CN103929840A - Production technology of stainless steel mineral heating cables - Google Patents
Production technology of stainless steel mineral heating cables Download PDFInfo
- Publication number
- CN103929840A CN103929840A CN201410154726.0A CN201410154726A CN103929840A CN 103929840 A CN103929840 A CN 103929840A CN 201410154726 A CN201410154726 A CN 201410154726A CN 103929840 A CN103929840 A CN 103929840A
- Authority
- CN
- China
- Prior art keywords
- rolling
- heating
- stainless steel
- production technology
- cooling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a production technology of stainless steel mineral heating cables. The technology includes the following steps of strap unwinding, washing, drying, pipe coiling, padding and wire resisting, automatic argon arc welding, vibrating, rolling, high-frequency heating, cooling, rolling, high-frequency heating, cooling, rolling (heating, cooling and rolling are repeated till the heating cable meets the size requirements), cable winding, cable unwinding, discharging, peeling, cold and hot wire connecting, joint welding, joint rolling and finished product detecting, and then the stainless steel mineral heating cables are formed. Through the production technology, different purposes of heating cables meeting various power requirements can be produced, and the production technology has the advantages that the heating cables can be produced continuously, the length of the heating cables is not limited, and the production technology is low in production cost, high in efficiency and suitable for large batch production. The speed of welding the stainless steel heating cables reaches 1.5 m/min to 5m/min, and the product finishing speed reaches 20 m/min to 30 m/min.
Description
Technical field
The present invention relates to electrothermal tube and cable processing technique field, refer in particular to a kind of production technology of stainless steel mineral matter heating cable.
Background technology
Stainless steel mineral matter heating cable, taking electric power as the energy, utilizes resistance wire to carry out heating power, and the variation of the working temperature of cable surface adopts thermostat setting, reaches best result of use.
Stainless steel heating cable, resistance silk is contained in the center of seamless stainless-steel pipe, insulate by height, high heat radiation, resistant to elevated temperatures mineral material reaches heating in vacuum, magnetic field radiation after cable energising is shielded completely, to human body and object, without any infringement, its thermal conversion rate is high, and the coefficient of expansion is little, mechanical properties strength is high, has good anti-riot performance.
The processing technology of current stainless steel mineral matter heating cable is:---" rolling again---" annealing---" drawing after steel pipe--" adds powder inlet pipe---" and adds resistance wire to fit together---" annealing is until reach finished product caliber and the requirement of rice power, the method is because the restriction of steel pipe length, adopt and manually put tube cell, cannot carry out continuous production operation, process-cycle is long, production efficiency is low, and cost is high.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, the production technology of the mineral matter heating cable that a kind of speed of production is fast, efficiency is high, cost is low employing stainless steel band is raw material is provided.
For achieving the above object, technical scheme provided by the present invention is: the production technology of stainless steel mineral matter heating cable, described technique includes following steps: put band-cleaning-oven dry-pipe crimping-filler and resistance silk-argonaut welding-vibrations-rolling-high-frequency heating-cooling-rolling-high-frequency heating-cooling-rolling (Repeat-heating, cooling, rolling make heating cable reach dimensional requirement)-take-up-cable laying-blanking-peeling-cold and hot line connection-joint welding-joint rolling-finished product detection.
Described stainless steel band enters rolling machine by putting band machine, rinse bath, dryer, resistance wire and mineral matter are injected simultaneously, after moulding, weld, shake through over packing, enter roll mill, pass through again high-frequency heating and cooling system, after circulation rolling and annealing, reach finished size and rice power requirement.
Described finished product detection comprises high pressure, power, resistance, leakage current, mechanical strength, the joint waterproofing performance to cable.
The described needed special equipment of above-mentioned explained hereafter stainless steel mineral matter heating cable comprises rolling machine, filling machine, argon arc welding machine, high-frequency heating and cooling system, roll mill and corresponding control system; The said equipment all adopts the control of PLC panel, and every packet size adopts variable frequency control, reaches the object of automated job.
Technique of the present invention can be produced the heating cable of the various power requirements of different purposes, has continuous production, the unrestricted advantage of length, and production cost is low, and efficiency is high, is suitable for producing in enormous quantities.The speed of welding of stainless steel heating cable reaches 1.5～5 ms/min, and finished product speed reaches 20～30 ms/min.
Brief description of the drawings
Fig. 1 is process chart of the present invention.
Fig. 2 is production principle figure of the present invention.
Embodiment
Below in conjunction with institute's drawings attached, the invention will be further described, preferred embodiment of the present invention is: referring to accompanying drawing 1 and accompanying drawing 2, the production technology of the stainless steel mineral matter heating cable described in the present embodiment is: first, stainless steel band enters rolling machine by putting band machine, rinse bath, dryer, resistance wire and mineral matter are injected simultaneously, after moulding, weld, shake through over packing, enter roll mill, pass through again high-frequency heating and cooling system, after circulation rolling and annealing, reach finished size and rice power requirement.Above-mentioned technique specifically includes following steps: put band-cleaning-oven dry-pipe crimping-filler and resistance silk-argonaut welding-vibrations-rolling-high-frequency heating-cooling-rolling-high-frequency heating-cooling-rolling (Repeat-heating, cooling, synchronize with upper one group of roll mill speed, after rolling, in 2 seconds～12 seconds, be cooled to 20～30 degrees Celsius, make heating cable reach dimensional requirement)-take-up-cable laying-blanking-peeling, exactly by be connected with cold line/input power cord-joint of resistance line/hot line welding-joint rolling-finished product detection.Wherein, finished product detection, carries out according to International Power examination criteria, comprises the high pressure, power, resistance, leakage current, mechanical strength, joint waterproofing performance of cable etc.
The needed special equipment of above-mentioned explained hereafter stainless steel mineral matter heating cable comprises rolling machine, filling machine, argon arc welding machine, high-frequency heating and cooling system, roll mill and corresponding control system; The said equipment all adopts the control of PLC panel, and every packet size adopts variable frequency control, reaches the object of automated job.
The embodiment of the above is only the present invention's preferred embodiment, not limits practical range of the present invention with this, therefore the variation that all shapes according to the present invention, principle are done all should be encompassed in protection scope of the present invention.
Claims (4)
1. the production technology of stainless steel mineral matter heating cable, it is characterized in that: described technique includes following steps: put band-cleaning-oven dry-pipe crimping-filler and resistance silk-argonaut welding-vibrations-rolling-high-frequency heating-cooling-rolling-high-frequency heating-cooling-rolling (Repeat-heating, cooling, rolling make heating cable reach dimensional requirement)-take-up-cable laying-blanking-peeling-cold and hot line connection-joint welding-joint rolling-finished product detection.
2. the production technology of stainless steel mineral matter heating cable according to claim 1, it is characterized in that: stainless steel band enters rolling machine by putting band machine, rinse bath, dryer, resistance wire and mineral matter are injected simultaneously, after moulding, weld, through over packing vibrations, enter roll mill, then pass through high-frequency heating and cooling system, after circulation rolling and annealing, reach finished size and rice power requirement.
3. the production technology of stainless steel mineral matter heating cable according to claim 1, is characterized in that: finished product detection comprises high pressure, power, resistance, leakage current, mechanical strength, the joint waterproofing performance to cable.
4. the production technology of stainless steel mineral matter heating cable according to claim 1, is characterized in that: the needed special equipment of above-mentioned explained hereafter stainless steel mineral matter heating cable comprises rolling machine, filling machine, argon arc welding machine, high-frequency heating and cooling system, roll mill and corresponding control system; The said equipment all adopts the control of PLC panel, and every packet size adopts variable frequency control, reaches the object of automated job.