯、1,6-己二醇二丙烯酸酯,搅拌25分钟,加入其他剩余成分,加热至85℃,搅拌反应40分钟,即得。
所述的防腐蚀性涂料的制备方法,包括以下步骤:
(1)制备 A 组份 :将双酚A环氧树脂、乙酸乙酯、苯甲醇、1,6-已二醇二缩水甘油醚、双酚F环氧树脂混合,在6000转/分下搅拌25分钟,再加入氯醋树脂、聚酯树脂,继续搅拌1.5个小时,超声分散7分钟,制得A组份;
(2)制备 B 组份 :在密闭的搅拌器中,将芳香胺、脂肪醇、茶树精油混合,在4500转/分下加入缩水甘油醚氧丙基三甲氧基硅烷,搅拌25分钟,制得B组份;
(3)将其他剩余成分混合均匀,加入A组份和B组份,搅拌均匀研磨成浆料即得。
该涂料耐人工老化性3300小时,涂层在保持低光泽度和高耐磨性的前提下膜层厚度达到35微米以上,附着力为1 级,抗冲击强度≥50kg·cm,柔韧性为1mm。
Claims (2)
1.一种防腐蚀性涂料,其特征在于由下列重量份的原料制成:双酚A环氧树脂36-40、双酚F环氧树脂10-15、芳香胺8-12、丁氧基甲基环氧乙烷9-13、脂肪醇2-3、氯醋树脂16-20、茶树精油1-2、苯甲醇7-9、乙酸乙酯7-9、1,6-已二醇二缩水甘油醚8-10、甲酸钙3-5、缩水甘油醚氧丙基三甲氧基硅烷 1-3、醋酸正丁酯4-6、聚醚改性聚硅氧烷0.1-0.3、聚酯树脂1-3、附着助剂4-6;
所述附着助剂由下列重量份的原料制成:烯丙基硫脲 0.2-0.3、硅烷偶联剂KH5500.4-0.6、丙烯酸丁酯3-5、1,6-己二醇二丙烯酸酯4-7、聚氨酯树脂6-8、氯化聚丙烯树脂7-9、没食子酸丙酯2-3、三聚磷酸钠2-3、过氧化二异丙苯0.1-0.2、丙烯酸异辛酯5-7、乙酸乙酯10-15、正丁醇10-15、亚麻油1-2、乳母果油1-2、琥珀酸0.2-0.3;制作方法为:将乙酸乙酯、正丁醇、亚麻油、乳母果油混合,在3000-4000转/分下加入聚氨酯树脂、氯化聚丙烯树脂,溶解后再加入丙烯酸丁酯、1,6-己二醇二丙烯酸酯,搅拌20-30分钟,加入其他剩余成分,加热至80-90℃,搅拌反应30-50分钟,即得。
2.根据权利要求1所述的防腐蚀性涂料的制备方法,其特征在于包括以下步骤:
(1)制备 A 组份 :将双酚A环氧树脂、乙酸乙酯、苯甲醇、1,6-已二醇二缩水甘油醚、双酚F环氧树脂混合,在5000-7000转/分下搅拌20-30分钟,再加入氯醋树脂、聚酯树脂,继续搅拌1-2个小时,超声分散5-10分钟,制得A组份;
(2)制备 B 组份 :在密闭的搅拌器中,将芳香胺、脂肪醇、茶树精油混合,在4000-5000转/分下加入缩水甘油醚氧丙基三甲氧基硅烷,搅拌20-30分钟,制得B组份;
(3)将其他剩余成分混合均匀,加入A组份和B组份,搅拌均匀研磨成浆料即得。